- 吸水率 [%]: 1.9
- 缺口冲击强度: 1.67
- 拉伸强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 1.40
- 硬度: 98.0
- 热变形温度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | Wet |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 98 | 98 | Wet; ASTM D785 |
| 114 | 114 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Wet; ASTM D638 |
| 70.0 MPa | 10200 psi | Dry; ASTM D638 | |
| Elongation at Break | 20 % | 20 % | Dry; ASTM D638 |
| 220 % | 220 % | Wet; ASTM D638 | |
| Flexural Strength | 49.0 MPa | 7110 psi | Wet; ASTM D790 |
| 98.0 MPa | 14200 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.40 GPa | 203 ksi | Wet; ASTM D790 |
| 2.50 GPa | 363 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.67 J/cm | 3.13 ft-lb/in | Dry; ASTM D256 |
| 12.0 J/cm | 22.5 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 7.0 | 7.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Dry; ASTM D648 |