- 缺口冲击强度: 0.427
- 弯曲模量 [MPa]: 6.55
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 126 MPa | 18300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 6.55 GPa | 950 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.54 J/cm | 8.50 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
| Moisture Content | 0.080 - 0.12 % | 0.080 - 0.12 % | |