- 热变形温度 [℃]: 205.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.014 cm/cm @Thickness 3.175 mm | 0.0040 - 0.014 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D638 |
| Tensile Modulus | 4.299 GPa | 623.5 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 295 - 305 °C | 563 - 581 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |