- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 14.0
- 弯曲强度 [MPa]: 86.0
- 弯曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | dry; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 4.00 GPa | 580 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 8.30 J/cm² | 39.5 ft-lb/in² | ISO 179 | ||
| 8.10 J/cm² @Temperature -30.0 °C | 38.5 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 | ||
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||