- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 4.2
- 弯曲模量 [MPa]: 9.80
- 热变形温度 [℃]: 255.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527 | ||
| Flexural Modulus | 9.80 GPa | 1420 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 0.380 J/cm² @Temperature 23.0 °C | 1.81 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 288 - 305 °C | 550 - 581 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| Descriptive Properties | |||||
| Color | BK ND 3007 | ||||
| Commercial Status | North America | ||||