- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 6.4
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.4 % | 6.4 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/-2 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527-1/-2 | ||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.70 J/cm² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| High impact or impact modified | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release agent | Yes | ||||
| With fillers | Yes | ||||