塑胶原料之家
  1. 首页
  2. 英文物性
  3. PA66
  4. DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66

DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66

DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66 物性表: DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 吸水率 [%]: 1.8
  • 缺口冲击强度: 0.59
  • 弯曲模量 [MPa]: 5.24
  • 硬度: 120.0
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.48 g/cc1.48 g/ccDAM; ASTM D792
Density 1.45 g/cc0.0524 lb/in³DAM; ISO 1183
Filler Content 40 %40 %DAM
Water Absorption  1.8 %
@Temperature 23.0 °C		1.8 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 5.7 %
@Temperature 23.0 °C		5.7 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Viscosity  51000 cP
@Shear Rate 7000 1/s,
Temperature 315 °C		51000 cP
@Shear Rate 7000 1/s,
Temperature 599 °F		DAM; ISO 11443
 61000 cP
@Shear Rate 5000 1/s,
Temperature 315 °C		61000 cP
@Shear Rate 5000 1/s,
Temperature 599 °F		DAM; ISO 11443
 79000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		79000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		DAM; ISO 11443
 87000 cP
@Shear Rate 2000 1/s,
Temperature 315 °C		87000 cP
@Shear Rate 2000 1/s,
Temperature 599 °F		DAM; ISO 11443
 97000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		97000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		DAM; ISO 11443
 105000 cP
@Shear Rate 1000 1/s,
Temperature 315 °C		105000 cP
@Shear Rate 1000 1/s,
Temperature 599 °F		DAM; ISO 11443
 113000 cP
@Shear Rate 700 1/s,
Temperature 315 °C		113000 cP
@Shear Rate 700 1/s,
Temperature 599 °F		DAM; ISO 11443
 118000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		118000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		DAM; ISO 11443
 119000 cP
@Shear Rate 500 1/s,
Temperature 315 °C		119000 cP
@Shear Rate 500 1/s,
Temperature 599 °F		DAM; ISO 11443
 149000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		149000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		DAM; ISO 11443
 156000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		156000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		DAM; ISO 11443
 202000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		202000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		DAM; ISO 11443
 225000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		225000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		DAM; ISO 11443
 244000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		244000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		DAM; ISO 11443
 264000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		264000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		DAM; ISO 11443
 374000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		374000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		DAM; ISO 11443
 434000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		434000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		DAM; ISO 11443
 490000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		490000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		DAM; ISO 11443
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 8686DAM; ISO 2039/2
Hardness, Rockwell R 120120DAM; ISO 2039/2
Tensile Strength at Break  60.0 MPa
@Temperature 23.0 °C		8700 psi
@Temperature 73.4 °F		50%RH; ISO 527
 89.0 MPa
@Temperature 23.0 °C		12900 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  15.0 MPa
@Strain 3.64 %,
Temperature 120 °C		2180 psi
@Strain 3.64 %,
Temperature 248 °F		50%RH; ISO 527
 16.0 MPa
@Strain 3.03 %,
Temperature 90.0 °C		2320 psi
@Strain 3.03 %,
Temperature 194 °F		50%RH; ISO 527
 18.0 MPa
@Strain 4.35 %,
Temperature 120 °C		2610 psi
@Strain 4.35 %,
Temperature 248 °F		DAM; ISO 527
 20.0 MPa
@Strain 3.36 %,
Temperature 90.0 °C		2900 psi
@Strain 3.36 %,
Temperature 194 °F		DAM; ISO 527
 21.1 MPa
@Strain 3.00 %,
Temperature 60.0 °C		3060 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 527
 24.6 MPa
@Strain 7.28 %,
Temperature 120 °C		3570 psi
@Strain 7.28 %,
Temperature 248 °F		50%RH; ISO 527
 25.0 MPa
@Strain 3.03 %,
Temperature 40.0 °C		3630 psi
@Strain 3.03 %,
Temperature 104 °F		50%RH; ISO 527
 27.1 MPa
@Strain 0.350 %,
Temperature 23.0 °C		3930 psi
@Strain 0.350 %,
Temperature 73.4 °F		DAM; ISO 527
 27.3 MPa
@Strain 6.06 %,
Temperature 90.0 °C		3960 psi
@Strain 6.06 %,
Temperature 194 °F		50%RH; ISO 527
 28.0 MPa
@Strain 2.69 %,
Temperature 60.0 °C		4060 psi
@Strain 2.69 %,
Temperature 140 °F		DAM; ISO 527
 28.2 MPa
@Strain 10.9 %,
Temperature 120 °C		4090 psi
@Strain 10.9 %,
Temperature 248 °F		50%RH; ISO 527
 29.4 MPa
@Strain 8.70 %,
Temperature 120 °C		4260 psi
@Strain 8.70 %,
Temperature 248 °F		DAM; ISO 527
 29.7 MPa
@Strain 14.6 %,
Temperature 120 °C		4310 psi
@Strain 14.6 %,
Temperature 248 °F		50%RH; ISO 527
 30.0 MPa
@Strain 2.24 %,
Temperature 23.0 °C		4350 psi
@Strain 2.24 %,
Temperature 73.4 °F		50%RH; ISO 527
 30.5 MPa
@Strain 18.2 %,
Temperature 120 °C		4420 psi
@Strain 18.2 %,
Temperature 248 °F		50%RH; ISO 527
 31.0 MPa
@Strain 21.8 %,
Temperature 120 °C		4500 psi
@Strain 21.8 %,
Temperature 248 °F		50%RH; ISO 527
 31.2 MPa
@Strain 25.5 %,
Temperature 120 °C		4530 psi
@Strain 25.5 %,
Temperature 248 °F		50%RH; ISO 527
 31.2 MPa
@Strain 0.360 %,
Temperature 0.000 °C		4530 psi
@Strain 0.360 %,
Temperature 32.0 °F		DAM; ISO 527
 31.3 MPa
@Strain 29.1 %,
Temperature 120 °C		4540 psi
@Strain 29.1 %,
Temperature 248 °F		50%RH; ISO 527
 31.4 MPa
@Strain 32.8 %,
Temperature 120 °C		4550 psi
@Strain 32.8 %,
Temperature 248 °F		50%RH; ISO 527
 31.4 MPa
@Strain 36.4 %,
Temperature 120 °C		4550 psi
@Strain 36.4 %,
Temperature 248 °F		50%RH; Break; ISO 527
 32.3 MPa
@Strain 13.1 %,
Temperature 120 °C		4680 psi
@Strain 13.1 %,
Temperature 248 °F		DAM; ISO 527
 32.5 MPa
@Strain 9.09 %,
Temperature 90.0 °C		4710 psi
@Strain 9.09 %,
Temperature 194 °F		50%RH; ISO 527
 32.8 MPa
@Strain 6.00 %,
Temperature 60.0 °C		4760 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 527
 33.8 MPa
@Strain 0.360 %,
Temperature -20.0 °C		4900 psi
@Strain 0.360 %,
Temperature -4.00 °F		DAM; ISO 527
 34.0 MPa
@Strain 17.4 %,
Temperature 120 °C		4930 psi
@Strain 17.4 %,
Temperature 248 °F		DAM; ISO 527
 34.4 MPa
@Strain 6.72 %,
Temperature 90.0 °C		4990 psi
@Strain 6.72 %,
Temperature 194 °F		DAM; ISO 527
 35.0 MPa
@Strain 21.8 %,
Temperature 120 °C		5080 psi
@Strain 21.8 %,
Temperature 248 °F		DAM; ISO 527
 35.0 MPa
@Strain 12.1 %,
Temperature 90.0 °C		5080 psi
@Strain 12.1 %,
Temperature 194 °F		50%RH; ISO 527
 35.7 MPa
@Strain 26.1 %,
Temperature 120 °C		5180 psi
@Strain 26.1 %,
Temperature 248 °F		DAM; ISO 527
 35.9 MPa
@Strain 15.2 %,
Temperature 90.0 °C		5210 psi
@Strain 15.2 %,
Temperature 194 °F		50%RH; ISO 527
 36.1 MPa
@Strain 30.5 %,
Temperature 120 °C		5240 psi
@Strain 30.5 %,
Temperature 248 °F		DAM; ISO 527
 36.3 MPa
@Strain 18.2 %,
Temperature 90.0 °C		5260 psi
@Strain 18.2 %,
Temperature 194 °F		50%RH; ISO 527
 36.5 MPa
@Strain 34.8 %,
Temperature 120 °C		5290 psi
@Strain 34.8 %,
Temperature 248 °F		DAM; ISO 527
 36.6 MPa
@Strain 21.2 %,
Temperature 90.0 °C		5310 psi
@Strain 21.2 %,
Temperature 194 °F		50%RH; ISO 527
 36.8 MPa
@Strain 24.2 %,
Temperature 90.0 °C		5340 psi
@Strain 24.2 %,
Temperature 194 °F		50%RH; ISO 527
 36.9 MPa
@Strain 39.2 %,
Temperature 120 °C		5350 psi
@Strain 39.2 %,
Temperature 248 °F		DAM; ISO 527
 37.0 MPa
@Strain 1.26 %,
Temperature 40.0 °C		5370 psi
@Strain 1.26 %,
Temperature 104 °F		DAM; ISO 527
 37.1 MPa
@Strain 27.3 %,
Temperature 90.0 °C		5380 psi
@Strain 27.3 %,
Temperature 194 °F		50%RH; ISO 527
 37.2 MPa
@Strain 43.5 %,
Temperature 120 °C		5400 psi
@Strain 43.5 %,
Temperature 248 °F		DAM; Break; ISO 527
 37.3 MPa
@Strain 30.3 %,
Temperature 90.0 °C		5410 psi
@Strain 30.3 %,
Temperature 194 °F		50%RH; Break; ISO 527
 38.0 MPa
@Strain 9.00 %,
Temperature 60.0 °C		5510 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 527
 39.0 MPa
@Strain 10.1 %,
Temperature 90.0 °C		5660 psi
@Strain 10.1 %,
Temperature 194 °F		DAM; ISO 527
 40.3 MPa
@Strain 12.0 %,
Temperature 60.0 °C		5850 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 527
 40.7 MPa
@Strain 6.06 %,
Temperature 40.0 °C		5900 psi
@Strain 6.06 %,
Temperature 104 °F		50%RH; ISO 527
 40.8 MPa
@Strain 13.4 %,
Temperature 90.0 °C		5920 psi
@Strain 13.4 %,
Temperature 194 °F		DAM; ISO 527
 41.6 MPa
@Strain 16.8 %,
Temperature 90.0 °C		6030 psi
@Strain 16.8 %,
Temperature 194 °F		DAM; ISO 527
 42.0 MPa
@Strain 15.0 %,
Temperature 60.0 °C		6090 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 527
 42.3 MPa
@Strain 20.2 %,
Temperature 90.0 °C		6140 psi
@Strain 20.2 %,
Temperature 194 °F		DAM; ISO 527
 42.7 MPa
@Strain 18.0 %,
Temperature 60.0 °C		6190 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 527
 42.9 MPa
@Strain 23.5 %,
Temperature 90.0 °C		6220 psi
@Strain 23.5 %,
Temperature 194 °F		DAM; ISO 527
 43.2 MPa
@Strain 21.0 %,
Temperature 60.0 °C		6270 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 527
 43.4 MPa
@Strain 26.9 %,
Temperature 90.0 °C		6290 psi
@Strain 26.9 %,
Temperature 194 °F		DAM; ISO 527
 43.7 MPa
@Strain 24.0 %,
Temperature 60.0 °C		6340 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 527
 43.9 MPa
@Strain 30.2 %,
Temperature 90.0 °C		6370 psi
@Strain 30.2 %,
Temperature 194 °F		DAM; ISO 527
 44.0 MPa
@Strain 27.0 %,
Temperature 60.0 °C		6380 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 527
 44.4 MPa
@Strain 33.6 %,
Temperature 90.0 °C		6440 psi
@Strain 33.6 %,
Temperature 194 °F		DAM; Break; ISO 527
 44.6 MPa
@Strain 4.48 %,
Temperature 23.0 °C		6470 psi
@Strain 4.48 %,
Temperature 73.4 °F		50%RH; ISO 527
 45.4 MPa
@Strain 5.38 %,
Temperature 60.0 °C		6580 psi
@Strain 5.38 %,
Temperature 140 °F		DAM; ISO 527
 46.2 MPa
@Strain 9.09 %,
Temperature 40.0 °C		6700 psi
@Strain 9.09 %,
Temperature 104 °F		50%RH; ISO 527
 46.6 MPa
@Strain 0.700 %,
Temperature 23.0 °C		6760 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 527
 48.0 MPa
@Strain 1.33 %,
Temperature 0.000 °C		6960 psi
@Strain 1.33 %,
Temperature 32.0 °F		50%RH; ISO 527
 48.7 MPa
@Strain 12.1 %,
Temperature 40.0 °C		7060 psi
@Strain 12.1 %,
Temperature 104 °F		50%RH; ISO 527
 49.6 MPa
@Strain 8.07 %,
Temperature 60.0 °C		7190 psi
@Strain 8.07 %,
Temperature 140 °F		DAM; ISO 527
 50.3 MPa
@Strain 15.2 %,
Temperature 40.0 °C		7300 psi
@Strain 15.2 %,
Temperature 104 °F		50%RH; ISO 527
 50.7 MPa
@Strain 6.72 %,
Temperature 23.0 °C		7350 psi
@Strain 6.72 %,
Temperature 73.4 °F		50%RH; ISO 527
 51.1 MPa
@Strain 18.2 %,
Temperature 40.0 °C		7410 psi
@Strain 18.2 %,
Temperature 104 °F		50%RH; ISO 527
 51.5 MPa
@Strain 10.8 %,
Temperature 60.0 °C		7470 psi
@Strain 10.8 %,
Temperature 140 °F		DAM; ISO 527
 51.5 MPa
@Strain 21.2 %,
Temperature 40.0 °C		7470 psi
@Strain 21.2 %,
Temperature 104 °F		50%RH; ISO 527
 51.9 MPa
@Strain 24.2 %,
Temperature 40.0 °C		7530 psi
@Strain 24.2 %,
Temperature 104 °F		50%RH; ISO 527
 52.2 MPa
@Strain 27.3 %,
Temperature 40.0 °C		7570 psi
@Strain 27.3 %,
Temperature 104 °F		50%RH; ISO 527
 52.3 MPa
@Strain 1.39 %,
Temperature -20.0 °C		7590 psi
@Strain 1.39 %,
Temperature -4.00 °F		50%RH; ISO 527
 52.4 MPa
@Strain 13.5 %,
Temperature 60.0 °C		7600 psi
@Strain 13.5 %,
Temperature 140 °F		DAM; ISO 527
 52.5 MPa
@Strain 30.3 %,
Temperature 40.0 °C		7610 psi
@Strain 30.3 %,
Temperature 104 °F		50%RH; Break; ISO 527
 53.1 MPa
@Strain 16.1 %,
Temperature 60.0 °C		7700 psi
@Strain 16.1 %,
Temperature 140 °F		DAM; ISO 527
 53.7 MPa
@Strain 8.96 %,
Temperature 23.0 °C		7790 psi
@Strain 8.96 %,
Temperature 73.4 °F		50%RH; ISO 527
 53.9 MPa
@Strain 18.8 %,
Temperature 60.0 °C		7820 psi
@Strain 18.8 %,
Temperature 140 °F		DAM; ISO 527
 54.0 MPa
@Strain 0.720 %,
Temperature 0.000 °C		7830 psi
@Strain 0.720 %,
Temperature 32.0 °F		DAM; ISO 527
 54.7 MPa
@Strain 21.5 %,
Temperature 60.0 °C		7930 psi
@Strain 21.5 %,
Temperature 140 °F		DAM; ISO 527
 55.6 MPa
@Strain 24.2 %,
Temperature 60.0 °C		8060 psi
@Strain 24.2 %,
Temperature 140 °F		DAM; ISO 527
 55.9 MPa
@Strain 11.2 %,
Temperature 23.0 °C		8110 psi
@Strain 11.2 %,
Temperature 73.4 °F		50%RH; ISO 527
 56.5 MPa
@Strain 26.9 %,
Temperature 60.0 °C		8190 psi
@Strain 26.9 %,
Temperature 140 °F		DAM; Break; ISO 527
 57.4 MPa
@Strain 13.4 %,
Temperature 23.0 °C		8330 psi
@Strain 13.4 %,
Temperature 73.4 °F		50%RH; ISO 527
 58.3 MPa
@Strain 15.7 %,
Temperature 23.0 °C		8460 psi
@Strain 15.7 %,
Temperature 73.4 °F		50%RH; ISO 527
 58.9 MPa
@Strain 17.9 %,
Temperature 23.0 °C		8540 psi
@Strain 17.9 %,
Temperature 73.4 °F		50%RH; ISO 527
 59.0 MPa
@Strain 2.52 %,
Temperature 40.0 °C		8560 psi
@Strain 2.52 %,
Temperature 104 °F		DAM; ISO 527
 59.2 MPa
@Strain 20.2 %,
Temperature 23.0 °C		8590 psi
@Strain 20.2 %,
Temperature 73.4 °F		50%RH; ISO 527
 59.3 MPa
@Strain 22.4 %,
Temperature 23.0 °C		8600 psi
@Strain 22.4 %,
Temperature 73.4 °F		50%RH; Break; ISO 527
 59.4 MPa
@Strain 0.720 %,
Temperature -20.0 °C		8620 psi
@Strain 0.720 %,
Temperature -4.00 °F		DAM; ISO 527
 60.6 MPa
@Strain 1.05 %,
Temperature 23.0 °C		8790 psi
@Strain 1.05 %,
Temperature 73.4 °F		DAM; ISO 527
 62.2 MPa
@Strain 2.66 %,
Temperature 0.000 °C		9020 psi
@Strain 2.66 %,
Temperature 32.0 °F		50%RH; ISO 527
 66.9 MPa
@Strain 3.99 %,
Temperature 0.000 °C		9700 psi
@Strain 3.99 %,
Temperature 32.0 °F		50%RH; ISO 527
 67.0 MPa
@Strain 3.78 %,
Temperature 40.0 °C		9720 psi
@Strain 3.78 %,
Temperature 104 °F		DAM; ISO 527
 67.6 MPa
@Strain 2.78 %,
Temperature -20.0 °C		9800 psi
@Strain 2.78 %,
Temperature -4.00 °F		50%RH; ISO 527
 68.1 MPa
@Strain 5.04 %,
Temperature 40.0 °C		9880 psi
@Strain 5.04 %,
Temperature 104 °F		DAM; ISO 527
 68.4 MPa
@Strain 6.30 %,
Temperature 40.0 °C		9920 psi
@Strain 6.30 %,
Temperature 104 °F		DAM; ISO 527
 68.7 MPa
@Strain 7.56 %,
Temperature 40.0 °C		9960 psi
@Strain 7.56 %,
Temperature 104 °F		DAM; ISO 527
 69.1 MPa
@Strain 8.82 %,
Temperature 40.0 °C		10000 psi
@Strain 8.82 %,
Temperature 104 °F		DAM; ISO 527
 69.5 MPa
@Strain 10.1 %,
Temperature 40.0 °C		10100 psi
@Strain 10.1 %,
Temperature 104 °F		DAM; ISO 527
 69.9 MPa
@Strain 11.3 %,
Temperature 40.0 °C		10100 psi
@Strain 11.3 %,
Temperature 104 °F		DAM; ISO 527
 70.0 MPa
@Strain 5.32 %,
Temperature 0.000 °C		10200 psi
@Strain 5.32 %,
Temperature 32.0 °F		50%RH; ISO 527
 70.3 MPa
@Strain 12.6 %,
Temperature 40.0 °C		10200 psi
@Strain 12.6 %,
Temperature 104 °F		DAM; ISO 527
 70.4 MPa
@Strain 1.08 %,
Temperature 0.000 °C		10200 psi
@Strain 1.08 %,
Temperature 32.0 °F		DAM; ISO 527
 70.6 MPa
@Strain 1.40 %,
Temperature 23.0 °C		10200 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 527
 71.9 MPa
@Strain 6.65 %,
Temperature 0.000 °C		10400 psi
@Strain 6.65 %,
Temperature 32.0 °F		50%RH; ISO 527
 72.1 MPa
@Strain 4.17 %,
Temperature -20.0 °C		10500 psi
@Strain 4.17 %,
Temperature -4.00 °F		50%RH; ISO 527
 73.5 MPa
@Strain 7.98 %,
Temperature 0.000 °C		10700 psi
@Strain 7.98 %,
Temperature 32.0 °F		50%RH; ISO 527
 74.5 MPa
@Strain 5.56 %,
Temperature -20.0 °C		10800 psi
@Strain 5.56 %,
Temperature -4.00 °F		50%RH; ISO 527
 74.7 MPa
@Strain 9.31 %,
Temperature 0.000 °C		10800 psi
@Strain 9.31 %,
Temperature 32.0 °F		50%RH; ISO 527
 75.4 MPa
@Strain 10.6 %,
Temperature 0.000 °C		10900 psi
@Strain 10.6 %,
Temperature 32.0 °F		50%RH; ISO 527
 75.9 MPa
@Strain 12.0 %,
Temperature 0.000 °C		11000 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 76.1 MPa
@Strain 6.95 %,
Temperature -20.0 °C		11000 psi
@Strain 6.95 %,
Temperature -4.00 °F		50%RH; ISO 527
 76.2 MPa
@Strain 13.3 %,
Temperature 0.000 °C		11100 psi
@Strain 13.3 %,
Temperature 32.0 °F		50%RH; Break; ISO 527
 77.2 MPa
@Strain 8.34 %,
Temperature -20.0 °C		11200 psi
@Strain 8.34 %,
Temperature -4.00 °F		50%RH; ISO 527
 77.7 MPa
@Strain 1.75 %,
Temperature 23.0 °C		11300 psi
@Strain 1.75 %,
Temperature 73.4 °F		DAM; ISO 527
 78.0 MPa
@Strain 9.73 %,
Temperature -20.0 °C		11300 psi
@Strain 9.73 %,
Temperature -4.00 °F		50%RH; ISO 527
 78.3 MPa
@Strain 1.08 %,
Temperature -20.0 °C		11400 psi
@Strain 1.08 %,
Temperature -4.00 °F		DAM; ISO 527
 78.6 MPa
@Strain 11.1 %,
Temperature -20.0 °C		11400 psi
@Strain 11.1 %,
Temperature -4.00 °F		50%RH; ISO 527
 79.1 MPa
@Strain 12.5 %,
Temperature -20.0 °C		11500 psi
@Strain 12.5 %,
Temperature -4.00 °F		50%RH; ISO 527
 79.4 MPa
@Strain 13.9 %,
Temperature -20.0 °C		11500 psi
@Strain 13.9 %,
Temperature -4.00 °F		50%RH; Break; ISO 527
 82.1 MPa
@Strain 1.44 %,
Temperature 0.000 °C		11900 psi
@Strain 1.44 %,
Temperature 32.0 °F		DAM; ISO 527
 82.7 MPa
@Strain 2.10 %,
Temperature 23.0 °C		12000 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 527
 86.1 MPa
@Strain 2.45 %,
Temperature 23.0 °C		12500 psi
@Strain 2.45 %,
Temperature 73.4 °F		DAM; ISO 527
 88.3 MPa
@Strain 2.80 %,
Temperature 23.0 °C		12800 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 527
 89.6 MPa
@Strain 3.15 %,
Temperature 23.0 °C		13000 psi
@Strain 3.15 %,
Temperature 73.4 °F		DAM; ISO 527
 89.7 MPa
@Strain 3.50 %,
Temperature 23.0 °C		13000 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; Break; ISO 527
 90.4 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13100 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 527
 91.9 MPa
@Strain 1.44 %,
Temperature -20.0 °C		13300 psi
@Strain 1.44 %,
Temperature -4.00 °F		DAM; ISO 527
 96.0 MPa
@Strain 2.16 %,
Temperature 0.000 °C		13900 psi
@Strain 2.16 %,
Temperature 32.0 °F		DAM; ISO 527
 100 MPa
@Strain 2.52 %,
Temperature 0.000 °C		14500 psi
@Strain 2.52 %,
Temperature 32.0 °F		DAM; ISO 527
 101 MPa
@Strain 1.80 %,
Temperature -20.0 °C		14600 psi
@Strain 1.80 %,
Temperature -4.00 °F		DAM; ISO 527
 102 MPa
@Strain 2.88 %,
Temperature 0.000 °C		14800 psi
@Strain 2.88 %,
Temperature 32.0 °F		DAM; ISO 527
 103 MPa
@Strain 3.24 %,
Temperature 0.000 °C		14900 psi
@Strain 3.24 %,
Temperature 32.0 °F		DAM; ISO 527
 104 MPa
@Strain 3.60 %,
Temperature 0.000 °C		15100 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; Break; ISO 527
 108 MPa
@Strain 2.16 %,
Temperature -20.0 °C		15700 psi
@Strain 2.16 %,
Temperature -4.00 °F		DAM; ISO 527
 111 MPa
@Strain 2.52 %,
Temperature -20.0 °C		16100 psi
@Strain 2.52 %,
Temperature -4.00 °F		DAM; ISO 527
 113 MPa
@Strain 2.88 %,
Temperature -20.0 °C		16400 psi
@Strain 2.88 %,
Temperature -4.00 °F		DAM; ISO 527
 114 MPa
@Strain 3.24 %,
Temperature -20.0 °C		16500 psi
@Strain 3.24 %,
Temperature -4.00 °F		DAM; ISO 527
 115 MPa
@Strain 3.60 %,
Temperature -20.0 °C		16700 psi
@Strain 3.60 %,
Temperature -4.00 °F		DAM; Break; ISO 527
Elongation at Break  10 %
@Temperature 23.0 °C		10 %
@Temperature 73.4 °F		DAM; ISO 527
 13 %
@Temperature 23.0 °C		13 %
@Temperature 73.4 °F		DAM; ASTM D638
 24 %
@Temperature 23.0 °C		24 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  2.50 GPa
@Temperature 23.0 °C		363 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.80 GPa
@Temperature 23.0 °C		841 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 5.24 GPa
@Temperature 23.0 °C		760 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Modulus  0.0420 GPa
@Temperature 250 °C		6.09 ksi
@Temperature 482 °F		DAM; ISO 6721
 0.0850 GPa
@Temperature 240 °C		12.3 ksi
@Temperature 464 °F		DAM; ISO 6721
 0.118 GPa
@Temperature 230 °C		17.1 ksi
@Temperature 446 °F		DAM; ISO 6721
 0.153 GPa
@Temperature 220 °C		22.2 ksi
@Temperature 428 °F		DAM; ISO 6721
 0.180 GPa
@Temperature 210 °C		26.1 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.203 GPa
@Temperature 200 °C		29.4 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.223 GPa
@Temperature 190 °C		32.3 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.242 GPa
@Temperature 180 °C		35.1 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.258 GPa
@Temperature 170 °C		37.4 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.275 GPa
@Temperature 160 °C		39.9 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.292 GPa
@Temperature 150 °C		42.4 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.309 GPa
@Temperature 140 °C		44.8 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.325 GPa
@Temperature 130 °C		47.1 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.341 GPa
@Temperature 120 °C		49.5 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.359 GPa
@Temperature 110 °C		52.1 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.379 GPa
@Temperature 100 °C		55.0 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.404 GPa
@Temperature 90.0 °C		58.6 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.445 GPa
@Temperature 80.0 °C		64.5 ksi
@Temperature 176 °F		DAM; ISO 6721
 0.518 GPa
@Temperature 70.0 °C		75.1 ksi
@Temperature 158 °F		DAM; ISO 6721
 0.658 GPa
@Temperature 60.0 °C		95.4 ksi
@Temperature 140 °F		DAM; ISO 6721
 0.918 GPa
@Temperature 50.0 °C		133 ksi
@Temperature 122 °F		DAM; ISO 6721
 1.39 GPa
@Temperature 40.0 °C		202 ksi
@Temperature 104 °F		DAM; ISO 6721
 1.75 GPa
@Temperature 30.0 °C		254 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 1.91 GPa
@Temperature 20.0 °C		277 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 2.00 GPa
@Temperature 10.0 °C		290 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 2.06 GPa
@Temperature 0.000 °C		299 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 2.10 GPa
@Temperature -10.0 °C		305 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 2.12 GPa
@Temperature -20.0 °C		307 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 2.15 GPa
@Temperature -30.0 °C		312 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 2.19 GPa
@Temperature -40.0 °C		318 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 2.27 GPa
@Temperature -50.0 °C		329 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Izod Impact, Notched 0.590 J/cm
@Temperature 23.0 °C		1.11 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.00 kJ/m²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 9.00 kJ/m²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  8.00 J/cm²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 8.00 J/cm²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 13.0 J/cm²
@Temperature 23.0 °C		61.9 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.900 J/cm²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 2170 MPa
@Temperature 23.0 °C		315000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 80.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 176 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 80.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 176 °F		50%RH; 1h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.126 %,
Temperature 100 °C		174 psi
@Strain 0.126 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.139 %,
Temperature 100 °C		174 psi
@Strain 0.139 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 1.50 MPa
@Strain 0.123 %,
Temperature 80.0 °C		218 psi
@Strain 0.123 %,
Temperature 176 °F		50%RH; 10h; Isochronous; ISO 899
 1.50 MPa
@Strain 0.109 %,
Temperature 80.0 °C		218 psi
@Strain 0.109 %,
Temperature 176 °F		50%RH; 1h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.148 %,
Temperature 60.0 °C		290 psi
@Strain 0.148 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.178 %,
Temperature 60.0 °C		290 psi
@Strain 0.178 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.280 %,
Temperature 100 °C		348 psi
@Strain 0.280 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.252 %,
Temperature 100 °C		348 psi
@Strain 0.252 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.221 %,
Temperature 80.0 °C		435 psi
@Strain 0.221 %,
Temperature 176 °F		50%RH; 1h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.248 %,
Temperature 80.0 °C		435 psi
@Strain 0.248 %,
Temperature 176 °F		50%RH; 10h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.138 %,
Temperature 23.0 °C		435 psi
@Strain 0.138 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.159 %,
Temperature 23.0 °C		435 psi
@Strain 0.159 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.423 %,
Temperature 100 °C		522 psi
@Strain 0.423 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.381 %,
Temperature 100 °C		522 psi
@Strain 0.381 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.297 %,
Temperature 60.0 °C		580 psi
@Strain 0.297 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.357 %,
Temperature 60.0 °C		580 psi
@Strain 0.357 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.569 %,
Temperature 100 °C		696 psi
@Strain 0.569 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.513 %,
Temperature 100 °C		696 psi
@Strain 0.513 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.372 %,
Temperature 80.0 °C		725 psi
@Strain 0.372 %,
Temperature 176 °F		50%RH; 1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.420 %,
Temperature 80.0 °C		725 psi
@Strain 0.420 %,
Temperature 176 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.720 %,
Temperature 100 °C		870 psi
@Strain 0.720 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.279 %,
Temperature 23.0 °C		870 psi
@Strain 0.279 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.537 %,
Temperature 60.0 °C		870 psi
@Strain 0.537 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.322 %,
Temperature 23.0 °C		870 psi
@Strain 0.322 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.649 %,
Temperature 100 °C		870 psi
@Strain 0.649 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.448 %,
Temperature 60.0 °C		870 psi
@Strain 0.448 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.791 %,
Temperature 100 °C		1040 psi
@Strain 0.791 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.880 %,
Temperature 100 °C		1040 psi
@Strain 0.880 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.701 %,
Temperature 80.0 °C		1160 psi
@Strain 0.701 %,
Temperature 176 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.721 %,
Temperature 60.0 °C		1160 psi
@Strain 0.721 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.618 %,
Temperature 80.0 °C		1160 psi
@Strain 0.618 %,
Temperature 176 °F		50%RH; 1h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.603 %,
Temperature 60.0 °C		1160 psi
@Strain 0.603 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 8.40 MPa
@Strain 0.939 %,
Temperature 100 °C		1220 psi
@Strain 0.939 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 8.40 MPa
@Strain 1.04 %,
Temperature 100 °C		1220 psi
@Strain 1.04 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.431 %,
Temperature 23.0 °C		1310 psi
@Strain 0.431 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.493 %,
Temperature 23.0 °C		1310 psi
@Strain 0.493 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.22 %,
Temperature 100 °C		1390 psi
@Strain 1.22 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.10 %,
Temperature 100 °C		1390 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.806 %,
Temperature 80.0 °C		1450 psi
@Strain 0.806 %,
Temperature 176 °F		50%RH; 1h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 0.763 %,
Temperature 60.0 °C		1450 psi
@Strain 0.763 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.914 %,
Temperature 80.0 °C		1450 psi
@Strain 0.914 %,
Temperature 176 °F		50%RH; 10h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 0.908 %,
Temperature 60.0 °C		1450 psi
@Strain 0.908 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 10.8 MPa
@Strain 1.40 %,
Temperature 100 °C		1570 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; 10h; Isochronous; ISO 899
 10.8 MPa
@Strain 1.26 %,
Temperature 100 °C		1570 psi
@Strain 1.26 %,
Temperature 212 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.44 %,
Temperature 100 °C		1740 psi
@Strain 1.44 %,
Temperature 212 °F		50%RH; 1h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 0.929 %,
Temperature 60.0 °C		1740 psi
@Strain 0.929 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.60 %,
Temperature 100 °C		1740 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; 10h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 0.612 %,
Temperature 23.0 °C		1740 psi
@Strain 0.612 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1740 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.719 %,
Temperature 23.0 °C		1740 psi
@Strain 0.719 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.30 %,
Temperature 60.0 °C		2030 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.10 %,
Temperature 60.0 °C		2030 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.828 %,
Temperature 23.0 °C		2180 psi
@Strain 0.828 %,
Temperature 73.4 °F		50%RH; 1h; Break; Isochronous; ISO 899
 15.0 MPa
@Strain 0.976 %,
Temperature 23.0 °C		2180 psi
@Strain 0.976 %,
Temperature 73.4 °F		50%RH; 10h; Break; Isochronous; ISO 899
 16.0 MPa
@Strain 1.50 %,
Temperature 60.0 °C		2320 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 16.0 MPa
@Strain 1.29 %,
Temperature 60.0 °C		2320 psi
@Strain 1.29 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 1.48 %,
Temperature 60.0 °C		2610 psi
@Strain 1.48 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 1.72 %,
Temperature 60.0 °C		2610 psi
@Strain 1.72 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.94 %,
Temperature 60.0 °C		2900 psi
@Strain 1.94 %,
Temperature 140 °F		50%RH; 10h; Break; Isochronous; ISO 899
 20.0 MPa
@Strain 1.69 %,
Temperature 60.0 °C		2900 psi
@Strain 1.69 %,
Temperature 140 °F		50%RH; 1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 1400 MPa
@Temperature 23.0 °C		203000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 80.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 176 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 80.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 176 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 80.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 176 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 100 °C		0.000 psi
@Strain 0.000 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.190 %,
Temperature 100 °C		174 psi
@Strain 0.190 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.172 %,
Temperature 100 °C		174 psi
@Strain 0.172 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 1.20 MPa
@Strain 0.155 %,
Temperature 100 °C		174 psi
@Strain 0.155 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 1.50 MPa
@Strain 0.140 %,
Temperature 80.0 °C		218 psi
@Strain 0.140 %,
Temperature 176 °F		50%RH; 100h; Isochronous; ISO 899
 1.50 MPa
@Strain 0.168 %,
Temperature 80.0 °C		218 psi
@Strain 0.168 %,
Temperature 176 °F		50%RH; 10000h; Isochronous; ISO 899
 1.50 MPa
@Strain 0.154 %,
Temperature 80.0 °C		218 psi
@Strain 0.154 %,
Temperature 176 °F		50%RH; 1000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.257 %,
Temperature 60.0 °C		290 psi
@Strain 0.257 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.296 %,
Temperature 60.0 °C		290 psi
@Strain 0.296 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.214 %,
Temperature 60.0 °C		290 psi
@Strain 0.214 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.311 %,
Temperature 100 °C		348 psi
@Strain 0.311 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.345 %,
Temperature 100 °C		348 psi
@Strain 0.345 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.381 %,
Temperature 100 °C		348 psi
@Strain 0.381 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.340 %,
Temperature 80.0 °C		435 psi
@Strain 0.340 %,
Temperature 176 °F		50%RH; 10000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.213 %,
Temperature 23.0 °C		435 psi
@Strain 0.213 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.184 %,
Temperature 23.0 °C		435 psi
@Strain 0.184 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.310 %,
Temperature 80.0 °C		435 psi
@Strain 0.310 %,
Temperature 176 °F		50%RH; 1000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.282 %,
Temperature 80.0 °C		435 psi
@Strain 0.282 %,
Temperature 176 °F		50%RH; 100h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.249 %,
Temperature 23.0 °C		435 psi
@Strain 0.249 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.470 %,
Temperature 100 °C		522 psi
@Strain 0.470 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.522 %,
Temperature 100 °C		522 psi
@Strain 0.522 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.576 %,
Temperature 100 °C		522 psi
@Strain 0.576 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.591 %,
Temperature 60.0 °C		580 psi
@Strain 0.591 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.514 %,
Temperature 60.0 °C		580 psi
@Strain 0.514 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.429 %,
Temperature 60.0 °C		580 psi
@Strain 0.429 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.703 %,
Temperature 100 °C		696 psi
@Strain 0.703 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.775 %,
Temperature 100 °C		696 psi
@Strain 0.775 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.632 %,
Temperature 100 °C		696 psi
@Strain 0.632 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.577 %,
Temperature 80.0 °C		725 psi
@Strain 0.577 %,
Temperature 176 °F		50%RH; 10000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.525 %,
Temperature 80.0 °C		725 psi
@Strain 0.525 %,
Temperature 176 °F		50%RH; 1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.477 %,
Temperature 80.0 °C		725 psi
@Strain 0.477 %,
Temperature 176 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.644 %,
Temperature 60.0 °C		870 psi
@Strain 0.644 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.890 %,
Temperature 100 °C		870 psi
@Strain 0.890 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.373 %,
Temperature 23.0 °C		870 psi
@Strain 0.373 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.982 %,
Temperature 100 °C		870 psi
@Strain 0.982 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.887 %,
Temperature 60.0 °C		870 psi
@Strain 0.887 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.771 %,
Temperature 60.0 °C		870 psi
@Strain 0.771 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.435 %,
Temperature 23.0 °C		870 psi
@Strain 0.435 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.800 %,
Temperature 100 °C		870 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.509 %,
Temperature 23.0 °C		870 psi
@Strain 0.509 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.975 %,
Temperature 100 °C		1040 psi
@Strain 0.975 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 7.20 MPa
@Strain 1.20 %,
Temperature 100 °C		1040 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 1.08 %,
Temperature 100 °C		1040 psi
@Strain 1.08 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.875 %,
Temperature 80.0 °C		1160 psi
@Strain 0.875 %,
Temperature 176 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.862 %,
Temperature 60.0 °C		1160 psi
@Strain 0.862 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.03 %,
Temperature 60.0 °C		1160 psi
@Strain 1.03 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.18 %,
Temperature 60.0 °C		1160 psi
@Strain 1.18 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.952 %,
Temperature 80.0 °C		1160 psi
@Strain 0.952 %,
Temperature 176 °F		50%RH; 10000h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.797 %,
Temperature 80.0 °C		1160 psi
@Strain 0.797 %,
Temperature 176 °F		50%RH; 100h; Isochronous; ISO 899
 8.40 MPa
@Strain 1.16 %,
Temperature 100 °C		1220 psi
@Strain 1.16 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 8.40 MPa
@Strain 1.42 %,
Temperature 100 °C		1220 psi
@Strain 1.42 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 8.40 MPa
@Strain 1.29 %,
Temperature 100 °C		1220 psi
@Strain 1.29 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.568 %,
Temperature 23.0 °C		1310 psi
@Strain 0.568 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.667 %,
Temperature 23.0 °C		1310 psi
@Strain 0.667 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 9.00 MPa
@Strain 0.786 %,
Temperature 23.0 °C		1310 psi
@Strain 0.786 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.35 %,
Temperature 100 °C		1390 psi
@Strain 1.35 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.66 %,
Temperature 100 °C		1390 psi
@Strain 1.66 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.50 %,
Temperature 100 °C		1390 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.08 %,
Temperature 60.0 °C		1450 psi
@Strain 1.08 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.14 %,
Temperature 80.0 °C		1450 psi
@Strain 1.14 %,
Temperature 176 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 1.28 %,
Temperature 60.0 °C		1450 psi
@Strain 1.28 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.24 %,
Temperature 80.0 °C		1450 psi
@Strain 1.24 %,
Temperature 176 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 1.48 %,
Temperature 60.0 °C		1450 psi
@Strain 1.48 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.04 %,
Temperature 80.0 °C		1450 psi
@Strain 1.04 %,
Temperature 176 °F		50%RH; 100h; Break; Isochronous; ISO 899
 10.8 MPa
@Strain 1.56 %,
Temperature 100 °C		1570 psi
@Strain 1.56 %,
Temperature 212 °F		50%RH; 100h; Isochronous; ISO 899
 10.8 MPa
@Strain 1.91 %,
Temperature 100 °C		1570 psi
@Strain 1.91 %,
Temperature 212 °F		50%RH; 10000h; Isochronous; ISO 899
 10.8 MPa
@Strain 1.73 %,
Temperature 100 °C		1570 psi
@Strain 1.73 %,
Temperature 212 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.97 %,
Temperature 100 °C		1740 psi
@Strain 1.97 %,
Temperature 212 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1740 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.846 %,
Temperature 23.0 °C		1740 psi
@Strain 0.846 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 12.0 MPa
@Strain 2.18 %,
Temperature 100 °C		1740 psi
@Strain 2.18 %,
Temperature 212 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 12.0 MPa
@Strain 0.982 %,
Temperature 23.0 °C		1740 psi
@Strain 0.982 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.54 %,
Temperature 60.0 °C		1740 psi
@Strain 1.54 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.77 %,
Temperature 60.0 °C		1740 psi
@Strain 1.77 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.15 %,
Temperature 23.0 °C		1740 psi
@Strain 1.15 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.77 %,
Temperature 100 °C		1740 psi
@Strain 1.77 %,
Temperature 212 °F		50%RH; 100h; Break; Isochronous; ISO 899
 14.0 MPa
@Strain 2.07 %,
Temperature 60.0 °C		2030 psi
@Strain 2.07 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.80 %,
Temperature 60.0 °C		2030 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.53 %,
Temperature 60.0 °C		2030 psi
@Strain 1.53 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 15.0 MPa
@Strain 1.14 %,
Temperature 23.0 °C		2180 psi
@Strain 1.14 %,
Temperature 73.4 °F		50%RH; 100h; Break; Isochronous; ISO 899
 15.0 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2180 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 15.0 MPa
@Strain 1.53 %,
Temperature 23.0 °C		2180 psi
@Strain 1.53 %,
Temperature 73.4 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 16.0 MPa
@Strain 2.37 %,
Temperature 60.0 °C		2320 psi
@Strain 2.37 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 16.0 MPa
@Strain 2.06 %,
Temperature 60.0 °C		2320 psi
@Strain 2.06 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 16.0 MPa
@Strain 1.76 %,
Temperature 60.0 °C		2320 psi
@Strain 1.76 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 18.0 MPa
@Strain 1.99 %,
Temperature 60.0 °C		2610 psi
@Strain 1.99 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 18.0 MPa
@Strain 2.31 %,
Temperature 60.0 °C		2610 psi
@Strain 2.31 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 18.0 MPa
@Strain 2.66 %,
Temperature 60.0 °C		2610 psi
@Strain 2.66 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 2.96 %,
Temperature 60.0 °C		2900 psi
@Strain 2.96 %,
Temperature 140 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 20.0 MPa
@Strain 2.57 %,
Temperature 60.0 °C		2900 psi
@Strain 2.57 %,
Temperature 140 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 20.0 MPa
@Strain 2.23 %,
Temperature 60.0 °C		2900 psi
@Strain 2.23 %,
Temperature 140 °F		50%RH; 100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+11 ohm-cm
@Temperature 23.0 °C		1.00e+11 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
Surface Resistance 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.3
@Frequency 100 Hz,
Temperature 23.0 °C		4.3
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 12.6
@Frequency 100 Hz,
Temperature 23.0 °C		12.6
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength  27.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		686 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		50%RH; IEC 60243-1
 36.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		914 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.012
@Frequency 100 Hz,
Temperature 23.0 °C		0.012
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.024
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.024
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.075
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.075
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.44
@Frequency 100 Hz,
Temperature 23.0 °C		0.44
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  400 V
@Temperature 23.0 °C		400 V
@Temperature 73.4 °F		DAM; UL 746A
 550 V
@Temperature 23.0 °C		550 V
@Temperature 73.4 °F		DAM; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  86.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		47.8 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 86.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		47.8 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 259 °C498 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C194 °FDAM; ASTM D648
 110 °C230 °FDAM; ISO 75-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 256 °C493 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FillerMineral fillerDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-IMD40<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Warp ResinsDAM
 Mineral Reinforced ResinsDAM
Resin IdentificationPA66-IMD40ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45417.html

免责声明: 本文 DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4