  4. DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66

DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66

DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66 物性表: DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 成型收缩率 [%]: 0.005
  • 缺口冲击强度: 3.8
  • 弯曲模量 [MPa]: 7.00
  • 热变形温度 [℃]: 255.0
 
Physical PropertiesMetricEnglishComments
Density 1.45 g/cc0.0524 lb/in³DAM; ISO 1183
Filler Content 38 %38 %DAM
Linear Mold Shrinkage  0.0050 cm/cm
@Thickness 1.60 mm		0.0050 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0060 cm/cm
@Thickness 3.20 mm		0.0060 in/in
@Thickness 0.126 in		Flow; DAM
 0.0060 cm/cm
@Thickness 6.40 mm		0.0060 in/in
@Thickness 0.252 in		Flow; DAM
 0.0080 cm/cm
@Thickness 1.60 mm		0.0080 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.0080 cm/cm
@Thickness 3.20 mm		0.0080 in/in
@Thickness 0.126 in		Transverse; DAM
 0.010 cm/cm
@Thickness 6.40 mm		0.010 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0060 cm/cm
@Thickness 2.00 mm		0.0060 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  72.0 MPa
@Temperature 23.0 °C		10400 psi
@Temperature 73.4 °F		50%RH; ISO 527
 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  1.60 MPa
@Strain 0.100 %,
Temperature 150 °C		232 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.00 MPa
@Strain 0.100 %,
Temperature 150 °C		290 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.00 MPa
@Strain 0.100 %,
Temperature 120 °C		290 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.10 MPa
@Strain 0.100 %,
Temperature 120 °C		305 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.40 MPa
@Strain 0.100 %,
Temperature 100 °C		348 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.40 MPa
@Strain 0.100 %,
Temperature 60.0 °C		348 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 100 °C		363 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.60 MPa
@Strain 0.100 %,
Temperature 80.0 °C		377 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.70 MPa
@Strain 0.100 %,
Temperature 80.0 °C		392 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.60 MPa
@Strain 0.100 %,
Temperature 23.0 °C		522 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.10 MPa
@Strain 0.100 %,
Temperature 60.0 °C		595 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 4.50 MPa
@Strain 0.200 %,
Temperature 150 °C		653 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.200 %,
Temperature 150 °C		754 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.40 MPa
@Strain 0.200 %,
Temperature 120 °C		783 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.50 MPa
@Strain 0.200 %,
Temperature 120 °C		798 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.60 MPa
@Strain 0.100 %,
Temperature 23.0 °C		812 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.90 MPa
@Strain 0.100 %,
Temperature -40.0 °C		856 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.00 MPa
@Strain 0.100 %,
Temperature 0.000 °C		870 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 6.20 MPa
@Strain 0.200 %,
Temperature 100 °C		899 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.20 MPa
@Strain 0.100 %,
Temperature 0.000 °C		899 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.30 MPa
@Strain 0.200 %,
Temperature 80.0 °C		914 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.60 MPa
@Strain 0.200 %,
Temperature 100 °C		957 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.90 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1000 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.90 MPa
@Strain 0.300 %,
Temperature 150 °C		1000 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.90 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1000 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 7.50 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1090 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.70 MPa
@Strain 0.300 %,
Temperature 150 °C		1120 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.90 MPa
@Strain 0.300 %,
Temperature 120 °C		1150 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.50 MPa
@Strain 0.300 %,
Temperature 120 °C		1230 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.80 MPa
@Strain 0.300 %,
Temperature 100 °C		1280 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.80 MPa
@Strain 0.400 %,
Temperature 150 °C		1280 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.00 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1310 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.70 MPa
@Strain 0.300 %,
Temperature 100 °C		1410 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.0 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1450 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 10.0 MPa
@Strain 0.400 %,
Temperature 150 °C		1450 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.1 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1460 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 0.400 %,
Temperature 120 °C		1510 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.6 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1540 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 10.7 MPa
@Strain 0.500 %,
Temperature 150 °C		1550 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.0 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1600 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.3 MPa
@Strain 0.400 %,
Temperature 100 °C		1640 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.6 MPa
@Strain 0.400 %,
Temperature 120 °C		1680 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1700 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.2 MPa
@Strain 0.500 %,
Temperature 150 °C		1770 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.5 MPa
@Strain 0.600 %,
Temperature 150 °C		1810 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.6 MPa
@Strain 0.500 %,
Temperature 120 °C		1830 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.6 MPa
@Strain 0.400 %,
Temperature 100 °C		1830 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.8 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1860 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.9 MPa
@Strain 0.500 %,
Temperature 100 °C		2020 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.1 MPa
@Strain 0.500 %,
Temperature 120 °C		2050 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.1 MPa
@Strain 0.700 %,
Temperature 150 °C		2050 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.3 MPa
@Strain 0.400 %,
Temperature 80.0 °C		2070 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.4 MPa
@Strain 0.600 %,
Temperature 150 °C		2090 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.5 MPa
@Strain 0.500 %,
Temperature 80.0 °C		2100 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.7 MPa
@Strain 0.600 %,
Temperature 120 °C		2130 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.8 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2150 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.1 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2190 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 15.4 MPa
@Strain 0.500 %,
Temperature 100 °C		2230 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.6 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2260 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2280 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.8 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2290 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 15.8 MPa
@Strain 0.800 %,
Temperature 150 °C		2290 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.8 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2290 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 16.1 MPa
@Strain 0.600 %,
Temperature 100 °C		2340 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.3 MPa
@Strain 0.700 %,
Temperature 150 °C		2360 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.5 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2390 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 16.6 MPa
@Strain 0.700 %,
Temperature 120 °C		2410 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.7 MPa
@Strain 0.600 %,
Temperature 120 °C		2420 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.9 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2450 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.2 MPa
@Strain 0.900 %,
Temperature 150 °C		2490 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 0.500 %,
Temperature 80.0 °C		2520 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.0 MPa
@Strain 0.800 %,
Temperature 150 °C		2610 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.1 MPa
@Strain 0.600 %,
Temperature 100 °C		2630 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.3 MPa
@Strain 0.700 %,
Temperature 100 °C		2650 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.4 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2670 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.5 MPa
@Strain 0.800 %,
Temperature 120 °C		2680 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.6 MPa
@Strain 1.00 %,
Temperature 150 °C		2700 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.9 MPa
@Strain 0.700 %,
Temperature 120 °C		2740 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.1 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2770 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.2 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2780 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.2 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2780 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.6 MPa
@Strain 0.900 %,
Temperature 150 °C		2840 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.9 MPa
@Strain 1.10 %,
Temperature 150 °C		2890 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.2 MPa
@Strain 0.900 %,
Temperature 120 °C		2930 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.2 MPa
@Strain 0.800 %,
Temperature 100 °C		2930 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.4 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2960 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.6 MPa
@Strain 0.700 %,
Temperature 100 °C		2990 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.7 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3000 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.9 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3030 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.0 MPa
@Strain 0.800 %,
Temperature 120 °C		3050 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.2 MPa
@Strain 1.20 %,
Temperature 150 °C		3070 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.3 MPa
@Strain 1.00 %,
Temperature 150 °C		3090 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.4 MPa
@Strain 0.800 %,
Temperature 80.0 °C		3100 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.1 MPa
@Strain 1.00 %,
Temperature 120 °C		3210 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.2 MPa
@Strain 0.900 %,
Temperature 100 °C		3220 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 1.30 %,
Temperature 150 °C		3280 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 1.10 %,
Temperature 150 °C		3310 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.9 MPa
@Strain 0.800 %,
Temperature 100 °C		3320 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.9 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3320 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 23.1 MPa
@Strain 0.900 %,
Temperature 120 °C		3350 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.2 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3360 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 23.2 MPa
@Strain 0.700 %,
Temperature 80.0 °C		3360 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.3 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3380 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.4 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3390 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.6 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3420 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.6 MPa
@Strain 1.10 %,
Temperature 120 °C		3420 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.8 MPa
@Strain 1.40 %,
Temperature 150 °C		3450 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.8 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3450 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 24.1 MPa
@Strain 1.00 %,
Temperature 100 °C		3500 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.2 MPa
@Strain 1.20 %,
Temperature 150 °C		3510 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.7 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3580 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 24.8 MPa
@Strain 1.50 %,
Temperature 150 °C		3600 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.0 MPa
@Strain 1.00 %,
Temperature 120 °C		3630 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.1 MPa
@Strain 0.500 %,
Temperature 60.0 °C		3640 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 0.900 %,
Temperature 100 °C		3650 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 1.20 %,
Temperature 120 °C		3650 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3710 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 0.900 %,
Temperature 60.0 °C		3710 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.7 MPa
@Strain 1.30 %,
Temperature 150 °C		3730 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.8 MPa
@Strain 1.60 %,
Temperature 150 °C		3740 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.8 MPa
@Strain 0.800 %,
Temperature 80.0 °C		3740 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.9 MPa
@Strain 1.10 %,
Temperature 100 °C		3760 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 1.30 %,
Temperature 120 °C		3840 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 1.70 %,
Temperature 150 °C		3870 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.9 MPa
@Strain 1.10 %,
Temperature 120 °C		3900 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.2 MPa
@Strain 1.40 %,
Temperature 150 °C		3950 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.3 MPa
@Strain 1.00 %,
Temperature 100 °C		3960 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.4 MPa
@Strain 0.600 %,
Temperature 23.0 °C		3970 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.5 MPa
@Strain 1.80 %,
Temperature 150 °C		3990 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.6 MPa
@Strain 1.20 %,
Temperature 100 °C		4000 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.7 MPa
@Strain 1.10 %,
Temperature 80.0 °C		4020 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 1.00 %,
Temperature 60.0 °C		4030 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 1.40 %,
Temperature 120 °C		4030 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.3 MPa
@Strain 1.90 %,
Temperature 150 °C		4100 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.4 MPa
@Strain 1.50 %,
Temperature 150 °C		4120 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.4 MPa
@Strain 0.900 %,
Temperature 80.0 °C		4120 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.6 MPa
@Strain 1.20 %,
Temperature 120 °C		4150 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.8 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4180 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 29.0 MPa
@Strain 2.00 %,
Temperature 150 °C		4210 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 1.50 %,
Temperature 120 °C		4220 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 1.30 %,
Temperature 100 °C		4240 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.3 MPa
@Strain 1.10 %,
Temperature 100 °C		4250 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.4 MPa
@Strain 0.600 %,
Temperature 60.0 °C		4260 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.5 MPa
@Strain 1.20 %,
Temperature 80.0 °C		4280 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.5 MPa
@Strain 1.60 %,
Temperature 150 °C		4280 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.6 MPa
@Strain 2.10 %,
Temperature 150 °C		4290 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 1.10 %,
Temperature 60.0 °C		4350 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.1 MPa
@Strain 1.30 %,
Temperature 120 °C		4370 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.2 MPa
@Strain 2.20 %,
Temperature 150 °C		4380 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.4 MPa
@Strain 1.60 %,
Temperature 120 °C		4410 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		4440 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.6 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4440 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.7 MPa
@Strain 0.400 %,
Temperature 0.000 °C		4450 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 30.7 MPa
@Strain 1.40 %,
Temperature 100 °C		4450 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.7 MPa
@Strain 2.30 %,
Temperature 150 °C		4450 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.8 MPa
@Strain 1.70 %,
Temperature 150 °C		4470 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.0 MPa
@Strain 1.20 %,
Temperature 100 °C		4500 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.2 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4530 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.2 MPa
@Strain 2.40 %,
Temperature 150 °C		4530 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.3 MPa
@Strain 0.700 %,
Temperature 23.0 °C		4540 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.5 MPa
@Strain 0.400 %,
Temperature 0.000 °C		4570 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 1.70 %,
Temperature 120 °C		4570 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.7 MPa
@Strain 2.50 %,
Temperature 150 °C		4600 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.8 MPa
@Strain 1.80 %,
Temperature 150 °C		4610 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.8 MPa
@Strain 1.40 %,
Temperature 120 °C		4610 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.9 MPa
@Strain 1.20 %,
Temperature 60.0 °C		4630 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.0 MPa
@Strain 1.50 %,
Temperature 100 °C		4640 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 2.60 %,
Temperature 150 °C		4660 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 2.70 %,
Temperature 150 °C		4700 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 1.80 %,
Temperature 120 °C		4700 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 2.80 %,
Temperature 150 °C		4760 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 1.10 %,
Temperature 80.0 °C		4760 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4770 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.9 MPa
@Strain 1.30 %,
Temperature 100 °C		4770 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4770 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 1.90 %,
Temperature 150 °C		4770 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.0 MPa
@Strain 2.90 %,
Temperature 150 °C		4790 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 3.00 %,
Temperature 150 °C		4830 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 1.90 %,
Temperature 120 °C		4830 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 1.50 %,
Temperature 120 °C		4830 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.5 MPa
@Strain 1.60 %,
Temperature 100 °C		4860 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.5 MPa
@Strain 0.700 %,
Temperature 60.0 °C		4860 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.6 MPa
@Strain 3.10 %,
Temperature 150 °C		4870 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.8 MPa
@Strain 3.20 %,
Temperature 150 °C		4900 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.9 MPa
@Strain 2.00 %,
Temperature 150 °C		4920 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.9 MPa
@Strain 1.30 %,
Temperature 60.0 °C		4920 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.0 MPa
@Strain 3.30 %,
Temperature 150 °C		4930 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.0 MPa
@Strain 2.00 %,
Temperature 120 °C		4930 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.1 MPa
@Strain 3.40 %,
Temperature 150 °C		4950 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.3 MPa
@Strain 3.50 %,
Temperature 150 °C		4970 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 3.60 %,
Temperature 150 °C		5020 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 1.70 %,
Temperature 100 °C		5020 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 1.50 %,
Temperature 80.0 °C		5020 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.7 MPa
@Strain 1.40 %,
Temperature 100 °C		5030 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.7 MPa
@Strain 1.60 %,
Temperature 120 °C		5030 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.7 MPa
@Strain 3.70 %,
Temperature 150 °C		5030 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.7 MPa
@Strain 2.10 %,
Temperature 150 °C		5030 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.8 MPa
@Strain 3.80 %,
Temperature 150 °C		5050 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 2.10 %,
Temperature 120 °C		5050 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5050 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.0 MPa
@Strain 1.20 %,
Temperature 80.0 °C		5080 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.0 MPa
@Strain 3.90 %,
Temperature 150 °C		5080 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.2 MPa
@Strain 4.00 %,
Temperature 150 °C		5110 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.2 MPa
@Strain 4.10 %,
Temperature 150 °C		5110 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.3 MPa
@Strain 4.20 %,
Temperature 150 °C		5120 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 4.30 %,
Temperature 150 °C		5130 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 2.20 %,
Temperature 120 °C		5130 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 4.40 %,
Temperature 150 °C		5160 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 2.20 %,
Temperature 150 °C		5160 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.7 MPa
@Strain 4.50 %,
Temperature 150 °C		5180 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.7 MPa
@Strain 4.60 %,
Temperature 150 °C		5180 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.7 MPa
@Strain 1.80 %,
Temperature 100 °C		5180 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 4.90 %,
Temperature 150 °C		5190 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 1.40 %,
Temperature 60.0 °C		5190 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 4.70 %,
Temperature 150 °C		5210 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 4.80 %,
Temperature 150 °C		5210 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 2.30 %,
Temperature 120 °C		5210 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.1 MPa
@Strain 5.00 %,
Temperature 150 °C		5240 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 1.70 %,
Temperature 120 °C		5250 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.2 MPa
@Strain 1.60 %,
Temperature 80.0 °C		5250 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 1.50 %,
Temperature 100 °C		5260 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.3 MPa
@Strain 5.50 %,
Temperature 150 °C		5260 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.4 MPa
@Strain 2.30 %,
Temperature 150 °C		5280 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.5 MPa
@Strain 6.00 %,
Temperature 150 °C		5290 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.5 MPa
@Strain 8.00 %,
Temperature 150 °C		5290 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.5 MPa
@Strain 2.40 %,
Temperature 120 °C		5290 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 7.50 %,
Temperature 150 °C		5310 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 6.50 %,
Temperature 150 °C		5310 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.7 MPa
@Strain 7.00 %,
Temperature 150 °C		5320 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 2.50 %,
Temperature 120 °C		5340 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 1.90 %,
Temperature 100 °C		5340 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 1.30 %,
Temperature 80.0 °C		5370 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.2 MPa
@Strain 2.40 %,
Temperature 150 °C		5400 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 2.60 %,
Temperature 120 °C		5410 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.3 MPa
@Strain 1.80 %,
Temperature 120 °C		5410 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 0.800 %,
Temperature 60.0 °C		5410 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.6 MPa
@Strain 1.50 %,
Temperature 60.0 °C		5450 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 2.70 %,
Temperature 120 °C		5450 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.7 MPa
@Strain 2.00 %,
Temperature 100 °C		5470 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.7 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5470 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5480 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 2.80 %,
Temperature 120 °C		5480 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 0.400 %,
Temperature -40.0 °C		5480 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.9 MPa
@Strain 1.60 %,
Temperature 100 °C		5500 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.9 MPa
@Strain 2.50 %,
Temperature 150 °C		5500 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.0 MPa
@Strain 2.90 %,
Temperature 120 °C		5510 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5510 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.2 MPa
@Strain 0.900 %,
Temperature 23.0 °C		5540 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 3.00 %,
Temperature 120 °C		5550 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.5 MPa
@Strain 2.60 %,
Temperature 150 °C		5580 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.5 MPa
@Strain 3.10 %,
Temperature 120 °C		5580 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.6 MPa
@Strain 1.90 %,
Temperature 120 °C		5600 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.6 MPa
@Strain 2.10 %,
Temperature 100 °C		5600 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 3.20 %,
Temperature 120 °C		5610 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.8 MPa
@Strain 1.40 %,
Temperature 80.0 °C		5630 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.9 MPa
@Strain 3.30 %,
Temperature 120 °C		5640 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.1 MPa
@Strain 3.40 %,
Temperature 120 °C		5670 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.1 MPa
@Strain 2.70 %,
Temperature 150 °C		5670 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5670 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 3.50 %,
Temperature 120 °C		5690 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 2.20 %,
Temperature 100 °C		5690 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.3 MPa
@Strain 1.60 %,
Temperature 60.0 °C		5700 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.4 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5710 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.4 MPa
@Strain 3.60 %,
Temperature 120 °C		5710 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.5 MPa
@Strain 3.70 %,
Temperature 120 °C		5730 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.5 MPa
@Strain 1.70 %,
Temperature 100 °C		5730 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 3.80 %,
Temperature 120 °C		5740 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 2.80 %,
Temperature 150 °C		5740 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.7 MPa
@Strain 3.90 %,
Temperature 120 °C		5760 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 2.00 %,
Temperature 120 °C		5760 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 2.30 %,
Temperature 100 °C		5770 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.8 MPa
@Strain 4.00 %,
Temperature 120 °C		5770 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 4.10 %,
Temperature 120 °C		5790 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 4.20 %,
Temperature 120 °C		5790 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.1 MPa
@Strain 4.30 %,
Temperature 120 °C		5820 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.1 MPa
@Strain 2.90 %,
Temperature 150 °C		5820 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.3 MPa
@Strain 4.40 %,
Temperature 120 °C		5850 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 4.50 %,
Temperature 120 °C		5850 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 4.60 %,
Temperature 120 °C		5850 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 4.70 %,
Temperature 120 °C		5850 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 4.80 %,
Temperature 120 °C		5860 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 8.00 %,
Temperature 120 °C		5860 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 2.40 %,
Temperature 100 °C		5860 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5860 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.5 MPa
@Strain 7.50 %,
Temperature 120 °C		5870 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.5 MPa
@Strain 3.00 %,
Temperature 150 °C		5870 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.6 MPa
@Strain 4.90 %,
Temperature 120 °C		5890 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.6 MPa
@Strain 5.00 %,
Temperature 120 °C		5890 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.6 MPa
@Strain 1.50 %,
Temperature 80.0 °C		5890 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.7 MPa
@Strain 0.900 %,
Temperature 60.0 °C		5900 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.7 MPa
@Strain 5.50 %,
Temperature 120 °C		5900 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.7 MPa
@Strain 2.50 %,
Temperature 100 °C		5900 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.7 MPa
@Strain 2.10 %,
Temperature 120 °C		5900 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.7 MPa
@Strain 7.00 %,
Temperature 120 °C		5900 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 6.00 %,
Temperature 120 °C		5920 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 6.50 %,
Temperature 120 °C		5920 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 3.10 %,
Temperature 150 °C		5920 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.0 MPa
@Strain 2.60 %,
Temperature 100 °C		5950 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 1.80 %,
Temperature 100 °C		5950 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 1.70 %,
Temperature 60.0 °C		5960 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.2 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5980 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.3 MPa
@Strain 3.20 %,
Temperature 150 °C		5990 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.4 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6000 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.5 MPa
@Strain 2.00 %,
Temperature 80.0 °C		6020 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.5 MPa
@Strain 2.70 %,
Temperature 100 °C		6020 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.6 MPa
@Strain 3.30 %,
Temperature 150 °C		6030 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.7 MPa
@Strain 2.80 %,
Temperature 100 °C		6050 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 2.20 %,
Temperature 120 °C		6060 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.0 MPa
@Strain 2.90 %,
Temperature 100 °C		6090 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.0 MPa
@Strain 3.40 %,
Temperature 150 °C		6090 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.2 MPa
@Strain 3.50 %,
Temperature 150 °C		6120 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.3 MPa
@Strain 3.00 %,
Temperature 100 °C		6140 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.4 MPa
@Strain 1.90 %,
Temperature 100 °C		6150 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.4 MPa
@Strain 3.60 %,
Temperature 150 °C		6150 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.4 MPa
@Strain 1.60 %,
Temperature 80.0 °C		6150 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.5 MPa
@Strain 1.80 %,
Temperature 60.0 °C		6160 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.5 MPa
@Strain 3.10 %,
Temperature 100 °C		6160 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 3.70 %,
Temperature 150 °C		6180 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.6 MPa
@Strain 2.10 %,
Temperature 80.0 °C		6180 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 3.20 %,
Temperature 100 °C		6190 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 2.30 %,
Temperature 120 °C		6190 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.8 MPa
@Strain 3.30 %,
Temperature 100 °C		6210 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.8 MPa
@Strain 3.80 %,
Temperature 150 °C		6210 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 3.40 %,
Temperature 100 °C		6240 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.1 MPa
@Strain 3.90 %,
Temperature 150 °C		6250 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.2 MPa
@Strain 3.50 %,
Temperature 100 °C		6270 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 4.00 %,
Temperature 150 °C		6280 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.4 MPa
@Strain 3.60 %,
Temperature 100 °C		6290 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 3.70 %,
Temperature 100 °C		6290 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.5 MPa
@Strain 2.40 %,
Temperature 120 °C		6310 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.5 MPa
@Strain 4.10 %,
Temperature 150 °C		6310 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.5 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6310 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.6 MPa
@Strain 4.20 %,
Temperature 150 °C		6320 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.6 MPa
@Strain 3.80 %,
Temperature 100 °C		6320 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.6 MPa
@Strain 3.90 %,
Temperature 100 °C		6320 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.7 MPa
@Strain 4.30 %,
Temperature 150 °C		6340 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 4.00 %,
Temperature 100 °C		6350 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 4.20 %,
Temperature 100 °C		6350 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.9 MPa
@Strain 4.30 %,
Temperature 100 °C		6370 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.9 MPa
@Strain 4.10 %,
Temperature 100 °C		6370 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.9 MPa
@Strain 2.00 %,
Temperature 100 °C		6370 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 4.40 %,
Temperature 150 °C		6370 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.0 MPa
@Strain 4.40 %,
Temperature 100 °C		6380 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.0 MPa
@Strain 1.00 %,
Temperature 60.0 °C		6380 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 1.90 %,
Temperature 60.0 °C		6400 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 4.50 %,
Temperature 150 °C		6400 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 4.60 %,
Temperature 150 °C		6400 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 4.60 %,
Temperature 100 °C		6400 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 7.50 %,
Temperature 100 °C		6400 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.2 MPa
@Strain 7.00 %,
Temperature 100 °C		6410 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.2 MPa
@Strain 4.70 %,
Temperature 100 °C		6410 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.2 MPa
@Strain 4.50 %,
Temperature 100 °C		6410 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.2 MPa
@Strain 4.70 %,
Temperature 150 °C		6410 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.2 MPa
@Strain 1.70 %,
Temperature 80.0 °C		6410 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.3 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6430 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 0.600 %,
Temperature 0.000 °C		6430 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 4.80 %,
Temperature 150 °C		6430 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.3 MPa
@Strain 4.90 %,
Temperature 150 °C		6430 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.3 MPa
@Strain 4.80 %,
Temperature 100 °C		6430 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 4.90 %,
Temperature 100 °C		6430 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 5.00 %,
Temperature 100 °C		6430 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 2.50 %,
Temperature 120 °C		6430 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 5.50 %,
Temperature 100 °C		6440 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 6.00 %,
Temperature 100 °C		6440 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 6.50 %,
Temperature 100 °C		6440 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 5.00 %,
Temperature 150 °C		6440 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 1.10 %,
Temperature 23.0 °C		6440 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.9 MPa
@Strain 5.50 %,
Temperature 150 °C		6510 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 2.60 %,
Temperature 120 °C		6510 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.0 MPa
@Strain 2.10 %,
Temperature 100 °C		6530 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.0 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6530 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.2 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6560 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 6.00 %,
Temperature 150 °C		6570 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 8.00 %,
Temperature 150 °C		6580 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 6.50 %,
Temperature 150 °C		6580 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 2.00 %,
Temperature 60.0 °C		6580 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.5 MPa
@Strain 7.00 %,
Temperature 150 °C		6600 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.5 MPa
@Strain 7.50 %,
Temperature 150 °C		6600 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.6 MPa
@Strain 2.70 %,
Temperature 120 °C		6610 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.6 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6610 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.0 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6670 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.0 MPa
@Strain 1.80 %,
Temperature 80.0 °C		6670 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.0 MPa
@Strain 2.80 %,
Temperature 120 °C		6670 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 2.20 %,
Temperature 100 °C		6690 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.3 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6720 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.4 MPa
@Strain 2.90 %,
Temperature 120 °C		6730 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.7 MPa
@Strain 3.00 %,
Temperature 120 °C		6770 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.7 MPa
@Strain 2.10 %,
Temperature 60.0 °C		6770 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 2.80 %,
Temperature 80.0 °C		6790 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 0.500 %,
Temperature -40.0 °C		6790 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 0.600 %,
Temperature 0.000 °C		6820 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 47.1 MPa
@Strain 1.10 %,
Temperature 60.0 °C		6830 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.1 MPa
@Strain 2.90 %,
Temperature 80.0 °C		6830 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.1 MPa
@Strain 3.10 %,
Temperature 120 °C		6830 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 2.30 %,
Temperature 100 °C		6850 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 1.20 %,
Temperature 23.0 °C		6850 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 3.00 %,
Temperature 80.0 °C		6870 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.5 MPa
@Strain 1.90 %,
Temperature 80.0 °C		6890 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 3.20 %,
Temperature 120 °C		6890 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.6 MPa
@Strain 3.10 %,
Temperature 80.0 °C		6900 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 3.20 %,
Temperature 80.0 °C		6920 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.9 MPa
@Strain 2.20 %,
Temperature 60.0 °C		6950 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.9 MPa
@Strain 3.30 %,
Temperature 120 °C		6950 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.0 MPa
@Strain 3.30 %,
Temperature 80.0 °C		6960 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.1 MPa
@Strain 3.40 %,
Temperature 120 °C		6980 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		6990 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.2 MPa
@Strain 3.70 %,
Temperature 80.0 °C		6990 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.3 MPa
@Strain 2.40 %,
Temperature 100 °C		7010 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.4 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7020 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 3.60 %,
Temperature 80.0 °C		7020 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 3.80 %,
Temperature 80.0 °C		7030 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 3.50 %,
Temperature 120 °C		7030 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 3.60 %,
Temperature 120 °C		7060 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 2.30 %,
Temperature 60.0 °C		7060 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.7 MPa
@Strain 3.90 %,
Temperature 80.0 °C		7060 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.8 MPa
@Strain 4.00 %,
Temperature 80.0 °C		7080 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.9 MPa
@Strain 3.70 %,
Temperature 120 °C		7090 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.0 MPa
@Strain 2.50 %,
Temperature 100 °C		7110 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.0 MPa
@Strain 4.10 %,
Temperature 80.0 °C		7110 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.0 MPa
@Strain 2.00 %,
Temperature 80.0 °C		7110 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.1 MPa
@Strain 4.20 %,
Temperature 80.0 °C		7120 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.1 MPa
@Strain 4.30 %,
Temperature 80.0 °C		7120 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.1 MPa
@Strain 3.80 %,
Temperature 120 °C		7120 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.2 MPa
@Strain 4.40 %,
Temperature 80.0 °C		7140 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 4.50 %,
Temperature 80.0 °C		7150 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 7.00 %,
Temperature 80.0 °C		7150 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 3.90 %,
Temperature 120 °C		7150 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.3 MPa
@Strain 4.00 %,
Temperature 120 °C		7150 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.3 MPa
@Strain 0.600 %,
Temperature -40.0 °C		7150 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 49.4 MPa
@Strain 4.60 %,
Temperature 80.0 °C		7160 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 4.70 %,
Temperature 80.0 °C		7180 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 4.80 %,
Temperature 80.0 °C		7180 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 6.50 %,
Temperature 80.0 °C		7180 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		7180 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 2.40 %,
Temperature 60.0 °C		7180 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 4.10 %,
Temperature 120 °C		7180 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.5 MPa
@Strain 2.60 %,
Temperature 100 °C		7180 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.6 MPa
@Strain 5.50 %,
Temperature 80.0 °C		7190 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 6.00 %,
Temperature 80.0 °C		7190 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 4.90 %,
Temperature 80.0 °C		7190 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 4.20 %,
Temperature 120 °C		7210 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 4.30 %,
Temperature 120 °C		7220 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 4.40 %,
Temperature 120 °C		7220 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		7240 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.0 MPa
@Strain 1.30 %,
Temperature 23.0 °C		7250 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.0 MPa
@Strain 1.20 %,
Temperature 60.0 °C		7250 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 4.50 %,
Temperature 120 °C		7250 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 4.60 %,
Temperature 120 °C		7250 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 4.70 %,
Temperature 120 °C		7280 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 4.80 %,
Temperature 120 °C		7280 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.3 MPa
@Strain 4.90 %,
Temperature 120 °C		7300 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.3 MPa
@Strain 2.10 %,
Temperature 80.0 °C		7300 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.4 MPa
@Strain 5.00 %,
Temperature 120 °C		7310 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 5.50 %,
Temperature 120 °C		7320 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 2.70 %,
Temperature 100 °C		7320 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 2.60 %,
Temperature 60.0 °C		7320 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		7350 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 50.8 MPa
@Strain 6.00 %,
Temperature 120 °C		7370 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 7.50 %,
Temperature 120 °C		7370 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.9 MPa
@Strain 6.50 %,
Temperature 120 °C		7380 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.9 MPa
@Strain 7.00 %,
Temperature 120 °C		7380 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.0 MPa
@Strain 2.70 %,
Temperature 60.0 °C		7400 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 2.20 %,
Temperature 80.0 °C		7410 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 2.80 %,
Temperature 100 °C		7410 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.4 MPa
@Strain 2.80 %,
Temperature 60.0 °C		7450 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 2.90 %,
Temperature 60.0 °C		7500 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.8 MPa
@Strain 2.90 %,
Temperature 100 °C		7510 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.9 MPa
@Strain 1.40 %,
Temperature 23.0 °C		7530 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7540 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7590 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 3.00 %,
Temperature 100 °C		7590 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.4 MPa
@Strain 1.30 %,
Temperature 60.0 °C		7600 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 0.700 %,
Temperature 23.0 °C		7610 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 52.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7630 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.6 MPa
@Strain 3.10 %,
Temperature 100 °C		7630 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 2.30 %,
Temperature 80.0 °C		7640 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.9 MPa
@Strain 3.30 %,
Temperature 60.0 °C		7670 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.0 MPa
@Strain 3.20 %,
Temperature 100 °C		7690 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.1 MPa
@Strain 3.40 %,
Temperature 60.0 °C		7700 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.2 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7720 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.3 MPa
@Strain 3.30 %,
Temperature 100 °C		7730 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.5 MPa
@Strain 3.60 %,
Temperature 60.0 °C		7760 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 3.70 %,
Temperature 60.0 °C		7760 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.6 MPa
@Strain 3.40 %,
Temperature 100 °C		7770 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.7 MPa
@Strain 3.80 %,
Temperature 60.0 °C		7790 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.7 MPa
@Strain 3.90 %,
Temperature 60.0 °C		7790 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.8 MPa
@Strain 3.50 %,
Temperature 100 °C		7800 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.9 MPa
@Strain 4.00 %,
Temperature 60.0 °C		7820 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.9 MPa
@Strain 4.10 %,
Temperature 60.0 °C		7820 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 4.20 %,
Temperature 60.0 °C		7850 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 2.40 %,
Temperature 80.0 °C		7850 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.1 MPa
@Strain 3.60 %,
Temperature 100 °C		7850 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 3.70 %,
Temperature 100 °C		7860 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 4.30 %,
Temperature 60.0 °C		7860 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 4.40 %,
Temperature 60.0 °C		7860 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 4.50 %,
Temperature 60.0 °C		7860 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 1.50 %,
Temperature 23.0 °C		7860 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 7.00 %,
Temperature 60.0 °C		7860 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.3 MPa
@Strain 0.700 %,
Temperature 0.000 °C		7880 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.3 MPa
@Strain 4.60 %,
Temperature 60.0 °C		7880 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.3 MPa
@Strain 4.70 %,
Temperature 60.0 °C		7880 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 6.50 %,
Temperature 60.0 °C		7890 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 4.90 %,
Temperature 60.0 °C		7890 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 5.00 %,
Temperature 60.0 °C		7890 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 3.80 %,
Temperature 100 °C		7890 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 3.90 %,
Temperature 100 °C		7900 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 5.50 %,
Temperature 60.0 °C		7900 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 6.00 %,
Temperature 60.0 °C		7900 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 4.80 %,
Temperature 60.0 °C		7900 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.7 MPa
@Strain 1.40 %,
Temperature 60.0 °C		7930 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.7 MPa
@Strain 4.00 %,
Temperature 100 °C		7930 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 4.10 %,
Temperature 100 °C		7960 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 4.20 %,
Temperature 100 °C		7960 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.1 MPa
@Strain 4.30 %,
Temperature 100 °C		7990 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 4.50 %,
Temperature 100 °C		8010 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 2.50 %,
Temperature 80.0 °C		8010 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.3 MPa
@Strain 4.40 %,
Temperature 100 °C		8020 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.4 MPa
@Strain 4.60 %,
Temperature 100 °C		8040 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.5 MPa
@Strain 4.70 %,
Temperature 100 °C		8050 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.6 MPa
@Strain 4.80 %,
Temperature 100 °C		8060 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.6 MPa
@Strain 4.90 %,
Temperature 100 °C		8060 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.6 MPa
@Strain 5.00 %,
Temperature 100 °C		8060 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.9 MPa
@Strain 5.50 %,
Temperature 100 °C		8110 psi
@Strain 5.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.9 MPa
@Strain 0.600 %,
Temperature -40.0 °C		8110 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 56.1 MPa
@Strain 6.00 %,
Temperature 100 °C		8140 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.1 MPa
@Strain 2.60 %,
Temperature 80.0 °C		8140 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 0.800 %,
Temperature 0.000 °C		8150 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.2 MPa
@Strain 6.50 %,
Temperature 100 °C		8150 psi
@Strain 6.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 7.00 %,
Temperature 100 °C		8150 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.7 MPa
@Strain 1.60 %,
Temperature 23.0 °C		8220 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.8 MPa
@Strain 0.700 %,
Temperature -40.0 °C		8240 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 2.70 %,
Temperature 80.0 °C		8270 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		8340 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.6 MPa
@Strain 0.800 %,
Temperature 23.0 °C		8350 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 57.7 MPa
@Strain 2.80 %,
Temperature 80.0 °C		8370 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.3 MPa
@Strain 2.90 %,
Temperature 80.0 °C		8460 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.7 MPa
@Strain 3.00 %,
Temperature 80.0 °C		8510 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.1 MPa
@Strain 3.10 %,
Temperature 80.0 °C		8570 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.1 MPa
@Strain 1.70 %,
Temperature 23.0 °C		8570 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.6 MPa
@Strain 3.20 %,
Temperature 80.0 °C		8640 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.8 MPa
@Strain 3.30 %,
Temperature 80.0 °C		8670 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.9 MPa
@Strain 1.60 %,
Temperature 60.0 °C		8690 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		8730 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.4 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8760 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.6 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8790 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.9 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8830 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.0 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8850 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.2 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8880 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.2 MPa
@Strain 1.80 %,
Temperature 23.0 °C		8880 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.4 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8910 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.6 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8930 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.7 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8950 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.8 MPa
@Strain 0.800 %,
Temperature 0.000 °C		8960 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 61.9 MPa
@Strain 0.900 %,
Temperature 0.000 °C		8980 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.9 MPa
@Strain 4.30 %,
Temperature 80.0 °C		8980 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.9 MPa
@Strain 4.40 %,
Temperature 80.0 °C		8980 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.1 MPa
@Strain 4.50 %,
Temperature 80.0 °C		9010 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.1 MPa
@Strain 4.60 %,
Temperature 80.0 °C		9010 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.2 MPa
@Strain 1.70 %,
Temperature 60.0 °C		9020 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.3 MPa
@Strain 4.70 %,
Temperature 80.0 °C		9040 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 4.80 %,
Temperature 80.0 °C		9050 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 4.90 %,
Temperature 80.0 °C		9050 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		9060 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.7 MPa
@Strain 5.50 %,
Temperature 80.0 °C		9090 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.0 MPa
@Strain 6.00 %,
Temperature 80.0 °C		9140 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.1 MPa
@Strain 6.50 %,
Temperature 80.0 °C		9150 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.2 MPa
@Strain 7.00 %,
Temperature 80.0 °C		9170 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.2 MPa
@Strain 1.90 %,
Temperature 23.0 °C		9170 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.1 MPa
@Strain 0.700 %,
Temperature -40.0 °C		9300 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 64.2 MPa
@Strain 1.80 %,
Temperature 60.0 °C		9310 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 0.800 %,
Temperature -40.0 °C		9400 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 65.2 MPa
@Strain 2.00 %,
Temperature 23.0 °C		9460 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.5 MPa
@Strain 0.900 %,
Temperature 23.0 °C		9500 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.2 MPa
@Strain 1.90 %,
Temperature 60.0 °C		9600 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.0 MPa
@Strain 2.10 %,
Temperature 23.0 °C		9720 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 67.4 MPa
@Strain 1.00 %,
Temperature 0.000 °C		9780 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.2 MPa
@Strain 2.00 %,
Temperature 60.0 °C		9890 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.6 MPa
@Strain 2.20 %,
Temperature 23.0 °C		9950 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.8 MPa
@Strain 0.900 %,
Temperature 0.000 °C		9980 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 70.0 MPa
@Strain 2.10 %,
Temperature 60.0 °C		10200 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 70.2 MPa
@Strain 2.30 %,
Temperature 23.0 °C		10200 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.4 MPa
@Strain 2.40 %,
Temperature 23.0 °C		10400 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.6 MPa
@Strain 2.20 %,
Temperature 60.0 °C		10400 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.7 MPa
@Strain 1.00 %,
Temperature 23.0 °C		10400 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.0 MPa
@Strain 1.10 %,
Temperature 0.000 °C		10400 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.0 MPa
@Strain 0.800 %,
Temperature -40.0 °C		10400 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 72.2 MPa
@Strain 0.900 %,
Temperature -40.0 °C		10500 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10500 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.0 MPa
@Strain 2.30 %,
Temperature 60.0 °C		10600 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.2 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10600 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.8 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10700 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.3 MPa
@Strain 2.80 %,
Temperature 23.0 °C		10800 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.3 MPa
@Strain 2.40 %,
Temperature 60.0 °C		10800 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.4 MPa
@Strain 4.70 %,
Temperature 23.0 °C		10800 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.5 MPa
@Strain 4.60 %,
Temperature 23.0 °C		10800 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.6 MPa
@Strain 4.50 %,
Temperature 23.0 °C		10800 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 4.40 %,
Temperature 23.0 °C		10800 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 2.90 %,
Temperature 23.0 °C		10800 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.8 MPa
@Strain 3.00 %,
Temperature 23.0 °C		10800 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.8 MPa
@Strain 4.30 %,
Temperature 23.0 °C		10800 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.9 MPa
@Strain 4.20 %,
Temperature 23.0 °C		10900 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 3.20 %,
Temperature 23.0 °C		10900 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 3.90 %,
Temperature 23.0 °C		10900 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 4.00 %,
Temperature 23.0 °C		10900 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 4.10 %,
Temperature 23.0 °C		10900 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 3.70 %,
Temperature 23.0 °C		10900 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 3.80 %,
Temperature 23.0 °C		10900 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 3.50 %,
Temperature 23.0 °C		10900 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 3.60 %,
Temperature 23.0 °C		10900 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 3.10 %,
Temperature 23.0 °C		10900 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.2 MPa
@Strain 3.30 %,
Temperature 23.0 °C		10900 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.2 MPa
@Strain 3.40 %,
Temperature 23.0 °C		10900 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.4 MPa
@Strain 2.50 %,
Temperature 60.0 °C		10900 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.5 MPa
@Strain 1.00 %,
Temperature 0.000 °C		11000 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 2.60 %,
Temperature 60.0 °C		11100 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 1.20 %,
Temperature 0.000 °C		11100 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.9 MPa
@Strain 2.70 %,
Temperature 60.0 °C		11200 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.4 MPa
@Strain 2.80 %,
Temperature 60.0 °C		11200 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.7 MPa
@Strain 1.10 %,
Temperature 23.0 °C		11300 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.8 MPa
@Strain 2.90 %,
Temperature 60.0 °C		11300 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.8 MPa
@Strain 4.80 %,
Temperature 60.0 °C		11300 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.9 MPa
@Strain 4.60 %,
Temperature 60.0 °C		11300 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.0 MPa
@Strain 4.70 %,
Temperature 60.0 °C		11300 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C		11300 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.1 MPa
@Strain 4.50 %,
Temperature 60.0 °C		11300 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.2 MPa
@Strain 3.10 %,
Temperature 60.0 °C		11300 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.2 MPa
@Strain 4.20 %,
Temperature 60.0 °C		11300 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.2 MPa
@Strain 4.30 %,
Temperature 60.0 °C		11300 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.2 MPa
@Strain 4.40 %,
Temperature 60.0 °C		11300 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 3.30 %,
Temperature 60.0 °C		11400 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 3.40 %,
Temperature 60.0 °C		11400 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 3.90 %,
Temperature 60.0 °C		11400 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 4.00 %,
Temperature 60.0 °C		11400 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 4.10 %,
Temperature 60.0 °C		11400 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.50 %,
Temperature 60.0 °C		11400 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.60 %,
Temperature 60.0 °C		11400 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.70 %,
Temperature 60.0 °C		11400 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.80 %,
Temperature 60.0 °C		11400 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.20 %,
Temperature 60.0 °C		11400 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.4 MPa
@Strain 1.00 %,
Temperature -40.0 °C		11500 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 79.8 MPa
@Strain 0.900 %,
Temperature -40.0 °C		11600 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 80.6 MPa
@Strain 1.30 %,
Temperature 0.000 °C		11700 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 81.9 MPa
@Strain 1.10 %,
Temperature 0.000 °C		11900 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 1.20 %,
Temperature 23.0 °C		12100 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.4 MPa
@Strain 1.40 %,
Temperature 0.000 °C		12200 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.5 MPa
@Strain 1.10 %,
Temperature -40.0 °C		12500 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.3 MPa
@Strain 1.00 %,
Temperature -40.0 °C		12700 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.0 MPa
@Strain 1.50 %,
Temperature 0.000 °C		12800 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.0 MPa
@Strain 1.20 %,
Temperature 0.000 °C		12800 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.2 MPa
@Strain 1.30 %,
Temperature 23.0 °C		12800 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 91.1 MPa
@Strain 1.60 %,
Temperature 0.000 °C		13200 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 92.7 MPa
@Strain 1.40 %,
Temperature 23.0 °C		13400 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 93.5 MPa
@Strain 1.20 %,
Temperature -40.0 °C		13600 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.7 MPa
@Strain 1.30 %,
Temperature 0.000 °C		13600 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13600 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 94.3 MPa
@Strain 1.10 %,
Temperature -40.0 °C		13700 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.5 MPa
@Strain 1.80 %,
Temperature 0.000 °C		14000 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 96.9 MPa
@Strain 1.50 %,
Temperature 23.0 °C		14100 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.9 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14300 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.9 MPa
@Strain 1.40 %,
Temperature 0.000 °C		14300 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.7 MPa
@Strain 1.30 %,
Temperature -40.0 °C		14500 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.7 MPa
@Strain 1.20 %,
Temperature -40.0 °C		14610 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 100.7 MPa
@Strain 1.60 %,
Temperature 23.0 °C		14610 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 101.3 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14690 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 103.2 MPa
@Strain 2.10 %,
Temperature 0.000 °C		14970 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 103.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		15050 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 104.2 MPa
@Strain 1.70 %,
Temperature 23.0 °C		15110 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 105.2 MPa
@Strain 2.20 %,
Temperature 0.000 °C		15260 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 105.9 MPa
@Strain 1.40 %,
Temperature -40.0 °C		15360 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.7 MPa
@Strain 2.30 %,
Temperature 0.000 °C		15480 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.9 MPa
@Strain 1.30 %,
Temperature -40.0 °C		15500 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.4 MPa
@Strain 1.80 %,
Temperature 23.0 °C		15580 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 108.1 MPa
@Strain 2.40 %,
Temperature 0.000 °C		15680 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 108.3 MPa
@Strain 1.60 %,
Temperature 0.000 °C		15710 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 108.9 MPa
@Strain 2.50 %,
Temperature 0.000 °C		15790 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.4 MPa
@Strain 2.60 %,
Temperature 0.000 °C		15870 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.4 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15870 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 110.4 MPa
@Strain 1.90 %,
Temperature 23.0 °C		16010 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 111.8 MPa
@Strain 1.50 %,
Temperature -40.0 °C		16220 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 1.70 %,
Temperature 0.000 °C		16330 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.8 MPa
@Strain 1.40 %,
Temperature -40.0 °C		16360 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.9 MPa
@Strain 2.00 %,
Temperature 23.0 °C		16370 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 115.4 MPa
@Strain 2.10 %,
Temperature 23.0 °C		16740 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 116.5 MPa
@Strain 1.80 %,
Temperature 0.000 °C		16900 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 117.5 MPa
@Strain 2.20 %,
Temperature 23.0 °C		17040 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 117.7 MPa
@Strain 1.60 %,
Temperature -40.0 °C		17070 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.3 MPa
@Strain 1.50 %,
Temperature -40.0 °C		17160 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.1 MPa
@Strain 2.30 %,
Temperature 23.0 °C		17270 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120 MPa
@Strain 1.90 %,
Temperature 0.000 °C		17400 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 123.1 MPa
@Strain 1.70 %,
Temperature -40.0 °C		17850 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.3 MPa
@Strain 1.60 %,
Temperature -40.0 °C		17880 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 123.3 MPa
@Strain 2.00 %,
Temperature 0.000 °C		17880 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 126.3 MPa
@Strain 2.10 %,
Temperature 0.000 °C		18320 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 127.9 MPa
@Strain 1.70 %,
Temperature -40.0 °C		18550 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 128.2 MPa
@Strain 1.80 %,
Temperature -40.0 °C		18590 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 129.1 MPa
@Strain 2.20 %,
Temperature 0.000 °C		18720 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 131.4 MPa
@Strain 2.30 %,
Temperature 0.000 °C		19060 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 132.3 MPa
@Strain 1.80 %,
Temperature -40.0 °C		19190 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 132.9 MPa
@Strain 1.90 %,
Temperature -40.0 °C		19280 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 136.5 MPa
@Strain 1.90 %,
Temperature -40.0 °C		19800 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 137.4 MPa
@Strain 2.00 %,
Temperature -40.0 °C		19930 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		20380 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 141.6 MPa
@Strain 2.10 %,
Temperature -40.0 °C		20540 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 143.9 MPa
@Strain 2.10 %,
Temperature -40.0 °C		20870 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 145.6 MPa
@Strain 2.20 %,
Temperature -40.0 °C		21120 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 146.8 MPa
@Strain 2.20 %,
Temperature -40.0 °C		21290 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 149.2 MPa
@Strain 2.30 %,
Temperature -40.0 °C		21640 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 152.8 MPa
@Strain 2.40 %,
Temperature -40.0 °C		22160 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  5.00 GPa
@Temperature 23.0 °C		725 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 7.50 GPa
@Temperature 23.0 °C		1090 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 7.00 GPa
@Temperature 23.0 °C		1020 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched (ISO)  3.80 kJ/m²
@Temperature -40.0 °C		1.81 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
@Temperature 23.0 °C		16.7 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature 23.0 °C		1.43 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 255 °C491 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C446 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FillerGlass/MineralDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-(MD+GF)38<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass/Mineral Reinforced ResinsDAM
 Low Warp ResinsDAM
Resin IdentificationPA66-(MD+GF)38ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45421.html

免责声明: 本文 DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4