- 密度 [g/cm3]: 1.38
- 成型收缩率 [%]: 0.01
- 缺口冲击强度: 0.8
- 弯曲模量 [MPa]: 1.80
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | DAM; ASTM D792 | ||
| Density | 1.38 g/cc | 0.0499 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 32 % | 32 % | DAM | ||
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 1.60 mm | 0.010 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.010 cm/cm @Thickness 1.60 mm | 0.010 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.015 cm/cm @Thickness 6.40 mm | 0.015 in/in @Thickness 0.252 in | Flow; DAM | |||
| 0.015 cm/cm @Thickness 6.40 mm | 0.015 in/in @Thickness 0.252 in | Transverse; DAM | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 58.0 MPa @Temperature 23.0 °C | 8410 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 78.0 MPa @Temperature 23.0 °C | 11300 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 76.0 MPa @Temperature 23.0 °C | 11000 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 15 % @Temperature 23.0 °C | 15 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 17 % @Temperature 23.0 °C | 17 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.90 GPa @Temperature 23.0 °C | 276 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 4.80 GPa @Temperature 23.0 °C | 696 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C | 261 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 4.40 GPa @Temperature 23.0 °C | 638 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 4.41 GPa @Temperature 23.0 °C | 640 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 16.0 J/cm @Temperature 23.0 °C | 30.0 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 180/1A | |||
| 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1U | ||
| 85.0 kJ/m² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1U | |||
| 110 kJ/m² @Temperature 23.0 °C | 52.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | |||
| 330 kJ/m² @Temperature 23.0 °C | 157 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1U | |||
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C | 35.7 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 8.00 J/cm² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 12.0 J/cm² @Temperature 23.0 °C | 57.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 33.0 J/cm² @Temperature 23.0 °C | 157 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -40.0 °C | 1.43 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 258 °C | 496 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ASTM D648 | ||
| 80.0 °C | 176 °F | DAM; ISO 75-1/-2 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 257 °C | 495 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Impact Modifier | DAM | |||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Impact Resistance, Good | DAM | |||
| Warpage, Low | DAM | ||||
| Filler | Mineral filler | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IMD32< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Low Warp Resins | DAM | |||
| Mineral Reinforced Resins | DAM | ||||
| Toughened Resins | DAM | ||||
| Resin Identification | PA66-IMD32 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Tool, Power & Others | DAM | ||||