  4. DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66

DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66

DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66 物性表: DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.41
  • 成型收缩率 [%]: 0.01
  • 缺口冲击强度: 0.85
  • 弯曲模量 [MPa]: 1.80
  • 热变形温度 [℃]: 205.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.41 g/cc1.41 g/ccDAM; ASTM D792
Density 1.41 g/cc0.0509 lb/in³DAM; ISO 1183
Filler Content 36 %36 %DAM
Linear Mold Shrinkage  0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Flow; DAM
 0.010 cm/cm
@Thickness 1.60 mm		0.010 in/in
@Thickness 0.0630 in		Flow; DAM
 0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Transverse; DAM
 0.010 cm/cm
@Thickness 1.60 mm		0.010 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.014 cm/cm
@Thickness 6.40 mm		0.014 in/in
@Thickness 0.252 in		Flow; DAM
 0.014 cm/cm
@Thickness 6.40 mm		0.014 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  58.0 MPa
@Temperature 23.0 °C		8410 psi
@Temperature 73.4 °F		50%RH; ISO 527
 76.0 MPa
@Temperature 23.0 °C		11000 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength 74.0 MPa
@Temperature 23.0 °C		10700 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  0.600 MPa
@Strain 0.100 %,
Temperature 150 °C		87.0 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.700 MPa
@Strain 0.100 %,
Temperature 150 °C		102 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.810 MPa
@Strain 0.100 %,
Temperature 120 °C		117 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.850 MPa
@Strain 0.100 %,
Temperature 120 °C		123 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.900 MPa
@Strain 0.100 %,
Temperature 100 °C		131 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 0.900 MPa
@Strain 0.100 %,
Temperature 80.0 °C		131 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.00 MPa
@Strain 0.100 %,
Temperature 100 °C		145 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.05 MPa
@Strain 0.100 %,
Temperature 80.0 °C		152 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 1.12 MPa
@Strain 0.100 %,
Temperature 60.0 °C		162 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.16 MPa
@Strain 0.200 %,
Temperature 150 °C		168 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.42 MPa
@Strain 0.200 %,
Temperature 150 °C		206 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.51 MPa
@Strain 0.100 %,
Temperature 23.0 °C		219 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.59 MPa
@Strain 0.200 %,
Temperature 120 °C		231 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.72 MPa
@Strain 0.200 %,
Temperature 120 °C		249 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.73 MPa
@Strain 0.300 %,
Temperature 150 °C		251 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.77 MPa
@Strain 0.200 %,
Temperature 80.0 °C		257 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.80 MPa
@Strain 0.200 %,
Temperature 100 °C		261 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.00 MPa
@Strain 0.200 %,
Temperature 100 °C		290 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.09 MPa
@Strain 0.300 %,
Temperature 150 °C		303 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.12 MPa
@Strain 0.200 %,
Temperature 80.0 °C		307 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.14 MPa
@Strain 0.200 %,
Temperature 60.0 °C		310 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.15 MPa
@Strain 0.400 %,
Temperature 150 °C		312 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.19 MPa
@Strain 0.300 %,
Temperature 120 °C		318 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.40 MPa
@Strain 0.400 %,
Temperature 150 °C		348 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.300 %,
Temperature 100 °C		363 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.50 MPa
@Strain 0.300 %,
Temperature 120 °C		363 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.60 MPa
@Strain 0.300 %,
Temperature 80.0 °C		377 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.60 MPa
@Strain 0.100 %,
Temperature 60.0 °C		377 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 2.78 MPa
@Strain 0.400 %,
Temperature 120 °C		403 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.81 MPa
@Strain 0.500 %,
Temperature 150 °C		408 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.92 MPa
@Strain 0.300 %,
Temperature 100 °C		424 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.99 MPa
@Strain 0.200 %,
Temperature 23.0 °C		434 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.13 MPa
@Strain 0.500 %,
Temperature 150 °C		454 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.14 MPa
@Strain 0.300 %,
Temperature 80.0 °C		455 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.17 MPa
@Strain 0.300 %,
Temperature 60.0 °C		460 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.17 MPa
@Strain 0.600 %,
Temperature 150 °C		460 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.29 MPa
@Strain 0.400 %,
Temperature 80.0 °C		477 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.30 MPa
@Strain 0.400 %,
Temperature 100 °C		479 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.50 MPa
@Strain 0.400 %,
Temperature 100 °C		508 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.58 MPa
@Strain 0.500 %,
Temperature 120 °C		519 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.64 MPa
@Strain 0.700 %,
Temperature 150 °C		528 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.74 MPa
@Strain 0.400 %,
Temperature 120 °C		542 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.79 MPa
@Strain 0.600 %,
Temperature 150 °C		550 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.90 MPa
@Strain 0.400 %,
Temperature 80.0 °C		566 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.07 MPa
@Strain 0.400 %,
Temperature 60.0 °C		590 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.09 MPa
@Strain 0.800 %,
Temperature 150 °C		593 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.34 MPa
@Strain 0.500 %,
Temperature 100 °C		629 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.35 MPa
@Strain 0.600 %,
Temperature 120 °C		631 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.40 MPa
@Strain 0.300 %,
Temperature 23.0 °C		638 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.41 MPa
@Strain 0.500 %,
Temperature 80.0 °C		640 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.45 MPa
@Strain 0.500 %,
Temperature 120 °C		645 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.46 MPa
@Strain 0.700 %,
Temperature 150 °C		647 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.57 MPa
@Strain 0.900 %,
Temperature 150 °C		663 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.60 MPa
@Strain 0.100 %,
Temperature 0.000 °C		667 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 4.74 MPa
@Strain 0.500 %,
Temperature 100 °C		687 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.90 MPa
@Strain 0.100 %,
Temperature 23.0 °C		711 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 4.99 MPa
@Strain 1.00 %,
Temperature 150 °C		724 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.04 MPa
@Strain 0.600 %,
Temperature 100 °C		731 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.07 MPa
@Strain 0.700 %,
Temperature 120 °C		735 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.12 MPa
@Strain 0.800 %,
Temperature 150 °C		743 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.17 MPa
@Strain 0.500 %,
Temperature 60.0 °C		750 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.21 MPa
@Strain 0.200 %,
Temperature 60.0 °C		756 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.22 MPa
@Strain 0.600 %,
Temperature 120 °C		757 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.25 MPa
@Strain 0.600 %,
Temperature 80.0 °C		761 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.30 MPa
@Strain 0.100 %,
Temperature -40.0 °C		769 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 5.37 MPa
@Strain 1.10 %,
Temperature 150 °C		779 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.44 MPa
@Strain 0.500 %,
Temperature 80.0 °C		789 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.49 MPa
@Strain 0.400 %,
Temperature 23.0 °C		796 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.50 MPa
@Strain 0.700 %,
Temperature 120 °C		798 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.64 MPa
@Strain 0.600 %,
Temperature 100 °C		818 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.69 MPa
@Strain 0.800 %,
Temperature 120 °C		825 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.70 MPa
@Strain 0.100 %,
Temperature 0.000 °C		827 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.72 MPa
@Strain 0.900 %,
Temperature 150 °C		830 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.74 MPa
@Strain 0.700 %,
Temperature 100 °C		833 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.79 MPa
@Strain 1.20 %,
Temperature 150 °C		840 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.84 MPa
@Strain 0.600 %,
Temperature 60.0 °C		847 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.99 MPa
@Strain 0.800 %,
Temperature 120 °C		869 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.01 MPa
@Strain 0.100 %,
Temperature -40.0 °C		872 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.08 MPa
@Strain 0.700 %,
Temperature 80.0 °C		882 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.17 MPa
@Strain 1.30 %,
Temperature 150 °C		895 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.24 MPa
@Strain 0.900 %,
Temperature 120 °C		905 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.32 MPa
@Strain 1.00 %,
Temperature 150 °C		917 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.43 MPa
@Strain 0.600 %,
Temperature 80.0 °C		933 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.44 MPa
@Strain 0.800 %,
Temperature 100 °C		934 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.52 MPa
@Strain 0.700 %,
Temperature 100 °C		946 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.52 MPa
@Strain 1.40 %,
Temperature 150 °C		946 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.64 MPa
@Strain 0.900 %,
Temperature 120 °C		963 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.65 MPa
@Strain 0.800 %,
Temperature 80.0 °C		965 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.67 MPa
@Strain 1.00 %,
Temperature 120 °C		967 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.82 MPa
@Strain 0.700 %,
Temperature 60.0 °C		989 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.84 MPa
@Strain 1.50 %,
Temperature 150 °C		992 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.93 MPa
@Strain 1.10 %,
Temperature 150 °C		1010 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.11 MPa
@Strain 0.900 %,
Temperature 100 °C		1030 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.12 MPa
@Strain 0.800 %,
Temperature 100 °C		1030 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.13 MPa
@Strain 1.60 %,
Temperature 150 °C		1030 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.30 MPa
@Strain 1.10 %,
Temperature 120 °C		1060 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.41 MPa
@Strain 1.00 %,
Temperature 120 °C		1070 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.42 MPa
@Strain 1.70 %,
Temperature 150 °C		1080 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.47 MPa
@Strain 1.20 %,
Temperature 150 °C		1080 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.48 MPa
@Strain 0.900 %,
Temperature 80.0 °C		1080 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.50 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1090 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.58 MPa
@Strain 0.500 %,
Temperature 23.0 °C		1100 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 0.800 %,
Temperature 60.0 °C		1110 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.68 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1110 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.72 MPa
@Strain 0.900 %,
Temperature 100 °C		1120 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.74 MPa
@Strain 1.80 %,
Temperature 150 °C		1120 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.78 MPa
@Strain 1.00 %,
Temperature 100 °C		1130 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.90 MPa
@Strain 1.20 %,
Temperature 120 °C		1150 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.95 MPa
@Strain 1.30 %,
Temperature 150 °C		1150 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.03 MPa
@Strain 1.90 %,
Temperature 150 °C		1160 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.20 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1190 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.24 MPa
@Strain 1.30 %,
Temperature 120 °C		1200 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.38 MPa
@Strain 2.00 %,
Temperature 150 °C		1220 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.39 MPa
@Strain 1.10 %,
Temperature 100 °C		1220 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.45 MPa
@Strain 0.900 %,
Temperature 60.0 °C		1230 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.48 MPa
@Strain 1.00 %,
Temperature 100 °C		1230 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.49 MPa
@Strain 1.50 %,
Temperature 150 °C		1230 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.63 MPa
@Strain 2.10 %,
Temperature 150 °C		1250 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 1.40 %,
Temperature 120 °C		1260 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 1.20 %,
Temperature 120 °C		1260 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.78 MPa
@Strain 0.800 %,
Temperature 80.0 °C		1270 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.91 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1290 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.92 MPa
@Strain 1.60 %,
Temperature 150 °C		1290 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.95 MPa
@Strain 2.20 %,
Temperature 150 °C		1300 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.00 MPa
@Strain 1.20 %,
Temperature 100 °C		1310 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.05 MPa
@Strain 1.10 %,
Temperature 100 °C		1310 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.09 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1320 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.16 MPa
@Strain 1.50 %,
Temperature 120 °C		1330 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.18 MPa
@Strain 2.30 %,
Temperature 150 °C		1330 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.20 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1330 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 9.26 MPa
@Strain 1.00 %,
Temperature 60.0 °C		1340 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.28 MPa
@Strain 1.30 %,
Temperature 120 °C		1350 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.37 MPa
@Strain 2.40 %,
Temperature 150 °C		1360 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.44 MPa
@Strain 0.600 %,
Temperature 23.0 °C		1370 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.46 MPa
@Strain 1.70 %,
Temperature 150 °C		1370 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.56 MPa
@Strain 1.20 %,
Temperature 100 °C		1390 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.57 MPa
@Strain 1.30 %,
Temperature 100 °C		1390 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.59 MPa
@Strain 2.50 %,
Temperature 150 °C		1390 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.62 MPa
@Strain 0.900 %,
Temperature 80.0 °C		1400 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.63 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1400 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.70 MPa
@Strain 1.60 %,
Temperature 120 °C		1410 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.85 MPa
@Strain 2.60 %,
Temperature 150 °C		1430 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.86 MPa
@Strain 1.40 %,
Temperature 120 °C		1430 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.88 MPa
@Strain 1.80 %,
Temperature 150 °C		1430 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.93 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1440 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 10.02 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1453 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.02 MPa
@Strain 1.40 %,
Temperature 100 °C		1453 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.1 MPa
@Strain 2.70 %,
Temperature 150 °C		1460 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.16 MPa
@Strain 1.70 %,
Temperature 120 °C		1474 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.16 MPa
@Strain 1.30 %,
Temperature 100 °C		1474 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.26 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1488 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.3 MPa
@Strain 1.90 %,
Temperature 150 °C		1490 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.36 MPa
@Strain 2.80 %,
Temperature 150 °C		1503 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.43 MPa
@Strain 1.50 %,
Temperature 100 °C		1513 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.44 MPa
@Strain 1.50 %,
Temperature 120 °C		1514 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.49 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1521 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.53 MPa
@Strain 1.80 %,
Temperature 120 °C		1527 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.6 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1540 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 10.61 MPa
@Strain 2.90 %,
Temperature 150 °C		1539 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.7 MPa
@Strain 1.20 %,
Temperature 60.0 °C		1550 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.72 MPa
@Strain 2.00 %,
Temperature 150 °C		1555 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.81 MPa
@Strain 3.00 %,
Temperature 150 °C		1568 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.87 MPa
@Strain 1.90 %,
Temperature 120 °C		1577 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.89 MPa
@Strain 1.40 %,
Temperature 100 °C		1579 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.92 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1584 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.93 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1585 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 10.97 MPa
@Strain 1.60 %,
Temperature 100 °C		1591 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.0 MPa
@Strain 3.10 %,
Temperature 150 °C		1600 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.02 MPa
@Strain 1.60 %,
Temperature 120 °C		1598 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.14 MPa
@Strain 2.10 %,
Temperature 150 °C		1616 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.19 MPa
@Strain 3.20 %,
Temperature 150 °C		1623 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.19 MPa
@Strain 0.700 %,
Temperature 23.0 °C		1623 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.28 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1636 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.3 MPa
@Strain 2.00 %,
Temperature 120 °C		1640 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.35 MPa
@Strain 3.30 %,
Temperature 150 °C		1646 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.41 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1655 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.43 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1658 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.47 MPa
@Strain 1.70 %,
Temperature 120 °C		1664 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.52 MPa
@Strain 1.70 %,
Temperature 100 °C		1671 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.52 MPa
@Strain 1.50 %,
Temperature 100 °C		1671 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.57 MPa
@Strain 3.40 %,
Temperature 150 °C		1678 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.57 MPa
@Strain 2.20 %,
Temperature 150 °C		1678 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 2.10 %,
Temperature 120 °C		1700 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.77 MPa
@Strain 3.50 %,
Temperature 150 °C		1707 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.86 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1720 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.93 MPa
@Strain 2.40 %,
Temperature 150 °C		1730 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.94 MPa
@Strain 1.60 %,
Temperature 100 °C		1732 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.96 MPa
@Strain 3.60 %,
Temperature 150 °C		1735 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.99 MPa
@Strain 1.80 %,
Temperature 100 °C		1739 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.03 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1745 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.05 MPa
@Strain 1.80 %,
Temperature 120 °C		1748 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.05 MPa
@Strain 3.70 %,
Temperature 150 °C		1748 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.1 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1750 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 12.13 MPa
@Strain 1.40 %,
Temperature 60.0 °C		1759 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.13 MPa
@Strain 2.20 %,
Temperature 120 °C		1759 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.14 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1761 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 1.90 %,
Temperature 120 °C		1770 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.28 MPa
@Strain 3.80 %,
Temperature 150 °C		1781 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.29 MPa
@Strain 2.50 %,
Temperature 150 °C		1783 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.33 MPa
@Strain 0.800 %,
Temperature 23.0 °C		1788 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 12.4 MPa
@Strain 1.70 %,
Temperature 100 °C		1800 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.42 MPa
@Strain 2.30 %,
Temperature 120 °C		1801 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.47 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1809 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.5 MPa
@Strain 2.00 %,
Temperature 120 °C		1810 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.5 MPa
@Strain 3.90 %,
Temperature 150 °C		1810 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.51 MPa
@Strain 1.90 %,
Temperature 100 °C		1814 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.58 MPa
@Strain 0.600 %,
Temperature 60.0 °C		1825 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 12.59 MPa
@Strain 2.60 %,
Temperature 150 °C		1826 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.66 MPa
@Strain 4.00 %,
Temperature 150 °C		1836 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.68 MPa
@Strain 2.40 %,
Temperature 120 °C		1839 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.69 MPa
@Strain 4.10 %,
Temperature 150 °C		1841 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.72 MPa
@Strain 1.50 %,
Temperature 60.0 °C		1845 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.78 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1854 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.92 MPa
@Strain 4.20 %,
Temperature 150 °C		1874 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.95 MPa
@Strain 2.70 %,
Temperature 150 °C		1878 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.95 MPa
@Strain 2.00 %,
Temperature 100 °C		1878 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.95 MPa
@Strain 2.10 %,
Temperature 120 °C		1878 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.01 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1887 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.03 MPa
@Strain 1.80 %,
Temperature 100 °C		1890 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.08 MPa
@Strain 4.30 %,
Temperature 150 °C		1897 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.08 MPa
@Strain 2.50 %,
Temperature 120 °C		1897 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.2 MPa
@Strain 4.40 %,
Temperature 150 °C		1910 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.25 MPa
@Strain 1.60 %,
Temperature 60.0 °C		1922 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.3 MPa
@Strain 4.50 %,
Temperature 150 °C		1930 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.31 MPa
@Strain 2.80 %,
Temperature 150 °C		1930 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.43 MPa
@Strain 2.10 %,
Temperature 100 °C		1948 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.45 MPa
@Strain 2.60 %,
Temperature 120 °C		1951 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.47 MPa
@Strain 2.20 %,
Temperature 120 °C		1954 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.47 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1954 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.49 MPa
@Strain 4.60 %,
Temperature 150 °C		1957 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.51 MPa
@Strain 1.90 %,
Temperature 100 °C		1959 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.54 MPa
@Strain 0.900 %,
Temperature 23.0 °C		1964 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.55 MPa
@Strain 1.90 %,
Temperature 80.0 °C		1965 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.61 MPa
@Strain 2.90 %,
Temperature 150 °C		1974 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.65 MPa
@Strain 4.70 %,
Temperature 150 °C		1980 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.7 MPa
@Strain 1.70 %,
Temperature 60.0 °C		1990 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.78 MPa
@Strain 4.80 %,
Temperature 150 °C		1999 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.78 MPa
@Strain 2.20 %,
Temperature 100 °C		1999 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.79 MPa
@Strain 2.70 %,
Temperature 120 °C		2000 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.82 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2004 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 13.85 MPa
@Strain 2.30 %,
Temperature 120 °C		2009 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.88 MPa
@Strain 4.90 %,
Temperature 150 °C		2013 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.91 MPa
@Strain 3.00 %,
Temperature 150 °C		2017 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.96 MPa
@Strain 2.80 %,
Temperature 120 °C		2025 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.97 MPa
@Strain 5.00 %,
Temperature 150 °C		2026 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.0 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2030 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 14.03 MPa
@Strain 2.00 %,
Temperature 100 °C		2035 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.1 MPa
@Strain 2.00 %,
Temperature 80.0 °C		2050 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.1 MPa
@Strain 2.30 %,
Temperature 100 °C		2050 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.19 MPa
@Strain 1.50 %,
Temperature 80.0 °C		2058 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.22 MPa
@Strain 3.20 %,
Temperature 150 °C		2062 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.26 MPa
@Strain 1.80 %,
Temperature 60.0 °C		2068 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.28 MPa
@Strain 2.90 %,
Temperature 120 °C		2071 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.3 MPa
@Strain 2.40 %,
Temperature 120 °C		2070 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.46 MPa
@Strain 3.30 %,
Temperature 150 °C		2097 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.47 MPa
@Strain 5.50 %,
Temperature 150 °C		2099 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.48 MPa
@Strain 2.10 %,
Temperature 100 °C		2100 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.52 MPa
@Strain 2.40 %,
Temperature 100 °C		2106 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.62 MPa
@Strain 3.00 %,
Temperature 120 °C		2120 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.63 MPa
@Strain 2.50 %,
Temperature 120 °C		2122 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.67 MPa
@Strain 2.10 %,
Temperature 80.0 °C		2128 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.76 MPa
@Strain 3.40 %,
Temperature 150 °C		2141 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.76 MPa
@Strain 1.60 %,
Temperature 80.0 °C		2141 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.77 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2142 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 14.81 MPa
@Strain 2.20 %,
Temperature 100 °C		2148 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.88 MPa
@Strain 1.90 %,
Temperature 60.0 °C		2158 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.91 MPa
@Strain 3.10 %,
Temperature 120 °C		2163 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.96 MPa
@Strain 2.50 %,
Temperature 100 °C		2170 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.98 MPa
@Strain 1.00 %,
Temperature 23.0 °C		2173 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.06 MPa
@Strain 3.50 %,
Temperature 150 °C		2184 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.14 MPa
@Strain 2.60 %,
Temperature 120 °C		2196 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.15 MPa
@Strain 6.00 %,
Temperature 150 °C		2197 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.16 MPa
@Strain 2.20 %,
Temperature 80.0 °C		2199 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.22 MPa
@Strain 3.20 %,
Temperature 120 °C		2207 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.29 MPa
@Strain 0.800 %,
Temperature 60.0 °C		2218 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 15.3 MPa
@Strain 3.60 %,
Temperature 150 °C		2220 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.35 MPa
@Strain 2.30 %,
Temperature 100 °C		2226 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.38 MPa
@Strain 2.60 %,
Temperature 100 °C		2231 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.38 MPa
@Strain 2.00 %,
Temperature 60.0 °C		2231 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 3.30 %,
Temperature 120 °C		2230 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.46 MPa
@Strain 2.70 %,
Temperature 120 °C		2242 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.46 MPa
@Strain 1.70 %,
Temperature 80.0 °C		2242 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.59 MPa
@Strain 6.50 %,
Temperature 150 °C		2261 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.6 MPa
@Strain 3.70 %,
Temperature 150 °C		2260 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.62 MPa
@Strain 2.30 %,
Temperature 80.0 °C		2265 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.68 MPa
@Strain 3.40 %,
Temperature 120 °C		2274 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 2.70 %,
Temperature 100 °C		2281 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.79 MPa
@Strain 2.80 %,
Temperature 120 °C		2290 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.84 MPa
@Strain 2.40 %,
Temperature 100 °C		2297 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.84 MPa
@Strain 3.80 %,
Temperature 150 °C		2297 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.9 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2310 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 15.91 MPa
@Strain 3.50 %,
Temperature 120 °C		2308 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.95 MPa
@Strain 2.10 %,
Temperature 60.0 °C		2313 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.02 MPa
@Strain 4.00 %,
Temperature 150 °C		2324 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.04 MPa
@Strain 7.00 %,
Temperature 150 °C		2326 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.06 MPa
@Strain 1.80 %,
Temperature 80.0 °C		2329 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.08 MPa
@Strain 3.60 %,
Temperature 120 °C		2332 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.11 MPa
@Strain 2.50 %,
Temperature 100 °C		2337 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.13 MPa
@Strain 2.40 %,
Temperature 80.0 °C		2339 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.14 MPa
@Strain 2.80 %,
Temperature 100 °C		2341 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.17 MPa
@Strain 2.90 %,
Temperature 120 °C		2345 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.26 MPa
@Strain 4.10 %,
Temperature 150 °C		2358 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.29 MPa
@Strain 1.10 %,
Temperature 23.0 °C		2363 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.34 MPa
@Strain 3.70 %,
Temperature 120 °C		2370 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.42 MPa
@Strain 7.50 %,
Temperature 150 °C		2382 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.45 MPa
@Strain 2.50 %,
Temperature 80.0 °C		2386 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.48 MPa
@Strain 2.20 %,
Temperature 60.0 °C		2390 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.51 MPa
@Strain 0.900 %,
Temperature 60.0 °C		2395 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 16.52 MPa
@Strain 2.90 %,
Temperature 100 °C		2396 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.53 MPa
@Strain 2.60 %,
Temperature 100 °C		2397 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.57 MPa
@Strain 4.20 %,
Temperature 150 °C		2403 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.6 MPa
@Strain 3.80 %,
Temperature 120 °C		2410 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.62 MPa
@Strain 3.00 %,
Temperature 120 °C		2411 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.63 MPa
@Strain 1.90 %,
Temperature 80.0 °C		2412 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.7 MPa
@Strain 3.10 %,
Temperature 120 °C		2420 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.75 MPa
@Strain 4.30 %,
Temperature 150 °C		2429 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.81 MPa
@Strain 8.00 %,
Temperature 150 °C		2438 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.83 MPa
@Strain 3.90 %,
Temperature 120 °C		2441 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.88 MPa
@Strain 3.20 %,
Temperature 120 °C		2448 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.88 MPa
@Strain 3.00 %,
Temperature 100 °C		2448 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.94 MPa
@Strain 2.60 %,
Temperature 80.0 °C		2457 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.97 MPa
@Strain 4.00 %,
Temperature 120 °C		2461 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.98 MPa
@Strain 2.30 %,
Temperature 60.0 °C		2463 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.99 MPa
@Strain 4.40 %,
Temperature 150 °C		2464 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.01 MPa
@Strain 2.70 %,
Temperature 100 °C		2467 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.08 MPa
@Strain 2.00 %,
Temperature 80.0 °C		2477 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.1 MPa
@Strain 3.10 %,
Temperature 100 °C		2480 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.17 MPa
@Strain 4.60 %,
Temperature 150 °C		2490 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.17 MPa
@Strain 4.10 %,
Temperature 120 °C		2490 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.17 MPa
@Strain 8.50 %,
Temperature 150 °C		2490 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.2 MPa
@Strain 3.30 %,
Temperature 120 °C		2490 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.22 MPa
@Strain 1.20 %,
Temperature 23.0 °C		2498 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.25 MPa
@Strain 2.80 %,
Temperature 100 °C		2502 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.35 MPa
@Strain 4.70 %,
Temperature 150 °C		2516 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.4 MPa
@Strain 4.20 %,
Temperature 120 °C		2520 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2520 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.42 MPa
@Strain 3.20 %,
Temperature 100 °C		2527 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.44 MPa
@Strain 2.10 %,
Temperature 80.0 °C		2529 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.45 MPa
@Strain 2.70 %,
Temperature 80.0 °C		2531 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.46 MPa
@Strain 9.00 %,
Temperature 150 °C		2532 psi
@Strain 9.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.46 MPa
@Strain 2.40 %,
Temperature 60.0 °C		2532 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.5 MPa
@Strain 0.400 %,
Temperature 0.000 °C		2540 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 17.55 MPa
@Strain 2.90 %,
Temperature 100 °C		2545 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.57 MPa
@Strain 4.30 %,
Temperature 120 °C		2548 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.59 MPa
@Strain 4.80 %,
Temperature 150 °C		2551 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.65 MPa
@Strain 3.40 %,
Temperature 120 °C		2560 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.71 MPa
@Strain 4.90 %,
Temperature 150 °C		2569 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.71 MPa
@Strain 2.50 %,
Temperature 60.0 °C		2569 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.74 MPa
@Strain 9.50 %,
Temperature 150 °C		2573 psi
@Strain 9.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.77 MPa
@Strain 4.40 %,
Temperature 120 °C		2577 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.77 MPa
@Strain 3.30 %,
Temperature 100 °C		2577 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.79 MPa
@Strain 1.00 %,
Temperature 60.0 °C		2580 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.82 MPa
@Strain 2.80 %,
Temperature 80.0 °C		2585 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.91 MPa
@Strain 3.50 %,
Temperature 120 °C		2598 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.97 MPa
@Strain 4.50 %,
Temperature 120 °C		2606 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.98 MPa
@Strain 10.0 %,
Temperature 150 °C		2608 psi
@Strain 10.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.01 MPa
@Strain 3.00 %,
Temperature 100 °C		2612 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.04 MPa
@Strain 2.20 %,
Temperature 80.0 °C		2616 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.08 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2622 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.09 MPa
@Strain 3.40 %,
Temperature 100 °C		2624 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.09 MPa
@Strain 4.60 %,
Temperature 120 °C		2624 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.11 MPa
@Strain 2.90 %,
Temperature 80.0 °C		2627 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.23 MPa
@Strain 3.60 %,
Temperature 120 °C		2644 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.25 MPa
@Strain 2.60 %,
Temperature 60.0 °C		2647 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.29 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2653 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 18.29 MPa
@Strain 4.70 %,
Temperature 120 °C		2653 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.39 MPa
@Strain 5.40 %,
Temperature 150 °C		2667 psi
@Strain 5.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.4 MPa
@Strain 3.10 %,
Temperature 100 °C		2670 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.41 MPa
@Strain 3.50 %,
Temperature 100 °C		2670 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.43 MPa
@Strain 11.0 %,
Temperature 150 °C		2673 psi
@Strain 11.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.46 MPa
@Strain 4.80 %,
Temperature 120 °C		2677 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.46 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2677 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.49 MPa
@Strain 3.70 %,
Temperature 120 °C		2682 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.55 MPa
@Strain 2.30 %,
Temperature 80.0 °C		2690 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.69 MPa
@Strain 4.90 %,
Temperature 120 °C		2711 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.7 MPa
@Strain 3.80 %,
Temperature 120 °C		2710 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.73 MPa
@Strain 2.70 %,
Temperature 60.0 °C		2717 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.76 MPa
@Strain 3.60 %,
Temperature 100 °C		2721 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.81 MPa
@Strain 3.90 %,
Temperature 120 °C		2728 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.85 MPa
@Strain 3.20 %,
Temperature 100 °C		2734 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.86 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2735 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.89 MPa
@Strain 12.0 %,
Temperature 150 °C		2740 psi
@Strain 12.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.92 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2744 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 19.01 MPa
@Strain 3.70 %,
Temperature 100 °C		2757 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.03 MPa
@Strain 1.10 %,
Temperature 60.0 °C		2760 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.06 MPa
@Strain 2.40 %,
Temperature 80.0 °C		2764 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.07 MPa
@Strain 4.00 %,
Temperature 120 °C		2766 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.12 MPa
@Strain 3.30 %,
Temperature 100 °C		2773 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.14 MPa
@Strain 5.90 %,
Temperature 150 °C		2776 psi
@Strain 5.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.2 MPa
@Strain 3.80 %,
Temperature 100 °C		2780 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.22 MPa
@Strain 1.40 %,
Temperature 23.0 °C		2788 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.25 MPa
@Strain 5.00 %,
Temperature 120 °C		2792 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.26 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2793 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.26 MPa
@Strain 2.80 %,
Temperature 60.0 °C		2793 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.27 MPa
@Strain 13.0 %,
Temperature 150 °C		2795 psi
@Strain 13.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.33 MPa
@Strain 4.10 %,
Temperature 120 °C		2804 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.36 MPa
@Strain 3.40 %,
Temperature 100 °C		2808 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.46 MPa
@Strain 3.90 %,
Temperature 100 °C		2822 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.54 MPa
@Strain 2.90 %,
Temperature 60.0 °C		2834 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.55 MPa
@Strain 14.0 %,
Temperature 150 °C		2835 psi
@Strain 14.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.59 MPa
@Strain 4.20 %,
Temperature 120 °C		2841 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.6 MPa
@Strain 2.50 %,
Temperature 80.0 °C		2840 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.63 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2847 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.73 MPa
@Strain 6.40 %,
Temperature 150 °C		2862 psi
@Strain 6.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.75 MPa
@Strain 4.00 %,
Temperature 100 °C		2865 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.79 MPa
@Strain 3.50 %,
Temperature 100 °C		2870 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.82 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2875 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.84 MPa
@Strain 4.30 %,
Temperature 120 °C		2878 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.85 MPa
@Strain 1.20 %,
Temperature 60.0 °C		2879 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.86 MPa
@Strain 15.0 %,
Temperature 150 °C		2880 psi
@Strain 15.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.03 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2905 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.07 MPa
@Strain 4.10 %,
Temperature 100 °C		2911 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.09 MPa
@Strain 3.60 %,
Temperature 100 °C		2914 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.1 MPa
@Strain 4.40 %,
Temperature 120 °C		2920 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.11 MPa
@Strain 5.50 %,
Temperature 120 °C		2917 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.12 MPa
@Strain 2.60 %,
Temperature 80.0 °C		2918 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.13 MPa
@Strain 16.0 %,
Temperature 150 °C		2920 psi
@Strain 16.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.16 MPa
@Strain 4.20 %,
Temperature 100 °C		2924 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.25 MPa
@Strain 6.90 %,
Temperature 150 °C		2937 psi
@Strain 6.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.3 MPa
@Strain 3.70 %,
Temperature 100 °C		2940 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.3 MPa
@Strain 3.10 %,
Temperature 60.0 °C		2940 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.32 MPa
@Strain 1.50 %,
Temperature 23.0 °C		2947 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.35 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2952 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.36 MPa
@Strain 4.50 %,
Temperature 120 °C		2953 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.38 MPa
@Strain 4.30 %,
Temperature 100 °C		2956 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.38 MPa
@Strain 17.0 %,
Temperature 150 °C		2956 psi
@Strain 17.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.5 MPa
@Strain 4.60 %,
Temperature 120 °C		2970 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.59 MPa
@Strain 18.0 %,
Temperature 150 °C		2986 psi
@Strain 18.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.6 MPa
@Strain 3.80 %,
Temperature 100 °C		2990 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.62 MPa
@Strain 4.70 %,
Temperature 120 °C		2991 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.63 MPa
@Strain 3.60 %,
Temperature 80.0 °C		2992 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.63 MPa
@Strain 2.70 %,
Temperature 80.0 °C		2992 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.64 MPa
@Strain 4.40 %,
Temperature 100 °C		2994 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.69 MPa
@Strain 3.20 %,
Temperature 60.0 °C		3001 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.71 MPa
@Strain 1.30 %,
Temperature 60.0 °C		3004 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.72 MPa
@Strain 7.40 %,
Temperature 150 °C		3005 psi
@Strain 7.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.73 MPa
@Strain 6.00 %,
Temperature 120 °C		3007 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.76 MPa
@Strain 19.0 %,
Temperature 150 °C		3011 psi
@Strain 19.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.8 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3020 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 20.86 MPa
@Strain 4.50 %,
Temperature 100 °C		3025 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.86 MPa
@Strain 3.70 %,
Temperature 80.0 °C		3025 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.88 MPa
@Strain 4.80 %,
Temperature 120 °C		3028 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.93 MPa
@Strain 3.90 %,
Temperature 100 °C		3036 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.0 MPa
@Strain 20.0 %,
Temperature 150 °C		3050 psi
@Strain 20.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.01 MPa
@Strain 1.60 %,
Temperature 23.0 °C		3047 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.08 MPa
@Strain 2.80 %,
Temperature 80.0 °C		3057 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.11 MPa
@Strain 3.30 %,
Temperature 60.0 °C		3062 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.13 MPa
@Strain 4.90 %,
Temperature 120 °C		3065 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.15 MPa
@Strain 4.60 %,
Temperature 100 °C		3068 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.17 MPa
@Strain 4.00 %,
Temperature 100 °C		3070 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.17 MPa
@Strain 21.0 %,
Temperature 150 °C		3070 psi
@Strain 21.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.19 MPa
@Strain 7.90 %,
Temperature 150 °C		3073 psi
@Strain 7.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.21 MPa
@Strain 3.80 %,
Temperature 80.0 °C		3076 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.23 MPa
@Strain 6.50 %,
Temperature 120 °C		3079 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.33 MPa
@Strain 5.00 %,
Temperature 120 °C		3094 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.34 MPa
@Strain 22.0 %,
Temperature 150 °C		3095 psi
@Strain 22.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.37 MPa
@Strain 4.70 %,
Temperature 100 °C		3099 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.45 MPa
@Strain 4.10 %,
Temperature 100 °C		3111 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.48 MPa
@Strain 3.40 %,
Temperature 60.0 °C		3115 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.49 MPa
@Strain 23.0 %,
Temperature 150 °C		3117 psi
@Strain 23.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.53 MPa
@Strain 2.90 %,
Temperature 80.0 °C		3123 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.55 MPa
@Strain 8.40 %,
Temperature 150 °C		3126 psi
@Strain 8.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.57 MPa
@Strain 4.80 %,
Temperature 100 °C		3128 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.58 MPa
@Strain 3.90 %,
Temperature 80.0 °C		3130 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.62 MPa
@Strain 24.0 %,
Temperature 150 °C		3136 psi
@Strain 24.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.66 MPa
@Strain 1.40 %,
Temperature 60.0 °C		3142 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.71 MPa
@Strain 7.00 %,
Temperature 120 °C		3149 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.72 MPa
@Strain 4.90 %,
Temperature 100 °C		3150 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.73 MPa
@Strain 3.50 %,
Temperature 60.0 °C		3152 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.77 MPa
@Strain 1.70 %,
Temperature 23.0 °C		3157 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.78 MPa
@Strain 4.20 %,
Temperature 100 °C		3159 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.78 MPa
@Strain 25.0 %,
Temperature 150 °C		3159 psi
@Strain 25.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.83 MPa
@Strain 3.00 %,
Temperature 80.0 °C		3166 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.87 MPa
@Strain 4.00 %,
Temperature 80.0 °C		3172 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.92 MPa
@Strain 26.0 %,
Temperature 150 °C		3179 psi
@Strain 26.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.93 MPa
@Strain 8.90 %,
Temperature 150 °C		3181 psi
@Strain 8.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.95 MPa
@Strain 5.00 %,
Temperature 100 °C		3184 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.01 MPa
@Strain 3.60 %,
Temperature 60.0 °C		3192 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.03 MPa
@Strain 27.0 %,
Temperature 150 °C		3195 psi
@Strain 27.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.08 MPa
@Strain 4.30 %,
Temperature 100 °C		3202 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.09 MPa
@Strain 5.50 %,
Temperature 120 °C		3204 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.15 MPa
@Strain 28.0 %,
Temperature 150 °C		3213 psi
@Strain 28.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.17 MPa
@Strain 7.50 %,
Temperature 120 °C		3215 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.18 MPa
@Strain 4.10 %,
Temperature 80.0 °C		3217 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.19 MPa
@Strain 3.10 %,
Temperature 80.0 °C		3218 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.26 MPa
@Strain 4.40 %,
Temperature 100 °C		3229 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.27 MPa
@Strain 29.0 %,
Temperature 150 °C		3230 psi
@Strain 29.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.29 MPa
@Strain 9.40 %,
Temperature 150 °C		3233 psi
@Strain 9.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.36 MPa
@Strain 30.0 %,
Temperature 150 °C		3243 psi
@Strain 30.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.4 MPa
@Strain 3.70 %,
Temperature 60.0 °C		3250 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.4 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3250 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 22.41 MPa
@Strain 4.20 %,
Temperature 80.0 °C		3250 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.46 MPa
@Strain 31.0 %,
Temperature 150 °C		3258 psi
@Strain 31.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.5 MPa
@Strain 4.50 %,
Temperature 100 °C		3260 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.52 MPa
@Strain 1.50 %,
Temperature 60.0 °C		3266 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.56 MPa
@Strain 32.0 %,
Temperature 150 °C		3272 psi
@Strain 32.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 9.90 %,
Temperature 150 °C		3280 psi
@Strain 9.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.6 MPa
@Strain 1.80 %,
Temperature 23.0 °C		3280 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.61 MPa
@Strain 3.20 %,
Temperature 80.0 °C		3279 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.61 MPa
@Strain 8.00 %,
Temperature 120 °C		3279 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.61 MPa
@Strain 4.30 %,
Temperature 80.0 °C		3279 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.68 MPa
@Strain 33.0 %,
Temperature 150 °C		3289 psi
@Strain 33.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.71 MPa
@Strain 5.50 %,
Temperature 100 °C		3294 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.71 MPa
@Strain 3.80 %,
Temperature 60.0 °C		3294 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.77 MPa
@Strain 4.60 %,
Temperature 100 °C		3303 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.77 MPa
@Strain 34.0 %,
Temperature 150 °C		3303 psi
@Strain 34.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.86 MPa
@Strain 35.0 %,
Temperature 150 °C		3316 psi
@Strain 35.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.93 MPa
@Strain 4.40 %,
Temperature 80.0 °C		3326 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.95 MPa
@Strain 36.0 %,
Temperature 150 °C		3329 psi
@Strain 36.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.97 MPa
@Strain 8.50 %,
Temperature 120 °C		3332 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.98 MPa
@Strain 4.70 %,
Temperature 100 °C		3333 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.0 MPa
@Strain 37.0 %,
Temperature 150 °C		3340 psi
@Strain 37.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.0 MPa
@Strain 3.30 %,
Temperature 80.0 °C		3340 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.02 MPa
@Strain 6.00 %,
Temperature 120 °C		3339 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.07 MPa
@Strain 38.0 %,
Temperature 150 °C		3346 psi
@Strain 38.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.11 MPa
@Strain 10.9 %,
Temperature 150 °C		3352 psi
@Strain 10.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.11 MPa
@Strain 3.90 %,
Temperature 60.0 °C		3352 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.18 MPa
@Strain 4.50 %,
Temperature 80.0 °C		3362 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.19 MPa
@Strain 4.80 %,
Temperature 100 °C		3363 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.2 MPa
@Strain 39.0 %,
Temperature 150 °C		3360 psi
@Strain 39.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.23 MPa
@Strain 1.60 %,
Temperature 60.0 °C		3369 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.3 MPa
@Strain 40.0 %,
Temperature 150 °C		3380 psi
@Strain 40.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.3 MPa
@Strain 9.00 %,
Temperature 120 °C		3380 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.41 MPa
@Strain 4.00 %,
Temperature 60.0 °C		3395 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.42 MPa
@Strain 3.40 %,
Temperature 80.0 °C		3397 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.44 MPa
@Strain 4.60 %,
Temperature 80.0 °C		3400 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.47 MPa
@Strain 4.90 %,
Temperature 100 °C		3404 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.49 MPa
@Strain 1.90 %,
Temperature 23.0 °C		3407 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.61 MPa
@Strain 4.70 %,
Temperature 80.0 °C		3424 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.61 MPa
@Strain 9.50 %,
Temperature 120 °C		3424 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.69 MPa
@Strain 4.10 %,
Temperature 60.0 °C		3436 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.7 MPa
@Strain 11.9 %,
Temperature 150 °C		3440 psi
@Strain 11.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.71 MPa
@Strain 6.00 %,
Temperature 100 °C		3439 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.76 MPa
@Strain 6.50 %,
Temperature 120 °C		3446 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.78 MPa
@Strain 3.50 %,
Temperature 80.0 °C		3449 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.84 MPa
@Strain 4.80 %,
Temperature 80.0 °C		3458 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.89 MPa
@Strain 4.20 %,
Temperature 60.0 °C		3465 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.9 MPa
@Strain 0.500 %,
Temperature 0.000 °C		3470 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 23.97 MPa
@Strain 2.00 %,
Temperature 23.0 °C		3477 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.07 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3491 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 24.07 MPa
@Strain 10.0 %,
Temperature 120 °C		3491 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.09 MPa
@Strain 1.70 %,
Temperature 60.0 °C		3494 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.13 MPa
@Strain 4.90 %,
Temperature 80.0 °C		3500 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.15 MPa
@Strain 12.9 %,
Temperature 150 °C		3503 psi
@Strain 12.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.18 MPa
@Strain 3.60 %,
Temperature 80.0 °C		3507 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.23 MPa
@Strain 4.30 %,
Temperature 60.0 °C		3514 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.3 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3520 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 24.33 MPa
@Strain 5.40 %,
Temperature 100 °C		3529 psi
@Strain 5.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.36 MPa
@Strain 5.00 %,
Temperature 80.0 °C		3533 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.39 MPa
@Strain 7.00 %,
Temperature 120 °C		3537 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.43 MPa
@Strain 6.50 %,
Temperature 100 °C		3543 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.48 MPa
@Strain 3.70 %,
Temperature 80.0 °C		3551 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.5 MPa
@Strain 13.9 %,
Temperature 150 °C		3550 psi
@Strain 13.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.54 MPa
@Strain 4.40 %,
Temperature 60.0 °C		3559 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.63 MPa
@Strain 2.10 %,
Temperature 23.0 °C		3572 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.64 MPa
@Strain 11.0 %,
Temperature 120 °C		3574 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.72 MPa
@Strain 1.80 %,
Temperature 60.0 °C		3585 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.75 MPa
@Strain 3.80 %,
Temperature 80.0 °C		3590 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.82 MPa
@Strain 4.50 %,
Temperature 60.0 °C		3600 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.89 MPa
@Strain 14.9 %,
Temperature 150 °C		3610 psi
@Strain 14.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.95 MPa
@Strain 7.50 %,
Temperature 120 °C		3619 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.04 MPa
@Strain 4.60 %,
Temperature 60.0 °C		3632 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.07 MPa
@Strain 12.0 %,
Temperature 120 °C		3636 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.08 MPa
@Strain 7.00 %,
Temperature 100 °C		3638 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.11 MPa
@Strain 3.90 %,
Temperature 80.0 °C		3642 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.19 MPa
@Strain 15.9 %,
Temperature 150 °C		3654 psi
@Strain 15.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.21 MPa
@Strain 5.50 %,
Temperature 80.0 °C		3656 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.24 MPa
@Strain 4.70 %,
Temperature 60.0 °C		3661 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.3 MPa
@Strain 1.90 %,
Temperature 60.0 °C		3670 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.35 MPa
@Strain 2.20 %,
Temperature 23.0 °C		3677 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.44 MPa
@Strain 13.0 %,
Temperature 120 °C		3690 psi
@Strain 13.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.47 MPa
@Strain 4.00 %,
Temperature 80.0 °C		3694 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.48 MPa
@Strain 5.90 %,
Temperature 100 °C		3696 psi
@Strain 5.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.51 MPa
@Strain 8.00 %,
Temperature 120 °C		3700 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.51 MPa
@Strain 16.9 %,
Temperature 150 °C		3700 psi
@Strain 16.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.55 MPa
@Strain 4.80 %,
Temperature 60.0 °C		3706 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.64 MPa
@Strain 7.50 %,
Temperature 100 °C		3719 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.75 MPa
@Strain 17.9 %,
Temperature 150 °C		3735 psi
@Strain 17.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.78 MPa
@Strain 14.0 %,
Temperature 120 °C		3739 psi
@Strain 14.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.8 MPa
@Strain 4.10 %,
Temperature 80.0 °C		3740 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.83 MPa
@Strain 4.90 %,
Temperature 60.0 °C		3746 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.99 MPa
@Strain 2.00 %,
Temperature 60.0 °C		3770 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.0 MPa
@Strain 18.9 %,
Temperature 150 °C		3770 psi
@Strain 18.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.01 MPa
@Strain 8.50 %,
Temperature 120 °C		3772 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.07 MPa
@Strain 2.30 %,
Temperature 23.0 °C		3781 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.1 MPa
@Strain 4.20 %,
Temperature 80.0 °C		3790 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.11 MPa
@Strain 15.0 %,
Temperature 120 °C		3787 psi
@Strain 15.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.14 MPa
@Strain 5.00 %,
Temperature 60.0 °C		3791 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.17 MPa
@Strain 8.00 %,
Temperature 100 °C		3796 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.25 MPa
@Strain 19.9 %,
Temperature 150 °C		3807 psi
@Strain 19.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.3 MPa
@Strain 2.10 %,
Temperature 60.0 °C		3810 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.35 MPa
@Strain 16.0 %,
Temperature 120 °C		3822 psi
@Strain 16.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.36 MPa
@Strain 6.00 %,
Temperature 80.0 °C		3823 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.37 MPa
@Strain 6.40 %,
Temperature 100 °C		3825 psi
@Strain 6.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.4 MPa
@Strain 4.30 %,
Temperature 80.0 °C		3830 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.44 MPa
@Strain 20.9 %,
Temperature 150 °C		3835 psi
@Strain 20.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.51 MPa
@Strain 9.00 %,
Temperature 120 °C		3845 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.52 MPa
@Strain 2.40 %,
Temperature 23.0 °C		3846 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.62 MPa
@Strain 17.0 %,
Temperature 120 °C		3861 psi
@Strain 17.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.64 MPa
@Strain 21.9 %,
Temperature 150 °C		3864 psi
@Strain 21.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.64 MPa
@Strain 8.50 %,
Temperature 100 °C		3864 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 4.40 %,
Temperature 80.0 °C		3870 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.84 MPa
@Strain 22.9 %,
Temperature 150 °C		3893 psi
@Strain 22.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.85 MPa
@Strain 18.0 %,
Temperature 120 °C		3894 psi
@Strain 18.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.88 MPa
@Strain 4.50 %,
Temperature 80.0 °C		3899 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.92 MPa
@Strain 2.20 %,
Temperature 60.0 °C		3904 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.98 MPa
@Strain 9.50 %,
Temperature 120 °C		3913 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.02 MPa
@Strain 23.9 %,
Temperature 150 °C		3919 psi
@Strain 23.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.04 MPa
@Strain 19.0 %,
Temperature 120 °C		3922 psi
@Strain 19.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.05 MPa
@Strain 5.50 %,
Temperature 60.0 °C		3923 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.08 MPa
@Strain 9.00 %,
Temperature 100 °C		3928 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.11 MPa
@Strain 2.50 %,
Temperature 23.0 °C		3932 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.13 MPa
@Strain 6.90 %,
Temperature 100 °C		3935 psi
@Strain 6.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.17 MPa
@Strain 6.50 %,
Temperature 80.0 °C		3941 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.2 MPa
@Strain 0.500 %,
Temperature 0.000 °C		3950 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 27.2 MPa
@Strain 0.500 %,
Temperature -40.0 °C		3950 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 27.21 MPa
@Strain 4.60 %,
Temperature 80.0 °C		3946 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.22 MPa
@Strain 20.0 %,
Temperature 120 °C		3948 psi
@Strain 20.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.23 MPa
@Strain 24.9 %,
Temperature 150 °C		3949 psi
@Strain 24.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.36 MPa
@Strain 25.9 %,
Temperature 150 °C		3968 psi
@Strain 25.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.38 MPa
@Strain 2.30 %,
Temperature 60.0 °C		3971 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.4 MPa
@Strain 10.0 %,
Temperature 120 °C		3970 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.42 MPa
@Strain 21.0 %,
Temperature 120 °C		3977 psi
@Strain 21.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.47 MPa
@Strain 9.50 %,
Temperature 100 °C		3984 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.53 MPa
@Strain 26.9 %,
Temperature 150 °C		3993 psi
@Strain 26.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.54 MPa
@Strain 4.70 %,
Temperature 80.0 °C		3994 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.57 MPa
@Strain 2.40 %,
Temperature 60.0 °C		3999 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.6 MPa
@Strain 22.0 %,
Temperature 120 °C		4000 psi
@Strain 22.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.69 MPa
@Strain 27.9 %,
Temperature 150 °C		4016 psi
@Strain 27.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.69 MPa
@Strain 2.60 %,
Temperature 23.0 °C		4016 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.75 MPa
@Strain 23.0 %,
Temperature 120 °C		4025 psi
@Strain 23.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 10.0 %,
Temperature 100 °C		4030 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.81 MPa
@Strain 4.80 %,
Temperature 80.0 °C		4034 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.82 MPa
@Strain 28.9 %,
Temperature 150 °C		4035 psi
@Strain 28.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.87 MPa
@Strain 24.0 %,
Temperature 120 °C		4042 psi
@Strain 24.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.9 MPa
@Strain 7.40 %,
Temperature 100 °C		4050 psi
@Strain 7.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.93 MPa
@Strain 7.00 %,
Temperature 80.0 °C		4051 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.96 MPa
@Strain 11.0 %,
Temperature 120 °C		4055 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.97 MPa
@Strain 29.9 %,
Temperature 150 °C		4057 psi
@Strain 29.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.02 MPa
@Strain 25.0 %,
Temperature 120 °C		4064 psi
@Strain 25.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.02 MPa
@Strain 4.90 %,
Temperature 80.0 °C		4064 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.09 MPa
@Strain 30.9 %,
Temperature 150 °C		4074 psi
@Strain 30.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.11 MPa
@Strain 26.0 %,
Temperature 120 °C		4077 psi
@Strain 26.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.19 MPa
@Strain 2.50 %,
Temperature 60.0 °C		4089 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.2 MPa
@Strain 5.40 %,
Temperature 80.0 °C		4090 psi
@Strain 5.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.23 MPa
@Strain 31.9 %,
Temperature 150 °C		4094 psi
@Strain 31.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.24 MPa
@Strain 6.00 %,
Temperature 60.0 °C		4096 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.27 MPa
@Strain 27.0 %,
Temperature 120 °C		4100 psi
@Strain 27.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.31 MPa
@Strain 2.70 %,
Temperature 23.0 °C		4106 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.34 MPa
@Strain 32.9 %,
Temperature 150 °C		4110 psi
@Strain 32.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.34 MPa
@Strain 11.0 %,
Temperature 100 °C		4110 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.37 MPa
@Strain 28.0 %,
Temperature 120 °C		4115 psi
@Strain 28.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.47 MPa
@Strain 33.9 %,
Temperature 150 °C		4129 psi
@Strain 33.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.48 MPa
@Strain 29.0 %,
Temperature 120 °C		4131 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.55 MPa
@Strain 7.50 %,
Temperature 80.0 °C		4141 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.56 MPa
@Strain 7.90 %,
Temperature 100 °C		4142 psi
@Strain 7.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.59 MPa
@Strain 30.0 %,
Temperature 120 °C		4147 psi
@Strain 30.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.59 MPa
@Strain 34.9 %,
Temperature 150 °C		4147 psi
@Strain 34.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.6 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4150 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 28.63 MPa
@Strain 31.0 %,
Temperature 120 °C		4152 psi
@Strain 31.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.66 MPa
@Strain 12.0 %,
Temperature 120 °C		4157 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.71 MPa
@Strain 35.9 %,
Temperature 150 °C		4164 psi
@Strain 35.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.71 MPa
@Strain 2.60 %,
Temperature 60.0 °C		4164 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.72 MPa
@Strain 32.0 %,
Temperature 120 °C		4165 psi
@Strain 32.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.78 MPa
@Strain 34.0 %,
Temperature 120 °C		4174 psi
@Strain 34.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.8 MPa
@Strain 33.0 %,
Temperature 120 °C		4180 psi
@Strain 33.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.82 MPa
@Strain 36.9 %,
Temperature 150 °C		4180 psi
@Strain 36.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.85 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4184 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 2.80 %,
Temperature 23.0 °C		4190 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.94 MPa
@Strain 37.9 %,
Temperature 150 °C		4197 psi
@Strain 37.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.95 MPa
@Strain 12.0 %,
Temperature 100 °C		4199 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.03 MPa
@Strain 38.9 %,
Temperature 150 °C		4210 psi
@Strain 38.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.12 MPa
@Strain 39.9 %,
Temperature 150 °C		4224 psi
@Strain 39.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.15 MPa
@Strain 6.50 %,
Temperature 60.0 °C		4228 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.17 MPa
@Strain 2.70 %,
Temperature 60.0 °C		4231 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.17 MPa
@Strain 8.40 %,
Temperature 100 °C		4231 psi
@Strain 8.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.21 MPa
@Strain 8.00 %,
Temperature 80.0 °C		4237 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.21 MPa
@Strain 5.90 %,
Temperature 80.0 °C		4237 psi
@Strain 5.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.22 MPa
@Strain 40.9 %,
Temperature 150 °C		4238 psi
@Strain 40.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.26 MPa
@Strain 13.0 %,
Temperature 120 °C		4244 psi
@Strain 13.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.31 MPa
@Strain 41.9 %,
Temperature 150 °C		4251 psi
@Strain 41.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.35 MPa
@Strain 2.90 %,
Temperature 23.0 °C		4257 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.38 MPa
@Strain 13.0 %,
Temperature 100 °C		4261 psi
@Strain 13.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.4 MPa
@Strain 2.80 %,
Temperature 60.0 °C		4260 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.41 MPa
@Strain 42.9 %,
Temperature 150 °C		4266 psi
@Strain 42.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.49 MPa
@Strain 43.9 %,
Temperature 150 °C		4277 psi
@Strain 43.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.57 MPa
@Strain 44.9 %,
Temperature 150 °C		4289 psi
@Strain 44.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.62 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4296 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 29.64 MPa
@Strain 45.9 %,
Temperature 150 °C		4299 psi
@Strain 45.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.72 MPa
@Strain 8.90 %,
Temperature 100 °C		4311 psi
@Strain 8.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.74 MPa
@Strain 8.50 %,
Temperature 80.0 °C		4313 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.74 MPa
@Strain 46.9 %,
Temperature 150 °C		4313 psi
@Strain 46.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.79 MPa
@Strain 14.0 %,
Temperature 100 °C		4321 psi
@Strain 14.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.79 MPa
@Strain 14.0 %,
Temperature 120 °C		4321 psi
@Strain 14.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.79 MPa
@Strain 3.00 %,
Temperature 23.0 °C		4321 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.8 MPa
@Strain 47.9 %,
Temperature 150 °C		4320 psi
@Strain 47.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.88 MPa
@Strain 48.9 %,
Temperature 150 °C		4334 psi
@Strain 48.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.93 MPa
@Strain 49.9 %,
Temperature 150 °C		4341 psi
@Strain 49.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.97 MPa
@Strain 2.90 %,
Temperature 60.0 °C		4347 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.97 MPa
@Strain 7.00 %,
Temperature 60.0 °C		4347 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C		4350 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.14 MPa
@Strain 15.0 %,
Temperature 100 °C		4371 psi
@Strain 15.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.2 MPa
@Strain 9.00 %,
Temperature 80.0 °C		4380 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.25 MPa
@Strain 9.40 %,
Temperature 100 °C		4387 psi
@Strain 9.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.26 MPa
@Strain 15.0 %,
Temperature 120 °C		4389 psi
@Strain 15.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.35 MPa
@Strain 3.10 %,
Temperature 23.0 °C		4402 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.39 MPa
@Strain 3.10 %,
Temperature 60.0 °C		4408 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.43 MPa
@Strain 16.0 %,
Temperature 100 °C		4414 psi
@Strain 16.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 6.40 %,
Temperature 80.0 °C		4420 psi
@Strain 6.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.65 MPa
@Strain 9.50 %,
Temperature 80.0 °C		4445 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.67 MPa
@Strain 7.50 %,
Temperature 60.0 °C		4448 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.68 MPa
@Strain 16.0 %,
Temperature 120 °C		4450 psi
@Strain 16.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.72 MPa
@Strain 9.90 %,
Temperature 100 °C		4456 psi
@Strain 9.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.74 MPa
@Strain 17.0 %,
Temperature 100 °C		4458 psi
@Strain 17.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.79 MPa
@Strain 3.20 %,
Temperature 23.0 °C		4466 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.96 MPa
@Strain 3.20 %,
Temperature 60.0 °C		4490 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.98 MPa
@Strain 18.0 %,
Temperature 100 °C		4493 psi
@Strain 18.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.05 MPa
@Strain 10.0 %,
Temperature 80.0 °C		4503 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.07 MPa
@Strain 17.0 %,
Temperature 120 °C		4506 psi
@Strain 17.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.14 MPa
@Strain 3.30 %,
Temperature 60.0 °C		4516 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.17 MPa
@Strain 3.30 %,
Temperature 23.0 °C		4521 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.19 MPa
@Strain 19.0 %,
Temperature 100 °C		4524 psi
@Strain 19.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.39 MPa
@Strain 20.0 %,
Temperature 100 °C		4553 psi
@Strain 20.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.42 MPa
@Strain 18.0 %,
Temperature 120 °C		4557 psi
@Strain 18.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.44 MPa
@Strain 8.00 %,
Temperature 60.0 °C		4560 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.5 MPa
@Strain 6.90 %,
Temperature 80.0 °C		4570 psi
@Strain 6.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.51 MPa
@Strain 10.9 %,
Temperature 100 °C		4570 psi
@Strain 10.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.55 MPa
@Strain 3.40 %,
Temperature 60.0 °C		4576 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.63 MPa
@Strain 21.0 %,
Temperature 100 °C		4588 psi
@Strain 21.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.65 MPa
@Strain 3.40 %,
Temperature 23.0 °C		4590 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.66 MPa
@Strain 11.0 %,
Temperature 80.0 °C		4592 psi
@Strain 11.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.76 MPa
@Strain 3.50 %,
Temperature 60.0 °C		4606 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.79 MPa
@Strain 18.9 %,
Temperature 120 °C		4611 psi
@Strain 18.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.8 MPa
@Strain 22.0 %,
Temperature 100 °C		4610 psi
@Strain 22.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.98 MPa
@Strain 23.0 %,
Temperature 100 °C		4638 psi
@Strain 23.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.0 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4640 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 32.04 MPa
@Strain 3.60 %,
Temperature 60.0 °C		4647 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.05 MPa
@Strain 8.50 %,
Temperature 60.0 °C		4648 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.09 MPa
@Strain 19.9 %,
Temperature 120 °C		4654 psi
@Strain 19.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.14 MPa
@Strain 24.0 %,
Temperature 100 °C		4662 psi
@Strain 24.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.21 MPa
@Strain 3.50 %,
Temperature 23.0 °C		4672 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.29 MPa
@Strain 25.0 %,
Temperature 100 °C		4683 psi
@Strain 25.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.35 MPa
@Strain 12.0 %,
Temperature 80.0 °C		4692 psi
@Strain 12.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.36 MPa
@Strain 7.40 %,
Temperature 80.0 °C		4693 psi
@Strain 7.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.38 MPa
@Strain 20.9 %,
Temperature 120 °C		4696 psi
@Strain 20.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.39 MPa
@Strain 11.9 %,
Temperature 100 °C		4698 psi
@Strain 11.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.41 MPa
@Strain 26.0 %,
Temperature 100 °C		4701 psi
@Strain 26.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.48 MPa
@Strain 3.70 %,
Temperature 60.0 °C		4711 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.57 MPa
@Strain 9.00 %,
Temperature 60.0 °C		4724 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.57 MPa
@Strain 27.0 %,
Temperature 100 °C		4724 psi
@Strain 27.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.66 MPa
@Strain 28.0 %,
Temperature 100 °C		4737 psi
@Strain 28.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.67 MPa
@Strain 21.9 %,
Temperature 120 °C		4738 psi
@Strain 21.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.69 MPa
@Strain 3.60 %,
Temperature 23.0 °C		4741 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		4740 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 32.82 MPa
@Strain 3.80 %,
Temperature 60.0 °C		4760 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.85 MPa
@Strain 3.90 %,
Temperature 60.0 °C		4764 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.86 MPa
@Strain 13.0 %,
Temperature 80.0 °C		4766 psi
@Strain 13.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.9 MPa
@Strain 29.0 %,
Temperature 100 °C		4770 psi
@Strain 29.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.95 MPa
@Strain 22.9 %,
Temperature 120 °C		4779 psi
@Strain 22.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.0 MPa
@Strain 3.70 %,
Temperature 23.0 °C		4790 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.08 MPa
@Strain 12.9 %,
Temperature 100 °C		4798 psi
@Strain 12.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.1 MPa
@Strain 30.0 %,
Temperature 100 °C		4800 psi
@Strain 30.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 0.600 %,
Temperature -40.0 °C		4800 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 33.11 MPa
@Strain 9.50 %,
Temperature 60.0 °C		4802 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.15 MPa
@Strain 7.90 %,
Temperature 80.0 °C		4808 psi
@Strain 7.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.18 MPa
@Strain 4.00 %,
Temperature 60.0 °C		4812 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.19 MPa
@Strain 23.9 %,
Temperature 120 °C		4814 psi
@Strain 23.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.2 MPa
@Strain 31.0 %,
Temperature 100 °C		4820 psi
@Strain 31.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 14.0 %,
Temperature 80.0 °C		4830 psi
@Strain 14.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.38 MPa
@Strain 3.80 %,
Temperature 23.0 °C		4841 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.44 MPa
@Strain 24.9 %,
Temperature 120 °C		4850 psi
@Strain 24.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.51 MPa
@Strain 4.10 %,
Temperature 60.0 °C		4860 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.56 MPa
@Strain 10.0 %,
Temperature 60.0 °C		4867 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.67 MPa
@Strain 0.700 %,
Temperature 23.0 °C		4883 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.67 MPa
@Strain 25.9 %,
Temperature 120 °C		4883 psi
@Strain 25.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.68 MPa
@Strain 15.0 %,
Temperature 80.0 °C		4885 psi
@Strain 15.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.71 MPa
@Strain 13.9 %,
Temperature 100 °C		4889 psi
@Strain 13.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.85 MPa
@Strain 4.20 %,
Temperature 60.0 °C		4910 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.86 MPa
@Strain 3.90 %,
Temperature 23.0 °C		4911 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.88 MPa
@Strain 26.9 %,
Temperature 120 °C		4914 psi
@Strain 26.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.9 MPa
@Strain 8.40 %,
Temperature 80.0 °C		4920 psi
@Strain 8.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.02 MPa
@Strain 16.0 %,
Temperature 80.0 °C		4934 psi
@Strain 16.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.04 MPa
@Strain 4.30 %,
Temperature 60.0 °C		4937 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.08 MPa
@Strain 27.9 %,
Temperature 120 °C		4943 psi
@Strain 27.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.14 MPa
@Strain 4.40 %,
Temperature 60.0 °C		4952 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.26 MPa
@Strain 28.9 %,
Temperature 120 °C		4969 psi
@Strain 28.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.28 MPa
@Strain 11.0 %,
Temperature 60.0 °C		4972 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.29 MPa
@Strain 14.9 %,
Temperature 100 °C		4973 psi
@Strain 14.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.31 MPa
@Strain 17.0 %,
Temperature 80.0 °C		4976 psi
@Strain 17.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.38 MPa
@Strain 4.00 %,
Temperature 23.0 °C		4986 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.42 MPa
@Strain 4.50 %,
Temperature 60.0 °C		4992 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.44 MPa
@Strain 29.9 %,
Temperature 120 °C		4995 psi
@Strain 29.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.53 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5008 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 34.57 MPa
@Strain 8.90 %,
Temperature 80.0 °C		5014 psi
@Strain 8.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.58 MPa
@Strain 18.0 %,
Temperature 80.0 °C		5015 psi
@Strain 18.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.65 MPa
@Strain 30.9 %,
Temperature 120 °C		5026 psi
@Strain 30.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.65 MPa
@Strain 4.10 %,
Temperature 23.0 °C		5026 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.76 MPa
@Strain 4.60 %,
Temperature 60.0 °C		5042 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.81 MPa
@Strain 15.9 %,
Temperature 100 °C		5049 psi
@Strain 15.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.82 MPa
@Strain 31.9 %,
Temperature 120 °C		5050 psi
@Strain 31.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.83 MPa
@Strain 19.0 %,
Temperature 80.0 °C		5052 psi
@Strain 19.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.96 MPa
@Strain 4.20 %,
Temperature 23.0 °C		5071 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.02 MPa
@Strain 32.9 %,
Temperature 120 °C		5079 psi
@Strain 32.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.04 MPa
@Strain 12.0 %,
Temperature 60.0 °C		5082 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.05 MPa
@Strain 4.70 %,
Temperature 60.0 °C		5084 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.05 MPa
@Strain 4.80 %,
Temperature 60.0 °C		5084 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.05 MPa
@Strain 20.0 %,
Temperature 80.0 °C		5084 psi
@Strain 20.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.17 MPa
@Strain 9.40 %,
Temperature 80.0 °C		5101 psi
@Strain 9.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.19 MPa
@Strain 33.9 %,
Temperature 120 °C		5104 psi
@Strain 33.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.24 MPa
@Strain 21.0 %,
Temperature 80.0 °C		5111 psi
@Strain 21.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.31 MPa
@Strain 16.9 %,
Temperature 100 °C		5121 psi
@Strain 16.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.34 MPa
@Strain 34.9 %,
Temperature 120 °C		5126 psi
@Strain 34.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.41 MPa
@Strain 4.30 %,
Temperature 23.0 °C		5136 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.43 MPa
@Strain 4.90 %,
Temperature 60.0 °C		5139 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.44 MPa
@Strain 22.0 %,
Temperature 80.0 °C		5140 psi
@Strain 22.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.5 MPa
@Strain 35.9 %,
Temperature 120 °C		5150 psi
@Strain 35.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.59 MPa
@Strain 23.0 %,
Temperature 80.0 °C		5162 psi
@Strain 23.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.61 MPa
@Strain 13.0 %,
Temperature 60.0 °C		5165 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.64 MPa
@Strain 36.9 %,
Temperature 120 °C		5169 psi
@Strain 36.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.68 MPa
@Strain 4.40 %,
Temperature 23.0 °C		5175 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.76 MPa
@Strain 24.0 %,
Temperature 80.0 °C		5187 psi
@Strain 24.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.76 MPa
@Strain 17.9 %,
Temperature 100 °C		5187 psi
@Strain 17.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.78 MPa
@Strain 9.90 %,
Temperature 80.0 °C		5189 psi
@Strain 9.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.79 MPa
@Strain 37.9 %,
Temperature 120 °C		5191 psi
@Strain 37.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.93 MPa
@Strain 25.0 %,
Temperature 80.0 °C		5211 psi
@Strain 25.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.94 MPa
@Strain 38.9 %,
Temperature 120 °C		5213 psi
@Strain 38.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.99 MPa
@Strain 4.50 %,
Temperature 23.0 °C		5220 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.05 MPa
@Strain 26.0 %,
Temperature 80.0 °C		5229 psi
@Strain 26.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.08 MPa
@Strain 39.9 %,
Temperature 120 °C		5233 psi
@Strain 39.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.16 MPa
@Strain 14.0 %,
Temperature 60.0 °C		5245 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.17 MPa
@Strain 27.0 %,
Temperature 80.0 °C		5246 psi
@Strain 27.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.18 MPa
@Strain 18.9 %,
Temperature 100 °C		5247 psi
@Strain 18.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.2 MPa
@Strain 40.9 %,
Temperature 120 °C		5250 psi
@Strain 40.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.21 MPa
@Strain 5.40 %,
Temperature 60.0 °C		5252 psi
@Strain 5.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.28 MPa
@Strain 28.0 %,
Temperature 80.0 °C		5262 psi
@Strain 28.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.31 MPa
@Strain 41.9 %,
Temperature 120 °C		5266 psi
@Strain 41.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.32 MPa
@Strain 10.9 %,
Temperature 80.0 °C		5268 psi
@Strain 10.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.39 MPa
@Strain 29.0 %,
Temperature 80.0 °C		5278 psi
@Strain 29.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.44 MPa
@Strain 4.60 %,
Temperature 23.0 °C		5285 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.45 MPa
@Strain 42.9 %,
Temperature 120 °C		5287 psi
@Strain 42.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.47 MPa
@Strain 31.0 %,
Temperature 80.0 °C		5290 psi
@Strain 31.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.48 MPa
@Strain 30.0 %,
Temperature 80.0 °C		5291 psi
@Strain 30.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.56 MPa
@Strain 19.9 %,
Temperature 100 °C		5303 psi
@Strain 19.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.57 MPa
@Strain 43.9 %,
Temperature 120 °C		5304 psi
@Strain 43.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.62 MPa
@Strain 15.0 %,
Temperature 60.0 °C		5311 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5320 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 36.7 MPa
@Strain 0.800 %,
Temperature 0.000 °C		5320 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.73 MPa
@Strain 44.9 %,
Temperature 120 °C		5327 psi
@Strain 44.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.82 MPa
@Strain 4.70 %,
Temperature 23.0 °C		5340 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.84 MPa
@Strain 45.9 %,
Temperature 120 °C		5343 psi
@Strain 45.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.9 MPa
@Strain 20.9 %,
Temperature 100 °C		5350 psi
@Strain 20.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.95 MPa
@Strain 46.9 %,
Temperature 120 °C		5359 psi
@Strain 46.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.99 MPa
@Strain 16.0 %,
Temperature 60.0 °C		5365 psi
@Strain 16.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.06 MPa
@Strain 4.80 %,
Temperature 23.0 °C		5375 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.08 MPa
@Strain 47.9 %,
Temperature 120 °C		5378 psi
@Strain 47.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.18 MPa
@Strain 48.9 %,
Temperature 120 °C		5393 psi
@Strain 48.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.21 MPa
@Strain 11.9 %,
Temperature 80.0 °C		5397 psi
@Strain 11.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.27 MPa
@Strain 49.9 %,
Temperature 120 °C		5406 psi
@Strain 49.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.29 MPa
@Strain 21.9 %,
Temperature 100 °C		5408 psi
@Strain 21.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.32 MPa
@Strain 17.0 %,
Temperature 60.0 °C		5413 psi
@Strain 17.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.37 MPa
@Strain 4.90 %,
Temperature 23.0 °C		5420 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.41 MPa
@Strain 5.90 %,
Temperature 60.0 °C		5426 psi
@Strain 5.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.6 MPa
@Strain 22.9 %,
Temperature 100 °C		5450 psi
@Strain 22.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.68 MPa
@Strain 18.0 %,
Temperature 60.0 °C		5465 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.79 MPa
@Strain 5.00 %,
Temperature 23.0 °C		5481 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.87 MPa
@Strain 23.9 %,
Temperature 100 °C		5493 psi
@Strain 23.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.94 MPa
@Strain 19.0 %,
Temperature 60.0 °C		5503 psi
@Strain 19.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.15 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5533 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.16 MPa
@Strain 20.0 %,
Temperature 60.0 °C		5535 psi
@Strain 20.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.17 MPa
@Strain 24.9 %,
Temperature 100 °C		5536 psi
@Strain 24.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.19 MPa
@Strain 12.9 %,
Temperature 80.0 °C		5539 psi
@Strain 12.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.27 MPa
@Strain 6.40 %,
Temperature 60.0 °C		5551 psi
@Strain 6.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.43 MPa
@Strain 21.0 %,
Temperature 60.0 °C		5574 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.47 MPa
@Strain 25.9 %,
Temperature 100 °C		5580 psi
@Strain 25.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.63 MPa
@Strain 22.0 %,
Temperature 60.0 °C		5603 psi
@Strain 22.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.68 MPa
@Strain 26.9 %,
Temperature 100 °C		5610 psi
@Strain 26.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.84 MPa
@Strain 23.0 %,
Temperature 60.0 °C		5633 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.9 MPa
@Strain 0.700 %,
Temperature -40.0 °C		5640 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 38.95 MPa
@Strain 5.50 %,
Temperature 23.0 °C		5649 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.97 MPa
@Strain 6.90 %,
Temperature 60.0 °C		5652 psi
@Strain 6.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.97 MPa
@Strain 27.9 %,
Temperature 100 °C		5652 psi
@Strain 27.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.98 MPa
@Strain 13.9 %,
Temperature 80.0 °C		5654 psi
@Strain 13.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.0 MPa
@Strain 24.0 %,
Temperature 60.0 °C		5660 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.13 MPa
@Strain 25.0 %,
Temperature 60.0 °C		5675 psi
@Strain 25.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.24 MPa
@Strain 28.9 %,
Temperature 100 °C		5691 psi
@Strain 28.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.28 MPa
@Strain 0.700 %,
Temperature -40.0 °C		5697 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 39.34 MPa
@Strain 26.0 %,
Temperature 60.0 °C		5706 psi
@Strain 26.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.42 MPa
@Strain 29.9 %,
Temperature 100 °C		5717 psi
@Strain 29.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.49 MPa
@Strain 27.0 %,
Temperature 60.0 °C		5728 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.62 MPa
@Strain 28.0 %,
Temperature 60.0 °C		5746 psi
@Strain 28.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.67 MPa
@Strain 14.9 %,
Temperature 80.0 °C		5754 psi
@Strain 14.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.68 MPa
@Strain 30.9 %,
Temperature 100 °C		5755 psi
@Strain 30.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.76 MPa
@Strain 29.0 %,
Temperature 60.0 °C		5767 psi
@Strain 29.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.82 MPa
@Strain 7.40 %,
Temperature 60.0 °C		5775 psi
@Strain 7.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.87 MPa
@Strain 31.9 %,
Temperature 100 °C		5783 psi
@Strain 31.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.88 MPa
@Strain 30.0 %,
Temperature 60.0 °C		5784 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.0 MPa
@Strain 31.0 %,
Temperature 60.0 °C		5800 psi
@Strain 31.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.08 MPa
@Strain 32.9 %,
Temperature 100 °C		5813 psi
@Strain 32.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.12 MPa
@Strain 32.0 %,
Temperature 60.0 °C		5819 psi
@Strain 32.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.21 MPa
@Strain 33.0 %,
Temperature 60.0 °C		5832 psi
@Strain 33.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.24 MPa
@Strain 33.9 %,
Temperature 100 °C		5836 psi
@Strain 33.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.33 MPa
@Strain 34.0 %,
Temperature 60.0 °C		5849 psi
@Strain 34.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.35 MPa
@Strain 15.9 %,
Temperature 80.0 °C		5852 psi
@Strain 15.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.4 MPa
@Strain 0.900 %,
Temperature 0.000 °C		5860 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 40.42 MPa
@Strain 35.0 %,
Temperature 60.0 °C		5862 psi
@Strain 35.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.48 MPa
@Strain 34.9 %,
Temperature 100 °C		5871 psi
@Strain 34.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.53 MPa
@Strain 36.0 %,
Temperature 60.0 °C		5878 psi
@Strain 36.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.57 MPa
@Strain 37.0 %,
Temperature 60.0 °C		5884 psi
@Strain 37.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.6 MPa
@Strain 38.0 %,
Temperature 60.0 °C		5890 psi
@Strain 38.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.66 MPa
@Strain 6.00 %,
Temperature 23.0 °C		5897 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.66 MPa
@Strain 35.9 %,
Temperature 100 °C		5897 psi
@Strain 35.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.69 MPa
@Strain 7.90 %,
Temperature 60.0 °C		5902 psi
@Strain 7.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.85 MPa
@Strain 36.9 %,
Temperature 100 °C		5925 psi
@Strain 36.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.95 MPa
@Strain 16.9 %,
Temperature 80.0 °C		5939 psi
@Strain 16.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.03 MPa
@Strain 37.9 %,
Temperature 100 °C		5951 psi
@Strain 37.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.14 MPa
@Strain 38.9 %,
Temperature 100 °C		5967 psi
@Strain 38.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.3 MPa
@Strain 0.800 %,
Temperature 0.000 °C		5990 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 41.32 MPa
@Strain 8.40 %,
Temperature 60.0 °C		5993 psi
@Strain 8.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.49 MPa
@Strain 17.9 %,
Temperature 80.0 °C		6018 psi
@Strain 17.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.92 MPa
@Strain 6.50 %,
Temperature 23.0 °C		6080 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.01 MPa
@Strain 8.90 %,
Temperature 60.0 °C		6093 psi
@Strain 8.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.02 MPa
@Strain 0.900 %,
Temperature 23.0 °C		6094 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 42.05 MPa
@Strain 18.9 %,
Temperature 80.0 °C		6099 psi
@Strain 18.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.54 MPa
@Strain 19.9 %,
Temperature 80.0 °C		6170 psi
@Strain 19.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.58 MPa
@Strain 9.40 %,
Temperature 60.0 °C		6176 psi
@Strain 9.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.99 MPa
@Strain 7.00 %,
Temperature 23.0 °C		6235 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.99 MPa
@Strain 20.9 %,
Temperature 80.0 °C		6235 psi
@Strain 20.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.16 MPa
@Strain 9.90 %,
Temperature 60.0 °C		6260 psi
@Strain 9.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.42 MPa
@Strain 21.9 %,
Temperature 80.0 °C		6298 psi
@Strain 21.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.6 MPa
@Strain 1.00 %,
Temperature 0.000 °C		6320 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.82 MPa
@Strain 22.9 %,
Temperature 80.0 °C		6356 psi
@Strain 22.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.09 MPa
@Strain 7.50 %,
Temperature 23.0 °C		6395 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.11 MPa
@Strain 10.9 %,
Temperature 60.0 °C		6398 psi
@Strain 10.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.16 MPa
@Strain 0.800 %,
Temperature -40.0 °C		6405 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.19 MPa
@Strain 23.9 %,
Temperature 80.0 °C		6409 psi
@Strain 23.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.5 MPa
@Strain 0.800 %,
Temperature -40.0 °C		6450 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 44.55 MPa
@Strain 24.9 %,
Temperature 80.0 °C		6461 psi
@Strain 24.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 25.9 %,
Temperature 80.0 °C		6510 psi
@Strain 25.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.06 MPa
@Strain 8.00 %,
Temperature 23.0 °C		6535 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.18 MPa
@Strain 11.9 %,
Temperature 60.0 °C		6553 psi
@Strain 11.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.22 MPa
@Strain 26.9 %,
Temperature 80.0 °C		6559 psi
@Strain 26.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.48 MPa
@Strain 27.9 %,
Temperature 80.0 °C		6596 psi
@Strain 27.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.59 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6612 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.8 MPa
@Strain 28.9 %,
Temperature 80.0 °C		6640 psi
@Strain 28.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.9 MPa
@Strain 0.900 %,
Temperature 0.000 °C		6660 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 45.93 MPa
@Strain 8.50 %,
Temperature 23.0 °C		6662 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.06 MPa
@Strain 12.9 %,
Temperature 60.0 °C		6680 psi
@Strain 12.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 29.9 %,
Temperature 80.0 °C		6690 psi
@Strain 29.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.2 MPa
@Strain 1.10 %,
Temperature 0.000 °C		6700 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 46.3 MPa
@Strain 30.9 %,
Temperature 80.0 °C		6720 psi
@Strain 30.9 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.69 MPa
@Strain 9.00 %,
Temperature 23.0 °C		6772 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.86 MPa
@Strain 13.9 %,
Temperature 60.0 °C		6796 psi
@Strain 13.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.45 MPa
@Strain 9.50 %,
Temperature 23.0 °C		6882 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.61 MPa
@Strain 14.9 %,
Temperature 60.0 °C		6905 psi
@Strain 14.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.12 MPa
@Strain 10.0 %,
Temperature 23.0 °C		6979 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.27 MPa
@Strain 15.9 %,
Temperature 60.0 °C		7001 psi
@Strain 15.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.6 MPa
@Strain 1.20 %,
Temperature 0.000 °C		7050 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.63 MPa
@Strain 0.900 %,
Temperature -40.0 °C		7053 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 48.86 MPa
@Strain 16.9 %,
Temperature 60.0 °C		7087 psi
@Strain 16.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.11 MPa
@Strain 1.10 %,
Temperature 23.0 °C		7123 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.13 MPa
@Strain 11.0 %,
Temperature 23.0 °C		7126 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.47 MPa
@Strain 17.9 %,
Temperature 60.0 °C		7175 psi
@Strain 17.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 1.00 %,
Temperature 0.000 °C		7220 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.01 MPa
@Strain 18.9 %,
Temperature 60.0 °C		7253 psi
@Strain 18.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 0.900 %,
Temperature -40.0 °C		7280 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 50.26 MPa
@Strain 12.0 %,
Temperature 23.0 °C		7290 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.52 MPa
@Strain 19.9 %,
Temperature 60.0 °C		7327 psi
@Strain 19.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.0 MPa
@Strain 1.30 %,
Temperature 0.000 °C		7400 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 51.01 MPa
@Strain 20.9 %,
Temperature 60.0 °C		7398 psi
@Strain 20.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.11 MPa
@Strain 13.0 %,
Temperature 23.0 °C		7413 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.44 MPa
@Strain 21.9 %,
Temperature 60.0 °C		7461 psi
@Strain 21.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.85 MPa
@Strain 14.0 %,
Temperature 23.0 °C		7520 psi
@Strain 14.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.86 MPa
@Strain 22.9 %,
Temperature 60.0 °C		7522 psi
@Strain 22.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.3 MPa
@Strain 23.9 %,
Temperature 60.0 °C		7590 psi
@Strain 23.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.41 MPa
@Strain 1.20 %,
Temperature 23.0 °C		7601 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 52.51 MPa
@Strain 15.0 %,
Temperature 23.0 °C		7616 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.67 MPa
@Strain 24.9 %,
Temperature 60.0 °C		7639 psi
@Strain 24.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.8 MPa
@Strain 1.40 %,
Temperature 0.000 °C		7660 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.96 MPa
@Strain 1.00 %,
Temperature -40.0 °C		7681 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 53.03 MPa
@Strain 25.9 %,
Temperature 60.0 °C		7691 psi
@Strain 25.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.09 MPa
@Strain 16.0 %,
Temperature 23.0 °C		7700 psi
@Strain 16.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 26.9 %,
Temperature 60.0 °C		7750 psi
@Strain 26.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.6 MPa
@Strain 17.0 %,
Temperature 23.0 °C		7770 psi
@Strain 17.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.74 MPa
@Strain 27.9 %,
Temperature 60.0 °C		7794 psi
@Strain 27.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.8 MPa
@Strain 1.10 %,
Temperature 0.000 °C		7800 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.04 MPa
@Strain 18.0 %,
Temperature 23.0 °C		7838 psi
@Strain 18.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.05 MPa
@Strain 28.9 %,
Temperature 60.0 °C		7839 psi
@Strain 28.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.29 MPa
@Strain 29.9 %,
Temperature 60.0 °C		7874 psi
@Strain 29.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.44 MPa
@Strain 19.0 %,
Temperature 23.0 °C		7896 psi
@Strain 19.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 1.50 %,
Temperature 0.000 °C		7900 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 54.54 MPa
@Strain 30.9 %,
Temperature 60.0 °C		7910 psi
@Strain 30.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.84 MPa
@Strain 20.0 %,
Temperature 23.0 °C		7954 psi
@Strain 20.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.17 MPa
@Strain 21.0 %,
Temperature 23.0 °C		8002 psi
@Strain 21.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.3 MPa
@Strain 1.00 %,
Temperature -40.0 °C		8020 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 55.48 MPa
@Strain 22.0 %,
Temperature 23.0 °C		8047 psi
@Strain 22.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.51 MPa
@Strain 1.30 %,
Temperature 23.0 °C		8051 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 55.79 MPa
@Strain 23.0 %,
Temperature 23.0 °C		8092 psi
@Strain 23.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.9 MPa
@Strain 1.60 %,
Temperature 0.000 °C		8110 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.06 MPa
@Strain 24.0 %,
Temperature 23.0 °C		8131 psi
@Strain 24.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.32 MPa
@Strain 25.0 %,
Temperature 23.0 °C		8169 psi
@Strain 25.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.59 MPa
@Strain 26.0 %,
Temperature 23.0 °C		8208 psi
@Strain 26.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.79 MPa
@Strain 27.0 %,
Temperature 23.0 °C		8237 psi
@Strain 27.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.02 MPa
@Strain 28.0 %,
Temperature 23.0 °C		8270 psi
@Strain 28.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.29 MPa
@Strain 29.0 %,
Temperature 23.0 °C		8309 psi
@Strain 29.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.3 MPa
@Strain 1.70 %,
Temperature 0.000 °C		8310 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.35 MPa
@Strain 1.10 %,
Temperature -40.0 °C		8318 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.49 MPa
@Strain 30.0 %,
Temperature 23.0 °C		8338 psi
@Strain 30.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.5 MPa
@Strain 1.20 %,
Temperature 0.000 °C		8340 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 57.71 MPa
@Strain 31.0 %,
Temperature 23.0 °C		8370 psi
@Strain 31.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.92 MPa
@Strain 32.0 %,
Temperature 23.0 °C		8401 psi
@Strain 32.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.12 MPa
@Strain 33.0 %,
Temperature 23.0 °C		8430 psi
@Strain 33.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.28 MPa
@Strain 34.0 %,
Temperature 23.0 °C		8453 psi
@Strain 34.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.36 MPa
@Strain 1.40 %,
Temperature 23.0 °C		8464 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.46 MPa
@Strain 35.0 %,
Temperature 23.0 °C		8479 psi
@Strain 35.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.6 MPa
@Strain 1.80 %,
Temperature 0.000 °C		8500 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.68 MPa
@Strain 36.0 %,
Temperature 23.0 °C		8511 psi
@Strain 36.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.84 MPa
@Strain 37.0 %,
Temperature 23.0 °C		8534 psi
@Strain 37.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.03 MPa
@Strain 38.0 %,
Temperature 23.0 °C		8562 psi
@Strain 38.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.21 MPa
@Strain 39.0 %,
Temperature 23.0 °C		8588 psi
@Strain 39.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.37 MPa
@Strain 40.0 %,
Temperature 23.0 °C		8611 psi
@Strain 40.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 1.90 %,
Temperature 0.000 °C		8660 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.0 MPa
@Strain 1.10 %,
Temperature -40.0 °C		8700 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 60.68 MPa
@Strain 1.50 %,
Temperature 23.0 °C		8801 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 60.7 MPa
@Strain 2.00 %,
Temperature 0.000 °C		8800 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.1 MPa
@Strain 1.30 %,
Temperature 0.000 °C		8860 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 61.4 MPa
@Strain 2.10 %,
Temperature 0.000 °C		8910 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.4 MPa
@Strain 1.20 %,
Temperature -40.0 °C		8910 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.2 MPa
@Strain 2.20 %,
Temperature 0.000 °C		9020 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.58 MPa
@Strain 1.60 %,
Temperature 23.0 °C		9076 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.8 MPa
@Strain 2.30 %,
Temperature 0.000 °C		9110 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.3 MPa
@Strain 2.40 %,
Temperature 0.000 °C		9180 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.7 MPa
@Strain 2.50 %,
Temperature 0.000 °C		9240 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.1 MPa
@Strain 2.60 %,
Temperature 0.000 °C		9300 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.4 MPa
@Strain 2.70 %,
Temperature 0.000 °C		9340 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.47 MPa
@Strain 1.70 %,
Temperature 23.0 °C		9351 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.6 MPa
@Strain 1.40 %,
Temperature 0.000 °C		9370 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 64.7 MPa
@Strain 1.20 %,
Temperature -40.0 °C		9380 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 64.7 MPa
@Strain 2.80 %,
Temperature 0.000 °C		9380 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.0 MPa
@Strain 2.90 %,
Temperature 0.000 °C		9430 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.4 MPa
@Strain 3.00 %,
Temperature 0.000 °C		9490 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.4 MPa
@Strain 1.30 %,
Temperature -40.0 °C		9490 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 65.6 MPa
@Strain 3.10 %,
Temperature 0.000 °C		9510 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.8 MPa
@Strain 3.20 %,
Temperature 0.000 °C		9540 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.1 MPa
@Strain 3.30 %,
Temperature 0.000 °C		9590 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.3 MPa
@Strain 1.80 %,
Temperature 23.0 °C		9620 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.5 MPa
@Strain 3.40 %,
Temperature 0.000 °C		9650 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.7 MPa
@Strain 3.50 %,
Temperature 0.000 °C		9670 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.0 MPa
@Strain 3.60 %,
Temperature 0.000 °C		9720 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.2 MPa
@Strain 3.70 %,
Temperature 0.000 °C		9750 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.4 MPa
@Strain 3.80 %,
Temperature 0.000 °C		9780 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.6 MPa
@Strain 3.90 %,
Temperature 0.000 °C		9800 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.61 MPa
@Strain 1.90 %,
Temperature 23.0 °C		9806 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.7 MPa
@Strain 1.50 %,
Temperature 0.000 °C		9820 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.9 MPa
@Strain 4.00 %,
Temperature 0.000 °C		9850 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.1 MPa
@Strain 4.10 %,
Temperature 0.000 °C		9880 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.3 MPa
@Strain 4.20 %,
Temperature 0.000 °C		9910 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.5 MPa
@Strain 4.30 %,
Temperature 0.000 °C		9940 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.65 MPa
@Strain 2.00 %,
Temperature 23.0 °C		9957 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.7 MPa
@Strain 4.40 %,
Temperature 0.000 °C		9960 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.0 MPa
@Strain 4.50 %,
Temperature 0.000 °C		10000 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.0 MPa
@Strain 1.30 %,
Temperature -40.0 °C		10000 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 69.13 MPa
@Strain 1.40 %,
Temperature -40.0 °C		10030 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.2 MPa
@Strain 4.60 %,
Temperature 0.000 °C		10000 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.55 MPa
@Strain 2.10 %,
Temperature 23.0 °C		10090 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 69.6 MPa
@Strain 4.80 %,
Temperature 0.000 °C		10100 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.8 MPa
@Strain 4.90 %,
Temperature 0.000 °C		10100 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.0 MPa
@Strain 5.00 %,
Temperature 0.000 °C		10200 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.34 MPa
@Strain 2.20 %,
Temperature 23.0 °C		10200 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 70.6 MPa
@Strain 1.60 %,
Temperature 0.000 °C		10200 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 70.7 MPa
@Strain 5.50 %,
Temperature 0.000 °C		10300 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.94 MPa
@Strain 2.30 %,
Temperature 23.0 °C		10290 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.45 MPa
@Strain 2.40 %,
Temperature 23.0 °C		10360 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.5 MPa
@Strain 6.00 %,
Temperature 0.000 °C		10400 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.9 MPa
@Strain 6.50 %,
Temperature 0.000 °C		10400 psi
@Strain 6.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10400 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.34 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10490 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.6 MPa
@Strain 1.40 %,
Temperature -40.0 °C		10500 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 72.68 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10540 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.69 MPa
@Strain 1.50 %,
Temperature -40.0 °C		10540 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.8 MPa
@Strain 7.00 %,
Temperature 0.000 °C		10600 psi
@Strain 7.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.93 MPa
@Strain 2.80 %,
Temperature 23.0 °C		10580 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.23 MPa
@Strain 2.90 %,
Temperature 23.0 °C		10620 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.27 MPa
@Strain 3.00 %,
Temperature 23.0 °C		10630 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.3 MPa
@Strain 1.70 %,
Temperature 0.000 °C		10600 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 73.4 MPa
@Strain 3.10 %,
Temperature 23.0 °C		10600 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.57 MPa
@Strain 3.20 %,
Temperature 23.0 °C		10670 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.61 MPa
@Strain 3.30 %,
Temperature 23.0 °C		10680 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.7 MPa
@Strain 7.50 %,
Temperature 0.000 °C		10700 psi
@Strain 7.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.71 MPa
@Strain 3.40 %,
Temperature 23.0 °C		10690 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.74 MPa
@Strain 3.50 %,
Temperature 23.0 °C		10700 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.84 MPa
@Strain 3.60 %,
Temperature 23.0 °C		10710 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		10700 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.95 MPa
@Strain 3.80 %,
Temperature 23.0 °C		10730 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.97 MPa
@Strain 3.90 %,
Temperature 23.0 °C		10730 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.03 MPa
@Strain 4.00 %,
Temperature 23.0 °C		10740 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.03 MPa
@Strain 4.10 %,
Temperature 23.0 °C		10740 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.07 MPa
@Strain 4.40 %,
Temperature 23.0 °C		10740 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.1 MPa
@Strain 8.00 %,
Temperature 0.000 °C		10700 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.12 MPa
@Strain 4.60 %,
Temperature 23.0 °C		10750 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.12 MPa
@Strain 4.20 %,
Temperature 23.0 °C		10750 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.16 MPa
@Strain 4.30 %,
Temperature 23.0 °C		10760 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.16 MPa
@Strain 4.50 %,
Temperature 23.0 °C		10760 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.2 MPa
@Strain 4.80 %,
Temperature 23.0 °C		10800 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.22 MPa
@Strain 4.70 %,
Temperature 23.0 °C		10760 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.29 MPa
@Strain 4.90 %,
Temperature 23.0 °C		10770 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.29 MPa
@Strain 5.00 %,
Temperature 23.0 °C		10770 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.42 MPa
@Strain 5.50 %,
Temperature 23.0 °C		10790 psi
@Strain 5.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.53 MPa
@Strain 6.00 %,
Temperature 23.0 °C		10810 psi
@Strain 6.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.6 MPa
@Strain 8.50 %,
Temperature 0.000 °C		10800 psi
@Strain 8.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.66 MPa
@Strain 6.50 %,
Temperature 23.0 °C		10830 psi
@Strain 6.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.77 MPa
@Strain 7.00 %,
Temperature 23.0 °C		10840 psi
@Strain 7.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.9 MPa
@Strain 7.40 %,
Temperature 23.0 °C		10900 psi
@Strain 7.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.9 MPa
@Strain 9.00 %,
Temperature 0.000 °C		10900 psi
@Strain 9.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.01 MPa
@Strain 7.50 %,
Temperature 23.0 °C		10880 psi
@Strain 7.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.12 MPa
@Strain 8.00 %,
Temperature 23.0 °C		10900 psi
@Strain 8.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.27 MPa
@Strain 8.50 %,
Temperature 23.0 °C		10920 psi
@Strain 8.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.41 MPa
@Strain 9.00 %,
Temperature 23.0 °C		10940 psi
@Strain 9.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.5 MPa
@Strain 9.50 %,
Temperature 0.000 °C		11000 psi
@Strain 9.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.51 MPa
@Strain 9.50 %,
Temperature 23.0 °C		10950 psi
@Strain 9.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.6 MPa
@Strain 10.0 %,
Temperature 0.000 °C		11000 psi
@Strain 10.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.6 MPa
@Strain 1.80 %,
Temperature 0.000 °C		11000 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.73 MPa
@Strain 10.0 %,
Temperature 23.0 °C		10980 psi
@Strain 10.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.99 MPa
@Strain 11.0 %,
Temperature 23.0 °C		11020 psi
@Strain 11.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.0 MPa
@Strain 1.50 %,
Temperature -40.0 °C		11000 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 76.21 MPa
@Strain 1.60 %,
Temperature -40.0 °C		11050 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 76.27 MPa
@Strain 12.0 %,
Temperature 23.0 °C		11060 psi
@Strain 12.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.49 MPa
@Strain 13.0 %,
Temperature 23.0 °C		11090 psi
@Strain 13.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.5 MPa
@Strain 11.0 %,
Temperature 0.000 °C		11100 psi
@Strain 11.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.68 MPa
@Strain 14.0 %,
Temperature 23.0 °C		11120 psi
@Strain 14.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.89 MPa
@Strain 15.0 %,
Temperature 23.0 °C		11150 psi
@Strain 15.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.0 MPa
@Strain 12.0 %,
Temperature 0.000 °C		11200 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.06 MPa
@Strain 16.0 %,
Temperature 23.0 °C		11180 psi
@Strain 16.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.5 MPa
@Strain 13.0 %,
Temperature 0.000 °C		11200 psi
@Strain 13.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.6 MPa
@Strain 14.0 %,
Temperature 0.000 °C		11300 psi
@Strain 14.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.9 MPa
@Strain 1.90 %,
Temperature 0.000 °C		11300 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.0 MPa
@Strain 15.0 %,
Temperature 0.000 °C		11300 psi
@Strain 15.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.0 MPa
@Strain 16.0 %,
Temperature 0.000 °C		11300 psi
@Strain 16.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.2 MPa
@Strain 17.0 %,
Temperature 0.000 °C		11300 psi
@Strain 17.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.2 MPa
@Strain 18.0 %,
Temperature 0.000 °C		11300 psi
@Strain 18.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 19.0 %,
Temperature 0.000 °C		11400 psi
@Strain 19.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 20.0 %,
Temperature 0.000 °C		11400 psi
@Strain 20.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 1.60 %,
Temperature -40.0 °C		11500 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.71 MPa
@Strain 1.70 %,
Temperature -40.0 °C		11560 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		11600 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 81.7 MPa
@Strain 2.10 %,
Temperature 0.000 °C		11800 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		12000 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 83.02 MPa
@Strain 1.80 %,
Temperature -40.0 °C		12040 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.3 MPa
@Strain 2.20 %,
Temperature 0.000 °C		12100 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.9 MPa
@Strain 2.30 %,
Temperature 0.000 °C		12300 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.6 MPa
@Strain 1.80 %,
Temperature -40.0 °C		12400 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 86.0 MPa
@Strain 2.40 %,
Temperature 0.000 °C		12500 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.26 MPa
@Strain 1.90 %,
Temperature -40.0 °C		12510 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.1 MPa
@Strain 2.50 %,
Temperature 0.000 °C		12600 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.2 MPa
@Strain 2.60 %,
Temperature 0.000 °C		12800 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.7 MPa
@Strain 1.90 %,
Temperature -40.0 °C		12900 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.0 MPa
@Strain 2.70 %,
Temperature 0.000 °C		12900 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.19 MPa
@Strain 2.00 %,
Temperature -40.0 °C		12940 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.8 MPa
@Strain 2.80 %,
Temperature 0.000 °C		13000 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.5 MPa
@Strain 2.90 %,
Temperature 0.000 °C		13100 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.0 MPa
@Strain 3.00 %,
Temperature 0.000 °C		13200 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.6 MPa
@Strain 3.10 %,
Temperature 0.000 °C		13300 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.7 MPa
@Strain 2.00 %,
Temperature -40.0 °C		13300 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.76 MPa
@Strain 2.10 %,
Temperature -40.0 °C		13310 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.9 MPa
@Strain 3.20 %,
Temperature 0.000 °C		13300 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.2 MPa
@Strain 3.30 %,
Temperature 0.000 °C		13400 psi
@Strain 3.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.6 MPa
@Strain 3.40 %,
Temperature 0.000 °C		13400 psi
@Strain 3.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.7 MPa
@Strain 3.50 %,
Temperature 0.000 °C		13400 psi
@Strain 3.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.9 MPa
@Strain 3.60 %,
Temperature 0.000 °C		13500 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.1 MPa
@Strain 3.70 %,
Temperature 0.000 °C		13500 psi
@Strain 3.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.1 MPa
@Strain 3.80 %,
Temperature 0.000 °C		13500 psi
@Strain 3.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.3 MPa
@Strain 3.90 %,
Temperature 0.000 °C		13500 psi
@Strain 3.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.4 MPa
@Strain 4.00 %,
Temperature 0.000 °C		13500 psi
@Strain 4.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.5 MPa
@Strain 4.10 %,
Temperature 0.000 °C		13600 psi
@Strain 4.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.5 MPa
@Strain 4.20 %,
Temperature 0.000 °C		13600 psi
@Strain 4.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.6 MPa
@Strain 4.30 %,
Temperature 0.000 °C		13600 psi
@Strain 4.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.6 MPa
@Strain 4.40 %,
Temperature 0.000 °C		13600 psi
@Strain 4.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.7 MPa
@Strain 4.50 %,
Temperature 0.000 °C		13600 psi
@Strain 4.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.7 MPa
@Strain 4.60 %,
Temperature 0.000 °C		13600 psi
@Strain 4.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.7 MPa
@Strain 8.00 %,
Temperature 0.000 °C		13600 psi
@Strain 8.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.8 MPa
@Strain 4.70 %,
Temperature 0.000 °C		13600 psi
@Strain 4.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.8 MPa
@Strain 7.50 %,
Temperature 0.000 °C		13600 psi
@Strain 7.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.8 MPa
@Strain 4.80 %,
Temperature 0.000 °C		13600 psi
@Strain 4.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 5.00 %,
Temperature 0.000 °C		13600 psi
@Strain 5.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 5.50 %,
Temperature 0.000 °C		13600 psi
@Strain 5.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 7.00 %,
Temperature 0.000 °C		13600 psi
@Strain 7.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.0 MPa
@Strain 6.00 %,
Temperature 0.000 °C		13600 psi
@Strain 6.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.0 MPa
@Strain 6.50 %,
Temperature 0.000 °C		13600 psi
@Strain 6.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.09 MPa
@Strain 2.20 %,
Temperature -40.0 °C		13650 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.2 MPa
@Strain 2.10 %,
Temperature -40.0 °C		13700 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.31 MPa
@Strain 2.30 %,
Temperature -40.0 °C		13970 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.4 MPa
@Strain 2.20 %,
Temperature -40.0 °C		14000 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 98.2 MPa
@Strain 2.30 %,
Temperature -40.0 °C		14200 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 98.3 MPa
@Strain 2.40 %,
Temperature -40.0 °C		14300 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 99.8 MPa
@Strain 2.40 %,
Temperature -40.0 °C		14500 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 100.07 MPa
@Strain 2.50 %,
Temperature -40.0 °C		14514 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.3 MPa
@Strain 2.50 %,
Temperature -40.0 °C		14690 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.61 MPa
@Strain 2.60 %,
Temperature -40.0 °C		14737 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 102.4 MPa
@Strain 2.60 %,
Temperature -40.0 °C		14850 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.1 MPa
@Strain 2.70 %,
Temperature -40.0 °C		14950 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.6 MPa
@Strain 2.70 %,
Temperature -40.0 °C		15030 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.55 MPa
@Strain 2.80 %,
Temperature -40.0 °C		15164 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 104.7 MPa
@Strain 2.80 %,
Temperature -40.0 °C		15190 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 105.81 MPa
@Strain 2.90 %,
Temperature -40.0 °C		15346 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.9 MPa
@Strain 2.90 %,
Temperature -40.0 °C		15360 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.95 MPa
@Strain 3.00 %,
Temperature -40.0 °C		15512 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.2 MPa
@Strain 3.00 %,
Temperature -40.0 °C		15550 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.86 MPa
@Strain 3.10 %,
Temperature -40.0 °C		15644 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.4 MPa
@Strain 3.10 %,
Temperature -40.0 °C		15720 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.62 MPa
@Strain 3.20 %,
Temperature -40.0 °C		15754 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.29 MPa
@Strain 3.30 %,
Temperature -40.0 °C		15851 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.7 MPa
@Strain 3.20 %,
Temperature -40.0 °C		15910 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.11 MPa
@Strain 3.40 %,
Temperature -40.0 °C		15970 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.7 MPa
@Strain 3.30 %,
Temperature -40.0 °C		16060 psi
@Strain 3.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.83 MPa
@Strain 3.50 %,
Temperature -40.0 °C		16075 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.43 MPa
@Strain 3.60 %,
Temperature -40.0 °C		16162 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.6 MPa
@Strain 3.40 %,
Temperature -40.0 °C		16190 psi
@Strain 3.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.9 MPa
@Strain 3.70 %,
Temperature -40.0 °C		16230 psi
@Strain 3.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.1 MPa
@Strain 3.50 %,
Temperature -40.0 °C		16260 psi
@Strain 3.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.35 MPa
@Strain 3.80 %,
Temperature -40.0 °C		16295 psi
@Strain 3.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 3.60 %,
Temperature -40.0 °C		16330 psi
@Strain 3.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.7 MPa
@Strain 3.90 %,
Temperature -40.0 °C		16350 psi
@Strain 3.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.11 MPa
@Strain 4.00 %,
Temperature -40.0 °C		16405 psi
@Strain 4.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.2 MPa
@Strain 3.70 %,
Temperature -40.0 °C		16420 psi
@Strain 3.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.5 MPa
@Strain 3.80 %,
Temperature -40.0 °C		16460 psi
@Strain 3.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.59 MPa
@Strain 4.10 %,
Temperature -40.0 °C		16475 psi
@Strain 4.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.9 MPa
@Strain 3.90 %,
Temperature -40.0 °C		16520 psi
@Strain 3.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.01 MPa
@Strain 4.20 %,
Temperature -40.0 °C		16536 psi
@Strain 4.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.3 MPa
@Strain 4.00 %,
Temperature -40.0 °C		16580 psi
@Strain 4.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.5 MPa
@Strain 4.30 %,
Temperature -40.0 °C		16610 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.7 MPa
@Strain 4.10 %,
Temperature -40.0 °C		16640 psi
@Strain 4.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.96 MPa
@Strain 4.40 %,
Temperature -40.0 °C		16674 psi
@Strain 4.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115 MPa
@Strain 4.20 %,
Temperature -40.0 °C		16700 psi
@Strain 4.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.15 MPa
@Strain 4.50 %,
Temperature -40.0 °C		16701 psi
@Strain 4.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.3 MPa
@Strain 4.30 %,
Temperature -40.0 °C		16720 psi
@Strain 4.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.41 MPa
@Strain 4.60 %,
Temperature -40.0 °C		16739 psi
@Strain 4.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.47 MPa
@Strain 7.00 %,
Temperature -40.0 °C		16748 psi
@Strain 7.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.6 MPa
@Strain 4.40 %,
Temperature -40.0 °C		16770 psi
@Strain 4.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.62 MPa
@Strain 4.70 %,
Temperature -40.0 °C		16769 psi
@Strain 4.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.69 MPa
@Strain 6.50 %,
Temperature -40.0 °C		16779 psi
@Strain 6.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.79 MPa
@Strain 4.80 %,
Temperature -40.0 °C		16794 psi
@Strain 4.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.8 MPa
@Strain 4.50 %,
Temperature -40.0 °C		16800 psi
@Strain 4.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.93 MPa
@Strain 4.90 %,
Temperature -40.0 °C		16814 psi
@Strain 4.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.99 MPa
@Strain 6.00 %,
Temperature -40.0 °C		16823 psi
@Strain 6.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116 MPa
@Strain 4.60 %,
Temperature -40.0 °C		16800 psi
@Strain 4.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.03 MPa
@Strain 5.00 %,
Temperature -40.0 °C		16829 psi
@Strain 5.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.08 MPa
@Strain 5.50 %,
Temperature -40.0 °C		16836 psi
@Strain 5.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.2 MPa
@Strain 4.70 %,
Temperature -40.0 °C		16850 psi
@Strain 4.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.4 MPa
@Strain 4.80 %,
Temperature -40.0 °C		16880 psi
@Strain 4.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.6 MPa
@Strain 4.90 %,
Temperature -40.0 °C		16910 psi
@Strain 4.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.7 MPa
@Strain 5.00 %,
Temperature -40.0 °C		16930 psi
@Strain 5.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117 MPa
@Strain 5.50 %,
Temperature -40.0 °C		17000 psi
@Strain 5.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.2 MPa
@Strain 6.00 %,
Temperature -40.0 °C		17000 psi
@Strain 6.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.4 MPa
@Strain 6.50 %,
Temperature -40.0 °C		17030 psi
@Strain 6.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.5 MPa
@Strain 7.00 %,
Temperature -40.0 °C		17040 psi
@Strain 7.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.55 MPa
@Strain 7.50 %,
Temperature -40.0 °C		17049 psi
@Strain 7.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
Elongation at Break  15 %
@Temperature 23.0 °C		15 %
@Temperature 73.4 °F		DAM; ISO 527
 17 %
@Temperature 23.0 °C		17 %
@Temperature 73.4 °F		DAM; ASTM D638
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  1.80 GPa
@Temperature 23.0 °C		261 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 4.90 GPa
@Temperature 23.0 °C		711 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  1.80 GPa
@Temperature 23.0 °C		261 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.50 GPa
@Temperature 23.0 °C		653 ksi
@Temperature 73.4 °F		DAM; ISO 178
 4.585 GPa
@Temperature 23.0 °C		665.0 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Izod Impact, Notched 0.850 J/cm
@Temperature 23.0 °C		1.59 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
Izod Impact, Unnotched 16.0 J/cm
@Temperature 23.0 °C		30.0 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature -40.0 °C		2.38 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature -40.0 °C		2.38 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature -30.0 °C		2.62 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  50.0 kJ/m²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 60.0 kJ/m²
@Temperature -30.0 °C		28.6 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 100 kJ/m²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 250 kJ/m²
@Temperature 23.0 °C		119 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  5.00 J/cm²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 6.50 J/cm²
@Temperature -30.0 °C		30.9 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 12.0 J/cm²
@Temperature 23.0 °C		57.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 25.0 J/cm²
@Temperature 23.0 °C		119 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.400 J/cm²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.700 J/cm²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.40 J/cm²
@Temperature 23.0 °C		6.66 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 400 V
@Temperature 23.0 °C		400 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 65.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		36.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 65.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		36.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 98.0 µm/m-°C
@Temperature 55.0 - 160 °C		54.4 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
 98.0 µm/m-°C
@Temperature 55.0 - 160 °C		54.4 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
Melting Point 258 °C496 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 205 °C401 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C167 °FDAM; ASTM D648
 80.0 °C176 °FDAM; ISO 75-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 256 °C493 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
 Impact ModifierDAM
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesImpact Resistance, GoodDAM
 Warpage, LowDAM
FillerMineral fillerDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-IMD36<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Warp ResinsDAM
 Mineral Reinforced ResinsDAM
 Toughened ResinsDAM
Resin IdentificationPA66-IMD36ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 GearsDAM
 HousingsDAM
 Parts, EngineeringDAM
 Tool, Power & OthersDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45431.html

免责声明: 本文 DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4