- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 5.5
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.5 % | 5.5 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | Humidity Absorption; Sim. to ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 9.20 GPa | 1330 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0080 @Frequency 100 Hz | 0.0080 @Frequency 100 Hz | IEC 60250 | ||
| 0.013 @Frequency 1e+6 Hz | 0.013 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 525 V | 525 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-1 @Thickness 1.60 mm | V-1 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||