  4. DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66

DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66

DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66 物性表: DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.47
  • 吸水率 [%]: 0.7
  • 成型收缩率 [%]: 0.009
  • 缺口冲击强度: 0.43
  • 弯曲模量 [MPa]: 0.827
  • 硬度: 121.0
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.47 g/cc1.47 g/ccDAM; ASTM D792
Density 1.47 g/cc0.0531 lb/in³DAM; ISO 1183
Filler Content 40 %40 %DAM
Water Absorption  0.70 %
@Temperature 23.0 °C		0.70 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.1 %
@Temperature 23.0 °C		1.1 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 1.6 %
@Temperature 23.0 °C		1.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 4.7 %
@Temperature 23.0 °C		4.7 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 6.0 %
@Temperature 23.0 °C		6.0 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0090 cm/cm
@Thickness 3.20 mm		0.0090 in/in
@Thickness 0.126 in		Flow; DAM
 0.0090 cm/cm
@Thickness 1.60 mm		0.0090 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0090 cm/cm
@Thickness 1.60 mm		0.0090 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.0090 cm/cm
@Thickness 3.20 mm		0.0090 in/in
@Thickness 0.126 in		Transverse; DAM
 0.014 cm/cm
@Thickness 6.40 mm		0.014 in/in
@Thickness 0.252 in		Flow; DAM
 0.014 cm/cm
@Thickness 6.40 mm		0.014 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 9090DAM; ASTM D785
Hardness, Rockwell R 121121DAM; ASTM D785
Tensile Strength at Break  63.0 MPa
@Temperature 23.0 °C		9140 psi
@Temperature 73.4 °F		50%RH; ISO 527
 90.0 MPa
@Temperature 23.0 °C		13100 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  32.0 MPa
@Temperature 121 °C		4640 psi
@Temperature 250 °F		50%RH; ASTM D638
 35.0 MPa
@Temperature 121 °C		5080 psi
@Temperature 250 °F		DAM; ASTM D638
 43.0 MPa
@Temperature 77.0 °C		6240 psi
@Temperature 171 °F		50%RH; ASTM D638
 59.0 MPa
@Temperature 77.0 °C		8560 psi
@Temperature 171 °F		DAM; ASTM D638
 63.0 MPa
@Temperature 23.0 °C		9140 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 90.0 MPa
@Temperature 23.0 °C		13100 psi
@Temperature 73.4 °F		DAM; ASTM D638
 124 MPa
@Temperature -40.0 °C		18000 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 128 MPa
@Temperature -40.0 °C		18600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  0.800 MPa
@Strain 0.100 %,
Temperature 150 °C		116 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.850 MPa
@Strain 0.100 %,
Temperature 150 °C		123 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.00 MPa
@Strain 0.100 %,
Temperature 120 °C		145 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.00 MPa
@Strain 0.100 %,
Temperature 120 °C		145 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.15 MPa
@Strain 0.100 %,
Temperature 100 °C		167 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.25 MPa
@Strain 0.100 %,
Temperature 80.0 °C		181 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.30 MPa
@Strain 0.100 %,
Temperature 100 °C		189 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.40 MPa
@Strain 0.100 %,
Temperature 80.0 °C		203 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 1.40 MPa
@Strain 0.100 %,
Temperature 60.0 °C		203 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.60 MPa
@Strain 0.200 %,
Temperature 150 °C		232 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.70 MPa
@Strain 0.200 %,
Temperature 150 °C		247 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.04 MPa
@Strain 0.200 %,
Temperature 120 °C		296 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.07 MPa
@Strain 0.200 %,
Temperature 120 °C		300 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.30 MPa
@Strain 0.200 %,
Temperature 100 °C		334 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.30 MPa
@Strain 0.100 %,
Temperature 60.0 °C		334 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 2.38 MPa
@Strain 0.300 %,
Temperature 150 °C		345 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.42 MPa
@Strain 0.100 %,
Temperature 23.0 °C		351 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 2.50 MPa
@Strain 0.300 %,
Temperature 150 °C		363 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.55 MPa
@Strain 0.200 %,
Temperature 80.0 °C		370 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.83 MPa
@Strain 0.200 %,
Temperature 100 °C		410 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.90 MPa
@Strain 0.400 %,
Temperature 150 °C		421 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.90 MPa
@Strain 0.200 %,
Temperature 80.0 °C		421 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.93 MPa
@Strain 0.200 %,
Temperature 60.0 °C		425 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.98 MPa
@Strain 0.300 %,
Temperature 120 °C		432 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.10 MPa
@Strain 0.400 %,
Temperature 150 °C		450 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.12 MPa
@Strain 0.300 %,
Temperature 120 °C		453 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.36 MPa
@Strain 0.300 %,
Temperature 100 °C		487 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.57 MPa
@Strain 0.400 %,
Temperature 120 °C		518 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.72 MPa
@Strain 0.400 %,
Temperature 120 °C		540 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.73 MPa
@Strain 0.300 %,
Temperature 80.0 °C		541 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.78 MPa
@Strain 0.300 %,
Temperature 100 °C		548 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.93 MPa
@Strain 0.500 %,
Temperature 150 °C		570 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.00 MPa
@Strain 0.500 %,
Temperature 150 °C		580 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.26 MPa
@Strain 0.300 %,
Temperature 80.0 °C		618 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.32 MPa
@Strain 0.300 %,
Temperature 60.0 °C		627 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.43 MPa
@Strain 0.400 %,
Temperature 100 °C		643 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.48 MPa
@Strain 0.600 %,
Temperature 150 °C		650 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.60 MPa
@Strain 0.400 %,
Temperature 100 °C		667 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.62 MPa
@Strain 0.200 %,
Temperature 60.0 °C		670 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 4.75 MPa
@Strain 0.400 %,
Temperature 80.0 °C		689 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.82 MPa
@Strain 0.500 %,
Temperature 120 °C		699 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.87 MPa
@Strain 0.500 %,
Temperature 120 °C		706 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.94 MPa
@Strain 0.200 %,
Temperature 23.0 °C		716 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.10 MPa
@Strain 0.600 %,
Temperature 150 °C		740 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.11 MPa
@Strain 0.700 %,
Temperature 150 °C		741 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.11 MPa
@Strain 0.400 %,
Temperature 80.0 °C		741 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.17 MPa
@Strain 0.400 %,
Temperature 60.0 °C		750 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.40 MPa
@Strain 0.100 %,
Temperature 0.000 °C		783 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		798 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.69 MPa
@Strain 0.500 %,
Temperature 100 °C		825 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.75 MPa
@Strain 0.800 %,
Temperature 150 °C		834 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.79 MPa
@Strain 0.600 %,
Temperature 120 °C		840 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.87 MPa
@Strain 0.600 %,
Temperature 120 °C		851 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.13 MPa
@Strain 0.500 %,
Temperature 100 °C		889 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.20 MPa
@Strain 0.700 %,
Temperature 150 °C		899 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.20 MPa
@Strain 0.100 %,
Temperature 0.000 °C		899 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.35 MPa
@Strain 0.500 %,
Temperature 80.0 °C		921 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.38 MPa
@Strain 0.900 %,
Temperature 150 °C		925 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.48 MPa
@Strain 0.600 %,
Temperature 100 °C		940 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.50 MPa
@Strain 0.100 %,
Temperature -40.0 °C		943 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.68 MPa
@Strain 0.600 %,
Temperature 100 °C		969 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.70 MPa
@Strain 0.800 %,
Temperature 150 °C		972 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.75 MPa
@Strain 0.500 %,
Temperature 60.0 °C		979 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.76 MPa
@Strain 0.700 %,
Temperature 120 °C		980 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.78 MPa
@Strain 0.700 %,
Temperature 120 °C		983 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.87 MPa
@Strain 0.300 %,
Temperature 60.0 °C		996 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 6.96 MPa
@Strain 1.00 %,
Temperature 150 °C		1010 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.98 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1010 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.14 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1040 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 7.23 MPa
@Strain 0.700 %,
Temperature 100 °C		1050 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.26 MPa
@Strain 0.600 %,
Temperature 80.0 °C		1050 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.40 MPa
@Strain 0.900 %,
Temperature 150 °C		1070 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.49 MPa
@Strain 0.700 %,
Temperature 100 °C		1090 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.56 MPa
@Strain 1.10 %,
Temperature 150 °C		1100 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 0.800 %,
Temperature 120 °C		1110 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.69 MPa
@Strain 0.800 %,
Temperature 120 °C		1120 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.80 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1130 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 7.99 MPa
@Strain 1.20 %,
Temperature 150 °C		1160 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.08 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1170 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.08 MPa
@Strain 0.600 %,
Temperature 60.0 °C		1170 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.10 MPa
@Strain 1.00 %,
Temperature 150 °C		1170 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.20 MPa
@Strain 0.800 %,
Temperature 100 °C		1190 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.23 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1190 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.35 MPa
@Strain 0.900 %,
Temperature 120 °C		1210 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.38 MPa
@Strain 1.30 %,
Temperature 150 °C		1220 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.43 MPa
@Strain 0.600 %,
Temperature 80.0 °C		1220 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.46 MPa
@Strain 0.900 %,
Temperature 120 °C		1230 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.53 MPa
@Strain 0.800 %,
Temperature 100 °C		1240 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.60 MPa
@Strain 1.10 %,
Temperature 150 °C		1250 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.61 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1250 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.89 MPa
@Strain 1.40 %,
Temperature 150 °C		1290 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.93 MPa
@Strain 1.00 %,
Temperature 120 °C		1300 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.08 MPa
@Strain 0.800 %,
Temperature 80.0 °C		1320 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.14 MPa
@Strain 0.900 %,
Temperature 100 °C		1330 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.20 MPa
@Strain 1.20 %,
Temperature 150 °C		1330 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.29 MPa
@Strain 0.700 %,
Temperature 60.0 °C		1350 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.30 MPa
@Strain 1.00 %,
Temperature 120 °C		1350 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.44 MPa
@Strain 1.50 %,
Temperature 150 °C		1370 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.47 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1370 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.56 MPa
@Strain 0.900 %,
Temperature 100 °C		1390 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.70 MPa
@Strain 1.30 %,
Temperature 150 °C		1410 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.74 MPa
@Strain 1.10 %,
Temperature 120 °C		1410 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.89 MPa
@Strain 1.60 %,
Temperature 150 °C		1430 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.06 MPa
@Strain 1.10 %,
Temperature 120 °C		1459 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.08 MPa
@Strain 1.00 %,
Temperature 100 °C		1462 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.08 MPa
@Strain 0.900 %,
Temperature 80.0 °C		1462 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.26 MPa
@Strain 1.00 %,
Temperature 100 °C		1488 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.3 MPa
@Strain 1.40 %,
Temperature 150 °C		1490 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.38 MPa
@Strain 1.70 %,
Temperature 150 °C		1505 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.44 MPa
@Strain 0.800 %,
Temperature 80.0 °C		1514 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.44 MPa
@Strain 0.800 %,
Temperature 60.0 °C		1514 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.53 MPa
@Strain 1.20 %,
Temperature 120 °C		1527 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.61 MPa
@Strain 1.20 %,
Temperature 120 °C		1539 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.71 MPa
@Strain 1.80 %,
Temperature 150 °C		1553 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.82 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1569 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 10.83 MPa
@Strain 1.10 %,
Temperature 100 °C		1571 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.98 MPa
@Strain 1.10 %,
Temperature 100 °C		1593 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.0 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1600 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.04 MPa
@Strain 1.90 %,
Temperature 150 °C		1601 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.08 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1607 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.18 MPa
@Strain 1.30 %,
Temperature 120 °C		1622 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 1.50 %,
Temperature 150 °C		1620 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.26 MPa
@Strain 1.30 %,
Temperature 120 °C		1633 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.47 MPa
@Strain 2.00 %,
Temperature 150 °C		1664 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.51 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1669 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.56 MPa
@Strain 0.900 %,
Temperature 60.0 °C		1677 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.59 MPa
@Strain 1.20 %,
Temperature 100 °C		1681 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.62 MPa
@Strain 0.900 %,
Temperature 80.0 °C		1685 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.68 MPa
@Strain 1.20 %,
Temperature 100 °C		1694 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.76 MPa
@Strain 0.500 %,
Temperature 23.0 °C		1706 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.88 MPa
@Strain 1.40 %,
Temperature 120 °C		1723 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.89 MPa
@Strain 1.40 %,
Temperature 120 °C		1725 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.89 MPa
@Strain 2.10 %,
Temperature 150 °C		1725 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.9 MPa
@Strain 1.60 %,
Temperature 150 °C		1730 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.95 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1733 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.23 MPa
@Strain 1.30 %,
Temperature 100 °C		1774 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.28 MPa
@Strain 2.20 %,
Temperature 150 °C		1781 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.29 MPa
@Strain 1.30 %,
Temperature 100 °C		1783 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.3 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1780 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 12.4 MPa
@Strain 1.70 %,
Temperature 150 °C		1800 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.41 MPa
@Strain 1.50 %,
Temperature 120 °C		1800 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.58 MPa
@Strain 1.50 %,
Temperature 120 °C		1825 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.59 MPa
@Strain 2.30 %,
Temperature 150 °C		1826 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.65 MPa
@Strain 1.00 %,
Temperature 60.0 °C		1835 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.71 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1843 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.77 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1852 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.8 MPa
@Strain 1.80 %,
Temperature 150 °C		1860 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.86 MPa
@Strain 2.40 %,
Temperature 150 °C		1865 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.86 MPa
@Strain 1.40 %,
Temperature 100 °C		1865 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.9 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1870 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 12.92 MPa
@Strain 1.60 %,
Temperature 120 °C		1874 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.08 MPa
@Strain 1.40 %,
Temperature 100 °C		1897 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.21 MPa
@Strain 1.60 %,
Temperature 120 °C		1916 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.22 MPa
@Strain 2.50 %,
Temperature 150 °C		1917 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.3 MPa
@Strain 1.90 %,
Temperature 150 °C		1930 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.38 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1941 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.5 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1960 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.53 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1962 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.56 MPa
@Strain 1.50 %,
Temperature 100 °C		1967 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.56 MPa
@Strain 1.70 %,
Temperature 120 °C		1967 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.58 MPa
@Strain 2.60 %,
Temperature 150 °C		1970 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.7 MPa
@Strain 2.00 %,
Temperature 150 °C		1990 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.85 MPa
@Strain 1.70 %,
Temperature 120 °C		2009 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.86 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2010 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.87 MPa
@Strain 1.50 %,
Temperature 100 °C		2012 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.92 MPa
@Strain 2.70 %,
Temperature 150 °C		2019 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.94 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2022 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.1 MPa
@Strain 1.20 %,
Temperature 60.0 °C		2050 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.2 MPa
@Strain 2.10 %,
Temperature 150 °C		2060 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.22 MPa
@Strain 1.80 %,
Temperature 120 °C		2062 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.22 MPa
@Strain 2.80 %,
Temperature 150 °C		2062 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.29 MPa
@Strain 1.20 %,
Temperature 80.0 °C		2073 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.3 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2070 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 14.34 MPa
@Strain 1.40 %,
Temperature 80.0 °C		2080 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.34 MPa
@Strain 1.60 %,
Temperature 100 °C		2080 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.44 MPa
@Strain 1.60 %,
Temperature 100 °C		2094 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.46 MPa
@Strain 1.80 %,
Temperature 120 °C		2097 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.46 MPa
@Strain 2.90 %,
Temperature 150 °C		2097 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.5 MPa
@Strain 2.20 %,
Temperature 150 °C		2100 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.65 MPa
@Strain 1.90 %,
Temperature 120 °C		2125 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.76 MPa
@Strain 3.00 %,
Temperature 150 °C		2141 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.91 MPa
@Strain 1.90 %,
Temperature 120 °C		2163 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.95 MPa
@Strain 1.50 %,
Temperature 80.0 °C		2168 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.99 MPa
@Strain 1.70 %,
Temperature 100 °C		2174 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.01 MPa
@Strain 1.70 %,
Temperature 100 °C		2177 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.04 MPa
@Strain 3.10 %,
Temperature 150 °C		2181 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.04 MPa
@Strain 1.30 %,
Temperature 60.0 °C		2181 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.07 MPa
@Strain 2.00 %,
Temperature 120 °C		2186 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.1 MPa
@Strain 2.30 %,
Temperature 150 °C		2190 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.26 MPa
@Strain 1.30 %,
Temperature 80.0 °C		2213 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.28 MPa
@Strain 3.20 %,
Temperature 150 °C		2216 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.37 MPa
@Strain 2.00 %,
Temperature 120 °C		2229 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.4 MPa
@Strain 2.40 %,
Temperature 150 °C		2230 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.49 MPa
@Strain 3.30 %,
Temperature 150 °C		2247 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.49 MPa
@Strain 1.80 %,
Temperature 100 °C		2247 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.53 MPa
@Strain 1.80 %,
Temperature 100 °C		2252 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.61 MPa
@Strain 2.10 %,
Temperature 120 °C		2264 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 3.40 %,
Temperature 150 °C		2281 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.77 MPa
@Strain 1.60 %,
Temperature 80.0 °C		2287 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.8 MPa
@Strain 2.50 %,
Temperature 150 °C		2290 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.86 MPa
@Strain 0.700 %,
Temperature 23.0 °C		2300 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.88 MPa
@Strain 2.10 %,
Temperature 120 °C		2303 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.01 MPa
@Strain 1.90 %,
Temperature 100 °C		2322 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.01 MPa
@Strain 1.40 %,
Temperature 60.0 °C		2322 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.05 MPa
@Strain 1.90 %,
Temperature 100 °C		2328 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.06 MPa
@Strain 3.50 %,
Temperature 150 °C		2329 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.09 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2334 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 16.13 MPa
@Strain 2.20 %,
Temperature 120 °C		2339 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.2 MPa
@Strain 1.40 %,
Temperature 80.0 °C		2350 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.31 MPa
@Strain 3.60 %,
Temperature 150 °C		2366 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.35 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2371 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 16.4 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2380 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 16.4 MPa
@Strain 2.60 %,
Temperature 150 °C		2380 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.43 MPa
@Strain 2.20 %,
Temperature 120 °C		2383 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.52 MPa
@Strain 1.70 %,
Temperature 80.0 °C		2396 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.52 MPa
@Strain 3.70 %,
Temperature 150 °C		2396 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.57 MPa
@Strain 2.00 %,
Temperature 100 °C		2403 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.58 MPa
@Strain 2.30 %,
Temperature 120 °C		2405 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.64 MPa
@Strain 2.00 %,
Temperature 100 °C		2413 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.7 MPa
@Strain 3.80 %,
Temperature 150 °C		2420 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.81 MPa
@Strain 1.50 %,
Temperature 80.0 °C		2438 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.83 MPa
@Strain 1.50 %,
Temperature 60.0 °C		2441 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.89 MPa
@Strain 2.40 %,
Temperature 120 °C		2450 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.91 MPa
@Strain 3.90 %,
Temperature 150 °C		2453 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.97 MPa
@Strain 2.30 %,
Temperature 120 °C		2461 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.0 MPa
@Strain 2.70 %,
Temperature 150 °C		2470 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.08 MPa
@Strain 2.10 %,
Temperature 100 °C		2477 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.18 MPa
@Strain 4.00 %,
Temperature 150 °C		2492 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.25 MPa
@Strain 2.10 %,
Temperature 100 °C		2502 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.28 MPa
@Strain 1.80 %,
Temperature 80.0 °C		2506 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.3 MPa
@Strain 2.80 %,
Temperature 150 °C		2510 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.34 MPa
@Strain 2.50 %,
Temperature 120 °C		2515 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.43 MPa
@Strain 4.10 %,
Temperature 150 °C		2528 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.43 MPa
@Strain 0.800 %,
Temperature 23.0 °C		2528 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.48 MPa
@Strain 1.60 %,
Temperature 80.0 °C		2535 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.52 MPa
@Strain 2.40 %,
Temperature 120 °C		2541 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.55 MPa
@Strain 4.20 %,
Temperature 150 °C		2545 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.6 MPa
@Strain 2.90 %,
Temperature 150 °C		2550 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.6 MPa
@Strain 2.20 %,
Temperature 100 °C		2550 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.73 MPa
@Strain 1.90 %,
Temperature 80.0 °C		2572 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.73 MPa
@Strain 4.30 %,
Temperature 150 °C		2572 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.73 MPa
@Strain 1.60 %,
Temperature 60.0 °C		2572 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.82 MPa
@Strain 2.60 %,
Temperature 120 °C		2585 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.82 MPa
@Strain 2.20 %,
Temperature 100 °C		2585 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.88 MPa
@Strain 2.50 %,
Temperature 120 °C		2593 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.9 MPa
@Strain 3.00 %,
Temperature 150 °C		2600 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.97 MPa
@Strain 4.40 %,
Temperature 150 °C		2606 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.05 MPa
@Strain 2.30 %,
Temperature 100 °C		2618 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.09 MPa
@Strain 4.50 %,
Temperature 150 °C		2624 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.1 MPa
@Strain 0.800 %,
Temperature 60.0 °C		2630 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 18.2 MPa
@Strain 3.10 %,
Temperature 150 °C		2640 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.21 MPa
@Strain 2.60 %,
Temperature 120 °C		2641 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.25 MPa
@Strain 2.00 %,
Temperature 80.0 °C		2647 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.28 MPa
@Strain 2.70 %,
Temperature 120 °C		2651 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.33 MPa
@Strain 4.60 %,
Temperature 150 °C		2659 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.34 MPa
@Strain 1.70 %,
Temperature 60.0 °C		2660 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.39 MPa
@Strain 1.70 %,
Temperature 80.0 °C		2667 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.4 MPa
@Strain 2.30 %,
Temperature 100 °C		2670 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.5 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2680 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 18.51 MPa
@Strain 2.40 %,
Temperature 100 °C		2685 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.55 MPa
@Strain 4.70 %,
Temperature 150 °C		2690 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.6 MPa
@Strain 3.20 %,
Temperature 150 °C		2700 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.7 MPa
@Strain 4.80 %,
Temperature 150 °C		2710 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.7 MPa
@Strain 2.70 %,
Temperature 120 °C		2710 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.76 MPa
@Strain 2.40 %,
Temperature 100 °C		2721 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.76 MPa
@Strain 2.80 %,
Temperature 120 °C		2721 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.8 MPa
@Strain 0.900 %,
Temperature 23.0 °C		2730 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.85 MPa
@Strain 4.90 %,
Temperature 150 °C		2734 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.9 MPa
@Strain 3.30 %,
Temperature 150 °C		2740 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.94 MPa
@Strain 2.10 %,
Temperature 80.0 °C		2747 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.96 MPa
@Strain 2.50 %,
Temperature 100 °C		2750 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.97 MPa
@Strain 1.80 %,
Temperature 60.0 °C		2751 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 5.00 %,
Temperature 150 °C		2760 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.06 MPa
@Strain 2.90 %,
Temperature 120 °C		2764 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.18 MPa
@Strain 2.80 %,
Temperature 120 °C		2782 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.18 MPa
@Strain 1.80 %,
Temperature 80.0 °C		2782 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.2 MPa
@Strain 3.40 %,
Temperature 150 °C		2780 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.25 MPa
@Strain 2.50 %,
Temperature 100 °C		2792 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.37 MPa
@Strain 3.00 %,
Temperature 120 °C		2809 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.43 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2818 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 19.5 MPa
@Strain 3.50 %,
Temperature 150 °C		2830 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.52 MPa
@Strain 2.90 %,
Temperature 120 °C		2831 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.52 MPa
@Strain 2.20 %,
Temperature 80.0 °C		2831 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.57 MPa
@Strain 2.60 %,
Temperature 100 °C		2838 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.63 MPa
@Strain 5.50 %,
Temperature 150 °C		2847 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.73 MPa
@Strain 2.60 %,
Temperature 100 °C		2862 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.76 MPa
@Strain 3.10 %,
Temperature 120 °C		2866 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.76 MPa
@Strain 1.90 %,
Temperature 60.0 °C		2866 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.78 MPa
@Strain 1.90 %,
Temperature 80.0 °C		2869 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.8 MPa
@Strain 3.60 %,
Temperature 150 °C		2870 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.88 MPa
@Strain 3.00 %,
Temperature 120 °C		2883 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.95 MPa
@Strain 0.900 %,
Temperature 60.0 °C		2894 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.96 MPa
@Strain 2.70 %,
Temperature 100 °C		2895 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.0 MPa
@Strain 3.70 %,
Temperature 150 °C		2900 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.03 MPa
@Strain 3.20 %,
Temperature 120 °C		2905 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.18 MPa
@Strain 2.30 %,
Temperature 80.0 °C		2927 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.24 MPa
@Strain 2.70 %,
Temperature 100 °C		2936 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.27 MPa
@Strain 3.10 %,
Temperature 120 °C		2940 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.27 MPa
@Strain 1.00 %,
Temperature 23.0 °C		2940 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.3 MPa
@Strain 3.80 %,
Temperature 150 °C		2940 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.33 MPa
@Strain 2.00 %,
Temperature 80.0 °C		2949 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.36 MPa
@Strain 3.30 %,
Temperature 120 °C		2953 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.39 MPa
@Strain 2.80 %,
Temperature 100 °C		2957 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.4 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2960 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 20.48 MPa
@Strain 6.00 %,
Temperature 150 °C		2970 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.52 MPa
@Strain 2.00 %,
Temperature 60.0 °C		2976 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.58 MPa
@Strain 2.40 %,
Temperature 80.0 °C		2985 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.58 MPa
@Strain 2.80 %,
Temperature 100 °C		2985 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.6 MPa
@Strain 3.90 %,
Temperature 150 °C		2990 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.7 MPa
@Strain 4.00 %,
Temperature 150 °C		3000 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.7 MPa
@Strain 3.40 %,
Temperature 120 °C		3000 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.7 MPa
@Strain 3.20 %,
Temperature 120 °C		3000 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.81 MPa
@Strain 2.90 %,
Temperature 100 °C		3018 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.89 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3030 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 20.97 MPa
@Strain 2.90 %,
Temperature 100 °C		3041 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.0 MPa
@Strain 3.50 %,
Temperature 120 °C		3050 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.0 MPa
@Strain 4.10 %,
Temperature 150 °C		3050 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.06 MPa
@Strain 3.30 %,
Temperature 120 °C		3055 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.09 MPa
@Strain 2.50 %,
Temperature 80.0 °C		3059 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.09 MPa
@Strain 2.10 %,
Temperature 80.0 °C		3059 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.1 MPa
@Strain 4.20 %,
Temperature 150 °C		3060 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.12 MPa
@Strain 6.50 %,
Temperature 150 °C		3063 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.21 MPa
@Strain 3.60 %,
Temperature 120 °C		3076 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.21 MPa
@Strain 3.00 %,
Temperature 100 °C		3076 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.21 MPa
@Strain 2.10 %,
Temperature 60.0 °C		3076 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.4 MPa
@Strain 4.30 %,
Temperature 150 °C		3100 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.42 MPa
@Strain 1.10 %,
Temperature 23.0 °C		3107 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.43 MPa
@Strain 3.00 %,
Temperature 100 °C		3108 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.49 MPa
@Strain 3.40 %,
Temperature 120 °C		3117 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.51 MPa
@Strain 3.70 %,
Temperature 120 °C		3120 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.61 MPa
@Strain 2.60 %,
Temperature 80.0 °C		3134 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.65 MPa
@Strain 7.00 %,
Temperature 150 °C		3140 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.66 MPa
@Strain 2.20 %,
Temperature 80.0 °C		3142 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.69 MPa
@Strain 3.10 %,
Temperature 100 °C		3146 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.7 MPa
@Strain 4.40 %,
Temperature 150 °C		3150 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.74 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3153 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.76 MPa
@Strain 3.50 %,
Temperature 120 °C		3156 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.79 MPa
@Strain 2.20 %,
Temperature 60.0 °C		3160 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.88 MPa
@Strain 3.80 %,
Temperature 120 °C		3173 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.9 MPa
@Strain 4.50 %,
Temperature 150 °C		3180 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.91 MPa
@Strain 3.10 %,
Temperature 100 °C		3178 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3190 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 22.03 MPa
@Strain 3.60 %,
Temperature 120 °C		3195 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.09 MPa
@Strain 3.90 %,
Temperature 120 °C		3204 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.1 MPa
@Strain 4.60 %,
Temperature 150 °C		3210 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.15 MPa
@Strain 3.20 %,
Temperature 100 °C		3213 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.15 MPa
@Strain 2.30 %,
Temperature 80.0 °C		3213 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.18 MPa
@Strain 2.70 %,
Temperature 80.0 °C		3217 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.18 MPa
@Strain 7.50 %,
Temperature 150 °C		3217 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.21 MPa
@Strain 3.20 %,
Temperature 100 °C		3221 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.27 MPa
@Strain 2.30 %,
Temperature 60.0 °C		3230 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.33 MPa
@Strain 4.00 %,
Temperature 120 °C		3239 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.34 MPa
@Strain 3.70 %,
Temperature 120 °C		3240 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.4 MPa
@Strain 4.70 %,
Temperature 150 °C		3250 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.45 MPa
@Strain 3.30 %,
Temperature 100 °C		3256 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.5 MPa
@Strain 4.80 %,
Temperature 150 °C		3260 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.58 MPa
@Strain 3.30 %,
Temperature 100 °C		3275 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 4.10 %,
Temperature 120 °C		3280 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.67 MPa
@Strain 3.80 %,
Temperature 120 °C		3288 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.68 MPa
@Strain 8.00 %,
Temperature 150 °C		3289 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.7 MPa
@Strain 4.90 %,
Temperature 150 °C		3290 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.76 MPa
@Strain 2.80 %,
Temperature 80.0 °C		3301 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.79 MPa
@Strain 1.20 %,
Temperature 23.0 °C		3305 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.82 MPa
@Strain 3.40 %,
Temperature 100 °C		3310 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.85 MPa
@Strain 2.40 %,
Temperature 80.0 °C		3314 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.88 MPa
@Strain 4.20 %,
Temperature 120 °C		3318 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.9 MPa
@Strain 5.00 %,
Temperature 150 °C		3320 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.91 MPa
@Strain 3.90 %,
Temperature 120 °C		3323 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.91 MPa
@Strain 3.40 %,
Temperature 100 °C		3323 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.97 MPa
@Strain 2.40 %,
Temperature 60.0 °C		3332 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.06 MPa
@Strain 4.30 %,
Temperature 120 °C		3345 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.12 MPa
@Strain 8.50 %,
Temperature 150 °C		3353 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.18 MPa
@Strain 4.00 %,
Temperature 120 °C		3362 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.3 MPa
@Strain 3.50 %,
Temperature 100 °C		3380 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.3 MPa
@Strain 2.90 %,
Temperature 80.0 °C		3380 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.3 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3380 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.33 MPa
@Strain 4.40 %,
Temperature 120 °C		3384 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.35 MPa
@Strain 1.10 %,
Temperature 60.0 °C		3387 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.39 MPa
@Strain 3.50 %,
Temperature 100 °C		3392 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.42 MPa
@Strain 2.50 %,
Temperature 80.0 °C		3397 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.5 MPa
@Strain 9.00 %,
Temperature 150 °C		3410 psi
@Strain 9.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.52 MPa
@Strain 4.10 %,
Temperature 120 °C		3411 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.54 MPa
@Strain 4.50 %,
Temperature 120 °C		3414 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.6 MPa
@Strain 2.50 %,
Temperature 60.0 °C		3420 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.66 MPa
@Strain 4.60 %,
Temperature 120 °C		3432 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.66 MPa
@Strain 3.00 %,
Temperature 80.0 °C		3432 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.7 MPa
@Strain 5.50 %,
Temperature 150 °C		3440 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.73 MPa
@Strain 3.60 %,
Temperature 100 °C		3442 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.73 MPa
@Strain 3.60 %,
Temperature 100 °C		3442 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.82 MPa
@Strain 4.20 %,
Temperature 120 °C		3455 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.86 MPa
@Strain 9.50 %,
Temperature 150 °C		3461 psi
@Strain 9.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.91 MPa
@Strain 4.70 %,
Temperature 120 °C		3468 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.91 MPa
@Strain 2.60 %,
Temperature 80.0 °C		3468 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.94 MPa
@Strain 3.70 %,
Temperature 100 °C		3472 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.06 MPa
@Strain 3.10 %,
Temperature 80.0 °C		3490 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.09 MPa
@Strain 4.30 %,
Temperature 120 °C		3494 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.15 MPa
@Strain 1.30 %,
Temperature 23.0 °C		3503 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.18 MPa
@Strain 4.80 %,
Temperature 120 °C		3507 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.19 MPa
@Strain 3.70 %,
Temperature 100 °C		3508 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.2 MPa
@Strain 10.0 %,
Temperature 150 °C		3510 psi
@Strain 10.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.24 MPa
@Strain 2.60 %,
Temperature 60.0 °C		3516 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.27 MPa
@Strain 2.70 %,
Temperature 80.0 °C		3520 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.3 MPa
@Strain 3.80 %,
Temperature 100 °C		3520 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.33 MPa
@Strain 4.90 %,
Temperature 120 °C		3529 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.37 MPa
@Strain 4.40 %,
Temperature 120 °C		3535 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.47 MPa
@Strain 1.20 %,
Temperature 60.0 °C		3549 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.51 MPa
@Strain 3.20 %,
Temperature 80.0 °C		3555 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.51 MPa
@Strain 5.00 %,
Temperature 120 °C		3555 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.52 MPa
@Strain 4.50 %,
Temperature 120 °C		3556 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.6 MPa
@Strain 6.00 %,
Temperature 150 °C		3570 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.64 MPa
@Strain 3.80 %,
Temperature 100 °C		3574 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.69 MPa
@Strain 3.90 %,
Temperature 100 °C		3581 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.69 MPa
@Strain 2.70 %,
Temperature 60.0 °C		3581 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.73 MPa
@Strain 2.80 %,
Temperature 80.0 °C		3587 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.73 MPa
@Strain 11.0 %,
Temperature 150 °C		3587 psi
@Strain 11.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.85 MPa
@Strain 4.60 %,
Temperature 120 °C		3604 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.94 MPa
@Strain 3.90 %,
Temperature 100 °C		3617 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.0 MPa
@Strain 3.30 %,
Temperature 80.0 °C		3630 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.0 MPa
@Strain 4.00 %,
Temperature 100 °C		3630 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.12 MPa
@Strain 4.70 %,
Temperature 120 °C		3643 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.18 MPa
@Strain 4.10 %,
Temperature 100 °C		3652 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.18 MPa
@Strain 2.80 %,
Temperature 60.0 °C		3652 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.24 MPa
@Strain 4.00 %,
Temperature 100 °C		3661 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.26 MPa
@Strain 5.50 %,
Temperature 120 °C		3664 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.3 MPa
@Strain 6.50 %,
Temperature 150 °C		3670 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.3 MPa
@Strain 2.90 %,
Temperature 80.0 °C		3670 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.31 MPa
@Strain 1.40 %,
Temperature 23.0 °C		3671 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.31 MPa
@Strain 12.0 %,
Temperature 150 °C		3671 psi
@Strain 12.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.34 MPa
@Strain 4.80 %,
Temperature 120 °C		3675 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.36 MPa
@Strain 3.40 %,
Temperature 80.0 °C		3678 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.54 MPa
@Strain 4.20 %,
Temperature 100 °C		3704 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.57 MPa
@Strain 1.30 %,
Temperature 60.0 °C		3709 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.58 MPa
@Strain 4.90 %,
Temperature 120 °C		3710 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.67 MPa
@Strain 4.10 %,
Temperature 100 °C		3723 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.68 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3725 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 25.72 MPa
@Strain 3.50 %,
Temperature 80.0 °C		3730 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.72 MPa
@Strain 4.30 %,
Temperature 100 °C		3730 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.75 MPa
@Strain 2.90 %,
Temperature 60.0 °C		3735 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.76 MPa
@Strain 13.0 %,
Temperature 150 °C		3736 psi
@Strain 13.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.79 MPa
@Strain 5.00 %,
Temperature 120 °C		3741 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.8 MPa
@Strain 7.00 %,
Temperature 150 °C		3740 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.88 MPa
@Strain 3.00 %,
Temperature 80.0 °C		3754 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.06 MPa
@Strain 4.40 %,
Temperature 100 °C		3780 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.12 MPa
@Strain 3.60 %,
Temperature 80.0 °C		3788 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.12 MPa
@Strain 4.20 %,
Temperature 100 °C		3788 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.15 MPa
@Strain 14.0 %,
Temperature 150 °C		3793 psi
@Strain 14.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.25 MPa
@Strain 6.00 %,
Temperature 120 °C		3807 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.3 MPa
@Strain 7.50 %,
Temperature 150 °C		3810 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.33 MPa
@Strain 4.50 %,
Temperature 100 °C		3819 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.33 MPa
@Strain 3.00 %,
Temperature 60.0 °C		3819 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.36 MPa
@Strain 1.50 %,
Temperature 23.0 °C		3823 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.49 MPa
@Strain 4.30 %,
Temperature 100 °C		3842 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.51 MPa
@Strain 15.0 %,
Temperature 150 °C		3845 psi
@Strain 15.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.52 MPa
@Strain 3.10 %,
Temperature 80.0 °C		3846 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.57 MPa
@Strain 3.70 %,
Temperature 80.0 °C		3854 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.62 MPa
@Strain 5.50 %,
Temperature 120 °C		3861 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.63 MPa
@Strain 4.60 %,
Temperature 100 °C		3862 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.75 MPa
@Strain 3.10 %,
Temperature 60.0 °C		3880 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.8 MPa
@Strain 8.00 %,
Temperature 150 °C		3890 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.81 MPa
@Strain 4.70 %,
Temperature 100 °C		3888 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.81 MPa
@Strain 3.80 %,
Temperature 80.0 °C		3888 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.82 MPa
@Strain 4.40 %,
Temperature 100 °C		3890 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.85 MPa
@Strain 16.0 %,
Temperature 150 °C		3894 psi
@Strain 16.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.87 MPa
@Strain 1.40 %,
Temperature 60.0 °C		3897 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.88 MPa
@Strain 3.20 %,
Temperature 80.0 °C		3899 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.99 MPa
@Strain 6.50 %,
Temperature 120 °C		3915 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.05 MPa
@Strain 4.80 %,
Temperature 100 °C		3923 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.11 MPa
@Strain 3.90 %,
Temperature 80.0 °C		3932 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.14 MPa
@Strain 17.0 %,
Temperature 150 °C		3936 psi
@Strain 17.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.17 MPa
@Strain 3.20 %,
Temperature 60.0 °C		3941 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.19 MPa
@Strain 4.50 %,
Temperature 100 °C		3944 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.2 MPa
@Strain 8.50 %,
Temperature 150 °C		3950 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.25 MPa
@Strain 3.30 %,
Temperature 80.0 °C		3952 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.27 MPa
@Strain 0.500 %,
Temperature 0.000 °C		3955 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 27.36 MPa
@Strain 4.90 %,
Temperature 100 °C		3968 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.38 MPa
@Strain 18.0 %,
Temperature 150 °C		3971 psi
@Strain 18.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.41 MPa
@Strain 1.60 %,
Temperature 23.0 °C		3975 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.57 MPa
@Strain 4.00 %,
Temperature 80.0 °C		3999 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.6 MPa
@Strain 9.00 %,
Temperature 150 °C		4000 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.62 MPa
@Strain 7.00 %,
Temperature 120 °C		4006 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.62 MPa
@Strain 19.0 %,
Temperature 150 °C		4006 psi
@Strain 19.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.63 MPa
@Strain 4.60 %,
Temperature 100 °C		4007 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.7 MPa
@Strain 0.500 %,
Temperature 23.0 °C		4020 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 27.72 MPa
@Strain 3.30 %,
Temperature 60.0 °C		4020 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.75 MPa
@Strain 6.00 %,
Temperature 120 °C		4025 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.82 MPa
@Strain 3.40 %,
Temperature 80.0 °C		4035 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.86 MPa
@Strain 20.0 %,
Temperature 150 °C		4041 psi
@Strain 20.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.9 MPa
@Strain 9.50 %,
Temperature 150 °C		4050 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.93 MPa
@Strain 4.10 %,
Temperature 80.0 °C		4051 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.97 MPa
@Strain 4.70 %,
Temperature 100 °C		4057 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.0 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4060 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 28.06 MPa
@Strain 21.0 %,
Temperature 150 °C		4070 psi
@Strain 21.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.14 MPa
@Strain 1.70 %,
Temperature 23.0 °C		4081 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.17 MPa
@Strain 5.00 %,
Temperature 100 °C		4086 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.18 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4087 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.19 MPa
@Strain 4.80 %,
Temperature 100 °C		4089 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.19 MPa
@Strain 7.50 %,
Temperature 120 °C		4089 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.2 MPa
@Strain 10.0 %,
Temperature 150 °C		4090 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.2 MPa
@Strain 4.20 %,
Temperature 80.0 °C		4090 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.2 MPa
@Strain 3.40 %,
Temperature 60.0 °C		4090 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.25 MPa
@Strain 22.0 %,
Temperature 150 °C		4097 psi
@Strain 22.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.28 MPa
@Strain 3.50 %,
Temperature 80.0 °C		4102 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.41 MPa
@Strain 23.0 %,
Temperature 150 °C		4121 psi
@Strain 23.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.51 MPa
@Strain 4.30 %,
Temperature 80.0 °C		4135 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.57 MPa
@Strain 3.50 %,
Temperature 60.0 °C		4144 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.58 MPa
@Strain 4.90 %,
Temperature 100 °C		4145 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.58 MPa
@Strain 24.0 %,
Temperature 150 °C		4145 psi
@Strain 24.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.61 MPa
@Strain 6.50 %,
Temperature 120 °C		4150 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.68 MPa
@Strain 8.00 %,
Temperature 120 °C		4160 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.7 MPa
@Strain 11.0 %,
Temperature 150 °C		4160 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.74 MPa
@Strain 25.0 %,
Temperature 150 °C		4168 psi
@Strain 25.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.79 MPa
@Strain 3.60 %,
Temperature 80.0 °C		4176 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.87 MPa
@Strain 26.0 %,
Temperature 150 °C		4187 psi
@Strain 26.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.87 MPa
@Strain 4.40 %,
Temperature 80.0 °C		4187 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.9 MPa
@Strain 3.60 %,
Temperature 60.0 °C		4190 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.99 MPa
@Strain 5.00 %,
Temperature 100 °C		4205 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.0 MPa
@Strain 27.0 %,
Temperature 150 °C		4210 psi
@Strain 27.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.09 MPa
@Strain 1.80 %,
Temperature 23.0 °C		4219 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.12 MPa
@Strain 28.0 %,
Temperature 150 °C		4224 psi
@Strain 28.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.16 MPa
@Strain 8.50 %,
Temperature 120 °C		4229 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.17 MPa
@Strain 4.50 %,
Temperature 80.0 °C		4231 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 12.0 %,
Temperature 150 °C		4240 psi
@Strain 12.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.24 MPa
@Strain 29.0 %,
Temperature 150 °C		4241 psi
@Strain 29.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.31 MPa
@Strain 3.70 %,
Temperature 80.0 °C		4251 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.32 MPa
@Strain 5.50 %,
Temperature 100 °C		4253 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.35 MPa
@Strain 4.60 %,
Temperature 80.0 °C		4257 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.35 MPa
@Strain 30.0 %,
Temperature 150 °C		4257 psi
@Strain 30.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.41 MPa
@Strain 3.70 %,
Temperature 60.0 °C		4266 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.42 MPa
@Strain 1.60 %,
Temperature 60.0 °C		4267 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.42 MPa
@Strain 7.00 %,
Temperature 120 °C		4267 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.45 MPa
@Strain 31.0 %,
Temperature 150 °C		4271 psi
@Strain 31.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.52 MPa
@Strain 32.0 %,
Temperature 150 °C		4282 psi
@Strain 32.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.55 MPa
@Strain 9.00 %,
Temperature 120 °C		4286 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.61 MPa
@Strain 3.80 %,
Temperature 80.0 °C		4295 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.64 MPa
@Strain 33.0 %,
Temperature 150 °C		4299 psi
@Strain 33.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.7 MPa
@Strain 13.0 %,
Temperature 150 °C		4310 psi
@Strain 13.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.72 MPa
@Strain 34.0 %,
Temperature 150 °C		4311 psi
@Strain 34.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.72 MPa
@Strain 4.70 %,
Temperature 80.0 °C		4311 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.8 MPa
@Strain 35.0 %,
Temperature 150 °C		4320 psi
@Strain 35.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.84 MPa
@Strain 3.80 %,
Temperature 60.0 °C		4328 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.86 MPa
@Strain 36.0 %,
Temperature 150 °C		4331 psi
@Strain 36.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.92 MPa
@Strain 37.0 %,
Temperature 150 °C		4340 psi
@Strain 37.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.92 MPa
@Strain 9.50 %,
Temperature 120 °C		4340 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.99 MPa
@Strain 38.0 %,
Temperature 150 °C		4350 psi
@Strain 38.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 14.0 %,
Temperature 150 °C		4350 psi
@Strain 14.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.02 MPa
@Strain 4.80 %,
Temperature 80.0 °C		4354 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.03 MPa
@Strain 1.90 %,
Temperature 23.0 °C		4355 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.04 MPa
@Strain 39.0 %,
Temperature 150 °C		4357 psi
@Strain 39.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.06 MPa
@Strain 3.90 %,
Temperature 80.0 °C		4360 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.09 MPa
@Strain 40.0 %,
Temperature 150 °C		4364 psi
@Strain 40.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.1 MPa
@Strain 6.00 %,
Temperature 100 °C		4370 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.11 MPa
@Strain 7.50 %,
Temperature 120 °C		4367 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.11 MPa
@Strain 3.90 %,
Temperature 60.0 °C		4367 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.24 MPa
@Strain 1.70 %,
Temperature 60.0 °C		4386 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.25 MPa
@Strain 10.0 %,
Temperature 120 °C		4387 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.26 MPa
@Strain 4.90 %,
Temperature 80.0 °C		4389 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.3 MPa
@Strain 15.0 %,
Temperature 150 °C		4390 psi
@Strain 15.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.3 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4390 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 30.35 MPa
@Strain 5.50 %,
Temperature 100 °C		4402 psi
@Strain 5.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		4420 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.52 MPa
@Strain 4.00 %,
Temperature 80.0 °C		4427 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.56 MPa
@Strain 4.00 %,
Temperature 60.0 °C		4432 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.6 MPa
@Strain 16.0 %,
Temperature 150 °C		4440 psi
@Strain 16.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.7 MPa
@Strain 8.00 %,
Temperature 120 °C		4450 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.77 MPa
@Strain 2.00 %,
Temperature 23.0 °C		4463 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.84 MPa
@Strain 6.50 %,
Temperature 100 °C		4473 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.84 MPa
@Strain 11.0 %,
Temperature 120 °C		4473 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.9 MPa
@Strain 17.0 %,
Temperature 150 °C		4480 psi
@Strain 17.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.92 MPa
@Strain 4.10 %,
Temperature 80.0 °C		4485 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.05 MPa
@Strain 4.10 %,
Temperature 60.0 °C		4503 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.06 MPa
@Strain 1.80 %,
Temperature 60.0 °C		4505 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.1 MPa
@Strain 18.0 %,
Temperature 150 °C		4510 psi
@Strain 18.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.25 MPa
@Strain 8.50 %,
Temperature 120 °C		4532 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.28 MPa
@Strain 4.20 %,
Temperature 80.0 °C		4537 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.35 MPa
@Strain 4.20 %,
Temperature 60.0 °C		4547 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 19.0 %,
Temperature 150 °C		4550 psi
@Strain 19.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.44 MPa
@Strain 12.0 %,
Temperature 120 °C		4560 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.49 MPa
@Strain 7.00 %,
Temperature 100 °C		4567 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.5 MPa
@Strain 20.0 %,
Temperature 150 °C		4570 psi
@Strain 20.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.55 MPa
@Strain 5.50 %,
Temperature 80.0 °C		4576 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.61 MPa
@Strain 2.10 %,
Temperature 23.0 °C		4585 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.65 MPa
@Strain 4.30 %,
Temperature 60.0 °C		4590 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.71 MPa
@Strain 4.30 %,
Temperature 80.0 °C		4599 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.8 MPa
@Strain 9.00 %,
Temperature 120 °C		4610 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.8 MPa
@Strain 21.0 %,
Temperature 150 °C		4610 psi
@Strain 21.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.9 MPa
@Strain 22.0 %,
Temperature 150 °C		4630 psi
@Strain 22.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.94 MPa
@Strain 13.0 %,
Temperature 120 °C		4633 psi
@Strain 13.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.0 MPa
@Strain 1.90 %,
Temperature 60.0 °C		4640 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.01 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4643 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.02 MPa
@Strain 6.00 %,
Temperature 100 °C		4644 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.05 MPa
@Strain 4.40 %,
Temperature 60.0 °C		4648 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 7.50 %,
Temperature 100 °C		4660 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 23.0 %,
Temperature 150 °C		4660 psi
@Strain 23.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.16 MPa
@Strain 4.40 %,
Temperature 80.0 °C		4664 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.26 MPa
@Strain 9.50 %,
Temperature 120 °C		4679 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 24.0 %,
Temperature 150 °C		4680 psi
@Strain 24.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.33 MPa
@Strain 14.0 %,
Temperature 120 °C		4689 psi
@Strain 14.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 25.0 %,
Temperature 150 °C		4700 psi
@Strain 25.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.45 MPa
@Strain 2.20 %,
Temperature 23.0 °C		4706 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.47 MPa
@Strain 4.50 %,
Temperature 60.0 °C		4709 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.48 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4711 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 32.5 MPa
@Strain 26.0 %,
Temperature 150 °C		4710 psi
@Strain 26.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.53 MPa
@Strain 4.50 %,
Temperature 80.0 °C		4718 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.66 MPa
@Strain 8.00 %,
Temperature 100 °C		4737 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.67 MPa
@Strain 15.0 %,
Temperature 120 °C		4738 psi
@Strain 15.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.69 MPa
@Strain 10.0 %,
Temperature 120 °C		4741 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.7 MPa
@Strain 27.0 %,
Temperature 150 °C		4740 psi
@Strain 27.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.74 MPa
@Strain 4.60 %,
Temperature 60.0 °C		4749 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 28.0 %,
Temperature 150 °C		4760 psi
@Strain 28.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.89 MPa
@Strain 4.60 %,
Temperature 80.0 °C		4770 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 6.00 %,
Temperature 80.0 °C		4770 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.97 MPa
@Strain 2.00 %,
Temperature 60.0 °C		4782 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.0 MPa
@Strain 29.0 %,
Temperature 150 °C		4790 psi
@Strain 29.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.02 MPa
@Strain 16.0 %,
Temperature 120 °C		4789 psi
@Strain 16.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.08 MPa
@Strain 4.70 %,
Temperature 60.0 °C		4798 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 30.0 %,
Temperature 150 °C		4800 psi
@Strain 30.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.12 MPa
@Strain 8.50 %,
Temperature 100 °C		4804 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.14 MPa
@Strain 6.50 %,
Temperature 100 °C		4807 psi
@Strain 6.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.18 MPa
@Strain 2.30 %,
Temperature 23.0 °C		4812 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.2 MPa
@Strain 31.0 %,
Temperature 150 °C		4820 psi
@Strain 31.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.28 MPa
@Strain 4.70 %,
Temperature 80.0 °C		4827 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.29 MPa
@Strain 17.0 %,
Temperature 120 °C		4828 psi
@Strain 17.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 32.0 %,
Temperature 150 °C		4830 psi
@Strain 32.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.3 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4830 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.4 MPa
@Strain 33.0 %,
Temperature 150 °C		4840 psi
@Strain 33.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.41 MPa
@Strain 11.0 %,
Temperature 120 °C		4846 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.44 MPa
@Strain 4.80 %,
Temperature 60.0 °C		4850 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.5 MPa
@Strain 34.0 %,
Temperature 150 °C		4860 psi
@Strain 34.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.57 MPa
@Strain 18.0 %,
Temperature 120 °C		4869 psi
@Strain 18.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.58 MPa
@Strain 9.00 %,
Temperature 100 °C		4870 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.6 MPa
@Strain 35.0 %,
Temperature 150 °C		4870 psi
@Strain 35.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.62 MPa
@Strain 4.80 %,
Temperature 80.0 °C		4876 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.7 MPa
@Strain 36.0 %,
Temperature 150 °C		4890 psi
@Strain 36.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.71 MPa
@Strain 4.90 %,
Temperature 60.0 °C		4889 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.71 MPa
@Strain 2.40 %,
Temperature 23.0 °C		4889 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.79 MPa
@Strain 6.50 %,
Temperature 80.0 °C		4901 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.8 MPa
@Strain 37.0 %,
Temperature 150 °C		4900 psi
@Strain 37.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.8 MPa
@Strain 19.0 %,
Temperature 120 °C		4900 psi
@Strain 19.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.82 MPa
@Strain 2.10 %,
Temperature 60.0 °C		4905 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.9 MPa
@Strain 38.0 %,
Temperature 150 °C		4920 psi
@Strain 38.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.92 MPa
@Strain 9.50 %,
Temperature 100 °C		4920 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.92 MPa
@Strain 5.00 %,
Temperature 60.0 °C		4920 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.92 MPa
@Strain 4.90 %,
Temperature 80.0 °C		4920 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.0 MPa
@Strain 39.0 %,
Temperature 150 °C		4930 psi
@Strain 39.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.0 MPa
@Strain 40.0 %,
Temperature 150 °C		4930 psi
@Strain 40.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.03 MPa
@Strain 20.0 %,
Temperature 120 °C		4936 psi
@Strain 20.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.1 MPa
@Strain 41.0 %,
Temperature 150 °C		4950 psi
@Strain 41.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.13 MPa
@Strain 7.00 %,
Temperature 100 °C		4950 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.19 MPa
@Strain 12.0 %,
Temperature 120 °C		4959 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.2 MPa
@Strain 42.0 %,
Temperature 150 °C		4960 psi
@Strain 42.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.22 MPa
@Strain 21.0 %,
Temperature 120 °C		4963 psi
@Strain 21.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.22 MPa
@Strain 5.00 %,
Temperature 80.0 °C		4963 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.3 MPa
@Strain 43.0 %,
Temperature 150 °C		4970 psi
@Strain 43.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.39 MPa
@Strain 22.0 %,
Temperature 120 °C		4988 psi
@Strain 22.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.4 MPa
@Strain 44.0 %,
Temperature 150 °C		4990 psi
@Strain 44.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.43 MPa
@Strain 2.20 %,
Temperature 60.0 °C		4994 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.5 MPa
@Strain 45.0 %,
Temperature 150 °C		5000 psi
@Strain 45.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.5 MPa
@Strain 46.0 %,
Temperature 150 °C		5000 psi
@Strain 46.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.54 MPa
@Strain 10.0 %,
Temperature 100 °C		5010 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.55 MPa
@Strain 2.50 %,
Temperature 23.0 °C		5011 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.57 MPa
@Strain 23.0 %,
Temperature 120 °C		5014 psi
@Strain 23.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 47.0 %,
Temperature 150 °C		5020 psi
@Strain 47.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.6 MPa
@Strain 48.0 %,
Temperature 150 °C		5020 psi
@Strain 48.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.65 MPa
@Strain 7.00 %,
Temperature 80.0 °C		5026 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.73 MPa
@Strain 24.0 %,
Temperature 120 °C		5037 psi
@Strain 24.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.85 MPa
@Strain 13.0 %,
Temperature 120 °C		5055 psi
@Strain 13.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.87 MPa
@Strain 25.0 %,
Temperature 120 °C		5057 psi
@Strain 25.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.01 MPa
@Strain 26.0 %,
Temperature 120 °C		5078 psi
@Strain 26.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.03 MPa
@Strain 7.50 %,
Temperature 100 °C		5081 psi
@Strain 7.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.07 MPa
@Strain 2.30 %,
Temperature 60.0 °C		5086 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.11 MPa
@Strain 27.0 %,
Temperature 120 °C		5092 psi
@Strain 27.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.19 MPa
@Strain 5.50 %,
Temperature 60.0 °C		5104 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.21 MPa
@Strain 28.0 %,
Temperature 120 °C		5107 psi
@Strain 28.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.23 MPa
@Strain 11.0 %,
Temperature 100 °C		5110 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.25 MPa
@Strain 30.0 %,
Temperature 120 °C		5113 psi
@Strain 30.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.28 MPa
@Strain 29.0 %,
Temperature 120 °C		5117 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.28 MPa
@Strain 2.60 %,
Temperature 23.0 °C		5117 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 7.50 %,
Temperature 80.0 °C		5133 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 31.0 %,
Temperature 120 °C		5130 psi
@Strain 31.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.41 MPa
@Strain 14.0 %,
Temperature 120 °C		5136 psi
@Strain 14.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.45 MPa
@Strain 5.50 %,
Temperature 80.0 °C		5142 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.45 MPa
@Strain 32.0 %,
Temperature 120 °C		5142 psi
@Strain 32.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.5 MPa
@Strain 33.0 %,
Temperature 120 °C		5150 psi
@Strain 33.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.55 MPa
@Strain 34.0 %,
Temperature 120 °C		5156 psi
@Strain 34.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 35.0 %,
Temperature 120 °C		5160 psi
@Strain 35.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.74 MPa
@Strain 8.00 %,
Temperature 100 °C		5184 psi
@Strain 8.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.75 MPa
@Strain 12.0 %,
Temperature 100 °C		5185 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.81 MPa
@Strain 2.70 %,
Temperature 23.0 °C		5194 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.83 MPa
@Strain 2.40 %,
Temperature 60.0 °C		5197 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.9 MPa
@Strain 0.600 %,
Temperature 0.000 °C		5210 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 35.91 MPa
@Strain 15.0 %,
Temperature 120 °C		5208 psi
@Strain 15.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.07 MPa
@Strain 8.00 %,
Temperature 80.0 °C		5232 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.17 MPa
@Strain 13.0 %,
Temperature 100 °C		5246 psi
@Strain 13.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5260 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 36.33 MPa
@Strain 2.80 %,
Temperature 23.0 °C		5269 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.38 MPa
@Strain 16.0 %,
Temperature 120 °C		5276 psi
@Strain 16.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.38 MPa
@Strain 8.50 %,
Temperature 100 °C		5276 psi
@Strain 8.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.44 MPa
@Strain 2.50 %,
Temperature 60.0 °C		5285 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.58 MPa
@Strain 14.0 %,
Temperature 100 °C		5305 psi
@Strain 14.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.71 MPa
@Strain 8.50 %,
Temperature 80.0 °C		5324 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.76 MPa
@Strain 6.00 %,
Temperature 60.0 °C		5332 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 17.0 %,
Temperature 120 °C		5340 psi
@Strain 17.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.89 MPa
@Strain 15.0 %,
Temperature 100 °C		5350 psi
@Strain 15.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.95 MPa
@Strain 2.60 %,
Temperature 60.0 °C		5359 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.96 MPa
@Strain 2.90 %,
Temperature 23.0 °C		5361 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.04 MPa
@Strain 9.00 %,
Temperature 100 °C		5372 psi
@Strain 9.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.11 MPa
@Strain 6.00 %,
Temperature 80.0 °C		5382 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.2 MPa
@Strain 16.0 %,
Temperature 100 °C		5400 psi
@Strain 16.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.23 MPa
@Strain 18.0 %,
Temperature 120 °C		5400 psi
@Strain 18.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.29 MPa
@Strain 9.00 %,
Temperature 80.0 °C		5408 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.48 MPa
@Strain 17.0 %,
Temperature 100 °C		5436 psi
@Strain 17.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.57 MPa
@Strain 19.0 %,
Temperature 120 °C		5449 psi
@Strain 19.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.59 MPa
@Strain 9.50 %,
Temperature 100 °C		5452 psi
@Strain 9.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.59 MPa
@Strain 3.00 %,
Temperature 23.0 °C		5452 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.68 MPa
@Strain 2.70 %,
Temperature 60.0 °C		5465 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.75 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5475 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.75 MPa
@Strain 18.0 %,
Temperature 100 °C		5475 psi
@Strain 18.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.77 MPa
@Strain 9.50 %,
Temperature 80.0 °C		5478 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.86 MPa
@Strain 6.50 %,
Temperature 60.0 °C		5491 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.91 MPa
@Strain 20.0 %,
Temperature 120 °C		5498 psi
@Strain 20.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.94 MPa
@Strain 19.0 %,
Temperature 100 °C		5503 psi
@Strain 19.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.05 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5519 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 38.08 MPa
@Strain 10.0 %,
Temperature 100 °C		5523 psi
@Strain 10.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.14 MPa
@Strain 2.80 %,
Temperature 60.0 °C		5532 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.16 MPa
@Strain 20.0 %,
Temperature 100 °C		5535 psi
@Strain 20.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.22 MPa
@Strain 3.10 %,
Temperature 23.0 °C		5543 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.24 MPa
@Strain 21.0 %,
Temperature 120 °C		5546 psi
@Strain 21.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.27 MPa
@Strain 10.0 %,
Temperature 80.0 °C		5551 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.33 MPa
@Strain 21.0 %,
Temperature 100 °C		5559 psi
@Strain 21.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.34 MPa
@Strain 6.50 %,
Temperature 80.0 °C		5561 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.51 MPa
@Strain 22.0 %,
Temperature 100 °C		5585 psi
@Strain 22.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.52 MPa
@Strain 22.0 %,
Temperature 120 °C		5587 psi
@Strain 22.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.62 MPa
@Strain 2.90 %,
Temperature 60.0 °C		5601 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.66 MPa
@Strain 23.0 %,
Temperature 100 °C		5607 psi
@Strain 23.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5610 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.75 MPa
@Strain 3.20 %,
Temperature 23.0 °C		5620 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.8 MPa
@Strain 24.0 %,
Temperature 100 °C		5630 psi
@Strain 24.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.82 MPa
@Strain 23.0 %,
Temperature 120 °C		5630 psi
@Strain 23.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.84 MPa
@Strain 7.00 %,
Temperature 60.0 °C		5633 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.86 MPa
@Strain 11.0 %,
Temperature 100 °C		5636 psi
@Strain 11.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.93 MPa
@Strain 11.0 %,
Temperature 80.0 °C		5646 psi
@Strain 11.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.93 MPa
@Strain 25.0 %,
Temperature 100 °C		5646 psi
@Strain 25.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.98 MPa
@Strain 26.0 %,
Temperature 100 °C		5654 psi
@Strain 26.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.09 MPa
@Strain 24.0 %,
Temperature 120 °C		5670 psi
@Strain 24.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 27.0 %,
Temperature 100 °C		5670 psi
@Strain 27.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.17 MPa
@Strain 3.30 %,
Temperature 23.0 °C		5681 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 28.0 %,
Temperature 100 °C		5690 psi
@Strain 28.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.29 MPa
@Strain 3.00 %,
Temperature 60.0 °C		5699 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.3 MPa
@Strain 29.0 %,
Temperature 100 °C		5700 psi
@Strain 29.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.32 MPa
@Strain 25.0 %,
Temperature 120 °C		5703 psi
@Strain 25.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.4 MPa
@Strain 30.0 %,
Temperature 100 °C		5710 psi
@Strain 30.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.44 MPa
@Strain 7.00 %,
Temperature 80.0 °C		5720 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.5 MPa
@Strain 31.0 %,
Temperature 100 °C		5730 psi
@Strain 31.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.53 MPa
@Strain 26.0 %,
Temperature 120 °C		5733 psi
@Strain 26.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 32.0 %,
Temperature 100 °C		5740 psi
@Strain 32.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.69 MPa
@Strain 3.40 %,
Temperature 23.0 °C		5757 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 33.0 %,
Temperature 100 °C		5760 psi
@Strain 33.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 12.0 %,
Temperature 80.0 °C		5760 psi
@Strain 12.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.71 MPa
@Strain 3.10 %,
Temperature 60.0 °C		5759 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.76 MPa
@Strain 7.50 %,
Temperature 60.0 °C		5767 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.78 MPa
@Strain 12.0 %,
Temperature 100 °C		5770 psi
@Strain 12.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 34.0 %,
Temperature 100 °C		5770 psi
@Strain 34.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.8 MPa
@Strain 27.0 %,
Temperature 120 °C		5770 psi
@Strain 27.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.9 MPa
@Strain 35.0 %,
Temperature 100 °C		5790 psi
@Strain 35.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.02 MPa
@Strain 28.0 %,
Temperature 120 °C		5804 psi
@Strain 28.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.11 MPa
@Strain 3.50 %,
Temperature 23.0 °C		5817 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.17 MPa
@Strain 3.20 %,
Temperature 60.0 °C		5826 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.21 MPa
@Strain 29.0 %,
Temperature 120 °C		5832 psi
@Strain 29.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.28 MPa
@Strain 13.0 %,
Temperature 80.0 °C		5842 psi
@Strain 13.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.35 MPa
@Strain 7.50 %,
Temperature 80.0 °C		5852 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.38 MPa
@Strain 30.0 %,
Temperature 120 °C		5857 psi
@Strain 30.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.51 MPa
@Strain 13.0 %,
Temperature 100 °C		5875 psi
@Strain 13.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.57 MPa
@Strain 8.00 %,
Temperature 60.0 °C		5884 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.61 MPa
@Strain 31.0 %,
Temperature 120 °C		5890 psi
@Strain 31.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.64 MPa
@Strain 3.60 %,
Temperature 23.0 °C		5894 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.69 MPa
@Strain 3.30 %,
Temperature 60.0 °C		5902 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.77 MPa
@Strain 32.0 %,
Temperature 120 °C		5913 psi
@Strain 32.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.81 MPa
@Strain 14.0 %,
Temperature 80.0 °C		5919 psi
@Strain 14.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.93 MPa
@Strain 33.0 %,
Temperature 120 °C		5936 psi
@Strain 33.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.06 MPa
@Strain 3.70 %,
Temperature 23.0 °C		5955 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.07 MPa
@Strain 34.0 %,
Temperature 120 °C		5957 psi
@Strain 34.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.11 MPa
@Strain 3.40 %,
Temperature 60.0 °C		5963 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.14 MPa
@Strain 14.0 %,
Temperature 100 °C		5967 psi
@Strain 14.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.19 MPa
@Strain 35.0 %,
Temperature 120 °C		5974 psi
@Strain 35.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.22 MPa
@Strain 15.0 %,
Temperature 80.0 °C		5978 psi
@Strain 15.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.31 MPa
@Strain 8.00 %,
Temperature 80.0 °C		5992 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.35 MPa
@Strain 8.50 %,
Temperature 60.0 °C		5997 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.38 MPa
@Strain 36.0 %,
Temperature 120 °C		6002 psi
@Strain 36.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.49 MPa
@Strain 37.0 %,
Temperature 120 °C		6018 psi
@Strain 37.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.51 MPa
@Strain 3.50 %,
Temperature 60.0 °C		6021 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.58 MPa
@Strain 3.80 %,
Temperature 23.0 °C		6031 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.62 MPa
@Strain 16.0 %,
Temperature 80.0 °C		6036 psi
@Strain 16.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.65 MPa
@Strain 38.0 %,
Temperature 120 °C		6041 psi
@Strain 38.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		6050 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 41.75 MPa
@Strain 15.0 %,
Temperature 100 °C		6055 psi
@Strain 15.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.76 MPa
@Strain 39.0 %,
Temperature 120 °C		6057 psi
@Strain 39.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.76 MPa
@Strain 40.0 %,
Temperature 120 °C		6057 psi
@Strain 40.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.93 MPa
@Strain 17.0 %,
Temperature 80.0 °C		6081 psi
@Strain 17.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.04 MPa
@Strain 9.00 %,
Temperature 60.0 °C		6097 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.08 MPa
@Strain 3.60 %,
Temperature 60.0 °C		6103 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.11 MPa
@Strain 3.90 %,
Temperature 23.0 °C		6108 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.12 MPa
@Strain 8.50 %,
Temperature 80.0 °C		6109 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.22 MPa
@Strain 16.0 %,
Temperature 100 °C		6124 psi
@Strain 16.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.23 MPa
@Strain 18.0 %,
Temperature 80.0 °C		6125 psi
@Strain 18.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.42 MPa
@Strain 4.00 %,
Temperature 23.0 °C		6153 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.45 MPa
@Strain 3.70 %,
Temperature 60.0 °C		6157 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.52 MPa
@Strain 19.0 %,
Temperature 80.0 °C		6167 psi
@Strain 19.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 0.600 %,
Temperature -40.0 °C		6180 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 42.67 MPa
@Strain 17.0 %,
Temperature 100 °C		6189 psi
@Strain 17.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.71 MPa
@Strain 9.50 %,
Temperature 60.0 °C		6195 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.73 MPa
@Strain 20.0 %,
Temperature 80.0 °C		6197 psi
@Strain 20.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.78 MPa
@Strain 3.80 %,
Temperature 60.0 °C		6205 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.89 MPa
@Strain 9.00 %,
Temperature 80.0 °C		6221 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.94 MPa
@Strain 21.0 %,
Temperature 80.0 °C		6228 psi
@Strain 21.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.95 MPa
@Strain 4.10 %,
Temperature 23.0 °C		6229 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.02 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6240 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.08 MPa
@Strain 18.0 %,
Temperature 100 °C		6248 psi
@Strain 18.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.11 MPa
@Strain 22.0 %,
Temperature 80.0 °C		6253 psi
@Strain 22.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.12 MPa
@Strain 3.90 %,
Temperature 60.0 °C		6254 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.25 MPa
@Strain 10.0 %,
Temperature 60.0 °C		6273 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.26 MPa
@Strain 4.20 %,
Temperature 23.0 °C		6274 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.33 MPa
@Strain 23.0 %,
Temperature 80.0 °C		6284 psi
@Strain 23.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.43 MPa
@Strain 19.0 %,
Temperature 100 °C		6299 psi
@Strain 19.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.49 MPa
@Strain 24.0 %,
Temperature 80.0 °C		6308 psi
@Strain 24.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.54 MPa
@Strain 4.00 %,
Temperature 60.0 °C		6315 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.62 MPa
@Strain 25.0 %,
Temperature 80.0 °C		6327 psi
@Strain 25.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.66 MPa
@Strain 9.50 %,
Temperature 80.0 °C		6332 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.68 MPa
@Strain 4.30 %,
Temperature 23.0 °C		6335 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.74 MPa
@Strain 26.0 %,
Temperature 80.0 °C		6344 psi
@Strain 26.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.74 MPa
@Strain 20.0 %,
Temperature 100 °C		6344 psi
@Strain 20.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.87 MPa
@Strain 27.0 %,
Temperature 80.0 °C		6363 psi
@Strain 27.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.91 MPa
@Strain 4.10 %,
Temperature 60.0 °C		6369 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.98 MPa
@Strain 28.0 %,
Temperature 80.0 °C		6379 psi
@Strain 28.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.05 MPa
@Strain 29.0 %,
Temperature 80.0 °C		6389 psi
@Strain 29.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.07 MPa
@Strain 21.0 %,
Temperature 100 °C		6392 psi
@Strain 21.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 30.0 %,
Temperature 80.0 °C		6400 psi
@Strain 30.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 11.0 %,
Temperature 60.0 °C		6400 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 4.40 %,
Temperature 23.0 °C		6400 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		6400 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.15 MPa
@Strain 31.0 %,
Temperature 80.0 °C		6403 psi
@Strain 31.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.16 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6405 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.2 MPa
@Strain 32.0 %,
Temperature 80.0 °C		6410 psi
@Strain 32.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.21 MPa
@Strain 4.20 %,
Temperature 60.0 °C		6412 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.25 MPa
@Strain 33.0 %,
Temperature 80.0 °C		6418 psi
@Strain 33.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 34.0 %,
Temperature 80.0 °C		6430 psi
@Strain 34.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 10.0 %,
Temperature 80.0 °C		6430 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.34 MPa
@Strain 22.0 %,
Temperature 100 °C		6431 psi
@Strain 22.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.35 MPa
@Strain 35.0 %,
Temperature 80.0 °C		6432 psi
@Strain 35.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.52 MPa
@Strain 4.50 %,
Temperature 23.0 °C		6457 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.54 MPa
@Strain 23.0 %,
Temperature 100 °C		6460 psi
@Strain 23.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.6 MPa
@Strain 4.30 %,
Temperature 60.0 °C		6470 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.73 MPa
@Strain 4.60 %,
Temperature 23.0 °C		6488 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.76 MPa
@Strain 24.0 %,
Temperature 100 °C		6492 psi
@Strain 24.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.0 MPa
@Strain 4.40 %,
Temperature 60.0 °C		6530 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.02 MPa
@Strain 25.0 %,
Temperature 100 °C		6530 psi
@Strain 25.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.05 MPa
@Strain 12.0 %,
Temperature 60.0 °C		6534 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.15 MPa
@Strain 4.70 %,
Temperature 23.0 °C		6548 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.19 MPa
@Strain 26.0 %,
Temperature 100 °C		6554 psi
@Strain 26.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 4.50 %,
Temperature 60.0 °C		6570 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.38 MPa
@Strain 27.0 %,
Temperature 100 °C		6582 psi
@Strain 27.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.41 MPa
@Strain 11.0 %,
Temperature 80.0 °C		6586 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.47 MPa
@Strain 4.80 %,
Temperature 23.0 °C		6595 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.57 MPa
@Strain 28.0 %,
Temperature 100 °C		6609 psi
@Strain 28.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.61 MPa
@Strain 4.60 %,
Temperature 60.0 °C		6615 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.77 MPa
@Strain 13.0 %,
Temperature 60.0 °C		6638 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.78 MPa
@Strain 4.90 %,
Temperature 23.0 °C		6640 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.82 MPa
@Strain 29.0 %,
Temperature 100 °C		6646 psi
@Strain 29.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.91 MPa
@Strain 4.70 %,
Temperature 60.0 °C		6659 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.08 MPa
@Strain 30.0 %,
Temperature 100 °C		6683 psi
@Strain 30.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 5.00 %,
Temperature 23.0 °C		6690 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.3 MPa
@Strain 4.80 %,
Temperature 60.0 °C		6720 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.35 MPa
@Strain 31.0 %,
Temperature 100 °C		6723 psi
@Strain 31.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.36 MPa
@Strain 14.0 %,
Temperature 60.0 °C		6724 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.58 MPa
@Strain 4.90 %,
Temperature 60.0 °C		6756 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.59 MPa
@Strain 12.0 %,
Temperature 80.0 °C		6757 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.61 MPa
@Strain 32.0 %,
Temperature 100 °C		6760 psi
@Strain 32.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.83 MPa
@Strain 33.0 %,
Temperature 100 °C		6792 psi
@Strain 33.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.85 MPa
@Strain 5.00 %,
Temperature 60.0 °C		6795 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.9 MPa
@Strain 15.0 %,
Temperature 60.0 °C		6800 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 34.0 %,
Temperature 100 °C		6820 psi
@Strain 34.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 35.0 %,
Temperature 100 °C		6850 psi
@Strain 35.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.34 MPa
@Strain 16.0 %,
Temperature 60.0 °C		6866 psi
@Strain 16.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 13.0 %,
Temperature 80.0 °C		6870 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.46 MPa
@Strain 5.50 %,
Temperature 23.0 °C		6884 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6920 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 47.74 MPa
@Strain 17.0 %,
Temperature 60.0 °C		6924 psi
@Strain 17.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.91 MPa
@Strain 5.50 %,
Temperature 60.0 °C		6949 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.08 MPa
@Strain 0.900 %,
Temperature 0.000 °C		6973 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.09 MPa
@Strain 18.0 %,
Temperature 60.0 °C		6975 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.15 MPa
@Strain 14.0 %,
Temperature 80.0 °C		6984 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.39 MPa
@Strain 19.0 %,
Temperature 60.0 °C		7018 psi
@Strain 19.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.66 MPa
@Strain 20.0 %,
Temperature 60.0 °C		7058 psi
@Strain 20.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.87 MPa
@Strain 15.0 %,
Temperature 80.0 °C		7088 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.92 MPa
@Strain 21.0 %,
Temperature 60.0 °C		7095 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.0 MPa
@Strain 0.900 %,
Temperature 23.0 °C		7110 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.1 MPa
@Strain 0.700 %,
Temperature -40.0 °C		7120 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 49.14 MPa
@Strain 6.00 %,
Temperature 23.0 °C		7127 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.14 MPa
@Strain 22.0 %,
Temperature 60.0 °C		7127 psi
@Strain 22.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.35 MPa
@Strain 23.0 %,
Temperature 60.0 °C		7158 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.45 MPa
@Strain 6.00 %,
Temperature 60.0 °C		7172 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.53 MPa
@Strain 16.0 %,
Temperature 80.0 °C		7184 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.55 MPa
@Strain 24.0 %,
Temperature 60.0 °C		7187 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.71 MPa
@Strain 25.0 %,
Temperature 60.0 °C		7210 psi
@Strain 25.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.87 MPa
@Strain 26.0 %,
Temperature 60.0 °C		7233 psi
@Strain 26.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.98 MPa
@Strain 27.0 %,
Temperature 60.0 °C		7249 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.0 MPa
@Strain 28.0 %,
Temperature 60.0 °C		7250 psi
@Strain 28.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.08 MPa
@Strain 29.0 %,
Temperature 60.0 °C		7264 psi
@Strain 29.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.14 MPa
@Strain 17.0 %,
Temperature 80.0 °C		7272 psi
@Strain 17.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.15 MPa
@Strain 30.0 %,
Temperature 60.0 °C		7274 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.2 MPa
@Strain 31.0 %,
Temperature 60.0 °C		7280 psi
@Strain 31.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.25 MPa
@Strain 32.0 %,
Temperature 60.0 °C		7288 psi
@Strain 32.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 33.0 %,
Temperature 60.0 °C		7300 psi
@Strain 33.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.35 MPa
@Strain 34.0 %,
Temperature 60.0 °C		7303 psi
@Strain 34.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.35 MPa
@Strain 35.0 %,
Temperature 60.0 °C		7303 psi
@Strain 35.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.36 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7304 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 50.4 MPa
@Strain 6.50 %,
Temperature 23.0 °C		7310 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.67 MPa
@Strain 6.50 %,
Temperature 60.0 °C		7349 psi
@Strain 6.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.69 MPa
@Strain 18.0 %,
Temperature 80.0 °C		7352 psi
@Strain 18.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.25 MPa
@Strain 19.0 %,
Temperature 80.0 °C		7433 psi
@Strain 19.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.66 MPa
@Strain 7.00 %,
Temperature 23.0 °C		7493 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.74 MPa
@Strain 7.00 %,
Temperature 60.0 °C		7504 psi
@Strain 7.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.79 MPa
@Strain 20.0 %,
Temperature 80.0 °C		7512 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.27 MPa
@Strain 21.0 %,
Temperature 80.0 °C		7581 psi
@Strain 21.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.61 MPa
@Strain 7.50 %,
Temperature 23.0 °C		7630 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.68 MPa
@Strain 22.0 %,
Temperature 80.0 °C		7641 psi
@Strain 22.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 1.00 %,
Temperature 0.000 °C		7640 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.71 MPa
@Strain 7.50 %,
Temperature 60.0 °C		7645 psi
@Strain 7.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.06 MPa
@Strain 23.0 %,
Temperature 80.0 °C		7696 psi
@Strain 23.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.4 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7750 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 53.41 MPa
@Strain 24.0 %,
Temperature 80.0 °C		7746 psi
@Strain 24.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.45 MPa
@Strain 8.00 %,
Temperature 23.0 °C		7752 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.58 MPa
@Strain 8.00 %,
Temperature 60.0 °C		7771 psi
@Strain 8.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.78 MPa
@Strain 25.0 %,
Temperature 80.0 °C		7800 psi
@Strain 25.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.9 MPa
@Strain 1.00 %,
Temperature 23.0 °C		7820 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 54.14 MPa
@Strain 26.0 %,
Temperature 80.0 °C		7852 psi
@Strain 26.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.29 MPa
@Strain 8.50 %,
Temperature 23.0 °C		7874 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.43 MPa
@Strain 8.50 %,
Temperature 60.0 °C		7894 psi
@Strain 8.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.45 MPa
@Strain 27.0 %,
Temperature 80.0 °C		7897 psi
@Strain 27.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.69 MPa
@Strain 28.0 %,
Temperature 80.0 °C		7932 psi
@Strain 28.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.94 MPa
@Strain 29.0 %,
Temperature 80.0 °C		7968 psi
@Strain 29.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.02 MPa
@Strain 9.00 %,
Temperature 23.0 °C		7980 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.21 MPa
@Strain 9.00 %,
Temperature 60.0 °C		8008 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.23 MPa
@Strain 30.0 %,
Temperature 80.0 °C		8010 psi
@Strain 30.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.4 MPa
@Strain 0.800 %,
Temperature -40.0 °C		8040 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 55.46 MPa
@Strain 31.0 %,
Temperature 80.0 °C		8044 psi
@Strain 31.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.65 MPa
@Strain 9.50 %,
Temperature 23.0 °C		8071 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.73 MPa
@Strain 32.0 %,
Temperature 80.0 °C		8083 psi
@Strain 32.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.93 MPa
@Strain 33.0 %,
Temperature 80.0 °C		8112 psi
@Strain 33.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.93 MPa
@Strain 9.50 %,
Temperature 60.0 °C		8112 psi
@Strain 9.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 56.21 MPa
@Strain 34.0 %,
Temperature 80.0 °C		8153 psi
@Strain 34.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.28 MPa
@Strain 10.0 %,
Temperature 23.0 °C		8163 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.33 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8170 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 56.42 MPa
@Strain 35.0 %,
Temperature 80.0 °C		8183 psi
@Strain 35.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.58 MPa
@Strain 10.0 %,
Temperature 60.0 °C		8206 psi
@Strain 10.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.23 MPa
@Strain 11.0 %,
Temperature 23.0 °C		8301 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.27 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8306 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.57 MPa
@Strain 11.0 %,
Temperature 60.0 °C		8350 psi
@Strain 11.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.17 MPa
@Strain 12.0 %,
Temperature 23.0 °C		8437 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.6 MPa
@Strain 1.10 %,
Temperature 23.0 °C		8500 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.7 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8510 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 58.77 MPa
@Strain 12.0 %,
Temperature 60.0 °C		8524 psi
@Strain 12.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 59.01 MPa
@Strain 13.0 %,
Temperature 23.0 °C		8559 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.64 MPa
@Strain 14.0 %,
Temperature 23.0 °C		8650 psi
@Strain 14.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.69 MPa
@Strain 13.0 %,
Temperature 60.0 °C		8657 psi
@Strain 13.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.06 MPa
@Strain 15.0 %,
Temperature 23.0 °C		8711 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.49 MPa
@Strain 14.0 %,
Temperature 60.0 °C		8773 psi
@Strain 14.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.59 MPa
@Strain 16.0 %,
Temperature 23.0 °C		8788 psi
@Strain 16.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.8 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8820 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 61.01 MPa
@Strain 17.0 %,
Temperature 23.0 °C		8849 psi
@Strain 17.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.21 MPa
@Strain 15.0 %,
Temperature 60.0 °C		8878 psi
@Strain 15.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.32 MPa
@Strain 18.0 %,
Temperature 23.0 °C		8894 psi
@Strain 18.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.64 MPa
@Strain 19.0 %,
Temperature 23.0 °C		8940 psi
@Strain 19.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.78 MPa
@Strain 1.20 %,
Temperature 0.000 °C		8960 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.87 MPa
@Strain 16.0 %,
Temperature 60.0 °C		8974 psi
@Strain 16.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.95 MPa
@Strain 20.0 %,
Temperature 23.0 °C		8985 psi
@Strain 20.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.16 MPa
@Strain 21.0 %,
Temperature 23.0 °C		9016 psi
@Strain 21.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.18 MPa
@Strain 1.00 %,
Temperature -40.0 °C		9018 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.44 MPa
@Strain 17.0 %,
Temperature 60.0 °C		9056 psi
@Strain 17.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.48 MPa
@Strain 22.0 %,
Temperature 23.0 °C		9062 psi
@Strain 22.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.69 MPa
@Strain 23.0 %,
Temperature 23.0 °C		9092 psi
@Strain 23.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.79 MPa
@Strain 24.0 %,
Temperature 23.0 °C		9107 psi
@Strain 24.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.9 MPa
@Strain 1.20 %,
Temperature 23.0 °C		9120 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.0 MPa
@Strain 25.0 %,
Temperature 23.0 °C		9140 psi
@Strain 25.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.01 MPa
@Strain 18.0 %,
Temperature 60.0 °C		9139 psi
@Strain 18.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.11 MPa
@Strain 26.0 %,
Temperature 23.0 °C		9153 psi
@Strain 26.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.21 MPa
@Strain 27.0 %,
Temperature 23.0 °C		9168 psi
@Strain 27.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.42 MPa
@Strain 28.0 %,
Temperature 23.0 °C		9198 psi
@Strain 28.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.48 MPa
@Strain 19.0 %,
Temperature 60.0 °C		9207 psi
@Strain 19.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.53 MPa
@Strain 29.0 %,
Temperature 23.0 °C		9214 psi
@Strain 29.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.63 MPa
@Strain 30.0 %,
Temperature 23.0 °C		9229 psi
@Strain 30.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.74 MPa
@Strain 31.0 %,
Temperature 23.0 °C		9245 psi
@Strain 31.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.84 MPa
@Strain 32.0 %,
Temperature 23.0 °C		9259 psi
@Strain 32.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.9 MPa
@Strain 1.10 %,
Temperature 0.000 °C		9270 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 63.95 MPa
@Strain 33.0 %,
Temperature 23.0 °C		9275 psi
@Strain 33.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.99 MPa
@Strain 20.0 %,
Temperature 60.0 °C		9281 psi
@Strain 20.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.16 MPa
@Strain 34.0 %,
Temperature 23.0 °C		9306 psi
@Strain 34.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.16 MPa
@Strain 35.0 %,
Temperature 23.0 °C		9306 psi
@Strain 35.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.41 MPa
@Strain 21.0 %,
Temperature 60.0 °C		9342 psi
@Strain 21.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.76 MPa
@Strain 22.0 %,
Temperature 60.0 °C		9393 psi
@Strain 22.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.15 MPa
@Strain 23.0 %,
Temperature 60.0 °C		9449 psi
@Strain 23.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.49 MPa
@Strain 24.0 %,
Temperature 60.0 °C		9499 psi
@Strain 24.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.77 MPa
@Strain 25.0 %,
Temperature 60.0 °C		9539 psi
@Strain 25.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.8 MPa
@Strain 1.30 %,
Temperature 0.000 °C		9540 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.09 MPa
@Strain 26.0 %,
Temperature 60.0 °C		9586 psi
@Strain 26.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.1 MPa
@Strain 1.00 %,
Temperature -40.0 °C		9590 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 66.39 MPa
@Strain 27.0 %,
Temperature 60.0 °C		9629 psi
@Strain 27.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.7 MPa
@Strain 28.0 %,
Temperature 60.0 °C		9670 psi
@Strain 28.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.0 MPa
@Strain 1.30 %,
Temperature 23.0 °C		9720 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.02 MPa
@Strain 29.0 %,
Temperature 60.0 °C		9720 psi
@Strain 29.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.24 MPa
@Strain 30.0 %,
Temperature 60.0 °C		9752 psi
@Strain 30.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.69 MPa
@Strain 1.10 %,
Temperature -40.0 °C		9818 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 68.8 MPa
@Strain 1.20 %,
Temperature 0.000 °C		9980 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.51 MPa
@Strain 1.40 %,
Temperature 0.000 °C		10080 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.7 MPa
@Strain 1.40 %,
Temperature 23.0 °C		10300 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.1 MPa
@Strain 1.10 %,
Temperature -40.0 °C		10300 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 73.05 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10600 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.08 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10600 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 73.1 MPa
@Strain 1.30 %,
Temperature 0.000 °C		10600 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 73.6 MPa
@Strain 1.50 %,
Temperature 23.0 °C		10700 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.7 MPa
@Strain 1.20 %,
Temperature -40.0 °C		11000 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 76.3 MPa
@Strain 1.60 %,
Temperature 0.000 °C		11100 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.5 MPa
@Strain 1.60 %,
Temperature 23.0 °C		11100 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11200 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.05 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11320 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 78.7 MPa
@Strain 1.70 %,
Temperature 23.0 °C		11400 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.29 MPa
@Strain 1.70 %,
Temperature 0.000 °C		11500 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 79.8 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11600 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 80.8 MPa
@Strain 1.80 %,
Temperature 23.0 °C		11700 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.1 MPa
@Strain 1.50 %,
Temperature 0.000 °C		11800 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 81.98 MPa
@Strain 1.80 %,
Temperature 0.000 °C		11890 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 82.8 MPa
@Strain 1.90 %,
Temperature 23.0 °C		12000 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.83 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12010 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.6 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12100 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 84.38 MPa
@Strain 1.90 %,
Temperature 0.000 °C		12240 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 84.4 MPa
@Strain 2.00 %,
Temperature 23.0 °C		12200 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.5 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12300 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.5 MPa
@Strain 2.10 %,
Temperature 23.0 °C		12400 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 86.51 MPa
@Strain 2.00 %,
Temperature 0.000 °C		12550 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.7 MPa
@Strain 2.20 %,
Temperature 23.0 °C		12600 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 87.3 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12700 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.53 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12700 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.6 MPa
@Strain 2.30 %,
Temperature 23.0 °C		12700 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 87.9 MPa
@Strain 1.70 %,
Temperature 0.000 °C		12700 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.28 MPa
@Strain 2.10 %,
Temperature 0.000 °C		12800 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.4 MPa
@Strain 2.40 %,
Temperature 23.0 °C		12800 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.0 MPa
@Strain 2.50 %,
Temperature 23.0 °C		12900 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.3 MPa
@Strain 10.0 %,
Temperature 23.0 °C		13000 psi
@Strain 10.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.4 MPa
@Strain 9.50 %,
Temperature 23.0 °C		13000 psi
@Strain 9.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 8.00 %,
Temperature 23.0 °C		13000 psi
@Strain 8.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 8.50 %,
Temperature 23.0 °C		13000 psi
@Strain 8.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 9.00 %,
Temperature 23.0 °C		13000 psi
@Strain 9.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 2.60 %,
Temperature 23.0 °C		13000 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.6 MPa
@Strain 7.50 %,
Temperature 23.0 °C		13000 psi
@Strain 7.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.7 MPa
@Strain 6.50 %,
Temperature 23.0 °C		13000 psi
@Strain 6.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.7 MPa
@Strain 7.00 %,
Temperature 23.0 °C		13000 psi
@Strain 7.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.9 MPa
@Strain 2.70 %,
Temperature 23.0 °C		13000 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.9 MPa
@Strain 6.00 %,
Temperature 23.0 °C		13000 psi
@Strain 6.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.1 MPa
@Strain 5.50 %,
Temperature 23.0 °C		13100 psi
@Strain 5.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.14 MPa
@Strain 2.20 %,
Temperature 0.000 °C		13070 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 90.2 MPa
@Strain 5.00 %,
Temperature 23.0 °C		13100 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.2 MPa
@Strain 2.80 %,
Temperature 23.0 °C		13100 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.3 MPa
@Strain 4.90 %,
Temperature 23.0 °C		13100 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.3 MPa
@Strain 4.70 %,
Temperature 23.0 °C		13100 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.3 MPa
@Strain 4.80 %,
Temperature 23.0 °C		13100 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.5 MPa
@Strain 4.50 %,
Temperature 23.0 °C		13100 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.5 MPa
@Strain 4.60 %,
Temperature 23.0 °C		13100 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.5 MPa
@Strain 2.90 %,
Temperature 23.0 °C		13100 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 3.00 %,
Temperature 23.0 °C		13100 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 4.20 %,
Temperature 23.0 °C		13100 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 4.30 %,
Temperature 23.0 °C		13100 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 4.40 %,
Temperature 23.0 °C		13100 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.6 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13100 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.7 MPa
@Strain 3.90 %,
Temperature 23.0 °C		13200 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.7 MPa
@Strain 4.00 %,
Temperature 23.0 °C		13200 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.7 MPa
@Strain 4.10 %,
Temperature 23.0 °C		13200 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.8 MPa
@Strain 3.80 %,
Temperature 23.0 °C		13200 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.8 MPa
@Strain 3.10 %,
Temperature 23.0 °C		13200 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.8 MPa
@Strain 3.20 %,
Temperature 23.0 °C		13200 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 3.30 %,
Temperature 23.0 °C		13200 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 3.40 %,
Temperature 23.0 °C		13200 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 3.50 %,
Temperature 23.0 °C		13200 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 3.60 %,
Temperature 23.0 °C		13200 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		13200 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13200 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.73 MPa
@Strain 2.30 %,
Temperature 0.000 °C		13300 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 91.99 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13340 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.1 MPa
@Strain 2.40 %,
Temperature 0.000 °C		13500 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 93.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		13600 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.7 MPa
@Strain 1.90 %,
Temperature 0.000 °C		13600 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.2 MPa
@Strain 2.50 %,
Temperature 0.000 °C		13700 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.03 MPa
@Strain 2.60 %,
Temperature 0.000 °C		13780 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.87 MPa
@Strain 2.70 %,
Temperature 0.000 °C		13900 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 96.0 MPa
@Strain 1.80 %,
Temperature -40.0 °C		13900 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.12 MPa
@Strain 1.70 %,
Temperature -40.0 °C		13940 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.2 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14000 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.64 MPa
@Strain 2.80 %,
Temperature 0.000 °C		14020 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.38 MPa
@Strain 2.90 %,
Temperature 0.000 °C		14120 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.89 MPa
@Strain 3.00 %,
Temperature 0.000 °C		14200 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.35 MPa
@Strain 3.10 %,
Temperature 0.000 °C		14260 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.4 MPa
@Strain 1.90 %,
Temperature -40.0 °C		14300 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 98.6 MPa
@Strain 2.10 %,
Temperature 0.000 °C		14300 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.72 MPa
@Strain 3.20 %,
Temperature 0.000 °C		14320 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.97 MPa
@Strain 3.30 %,
Temperature 0.000 °C		14350 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.2 MPa
@Strain 3.40 %,
Temperature 0.000 °C		14400 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.25 MPa
@Strain 3.50 %,
Temperature 0.000 °C		14400 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.38 MPa
@Strain 3.60 %,
Temperature 0.000 °C		14410 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.43 MPa
@Strain 3.70 %,
Temperature 0.000 °C		14420 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.65 MPa
@Strain 3.80 %,
Temperature 0.000 °C		14450 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.79 MPa
@Strain 3.90 %,
Temperature 0.000 °C		14470 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.86 MPa
@Strain 4.00 %,
Temperature 0.000 °C		14480 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.9 MPa
@Strain 4.10 %,
Temperature 0.000 °C		14500 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 100.02 MPa
@Strain 1.80 %,
Temperature -40.0 °C		14507 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.3 MPa
@Strain 2.00 %,
Temperature -40.0 °C		14550 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 100.6 MPa
@Strain 2.20 %,
Temperature 0.000 °C		14590 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 102 MPa
@Strain 2.10 %,
Temperature -40.0 °C		14800 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.2 MPa
@Strain 2.30 %,
Temperature 0.000 °C		14820 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 103.36 MPa
@Strain 1.90 %,
Temperature -40.0 °C		14991 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.7 MPa
@Strain 2.40 %,
Temperature 0.000 °C		15040 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 103.8 MPa
@Strain 2.20 %,
Temperature -40.0 °C		15050 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.9 MPa
@Strain 2.50 %,
Temperature 0.000 °C		15210 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 105.7 MPa
@Strain 2.30 %,
Temperature -40.0 °C		15330 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.1 MPa
@Strain 2.60 %,
Temperature 0.000 °C		15390 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 106.41 MPa
@Strain 2.00 %,
Temperature -40.0 °C		15433 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.3 MPa
@Strain 2.40 %,
Temperature -40.0 °C		15560 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.3 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15560 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 108.2 MPa
@Strain 2.80 %,
Temperature 0.000 °C		15690 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 108.9 MPa
@Strain 2.50 %,
Temperature -40.0 °C		15790 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.1 MPa
@Strain 2.90 %,
Temperature 0.000 °C		15820 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 109.62 MPa
@Strain 2.10 %,
Temperature -40.0 °C		15899 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.9 MPa
@Strain 3.00 %,
Temperature 0.000 °C		15940 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 110.1 MPa
@Strain 2.60 %,
Temperature -40.0 °C		15970 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.3 MPa
@Strain 3.10 %,
Temperature 0.000 °C		16000 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 110.8 MPa
@Strain 3.20 %,
Temperature 0.000 °C		16070 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.1 MPa
@Strain 3.30 %,
Temperature 0.000 °C		16110 psi
@Strain 3.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.1 MPa
@Strain 2.70 %,
Temperature -40.0 °C		16110 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.4 MPa
@Strain 3.40 %,
Temperature 0.000 °C		16160 psi
@Strain 3.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.6 MPa
@Strain 3.50 %,
Temperature 0.000 °C		16190 psi
@Strain 3.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.9 MPa
@Strain 3.60 %,
Temperature 0.000 °C		16230 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.9 MPa
@Strain 2.80 %,
Temperature -40.0 °C		16230 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.1 MPa
@Strain 3.70 %,
Temperature 0.000 °C		16260 psi
@Strain 3.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.3 MPa
@Strain 3.80 %,
Temperature 0.000 °C		16290 psi
@Strain 3.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.37 MPa
@Strain 2.20 %,
Temperature -40.0 °C		16298 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 4.50 %,
Temperature 0.000 °C		16320 psi
@Strain 4.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 4.60 %,
Temperature 0.000 °C		16320 psi
@Strain 4.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 3.90 %,
Temperature 0.000 °C		16320 psi
@Strain 3.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 4.70 %,
Temperature 0.000 °C		16320 psi
@Strain 4.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 4.00 %,
Temperature 0.000 °C		16330 psi
@Strain 4.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 4.10 %,
Temperature 0.000 °C		16330 psi
@Strain 4.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 4.40 %,
Temperature 0.000 °C		16330 psi
@Strain 4.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.7 MPa
@Strain 2.90 %,
Temperature -40.0 °C		16350 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.7 MPa
@Strain 4.20 %,
Temperature 0.000 °C		16350 psi
@Strain 4.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.7 MPa
@Strain 4.30 %,
Temperature 0.000 °C		16350 psi
@Strain 4.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 113.3 MPa
@Strain 3.00 %,
Temperature -40.0 °C		16430 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114 MPa
@Strain 3.10 %,
Temperature -40.0 °C		16500 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.65 MPa
@Strain 3.20 %,
Temperature -40.0 °C		16629 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.9 MPa
@Strain 2.30 %,
Temperature -40.0 °C		16660 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.2 MPa
@Strain 3.30 %,
Temperature -40.0 °C		16710 psi
@Strain 3.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.8 MPa
@Strain 3.40 %,
Temperature -40.0 °C		16800 psi
@Strain 3.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.4 MPa
@Strain 3.50 %,
Temperature -40.0 °C		16880 psi
@Strain 3.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117 MPa
@Strain 3.60 %,
Temperature -40.0 °C		17000 psi
@Strain 3.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.07 MPa
@Strain 2.40 %,
Temperature -40.0 °C		16980 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.4 MPa
@Strain 3.70 %,
Temperature -40.0 °C		17030 psi
@Strain 3.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.8 MPa
@Strain 3.80 %,
Temperature -40.0 °C		17090 psi
@Strain 3.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.1 MPa
@Strain 3.90 %,
Temperature -40.0 °C		17130 psi
@Strain 3.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.3 MPa
@Strain 4.00 %,
Temperature -40.0 °C		17160 psi
@Strain 4.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.5 MPa
@Strain 4.10 %,
Temperature -40.0 °C		17190 psi
@Strain 4.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.7 MPa
@Strain 4.20 %,
Temperature -40.0 °C		17220 psi
@Strain 4.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.8 MPa
@Strain 4.30 %,
Temperature -40.0 °C		17230 psi
@Strain 4.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 118.9 MPa
@Strain 4.40 %,
Temperature -40.0 °C		17250 psi
@Strain 4.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119 MPa
@Strain 4.50 %,
Temperature -40.0 °C		17300 psi
@Strain 4.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.09 MPa
@Strain 2.50 %,
Temperature -40.0 °C		17273 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.1 MPa
@Strain 4.60 %,
Temperature -40.0 °C		17270 psi
@Strain 4.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.2 MPa
@Strain 4.70 %,
Temperature -40.0 °C		17290 psi
@Strain 4.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.3 MPa
@Strain 4.80 %,
Temperature -40.0 °C		17300 psi
@Strain 4.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.4 MPa
@Strain 4.90 %,
Temperature -40.0 °C		17320 psi
@Strain 4.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 121.15 MPa
@Strain 2.60 %,
Temperature -40.0 °C		17571 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 122.81 MPa
@Strain 2.70 %,
Temperature -40.0 °C		17812 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.42 MPa
@Strain 2.80 %,
Temperature -40.0 °C		18046 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.97 MPa
@Strain 2.90 %,
Temperature -40.0 °C		18270 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 127.53 MPa
@Strain 3.00 %,
Temperature -40.0 °C		18497 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 128.4 MPa
@Strain 3.10 %,
Temperature -40.0 °C		18620 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature -40.0 °C		3.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 4.0 %
@Temperature -40.0 °C		4.0 %
@Temperature -40.0 °F		50%RH; ASTM D638
 10 %
@Temperature 23.0 °C		10 %
@Temperature 73.4 °F		DAM; ISO 527
 15 %
@Temperature 23.0 °C		15 %
@Temperature 73.4 °F		DAM; ASTM D638
 35 %
@Temperature 23.0 °C		35 %
@Temperature 73.4 °F		50%RH; ISO 527
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50%RH; ASTM D638
 52 %
@Temperature 77.0 °C		52 %
@Temperature 171 °F		DAM; ASTM D638
 64 %
@Temperature 77.0 °C		64 %
@Temperature 171 °F		50%RH; ASTM D638
 64 %
@Temperature 121 °C		64 %
@Temperature 250 °F		DAM; ASTM D638
 71 %
@Temperature 121 °C		71 %
@Temperature 250 °F		50%RH; ASTM D638
Tensile Modulus  2.60 GPa
@Temperature 23.0 °C		377 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.90 GPa
@Temperature 23.0 °C		856 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.827 GPa
@Temperature 121 °C		120 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.862 GPa
@Temperature 121 °C		125 ksi
@Temperature 250 °F		DAM; ASTM D790
 1.172 GPa
@Temperature 77.0 °C		170.0 ksi
@Temperature 171 °F		50%RH; ASTM D790
 1.379 GPa
@Temperature 77.0 °C		200.0 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.896 GPa
@Temperature 23.0 °C		275.0 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.00 GPa
@Temperature 23.0 °C		290 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 5.40 GPa
@Temperature 23.0 °C		783 ksi
@Temperature 73.4 °F		DAM; ISO 178
 5.52 GPa
@Temperature 23.0 °C		801 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 6.378 GPa
@Temperature -40.0 °C		925.1 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
 6.55 GPa
@Temperature -40.0 °C		950 ksi
@Temperature -40.0 °F		DAM; ASTM D790
Shear Strength 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.430 J/cm
@Temperature -40.0 °C		0.806 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.640 J/cm
@Temperature -40.0 °C		1.20 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.700 J/cm
@Temperature 23.0 °C		1.31 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.23 J/cm
@Temperature 23.0 °C		2.30 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature -40.0 °C		2.38 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.00 kJ/m²
@Temperature -40.0 °C		2.38 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  100 kJ/m²
@Temperature -30.0 °C		47.6 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 100 kJ/m²
@Temperature -30.0 °C		47.6 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 150 kJ/m²
@Temperature 23.0 °C		71.4 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 >= 250 kJ/m²
@Temperature 23.0 °C		>= 119 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  8.50 J/cm²
@Temperature -30.0 °C		40.4 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 10.0 J/cm²
@Temperature -30.0 °C		47.6 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 20.0 J/cm²
@Temperature 23.0 °C		95.2 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.700 J/cm²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.20 J/cm²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+8 ohm-cm
@Temperature 23.0 °C		1.00e+8 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.8
@Frequency 1000 Hz,
Temperature 23.0 °C		3.8
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.9
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.1
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.1
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 4.2
@Frequency 100 Hz,
Temperature 23.0 °C		4.2
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 7.2
@Frequency 1000 Hz,
Temperature 23.0 °C		7.2
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Dielectric Strength  16.5 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		419 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		50%RH; Short Time; ASTM D149
 18.1 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		460 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
 24.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		610 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.010
@Frequency 1000 Hz,
Temperature 23.0 °C		0.010
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.010
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.010
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.010
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.010
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.070
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.070
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.16
@Frequency 1000 Hz,
Temperature 23.0 °C		0.16
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 65.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		36.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 65.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		36.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 98.0 µm/m-°C
@Temperature 55.0 - 160 °C		54.4 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 98.0 µm/m-°C
@Temperature 55.0 - 160 °C		54.4 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 258 °C496 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C419 °FDAM; ISO 75-1/-2
 230 °C446 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C194 °FDAM; ASTM D648
 100 °C212 °FDAM; ISO 75-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
Oxygen Index 26 %26 %DAM; ISO 4589-1/-2
 30 %30 %DAM; ASTM D2863
 
Processing PropertiesMetricEnglishComments
Melt Temperature 256 °C493 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesHeat Resistance, GoodDAM
 Impact Resistance, GoodDAM
 Warpage, LowDAM
FillerMineral fillerDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-IMD40<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Warp ResinsDAM
 Mineral Reinforced ResinsDAM
Resin IdentificationPA66-IMD40ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 GearsDAM
 Industrial ApplicationsDAM
 Parts, EngineeringDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45426.html

免责声明: 本文 DuPont Performance Polymers Minlon® 11C40 NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4