  4. DuPont Performance Polymers Minlon® 22C BK086 Nylon 66

DuPont Performance Polymers Minlon® 22C BK086 Nylon 66

DuPont Performance Polymers Minlon® 22C BK086 Nylon 66 物性表: DuPont Performance Polymers Minlon® 22C BK086 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® 22C BK086 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® 22C BK086 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 成型收缩率 [%]: 0.005
  • 缺口冲击强度: 0.43
  • 弯曲模量 [MPa]: 6.90
  • 热变形温度 [℃]: 255.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.45 g/cc1.45 g/ccDAM; ASTM D792
Density 1.45 g/cc0.0524 lb/in³DAM; ISO 1183
Filler Content 38 %38 %DAM
Linear Mold Shrinkage  0.0050 cm/cm
@Thickness 1.60 mm		0.0050 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0060 cm/cm
@Thickness 6.40 mm		0.0060 in/in
@Thickness 0.252 in		Flow; DAM
 0.0060 cm/cm
@Thickness 3.20 mm		0.0060 in/in
@Thickness 0.126 in		Flow; DAM
 0.0080 cm/cm
@Thickness 1.60 mm		0.0080 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.0080 cm/cm
@Thickness 3.20 mm		0.0080 in/in
@Thickness 0.126 in		Transverse; DAM
 0.010 cm/cm
@Thickness 6.40 mm		0.010 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0060 cm/cm
@Thickness 2.00 mm		0.0060 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  72.0 MPa
@Temperature 23.0 °C		10400 psi
@Temperature 73.4 °F		50%RH; ISO 527
 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength 116 MPa
@Temperature 23.0 °C		16800 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  1.90 MPa
@Strain 0.100 %,
Temperature 150 °C		276 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.00 MPa
@Strain 0.100 %,
Temperature 150 °C		290 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.20 MPa
@Strain 0.100 %,
Temperature 120 °C		319 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.44 MPa
@Strain 0.100 %,
Temperature 120 °C		354 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 100 °C		363 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.60 MPa
@Strain 0.100 %,
Temperature 80.0 °C		377 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.65 MPa
@Strain 0.100 %,
Temperature 100 °C		384 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.00 MPa
@Strain 0.100 %,
Temperature 80.0 °C		435 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.20 MPa
@Strain 0.100 %,
Temperature 60.0 °C		464 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.80 MPa
@Strain 0.200 %,
Temperature 150 °C		551 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.08 MPa
@Strain 0.200 %,
Temperature 150 °C		592 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.10 MPa
@Strain 0.100 %,
Temperature 60.0 °C		595 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 4.10 MPa
@Strain 0.100 %,
Temperature 23.0 °C		595 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 4.40 MPa
@Strain 0.200 %,
Temperature 120 °C		638 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.87 MPa
@Strain 0.200 %,
Temperature 120 °C		706 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.00 MPa
@Strain 0.200 %,
Temperature 100 °C		725 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.10 MPa
@Strain 0.100 %,
Temperature 23.0 °C		740 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.200 %,
Temperature 80.0 °C		754 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.28 MPa
@Strain 0.200 %,
Temperature 100 °C		766 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.40 MPa
@Strain 0.300 %,
Temperature 150 °C		783 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.02 MPa
@Strain 0.300 %,
Temperature 150 °C		873 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.04 MPa
@Strain 0.200 %,
Temperature 80.0 °C		876 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.418 MPa
@Strain 0.200 %,
Temperature 60.0 °C		930.9 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.45 MPa
@Strain 0.300 %,
Temperature 120 °C		935 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.50 MPa
@Strain 0.400 %,
Temperature 150 °C		943 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.10 MPa
@Strain 0.300 %,
Temperature 120 °C		1030 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.20 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1040 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 7.50 MPa
@Strain 0.300 %,
Temperature 100 °C		1090 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.50 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1090 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.70 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1120 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 7.71 MPa
@Strain 0.300 %,
Temperature 100 °C		1120 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.85 MPa
@Strain 0.400 %,
Temperature 120 °C		1140 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.86 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1140 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 7.90 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1150 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 8.04 MPa
@Strain 0.400 %,
Temperature 150 °C		1170 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.142 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1181 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.142 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1181 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 8.80 MPa
@Strain 0.500 %,
Temperature 150 °C		1280 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.91 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1290 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.96 MPa
@Strain 0.400 %,
Temperature 120 °C		1300 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.20 MPa
@Strain 0.400 %,
Temperature 100 °C		1330 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.40 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1360 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.45 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1370 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.73 MPa
@Strain 0.400 %,
Temperature 100 °C		1410 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.91 MPa
@Strain 0.500 %,
Temperature 150 °C		1440 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.0 MPa
@Strain 0.500 %,
Temperature 120 °C		1450 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 0.600 %,
Temperature 150 °C		1510 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1510 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.500 %,
Temperature 100 °C		1620 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.26 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1633 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.47 MPa
@Strain 0.500 %,
Temperature 120 °C		1664 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 0.700 %,
Temperature 150 °C		1700 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.72 MPa
@Strain 0.600 %,
Temperature 150 °C		1700 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.8 MPa
@Strain 0.600 %,
Temperature 120 °C		1710 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.974 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1736.7 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.215 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1771.6 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 12.215 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1771.6 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 12.4 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1800 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.44 MPa
@Strain 0.500 %,
Temperature 100 °C		1804 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.2 MPa
@Strain 0.600 %,
Temperature 100 °C		1910 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.2 MPa
@Strain 0.800 %,
Temperature 150 °C		1910 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.44 MPa
@Strain 0.600 %,
Temperature 120 °C		1949 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.5 MPa
@Strain 0.700 %,
Temperature 120 °C		1960 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.56 MPa
@Strain 0.700 %,
Temperature 150 °C		1967 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.43 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2093 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 14.59 MPa
@Strain 0.600 %,
Temperature 100 °C		2116 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.6 MPa
@Strain 0.900 %,
Temperature 150 °C		2120 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.7 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2130 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.01 MPa
@Strain 0.500 %,
Temperature 80.0 °C		2177 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.05 MPa
@Strain 0.800 %,
Temperature 150 °C		2183 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.25 MPa
@Strain 0.800 %,
Temperature 120 °C		2212 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.3 MPa
@Strain 0.700 %,
Temperature 100 °C		2220 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.43 MPa
@Strain 0.700 %,
Temperature 120 °C		2238 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.438 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2239.1 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2280 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.71 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2279 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 15.878 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2302.9 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 15.878 MPa
@Strain 0.400 %,
Temperature 60.0 °C		2302.9 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 15.9 MPa
@Strain 1.00 %,
Temperature 150 °C		2310 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.9 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2310 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 16.45 MPa
@Strain 0.900 %,
Temperature 150 °C		2386 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.74 MPa
@Strain 0.700 %,
Temperature 100 °C		2428 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.8 MPa
@Strain 0.900 %,
Temperature 120 °C		2440 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.0 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2470 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.17 MPa
@Strain 0.800 %,
Temperature 120 °C		2490 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.2 MPa
@Strain 1.10 %,
Temperature 150 °C		2490 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.3 MPa
@Strain 0.800 %,
Temperature 100 °C		2510 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.94 MPa
@Strain 1.00 %,
Temperature 150 °C		2602 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.97 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2606 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.2 MPa
@Strain 1.00 %,
Temperature 120 °C		2640 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 1.20 %,
Temperature 150 °C		2650 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.382 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2666.1 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.63 MPa
@Strain 0.800 %,
Temperature 100 °C		2702 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.65 MPa
@Strain 0.900 %,
Temperature 120 °C		2705 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.0 MPa
@Strain 0.900 %,
Temperature 100 °C		2760 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2760 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.27 MPa
@Strain 1.10 %,
Temperature 150 °C		2795 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 1.30 %,
Temperature 150 °C		2800 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.377 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2810.4 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.377 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2810.4 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 19.55 MPa
@Strain 1.10 %,
Temperature 120 °C		2835 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.8 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2870 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.23 MPa
@Strain 0.900 %,
Temperature 100 °C		2934 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.25 MPa
@Strain 1.00 %,
Temperature 120 °C		2937 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.3 MPa
@Strain 1.40 %,
Temperature 150 °C		2940 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.5 MPa
@Strain 1.00 %,
Temperature 100 °C		2970 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.64 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2994 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.66 MPa
@Strain 1.20 %,
Temperature 150 °C		2996 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.85 MPa
@Strain 1.20 %,
Temperature 120 °C		3024 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.032 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3050.4 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.2 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3070 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.4 MPa
@Strain 1.50 %,
Temperature 150 °C		3100 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.43 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3108 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 21.8 MPa
@Strain 1.10 %,
Temperature 120 °C		3160 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.9 MPa
@Strain 1.10 %,
Temperature 100 °C		3180 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.98 MPa
@Strain 1.00 %,
Temperature 100 °C		3188 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.04 MPa
@Strain 1.30 %,
Temperature 150 °C		3197 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.1 MPa
@Strain 1.30 %,
Temperature 120 °C		3210 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.465 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3258.3 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 22.5 MPa
@Strain 1.60 %,
Temperature 150 °C		3260 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.763 MPa
@Strain 0.600 %,
Temperature 60.0 °C		3301.5 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.763 MPa
@Strain 0.600 %,
Temperature 23.0 °C		3301.5 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 22.93 MPa
@Strain 0.800 %,
Temperature 80.0 °C		3326 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.09 MPa
@Strain 1.40 %,
Temperature 150 °C		3349 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.1 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3350 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.19 MPa
@Strain 1.20 %,
Temperature 120 °C		3363 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.35 MPa
@Strain 1.40 %,
Temperature 120 °C		3387 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.4 MPa
@Strain 1.20 %,
Temperature 100 °C		3390 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.4 MPa
@Strain 1.70 %,
Temperature 150 °C		3390 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.442 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3400.0 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.65 MPa
@Strain 1.10 %,
Temperature 100 °C		3430 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.8 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3450 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 23.91 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3468 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 24.25 MPa
@Strain 1.50 %,
Temperature 150 °C		3517 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.4 MPa
@Strain 1.80 %,
Temperature 150 °C		3540 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.5 MPa
@Strain 1.50 %,
Temperature 120 °C		3550 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.66 MPa
@Strain 1.30 %,
Temperature 120 °C		3577 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.8 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3600 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.9 MPa
@Strain 1.30 %,
Temperature 100 °C		3610 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.17 MPa
@Strain 1.20 %,
Temperature 100 °C		3651 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3650 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 1.90 %,
Temperature 150 °C		3650 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.22 MPa
@Strain 1.60 %,
Temperature 150 °C		3658 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.65 MPa
@Strain 1.60 %,
Temperature 120 °C		3720 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.79 MPa
@Strain 0.900 %,
Temperature 60.0 °C		3741 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.8 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3740 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.898 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3756.2 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.898 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3756.2 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.0 MPa
@Strain 2.00 %,
Temperature 150 °C		3770 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.08 MPa
@Strain 1.40 %,
Temperature 120 °C		3783 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.27 MPa
@Strain 1.70 %,
Temperature 150 °C		3810 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.4 MPa
@Strain 1.40 %,
Temperature 100 °C		3830 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 2.10 %,
Temperature 150 °C		3870 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.75 MPa
@Strain 1.70 %,
Temperature 120 °C		3880 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.76 MPa
@Strain 1.30 %,
Temperature 100 °C		3881 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.8 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3890 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.22 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3948 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.23 MPa
@Strain 1.80 %,
Temperature 150 °C		3949 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.32 MPa
@Strain 1.50 %,
Temperature 120 °C		3962 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.5 MPa
@Strain 2.20 %,
Temperature 150 °C		3990 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.6 MPa
@Strain 1.50 %,
Temperature 100 °C		4000 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 1.80 %,
Temperature 120 °C		4030 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.978 MPa
@Strain 1.00 %,
Temperature 60.0 °C		4057.9 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.17 MPa
@Strain 1.90 %,
Temperature 150 °C		4086 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.3 MPa
@Strain 2.30 %,
Temperature 150 °C		4100 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.3 MPa
@Strain 1.40 %,
Temperature 100 °C		4100 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.3 MPa
@Strain 0.400 %,
Temperature 0.000 °C		4100 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.5 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4130 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.54 MPa
@Strain 1.60 %,
Temperature 120 °C		4139 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.75 MPa
@Strain 1.90 %,
Temperature 120 °C		4170 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.8 MPa
@Strain 1.60 %,
Temperature 100 °C		4180 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.896 MPa
@Strain 0.800 %,
Temperature 60.0 °C		4191.0 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.896 MPa
@Strain 0.800 %,
Temperature 23.0 °C		4191.0 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 2.40 %,
Temperature 150 °C		4190 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.98 MPa
@Strain 2.00 %,
Temperature 150 °C		4203 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.039 MPa
@Strain 0.400 %,
Temperature 0.000 °C		4211.8 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 29.14 MPa
@Strain 1.10 %,
Temperature 80.0 °C		4226 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.4 MPa
@Strain 2.50 %,
Temperature 150 °C		4260 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.65 MPa
@Strain 2.00 %,
Temperature 120 °C		4300 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.65 MPa
@Strain 1.50 %,
Temperature 100 °C		4300 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 1.70 %,
Temperature 120 °C		4310 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.89 MPa
@Strain 2.10 %,
Temperature 150 °C		4335 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.9 MPa
@Strain 2.60 %,
Temperature 150 °C		4340 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.1 MPa
@Strain 1.70 %,
Temperature 100 °C		4370 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.181 MPa
@Strain 1.10 %,
Temperature 60.0 °C		4377.4 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.3 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4390 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4420 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.55 MPa
@Strain 2.10 %,
Temperature 120 °C		4431 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.6 MPa
@Strain 2.70 %,
Temperature 150 °C		4440 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.74 MPa
@Strain 2.20 %,
Temperature 150 °C		4458 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.8 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4470 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 30.86 MPa
@Strain 1.80 %,
Temperature 120 °C		4476 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.97 MPa
@Strain 1.60 %,
Temperature 100 °C		4492 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.1 MPa
@Strain 2.80 %,
Temperature 150 °C		4510 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.14 MPa
@Strain 1.20 %,
Temperature 80.0 °C		4516 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.2 MPa
@Strain 1.80 %,
Temperature 100 °C		4530 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.45 MPa
@Strain 2.20 %,
Temperature 120 °C		4561 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.5 MPa
@Strain 2.90 %,
Temperature 150 °C		4570 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.59 MPa
@Strain 2.30 %,
Temperature 150 °C		4582 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.68 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4595 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 31.731 MPa
@Strain 0.900 %,
Temperature 60.0 °C		4602.2 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.731 MPa
@Strain 0.900 %,
Temperature 23.0 °C		4602.2 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.89 MPa
@Strain 1.90 %,
Temperature 120 °C		4625 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.9 MPa
@Strain 3.00 %,
Temperature 150 °C		4630 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.9 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4630 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.2 MPa
@Strain 2.30 %,
Temperature 120 °C		4670 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.23 MPa
@Strain 1.70 %,
Temperature 100 °C		4675 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.27 MPa
@Strain 2.40 %,
Temperature 150 °C		4680 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 1.90 %,
Temperature 100 °C		4680 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.31 MPa
@Strain 1.20 %,
Temperature 60.0 °C		4686 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 3.10 %,
Temperature 150 °C		4700 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.7 MPa
@Strain 3.20 %,
Temperature 150 °C		4740 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.9 MPa
@Strain 2.40 %,
Temperature 120 °C		4770 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.91 MPa
@Strain 2.00 %,
Temperature 120 °C		4773 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.95 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4779 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.02 MPa
@Strain 2.50 %,
Temperature 150 °C		4789 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.1 MPa
@Strain 3.30 %,
Temperature 150 °C		4800 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 2.00 %,
Temperature 100 °C		4830 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.4 MPa
@Strain 3.40 %,
Temperature 150 °C		4840 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.4 MPa
@Strain 1.60 %,
Temperature 80.0 °C		4840 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.49 MPa
@Strain 1.80 %,
Temperature 100 °C		4857 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.5 MPa
@Strain 2.50 %,
Temperature 120 °C		4860 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.51 MPa
@Strain 2.60 %,
Temperature 150 °C		4860 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.7 MPa
@Strain 3.50 %,
Temperature 150 °C		4890 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.93 MPa
@Strain 2.10 %,
Temperature 120 °C		4921 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.0 MPa
@Strain 3.60 %,
Temperature 150 °C		4930 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.1 MPa
@Strain 2.60 %,
Temperature 120 °C		4950 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.16 MPa
@Strain 2.70 %,
Temperature 150 °C		4954 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.2 MPa
@Strain 1.30 %,
Temperature 60.0 °C		4960 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.3 MPa
@Strain 3.70 %,
Temperature 150 °C		4970 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.322 MPa
@Strain 1.00 %,
Temperature 60.0 °C		4978.0 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.322 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4978.0 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 34.4 MPa
@Strain 2.10 %,
Temperature 100 °C		4990 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.45 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4997 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.6 MPa
@Strain 1.90 %,
Temperature 100 °C		5020 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.6 MPa
@Strain 3.80 %,
Temperature 150 °C		5020 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.66 MPa
@Strain 2.80 %,
Temperature 150 °C		5027 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.75 MPa
@Strain 2.70 %,
Temperature 120 °C		5040 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.78 MPa
@Strain 2.20 %,
Temperature 120 °C		5044 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.8 MPa
@Strain 3.90 %,
Temperature 150 °C		5050 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.81 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5049 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.9 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5060 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.9 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5060 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.1 MPa
@Strain 4.00 %,
Temperature 150 °C		5090 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.22 MPa
@Strain 2.90 %,
Temperature 150 °C		5108 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.25 MPa
@Strain 2.80 %,
Temperature 120 °C		5113 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.3 MPa
@Strain 4.10 %,
Temperature 150 °C		5120 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 2.20 %,
Temperature 100 °C		5130 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 4.20 %,
Temperature 150 °C		5160 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.67 MPa
@Strain 3.00 %,
Temperature 150 °C		5174 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.7 MPa
@Strain 2.90 %,
Temperature 120 °C		5180 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.71 MPa
@Strain 2.00 %,
Temperature 100 °C		5179 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.73 MPa
@Strain 2.30 %,
Temperature 120 °C		5182 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.8 MPa
@Strain 4.30 %,
Temperature 150 °C		5190 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.0 MPa
@Strain 4.40 %,
Temperature 150 °C		5220 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.02 MPa
@Strain 3.10 %,
Temperature 150 °C		5224 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.073 MPa
@Strain 1.40 %,
Temperature 60.0 °C		5232.0 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.08 MPa
@Strain 1.50 %,
Temperature 80.0 °C		5233 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.1 MPa
@Strain 2.30 %,
Temperature 100 °C		5240 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.15 MPa
@Strain 3.00 %,
Temperature 120 °C		5243 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 4.50 %,
Temperature 150 °C		5250 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 4.60 %,
Temperature 150 °C		5260 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5260 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.45 MPa
@Strain 3.20 %,
Temperature 150 °C		5287 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.5 MPa
@Strain 4.70 %,
Temperature 150 °C		5290 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.57 MPa
@Strain 2.40 %,
Temperature 120 °C		5304 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.6 MPa
@Strain 3.10 %,
Temperature 120 °C		5310 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.7 MPa
@Strain 4.80 %,
Temperature 150 °C		5320 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.7 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5320 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 4.90 %,
Temperature 150 °C		5340 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.82 MPa
@Strain 2.10 %,
Temperature 100 °C		5340 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.9 MPa
@Strain 2.40 %,
Temperature 100 °C		5350 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.91 MPa
@Strain 3.30 %,
Temperature 150 °C		5353 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.944 MPa
@Strain 1.10 %,
Temperature 60.0 °C		5358.3 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.944 MPa
@Strain 1.10 %,
Temperature 23.0 °C		5358.3 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 36.95 MPa
@Strain 3.20 %,
Temperature 120 °C		5359 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 5.00 %,
Temperature 150 °C		5370 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.19 MPa
@Strain 3.40 %,
Temperature 150 °C		5394 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.27 MPa
@Strain 2.50 %,
Temperature 120 °C		5406 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 3.30 %,
Temperature 120 °C		5410 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.52 MPa
@Strain 3.50 %,
Temperature 150 °C		5442 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.6 MPa
@Strain 5.50 %,
Temperature 150 °C		5450 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 3.40 %,
Temperature 120 °C		5450 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 2.50 %,
Temperature 100 °C		5450 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 1.60 %,
Temperature 80.0 °C		5450 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.74 MPa
@Strain 2.20 %,
Temperature 100 °C		5474 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.8 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5480 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.878 MPa
@Strain 1.50 %,
Temperature 60.0 °C		5493.7 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.89 MPa
@Strain 3.60 %,
Temperature 150 °C		5495 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.9 MPa
@Strain 3.50 %,
Temperature 120 °C		5500 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.95 MPa
@Strain 2.60 %,
Temperature 120 °C		5504 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.18 MPa
@Strain 3.70 %,
Temperature 150 °C		5538 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.2 MPa
@Strain 6.00 %,
Temperature 150 °C		5540 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.2 MPa
@Strain 3.60 %,
Temperature 120 °C		5540 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 2.60 %,
Temperature 100 °C		5550 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.37 MPa
@Strain 3.80 %,
Temperature 150 °C		5565 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.55 MPa
@Strain 3.70 %,
Temperature 120 °C		5591 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.62 MPa
@Strain 2.70 %,
Temperature 120 °C		5601 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.7 MPa
@Strain 6.50 %,
Temperature 150 °C		5610 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.72 MPa
@Strain 3.90 %,
Temperature 150 °C		5616 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.77 MPa
@Strain 2.30 %,
Temperature 100 °C		5623 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.8 MPa
@Strain 3.80 %,
Temperature 120 °C		5630 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.9 MPa
@Strain 2.70 %,
Temperature 100 °C		5640 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.0 MPa
@Strain 3.90 %,
Temperature 120 °C		5660 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.0 MPa
@Strain 7.00 %,
Temperature 150 °C		5660 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.04 MPa
@Strain 4.00 %,
Temperature 150 °C		5662 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.04 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5662 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5670 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.17 MPa
@Strain 4.10 %,
Temperature 150 °C		5681 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.2 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5690 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5690 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 39.22 MPa
@Strain 2.80 %,
Temperature 120 °C		5688 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.35 MPa
@Strain 4.00 %,
Temperature 120 °C		5707 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.386 MPa
@Strain 1.20 %,
Temperature 60.0 °C		5712.5 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.386 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5712.5 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 39.4 MPa
@Strain 2.80 %,
Temperature 100 °C		5710 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.4 MPa
@Strain 7.50 %,
Temperature 150 °C		5710 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.42 MPa
@Strain 4.20 %,
Temperature 150 °C		5717 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.5 MPa
@Strain 4.10 %,
Temperature 120 °C		5730 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 8.00 %,
Temperature 150 °C		5740 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 1.60 %,
Temperature 60.0 °C		5740 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.69 MPa
@Strain 2.40 %,
Temperature 100 °C		5757 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.73 MPa
@Strain 4.30 %,
Temperature 150 °C		5762 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.75 MPa
@Strain 4.20 %,
Temperature 120 °C		5765 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.78 MPa
@Strain 2.90 %,
Temperature 120 °C		5770 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 8.50 %,
Temperature 150 °C		5770 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.81 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5774 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 39.87 MPa
@Strain 4.40 %,
Temperature 150 °C		5783 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.9 MPa
@Strain 9.00 %,
Temperature 150 °C		5790 psi
@Strain 9.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 2.90 %,
Temperature 100 °C		5790 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.95 MPa
@Strain 4.30 %,
Temperature 120 °C		5794 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.97 MPa
@Strain 4.50 %,
Temperature 150 °C		5797 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.1 MPa
@Strain 9.50 %,
Temperature 150 °C		5820 psi
@Strain 9.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.1 MPa
@Strain 10.0 %,
Temperature 150 °C		5820 psi
@Strain 10.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.15 MPa
@Strain 4.40 %,
Temperature 120 °C		5823 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.18 MPa
@Strain 3.00 %,
Temperature 120 °C		5828 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.2 MPa
@Strain 11.0 %,
Temperature 150 °C		5830 psi
@Strain 11.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.21 MPa
@Strain 4.60 %,
Temperature 150 °C		5832 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.3 MPa
@Strain 4.50 %,
Temperature 120 °C		5850 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 12.0 %,
Temperature 150 °C		5850 psi
@Strain 12.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.36 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5854 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.4 MPa
@Strain 3.00 %,
Temperature 100 °C		5860 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.42 MPa
@Strain 4.70 %,
Temperature 150 °C		5862 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.44 MPa
@Strain 2.50 %,
Temperature 100 °C		5865 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.5 MPa
@Strain 2.10 %,
Temperature 80.0 °C		5870 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.5 MPa
@Strain 4.60 %,
Temperature 120 °C		5870 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.61 MPa
@Strain 4.80 %,
Temperature 150 °C		5890 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.7 MPa
@Strain 4.70 %,
Temperature 120 °C		5900 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.7 MPa
@Strain 3.10 %,
Temperature 120 °C		5900 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.8 MPa
@Strain 3.10 %,
Temperature 100 °C		5920 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 4.90 %,
Temperature 150 °C		5920 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.85 MPa
@Strain 5.00 %,
Temperature 150 °C		5925 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.9 MPa
@Strain 4.80 %,
Temperature 120 °C		5930 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 4.90 %,
Temperature 120 °C		5950 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.06 MPa
@Strain 3.20 %,
Temperature 120 °C		5955 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.15 MPa
@Strain 5.00 %,
Temperature 120 °C		5968 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.19 MPa
@Strain 2.60 %,
Temperature 100 °C		5974 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.22 MPa
@Strain 0.600 %,
Temperature 0.000 °C		5978 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 41.245 MPa
@Strain 1.70 %,
Temperature 60.0 °C		5982.1 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.38 MPa
@Strain 5.50 %,
Temperature 150 °C		6002 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.45 MPa
@Strain 3.30 %,
Temperature 120 °C		6012 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.5 MPa
@Strain 3.30 %,
Temperature 100 °C		6020 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.524 MPa
@Strain 1.30 %,
Temperature 60.0 °C		6022.6 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.524 MPa
@Strain 1.30 %,
Temperature 23.0 °C		6022.6 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 41.56 MPa
@Strain 1.90 %,
Temperature 80.0 °C		6028 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.6 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6030 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.75 MPa
@Strain 5.50 %,
Temperature 120 °C		6055 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.77 MPa
@Strain 3.40 %,
Temperature 120 °C		6058 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.8 MPa
@Strain 3.40 %,
Temperature 100 °C		6060 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.91 MPa
@Strain 2.70 %,
Temperature 100 °C		6079 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.1 MPa
@Strain 3.50 %,
Temperature 100 °C		6110 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.12 MPa
@Strain 6.00 %,
Temperature 150 °C		6109 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.16 MPa
@Strain 3.50 %,
Temperature 120 °C		6115 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.35 MPa
@Strain 6.00 %,
Temperature 120 °C		6142 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.4 MPa
@Strain 3.60 %,
Temperature 100 °C		6150 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.51 MPa
@Strain 3.60 %,
Temperature 120 °C		6166 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.52 MPa
@Strain 6.50 %,
Temperature 150 °C		6167 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.56 MPa
@Strain 2.80 %,
Temperature 100 °C		6173 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.748 MPa
@Strain 1.80 %,
Temperature 60.0 °C		6200.1 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.79 MPa
@Strain 3.70 %,
Temperature 120 °C		6206 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.8 MPa
@Strain 3.70 %,
Temperature 100 °C		6210 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.8 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6210 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.85 MPa
@Strain 6.50 %,
Temperature 120 °C		6215 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 0.900 %,
Temperature 23.0 °C		6220 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.93 MPa
@Strain 7.00 %,
Temperature 150 °C		6226 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.95 MPa
@Strain 2.00 %,
Temperature 80.0 °C		6229 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 3.80 %,
Temperature 100 °C		6240 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.06 MPa
@Strain 3.80 %,
Temperature 120 °C		6245 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.15 MPa
@Strain 7.00 %,
Temperature 120 °C		6258 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.17 MPa
@Strain 2.90 %,
Temperature 100 °C		6261 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.2 MPa
@Strain 3.90 %,
Temperature 100 °C		6270 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.23 MPa
@Strain 7.50 %,
Temperature 150 °C		6270 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.33 MPa
@Strain 3.90 %,
Temperature 120 °C		6284 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.46 MPa
@Strain 8.00 %,
Temperature 150 °C		6303 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.5 MPa
@Strain 7.50 %,
Temperature 120 °C		6310 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.55 MPa
@Strain 4.00 %,
Temperature 120 °C		6316 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.564 MPa
@Strain 0.600 %,
Temperature 0.000 °C		6318.4 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.596 MPa
@Strain 1.40 %,
Temperature 23.0 °C		6323.1 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.596 MPa
@Strain 1.40 %,
Temperature 60.0 °C		6323.1 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.6 MPa
@Strain 3.00 %,
Temperature 100 °C		6320 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.6 MPa
@Strain 4.00 %,
Temperature 100 °C		6320 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.67 MPa
@Strain 8.50 %,
Temperature 150 °C		6334 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.7 MPa
@Strain 4.10 %,
Temperature 100 °C		6340 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.7 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6340 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.75 MPa
@Strain 8.00 %,
Temperature 120 °C		6345 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.76 MPa
@Strain 4.10 %,
Temperature 120 °C		6347 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.85 MPa
@Strain 9.00 %,
Temperature 150 °C		6360 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 4.20 %,
Temperature 100 °C		6370 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.95 MPa
@Strain 8.50 %,
Temperature 120 °C		6374 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.0 MPa
@Strain 9.50 %,
Temperature 150 °C		6380 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.0 MPa
@Strain 4.20 %,
Temperature 120 °C		6380 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.05 MPa
@Strain 9.00 %,
Temperature 120 °C		6389 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 10.0 %,
Temperature 150 °C		6400 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 4.30 %,
Temperature 100 °C		6400 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.12 MPa
@Strain 11.0 %,
Temperature 150 °C		6399 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.16 MPa
@Strain 3.10 %,
Temperature 100 °C		6405 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.17 MPa
@Strain 2.10 %,
Temperature 80.0 °C		6406 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.2 MPa
@Strain 9.50 %,
Temperature 120 °C		6410 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.24 MPa
@Strain 4.30 %,
Temperature 120 °C		6416 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.245 MPa
@Strain 1.90 %,
Temperature 60.0 °C		6417.2 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.25 MPa
@Strain 10.0 %,
Temperature 120 °C		6418 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 11.0 %,
Temperature 120 °C		6430 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 4.40 %,
Temperature 100 °C		6430 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.35 MPa
@Strain 12.0 %,
Temperature 120 °C		6432 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 4.50 %,
Temperature 100 °C		6440 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.45 MPa
@Strain 4.40 %,
Temperature 120 °C		6447 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.5 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6450 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.56 MPa
@Strain 3.20 %,
Temperature 100 °C		6463 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.62 MPa
@Strain 4.50 %,
Temperature 120 °C		6472 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.7 MPa
@Strain 4.60 %,
Temperature 100 °C		6480 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.76 MPa
@Strain 4.60 %,
Temperature 120 °C		6492 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 4.70 %,
Temperature 100 °C		6510 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.945 MPa
@Strain 1.50 %,
Temperature 60.0 °C		6518.7 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.945 MPa
@Strain 1.50 %,
Temperature 23.0 °C		6518.7 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.97 MPa
@Strain 4.70 %,
Temperature 120 °C		6522 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.98 MPa
@Strain 3.30 %,
Temperature 100 °C		6524 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 4.80 %,
Temperature 100 °C		6540 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.16 MPa
@Strain 4.80 %,
Temperature 120 °C		6550 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.2 MPa
@Strain 4.90 %,
Temperature 100 °C		6560 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.28 MPa
@Strain 4.90 %,
Temperature 120 °C		6567 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 5.00 %,
Temperature 100 °C		6570 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.33 MPa
@Strain 3.40 %,
Temperature 100 °C		6575 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6580 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.44 MPa
@Strain 5.00 %,
Temperature 120 °C		6591 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.46 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6593 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.647 MPa
@Strain 2.00 %,
Temperature 60.0 °C		6620.5 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.75 MPa
@Strain 3.50 %,
Temperature 100 °C		6635 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.9 MPa
@Strain 5.50 %,
Temperature 100 °C		6660 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.99 MPa
@Strain 5.50 %,
Temperature 120 °C		6670 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6690 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.13 MPa
@Strain 3.60 %,
Temperature 100 °C		6691 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.44 MPa
@Strain 3.70 %,
Temperature 100 °C		6736 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.5 MPa
@Strain 6.00 %,
Temperature 100 °C		6740 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.58 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6756 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.6 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6760 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.68 MPa
@Strain 6.00 %,
Temperature 120 °C		6770 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.7 MPa
@Strain 2.80 %,
Temperature 80.0 °C		6770 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.73 MPa
@Strain 3.80 %,
Temperature 100 °C		6778 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.833 MPa
@Strain 2.10 %,
Temperature 60.0 °C		6792.6 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 6.50 %,
Temperature 100 °C		6820 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 0.600 %,
Temperature -40.0 °C		6820 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.02 MPa
@Strain 3.90 %,
Temperature 100 °C		6820 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.12 MPa
@Strain 6.50 %,
Temperature 120 °C		6834 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.14 MPa
@Strain 0.600 %,
Temperature -40.0 °C		6837 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 47.179 MPa
@Strain 1.60 %,
Temperature 60.0 °C		6842.7 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.179 MPa
@Strain 1.60 %,
Temperature 23.0 °C		6842.7 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 2.90 %,
Temperature 80.0 °C		6850 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.26 MPa
@Strain 4.00 %,
Temperature 100 °C		6854 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.3 MPa
@Strain 7.00 %,
Temperature 100 °C		6860 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.45 MPa
@Strain 0.700 %,
Temperature 0.000 °C		6882 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 47.48 MPa
@Strain 4.10 %,
Temperature 100 °C		6886 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.53 MPa
@Strain 7.00 %,
Temperature 120 °C		6894 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.57 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6899 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.6 MPa
@Strain 7.50 %,
Temperature 100 °C		6900 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 3.00 %,
Temperature 80.0 °C		6920 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.74 MPa
@Strain 4.20 %,
Temperature 100 °C		6924 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.825 MPa
@Strain 2.20 %,
Temperature 60.0 °C		6936.4 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.87 MPa
@Strain 7.50 %,
Temperature 120 °C		6943 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.9 MPa
@Strain 8.00 %,
Temperature 100 °C		6950 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.01 MPa
@Strain 4.30 %,
Temperature 100 °C		6963 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.1 MPa
@Strain 8.00 %,
Temperature 120 °C		6980 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.1 MPa
@Strain 3.10 %,
Temperature 80.0 °C		6980 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.2 MPa
@Strain 9.00 %,
Temperature 100 °C		6990 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.23 MPa
@Strain 4.40 %,
Temperature 100 °C		6995 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.3 MPa
@Strain 9.50 %,
Temperature 100 °C		7010 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 10.0 %,
Temperature 100 °C		7020 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 11.0 %,
Temperature 100 °C		7020 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 12.0 %,
Temperature 100 °C		7020 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.42 MPa
@Strain 4.50 %,
Temperature 100 °C		7023 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.43 MPa
@Strain 2.50 %,
Temperature 80.0 °C		7024 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.5 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7030 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.58 MPa
@Strain 4.60 %,
Temperature 100 °C		7046 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.771 MPa
@Strain 2.30 %,
Temperature 60.0 °C		7073.6 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.8 MPa
@Strain 4.70 %,
Temperature 100 °C		7080 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.9 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7090 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.938 MPa
@Strain 1.70 %,
Temperature 60.0 °C		7097.9 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.938 MPa
@Strain 1.70 %,
Temperature 23.0 °C		7097.9 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.0 MPa
@Strain 4.80 %,
Temperature 100 °C		7110 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.14 MPa
@Strain 4.90 %,
Temperature 100 °C		7127 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7140 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.31 MPa
@Strain 5.00 %,
Temperature 100 °C		7152 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.35 MPa
@Strain 2.60 %,
Temperature 80.0 °C		7158 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.5 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7180 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.58 MPa
@Strain 2.40 %,
Temperature 60.0 °C		7191 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 3.60 %,
Temperature 80.0 °C		7210 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.891 MPa
@Strain 0.700 %,
Temperature 0.000 °C		7236.1 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 49.9 MPa
@Strain 1.10 %,
Temperature 23.0 °C		7240 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.9 MPa
@Strain 5.50 %,
Temperature 100 °C		7240 psi
@Strain 5.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 3.70 %,
Temperature 80.0 °C		7250 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.12 MPa
@Strain 2.70 %,
Temperature 80.0 °C		7269 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 3.80 %,
Temperature 80.0 °C		7280 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.239 MPa
@Strain 2.50 %,
Temperature 60.0 °C		7286.6 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.4 MPa
@Strain 3.90 %,
Temperature 80.0 °C		7310 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.66 MPa
@Strain 6.00 %,
Temperature 100 °C		7348 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.698 MPa
@Strain 1.80 %,
Temperature 23.0 °C		7353.1 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 50.698 MPa
@Strain 1.80 %,
Temperature 60.0 °C		7353.1 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 4.00 %,
Temperature 80.0 °C		7350 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.74 MPa
@Strain 2.80 %,
Temperature 80.0 °C		7359 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.785 MPa
@Strain 2.60 %,
Temperature 60.0 °C		7365.8 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 4.10 %,
Temperature 80.0 °C		7380 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 4.20 %,
Temperature 80.0 °C		7410 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.14 MPa
@Strain 6.50 %,
Temperature 100 °C		7417 psi
@Strain 6.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.2 MPa
@Strain 4.30 %,
Temperature 80.0 °C		7430 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.307 MPa
@Strain 2.70 %,
Temperature 60.0 °C		7441.5 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.4 MPa
@Strain 4.40 %,
Temperature 80.0 °C		7450 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.52 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7472 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.57 MPa
@Strain 7.00 %,
Temperature 100 °C		7480 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 4.50 %,
Temperature 80.0 °C		7480 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 4.60 %,
Temperature 80.0 °C		7500 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.755 MPa
@Strain 2.80 %,
Temperature 60.0 °C		7506.4 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 4.70 %,
Temperature 80.0 °C		7530 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.95 MPa
@Strain 7.50 %,
Temperature 100 °C		7535 psi
@Strain 7.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.0 MPa
@Strain 4.80 %,
Temperature 80.0 °C		7540 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.08 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7554 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.12 MPa
@Strain 2.90 %,
Temperature 60.0 °C		7559 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.2 MPa
@Strain 4.90 %,
Temperature 80.0 °C		7570 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.2 MPa
@Strain 8.00 %,
Temperature 100 °C		7570 psi
@Strain 8.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.285 MPa
@Strain 1.90 %,
Temperature 60.0 °C		7583.3 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.285 MPa
@Strain 1.90 %,
Temperature 23.0 °C		7583.3 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 52.3 MPa
@Strain 5.00 %,
Temperature 80.0 °C		7590 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.485 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7612.3 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.56 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7623 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.56 MPa
@Strain 8.50 %,
Temperature 100 °C		7623 psi
@Strain 8.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.794 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7657.1 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.8 MPa
@Strain 5.50 %,
Temperature 80.0 °C		7660 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.8 MPa
@Strain 1.20 %,
Temperature 23.0 °C		7660 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.91 MPa
@Strain 9.00 %,
Temperature 100 °C		7674 psi
@Strain 9.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.97 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7683 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.113 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7703.4 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.17 MPa
@Strain 9.50 %,
Temperature 100 °C		7712 psi
@Strain 9.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.36 MPa
@Strain 0.800 %,
Temperature 0.000 °C		7739 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 53.364 MPa
@Strain 3.30 %,
Temperature 60.0 °C		7739.8 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.41 MPa
@Strain 10.0 %,
Temperature 100 °C		7746 psi
@Strain 10.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.5 MPa
@Strain 6.00 %,
Temperature 80.0 °C		7760 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.54 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7765 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.581 MPa
@Strain 3.40 %,
Temperature 60.0 °C		7771.3 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.692 MPa
@Strain 2.00 %,
Temperature 23.0 °C		7787.4 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.692 MPa
@Strain 2.00 %,
Temperature 60.0 °C		7787.4 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.72 MPa
@Strain 11.0 %,
Temperature 100 °C		7791 psi
@Strain 11.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.809 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7804.3 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.89 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7816 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.9 MPa
@Strain 6.50 %,
Temperature 80.0 °C		7820 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.99 MPa
@Strain 12.0 %,
Temperature 100 °C		7831 psi
@Strain 12.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.015 MPa
@Strain 3.60 %,
Temperature 60.0 °C		7834.2 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.243 MPa
@Strain 3.70 %,
Temperature 60.0 °C		7867.3 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.25 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7868 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.3 MPa
@Strain 7.00 %,
Temperature 80.0 °C		7880 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 54.414 MPa
@Strain 3.80 %,
Temperature 60.0 °C		7892.1 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.597 MPa
@Strain 3.90 %,
Temperature 60.0 °C		7918.6 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 7.50 %,
Temperature 80.0 °C		7920 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 0.700 %,
Temperature -40.0 °C		7920 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 54.69 MPa
@Strain 3.60 %,
Temperature 80.0 °C		7932 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.738 MPa
@Strain 4.00 %,
Temperature 60.0 °C		7939.1 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.84 MPa
@Strain 3.70 %,
Temperature 80.0 °C		7954 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.892 MPa
@Strain 4.10 %,
Temperature 60.0 °C		7961.4 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.9 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7960 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.095 MPa
@Strain 4.20 %,
Temperature 60.0 °C		7990.9 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.195 MPa
@Strain 2.10 %,
Temperature 60.0 °C		8005.4 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.195 MPa
@Strain 2.10 %,
Temperature 23.0 °C		8005.4 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 8.50 %,
Temperature 80.0 °C		8010 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.21 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8008 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.215 MPa
@Strain 4.30 %,
Temperature 60.0 °C		8008.3 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.22 MPa
@Strain 0.700 %,
Temperature -40.0 °C		8009 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.327 MPa
@Strain 4.40 %,
Temperature 60.0 °C		8024.5 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.4 MPa
@Strain 9.00 %,
Temperature 80.0 °C		8040 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.481 MPa
@Strain 4.50 %,
Temperature 60.0 °C		8046.9 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.53 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8054 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.588 MPa
@Strain 4.60 %,
Temperature 60.0 °C		8062.4 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.597 MPa
@Strain 0.800 %,
Temperature 0.000 °C		8063.7 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 55.6 MPa
@Strain 9.50 %,
Temperature 80.0 °C		8060 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.6 MPa
@Strain 10.0 %,
Temperature 80.0 °C		8060 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 1.30 %,
Temperature 23.0 °C		8080 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.715 MPa
@Strain 4.70 %,
Temperature 60.0 °C		8080.8 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.74 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8084 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.801 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8093.3 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.907 MPa
@Strain 4.90 %,
Temperature 60.0 °C		8108.6 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.014 MPa
@Strain 5.00 %,
Temperature 60.0 °C		8124.2 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.09 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8135 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.21 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8153 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.335 MPa
@Strain 5.50 %,
Temperature 60.0 °C		8170.7 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.49 MPa
@Strain 4.30 %,
Temperature 80.0 °C		8193 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.57 MPa
@Strain 2.20 %,
Temperature 23.0 °C		8205 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 56.57 MPa
@Strain 2.20 %,
Temperature 60.0 °C		8205 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 56.701 MPa
@Strain 6.00 %,
Temperature 60.0 °C		8223.8 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.78 MPa
@Strain 4.40 %,
Temperature 80.0 °C		8235 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.85 MPa
@Strain 6.50 %,
Temperature 60.0 °C		8245 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.99 MPa
@Strain 4.50 %,
Temperature 80.0 °C		8266 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.12 MPa
@Strain 4.60 %,
Temperature 80.0 °C		8285 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.33 MPa
@Strain 4.70 %,
Temperature 80.0 °C		8315 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.41 MPa
@Strain 4.80 %,
Temperature 80.0 °C		8327 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.66 MPa
@Strain 4.90 %,
Temperature 80.0 °C		8363 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.79 MPa
@Strain 5.00 %,
Temperature 80.0 °C		8382 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.883 MPa
@Strain 2.30 %,
Temperature 60.0 °C		8395.2 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.883 MPa
@Strain 2.30 %,
Temperature 23.0 °C		8395.2 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.3 MPa
@Strain 1.40 %,
Temperature 23.0 °C		8460 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.43 MPa
@Strain 5.50 %,
Temperature 80.0 °C		8475 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.0 MPa
@Strain 0.900 %,
Temperature 0.000 °C		8560 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 59.15 MPa
@Strain 2.40 %,
Temperature 23.0 °C		8579 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 59.15 MPa
@Strain 2.40 %,
Temperature 60.0 °C		8579 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 59.19 MPa
@Strain 6.00 %,
Temperature 80.0 °C		8585 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.71 MPa
@Strain 6.50 %,
Temperature 80.0 °C		8660 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.14 MPa
@Strain 7.00 %,
Temperature 80.0 °C		8723 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.213 MPa
@Strain 2.50 %,
Temperature 60.0 °C		8733.2 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.213 MPa
@Strain 2.50 %,
Temperature 23.0 °C		8733.2 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 60.58 MPa
@Strain 7.50 %,
Temperature 80.0 °C		8786 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.7 MPa
@Strain 1.50 %,
Temperature 23.0 °C		8800 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.87 MPa
@Strain 8.00 %,
Temperature 80.0 °C		8828 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.884 MPa
@Strain 0.900 %,
Temperature 0.000 °C		8830.5 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.198 MPa
@Strain 2.60 %,
Temperature 23.0 °C		8876.0 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.198 MPa
@Strain 2.60 %,
Temperature 60.0 °C		8876.0 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.2 MPa
@Strain 8.50 %,
Temperature 80.0 °C		8880 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.45 MPa
@Strain 9.00 %,
Temperature 80.0 °C		8913 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.65 MPa
@Strain 9.50 %,
Temperature 80.0 °C		8942 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.7 MPa
@Strain 0.800 %,
Temperature -40.0 °C		8950 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 61.85 MPa
@Strain 10.0 %,
Temperature 80.0 °C		8971 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.161 MPa
@Strain 2.70 %,
Temperature 60.0 °C		9015.7 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.161 MPa
@Strain 2.70 %,
Temperature 23.0 °C		9015.7 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.48 MPa
@Strain 0.800 %,
Temperature -40.0 °C		9062 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.9 MPa
@Strain 1.60 %,
Temperature 23.0 °C		9120 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.93 MPa
@Strain 2.80 %,
Temperature 23.0 °C		9127 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.93 MPa
@Strain 2.80 %,
Temperature 60.0 °C		9127 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.552 MPa
@Strain 2.90 %,
Temperature 60.0 °C		9217.5 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.552 MPa
@Strain 2.90 %,
Temperature 23.0 °C		9217.5 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.234 MPa
@Strain 3.00 %,
Temperature 23.0 °C		9316.4 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.234 MPa
@Strain 3.00 %,
Temperature 60.0 °C		9316.4 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.33 MPa
@Strain 1.00 %,
Temperature 0.000 °C		9330 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 64.656 MPa
@Strain 3.10 %,
Temperature 60.0 °C		9377.6 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.656 MPa
@Strain 3.10 %,
Temperature 23.0 °C		9377.6 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.0 MPa
@Strain 1.70 %,
Temperature 23.0 °C		9430 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.004 MPa
@Strain 3.20 %,
Temperature 23.0 °C		9428.0 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.004 MPa
@Strain 3.20 %,
Temperature 60.0 °C		9428.0 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.395 MPa
@Strain 3.30 %,
Temperature 60.0 °C		9484.8 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.395 MPa
@Strain 3.30 %,
Temperature 23.0 °C		9484.8 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.663 MPa
@Strain 3.40 %,
Temperature 23.0 °C		9523.6 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.663 MPa
@Strain 3.40 %,
Temperature 60.0 °C		9523.6 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.726 MPa
@Strain 1.00 %,
Temperature 0.000 °C		9532.8 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.984 MPa
@Strain 3.50 %,
Temperature 60.0 °C		9570.2 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.984 MPa
@Strain 3.50 %,
Temperature 23.0 °C		9570.2 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.164 MPa
@Strain 3.60 %,
Temperature 23.0 °C		9596.3 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.164 MPa
@Strain 3.60 %,
Temperature 60.0 °C		9596.3 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.424 MPa
@Strain 3.70 %,
Temperature 60.0 °C		9634.0 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.424 MPa
@Strain 3.70 %,
Temperature 23.0 °C		9634.0 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.535 MPa
@Strain 3.80 %,
Temperature 23.0 °C		9650.1 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.535 MPa
@Strain 3.80 %,
Temperature 60.0 °C		9650.1 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.674 MPa
@Strain 3.90 %,
Temperature 60.0 °C		9670.3 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.674 MPa
@Strain 3.90 %,
Temperature 23.0 °C		9670.3 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.728 MPa
@Strain 4.00 %,
Temperature 23.0 °C		9678.1 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.728 MPa
@Strain 4.00 %,
Temperature 60.0 °C		9678.1 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 1.80 %,
Temperature 23.0 °C		9690 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 66.952 MPa
@Strain 4.10 %,
Temperature 23.0 °C		9710.6 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.952 MPa
@Strain 4.10 %,
Temperature 60.0 °C		9710.6 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.045 MPa
@Strain 4.20 %,
Temperature 60.0 °C		9724.1 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.045 MPa
@Strain 4.20 %,
Temperature 23.0 °C		9724.1 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.092 MPa
@Strain 4.30 %,
Temperature 23.0 °C		9730.9 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.092 MPa
@Strain 4.30 %,
Temperature 60.0 °C		9730.9 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.24 MPa
@Strain 4.40 %,
Temperature 60.0 °C		9752 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.24 MPa
@Strain 4.40 %,
Temperature 23.0 °C		9752 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.379 MPa
@Strain 4.50 %,
Temperature 23.0 °C		9772.5 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.379 MPa
@Strain 4.50 %,
Temperature 60.0 °C		9772.5 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.418 MPa
@Strain 4.60 %,
Temperature 60.0 °C		9778.2 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.418 MPa
@Strain 4.60 %,
Temperature 23.0 °C		9778.2 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.518 MPa
@Strain 4.70 %,
Temperature 23.0 °C		9792.7 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.518 MPa
@Strain 4.70 %,
Temperature 60.0 °C		9792.7 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.611 MPa
@Strain 4.80 %,
Temperature 60.0 °C		9806.2 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.611 MPa
@Strain 4.80 %,
Temperature 23.0 °C		9806.2 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.619 MPa
@Strain 5.00 %,
Temperature 60.0 °C		9807.3 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.619 MPa
@Strain 5.00 %,
Temperature 23.0 °C		9807.3 psi
@Strain 5.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.696 MPa
@Strain 4.90 %,
Temperature 23.0 °C		9818.5 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.696 MPa
@Strain 4.90 %,
Temperature 60.0 °C		9818.5 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.967 MPa
@Strain 5.50 %,
Temperature 60.0 °C		9857.8 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.967 MPa
@Strain 5.50 %,
Temperature 23.0 °C		9857.8 psi
@Strain 5.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.214 MPa
@Strain 6.00 %,
Temperature 23.0 °C		9893.6 psi
@Strain 6.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.214 MPa
@Strain 6.00 %,
Temperature 60.0 °C		9893.6 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.4 MPa
@Strain 1.90 %,
Temperature 23.0 °C		9920 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.5 MPa
@Strain 0.900 %,
Temperature -40.0 °C		9940 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 69.49 MPa
@Strain 0.900 %,
Temperature -40.0 °C		10080 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.5 MPa
@Strain 1.10 %,
Temperature 0.000 °C		10100 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.9 MPa
@Strain 2.00 %,
Temperature 23.0 °C		10100 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.016 MPa
@Strain 1.10 %,
Temperature 0.000 °C		10155 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.5 MPa
@Strain 2.10 %,
Temperature 23.0 °C		10400 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.7 MPa
@Strain 2.20 %,
Temperature 23.0 °C		10500 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.9 MPa
@Strain 2.30 %,
Temperature 23.0 °C		10700 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.235 MPa
@Strain 1.20 %,
Temperature 0.000 °C		10767 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.27 MPa
@Strain 1.20 %,
Temperature 0.000 °C		10770 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.0 MPa
@Strain 2.40 %,
Temperature 23.0 °C		10900 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.2 MPa
@Strain 1.00 %,
Temperature -40.0 °C		10900 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 75.8 MPa
@Strain 2.50 %,
Temperature 23.0 °C		11000 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.31 MPa
@Strain 1.00 %,
Temperature -40.0 °C		11070 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 76.5 MPa
@Strain 2.60 %,
Temperature 23.0 °C		11100 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 77.2 MPa
@Strain 2.70 %,
Temperature 23.0 °C		11200 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 77.6 MPa
@Strain 2.80 %,
Temperature 23.0 °C		11300 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 77.9 MPa
@Strain 2.90 %,
Temperature 23.0 °C		11300 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.108 MPa
@Strain 1.30 %,
Temperature 0.000 °C		11329 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.3 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11400 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.4 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11400 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.6 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11400 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.7 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11400 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.7 MPa
@Strain 1.30 %,
Temperature 0.000 °C		11400 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.8 MPa
@Strain 3.40 %,
Temperature 23.0 °C		11400 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 3.50 %,
Temperature 23.0 °C		11400 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 3.60 %,
Temperature 23.0 °C		11400 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		11400 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.1 MPa
@Strain 3.80 %,
Temperature 23.0 °C		11500 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.1 MPa
@Strain 3.90 %,
Temperature 23.0 °C		11500 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.1 MPa
@Strain 4.00 %,
Temperature 23.0 °C		11500 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.2 MPa
@Strain 4.10 %,
Temperature 23.0 °C		11500 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.2 MPa
@Strain 4.20 %,
Temperature 23.0 °C		11500 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.3 MPa
@Strain 4.30 %,
Temperature 23.0 °C		11500 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.3 MPa
@Strain 4.40 %,
Temperature 23.0 °C		11500 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.3 MPa
@Strain 4.50 %,
Temperature 23.0 °C		11500 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 4.60 %,
Temperature 23.0 °C		11500 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 4.70 %,
Temperature 23.0 °C		11500 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 4.80 %,
Temperature 23.0 °C		11500 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 4.90 %,
Temperature 23.0 °C		11500 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.4 MPa
@Strain 5.00 %,
Temperature 23.0 °C		11500 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.496 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11820 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 81.5 MPa
@Strain 1.10 %,
Temperature -40.0 °C		11800 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 82.8 MPa
@Strain 1.10 %,
Temperature -40.0 °C		12000 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 82.96 MPa
@Strain 1.40 %,
Temperature 0.000 °C		12030 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.664 MPa
@Strain 1.50 %,
Temperature 0.000 °C		12279 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.83 MPa
@Strain 1.50 %,
Temperature 0.000 °C		12590 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.5 MPa
@Strain 1.20 %,
Temperature -40.0 °C		12700 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.64 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12710 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.97 MPa
@Strain 1.20 %,
Temperature -40.0 °C		12900 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.444 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13118 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 90.5 MPa
@Strain 1.60 %,
Temperature 0.000 °C		13100 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.892 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13473 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 93.3 MPa
@Strain 1.30 %,
Temperature -40.0 °C		13500 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.93 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13620 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.71 MPa
@Strain 1.30 %,
Temperature -40.0 °C		13740 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.179 MPa
@Strain 1.90 %,
Temperature 0.000 °C		13805 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.05 MPa
@Strain 1.80 %,
Temperature 0.000 °C		14080 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 97.285 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14110 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.7 MPa
@Strain 1.40 %,
Temperature -40.0 °C		14300 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.246 MPa
@Strain 2.10 %,
Temperature 0.000 °C		14394 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.32 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14410 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 100.1 MPa
@Strain 1.40 %,
Temperature -40.0 °C		14520 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.013 MPa
@Strain 2.20 %,
Temperature 0.000 °C		14650.7 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.39 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14850 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 102.585 MPa
@Strain 2.30 %,
Temperature 0.000 °C		14878.7 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104 MPa
@Strain 1.50 %,
Temperature -40.0 °C		15100 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.069 MPa
@Strain 2.40 %,
Temperature 0.000 °C		15094.0 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.78 MPa
@Strain 2.10 %,
Temperature 0.000 °C		15197 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 105.03 MPa
@Strain 1.50 %,
Temperature -40.0 °C		15233 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.393 MPa
@Strain 2.50 %,
Temperature 0.000 °C		15286.0 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.363 MPa
@Strain 2.60 %,
Temperature 0.000 °C		15426.7 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.96 MPa
@Strain 2.20 %,
Temperature 0.000 °C		15513 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 107.011 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15520.7 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 107.395 MPa
@Strain 2.80 %,
Temperature 0.000 °C		15576.4 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 107.575 MPa
@Strain 2.90 %,
Temperature 0.000 °C		15602.5 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 108.8 MPa
@Strain 1.60 %,
Temperature -40.0 °C		15780 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.87 MPa
@Strain 2.30 %,
Temperature 0.000 °C		15790 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 109.78 MPa
@Strain 1.60 %,
Temperature -40.0 °C		15922 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.56 MPa
@Strain 2.40 %,
Temperature 0.000 °C		16035 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.98 MPa
@Strain 2.50 %,
Temperature 0.000 °C		16241 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 113.4 MPa
@Strain 1.70 %,
Temperature -40.0 °C		16450 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.41 MPa
@Strain 2.60 %,
Temperature 0.000 °C		16449 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 114.01 MPa
@Strain 1.70 %,
Temperature -40.0 °C		16536 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.91 MPa
@Strain 2.70 %,
Temperature 0.000 °C		16666 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 115.34 MPa
@Strain 2.80 %,
Temperature 0.000 °C		16729 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 117.7 MPa
@Strain 1.80 %,
Temperature -40.0 °C		17070 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 117.86 MPa
@Strain 1.80 %,
Temperature -40.0 °C		17094 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 121.7 MPa
@Strain 1.90 %,
Temperature -40.0 °C		17650 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 121.9 MPa
@Strain 1.90 %,
Temperature -40.0 °C		17680 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.2 MPa
@Strain 2.00 %,
Temperature -40.0 °C		18160 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.3 MPa
@Strain 2.00 %,
Temperature -40.0 °C		18170 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 128.6 MPa
@Strain 2.10 %,
Temperature -40.0 °C		18650 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 128.8 MPa
@Strain 2.10 %,
Temperature -40.0 °C		18680 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 131.8 MPa
@Strain 2.20 %,
Temperature -40.0 °C		19120 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 132.32 MPa
@Strain 2.20 %,
Temperature -40.0 °C		19191 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 134.9 MPa
@Strain 2.30 %,
Temperature -40.0 °C		19570 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 135.07 MPa
@Strain 2.30 %,
Temperature -40.0 °C		19590 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137.6 MPa
@Strain 2.40 %,
Temperature -40.0 °C		19960 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 137.62 MPa
@Strain 2.40 %,
Temperature -40.0 °C		19960 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.1 MPa
@Strain 2.50 %,
Temperature -40.0 °C		20320 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 140.61 MPa
@Strain 2.50 %,
Temperature -40.0 °C		20394 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 142.4 MPa
@Strain 2.60 %,
Temperature -40.0 °C		20650 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 142.86 MPa
@Strain 2.60 %,
Temperature -40.0 °C		20720 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 144.5 MPa
@Strain 2.70 %,
Temperature -40.0 °C		20960 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 144.91 MPa
@Strain 2.70 %,
Temperature -40.0 °C		21017 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 146.4 MPa
@Strain 2.80 %,
Temperature -40.0 °C		21230 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 146.52 MPa
@Strain 2.80 %,
Temperature -40.0 °C		21251 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		DAM; ISO 527
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  5.00 GPa
@Temperature 23.0 °C		725 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 7.50 GPa
@Temperature 23.0 °C		1090 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 183 MPa
@Temperature 23.0 °C		26500 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  6.90 GPa
@Temperature 23.0 °C		1000 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 7.00 GPa
@Temperature 23.0 °C		1020 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched 0.430 J/cm
@Temperature 23.0 °C		0.806 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
Izod Impact, Unnotched 5.30 J/cm
@Temperature 23.0 °C		9.93 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  3.40 kJ/m²
@Temperature -40.0 °C		1.62 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Charpy Impact, Notched 0.300 J/cm²
@Temperature 23.0 °C		1.43 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 475 V
@Temperature 23.0 °C		475 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 62.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 62.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 100 µm/m-°C
@Temperature 55.0 - 160 °C		55.6 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
 100 µm/m-°C
@Temperature 55.0 - 160 °C		55.6 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 255 °C491 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C446 °FDAM; ASTM D648
 230 °C446 °FDAM; ISO 75-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesStiffness, GoodDAM
 Strength, GoodDAM
 Warpage, LowDAM
FillerMineral/GlassDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-(MD+GF)38<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass/Mineral Reinforced ResinsDAM
 Low Warp ResinsDAM
Resin IdentificationPA66-(MD+GF)38ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Industrial ApplicationsDAM
 Parts, EngineeringDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45441.html

免责声明: 本文 DuPont Performance Polymers Minlon® 22C BK086 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4