  4. DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66

DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66

DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.39
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 1.07
  • 弯曲模量 [MPa]: 8.965
  • 热变形温度 [℃]: 260.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.39 g/cc1.39 g/ccDAM; ASTM D792
Density 1.39 g/cc0.0502 lb/in³DAM; ISO 1183
Filler Content 33 %33 %DAM
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 1.60 mm		0.0020 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0030 cm/cm
@Thickness 3.20 mm		0.0030 in/in
@Thickness 0.126 in		Flow; DAM
 0.0050 cm/cm
@Thickness 6.40 mm		0.0050 in/in
@Thickness 0.252 in		Flow; DAM
 0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Transverse; DAM
 0.010 cm/cm
@Thickness 1.60 mm		0.010 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.011 cm/cm
@Thickness 6.40 mm		0.011 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
@Thickness 2.00 mm		0.011 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		50%RH; ISO 527
 200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength 186 MPa
@Temperature 23.0 °C		27000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  4.552 MPa
@Strain 0.100 %,
Temperature 150 °C		660.2 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.61 MPa
@Strain 0.100 %,
Temperature 120 °C		669 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.81 MPa
@Strain 0.100 %,
Temperature 150 °C		698 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.00 MPa
@Strain 0.100 %,
Temperature 100 °C		725 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.100 %,
Temperature 120 °C		754 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 80.0 °C		798 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.80 MPa
@Strain 0.100 %,
Temperature 60.0 °C		841 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.93 MPa
@Strain 0.100 %,
Temperature 100 °C		860 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.58 MPa
@Strain 0.100 %,
Temperature 80.0 °C		954 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1090 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.00 MPa
@Strain 0.100 %,
Temperature 60.0 °C		1160 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.312 MPa
@Strain 0.200 %,
Temperature 150 °C		1351 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.35 MPa
@Strain 0.200 %,
Temperature 150 °C		1360 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.51 MPa
@Strain 0.200 %,
Temperature 120 °C		1380 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.92 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1440 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 10.1 MPa
@Strain 0.200 %,
Temperature 100 °C		1460 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.3 MPa
@Strain 0.200 %,
Temperature 120 °C		1490 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.51 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1524 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.11 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1611 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1620 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1620 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 11.39 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1652 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1700 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.4 MPa
@Strain 0.200 %,
Temperature 100 °C		1800 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.24 MPa
@Strain 0.300 %,
Temperature 150 °C		1920 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.632 MPa
@Strain 0.300 %,
Temperature 150 °C		1977.2 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.77 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1997 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.86 MPa
@Strain 0.300 %,
Temperature 120 °C		2010 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.69 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2131 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 14.7 MPa
@Strain 0.300 %,
Temperature 100 °C		2130 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.05 MPa
@Strain 0.300 %,
Temperature 120 °C		2183 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.2 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2350 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.5 MPa
@Strain 0.200 %,
Temperature 60.0 °C		2390 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.19 MPa
@Strain 0.400 %,
Temperature 150 °C		2493 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.376 MPa
@Strain 0.400 %,
Temperature 150 °C		2520.2 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2520 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.84 MPa
@Strain 0.300 %,
Temperature 100 °C		2587 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.23 MPa
@Strain 0.400 %,
Temperature 120 °C		2644 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.8 MPa
@Strain 0.400 %,
Temperature 100 °C		2730 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.9 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2740 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 19.15 MPa
@Strain 0.400 %,
Temperature 120 °C		2777 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.81 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2873 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.7 MPa
@Strain 0.400 %,
Temperature 80.0 °C		3000 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.91 MPa
@Strain 0.200 %,
Temperature 23.0 °C		3033 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 21.76 MPa
@Strain 0.500 %,
Temperature 150 °C		3156 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.78 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3159 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.792 MPa
@Strain 0.500 %,
Temperature 150 °C		3160.7 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.22 MPa
@Strain 0.200 %,
Temperature -40.0 °C		3223 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 22.38 MPa
@Strain 0.200 %,
Temperature 0.000 °C		3246 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 22.4 MPa
@Strain 0.500 %,
Temperature 120 °C		3250 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.5 MPa
@Strain 0.400 %,
Temperature 60.0 °C		3260 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.55 MPa
@Strain 0.500 %,
Temperature 120 °C		3271 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.6 MPa
@Strain 0.200 %,
Temperature -40.0 °C		3280 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 22.69 MPa
@Strain 0.400 %,
Temperature 100 °C		3291 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.2 MPa
@Strain 0.500 %,
Temperature 100 °C		3360 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.0 MPa
@Strain 0.300 %,
Temperature 60.0 °C		3480 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.152 MPa
@Strain 0.600 %,
Temperature 150 °C		3648.0 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.19 MPa
@Strain 0.400 %,
Temperature 80.0 °C		3654 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3650 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.48 MPa
@Strain 0.600 %,
Temperature 150 °C		3696 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.49 MPa
@Strain 0.600 %,
Temperature 120 °C		3842 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.65 MPa
@Strain 0.600 %,
Temperature 120 °C		3865 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.95 MPa
@Strain 0.500 %,
Temperature 100 °C		3909 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.0 MPa
@Strain 0.600 %,
Temperature 100 °C		3920 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.31 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3961 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 27.77 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4028 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.512 MPa
@Strain 0.700 %,
Temperature 150 °C		4135.3 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.89 MPa
@Strain 0.700 %,
Temperature 150 °C		4190 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.2 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4240 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 0.500 %,
Temperature 60.0 °C		4240 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.82 MPa
@Strain 0.700 %,
Temperature 120 °C		4325 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.93 MPa
@Strain 0.500 %,
Temperature 80.0 °C		4341 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.41 MPa
@Strain 0.300 %,
Temperature 23.0 °C		4411 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.44 MPa
@Strain 0.700 %,
Temperature 120 °C		4415 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.7 MPa
@Strain 0.700 %,
Temperature 100 °C		4450 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.97 MPa
@Strain 0.600 %,
Temperature 100 °C		4492 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.0 MPa
@Strain 0.400 %,
Temperature 60.0 °C		4500 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.584 MPa
@Strain 0.800 %,
Temperature 150 °C		4580.9 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.09 MPa
@Strain 0.800 %,
Temperature 150 °C		4654 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.03 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4791 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 0.700 %,
Temperature 80.0 °C		4800 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.23 MPa
@Strain 0.800 %,
Temperature 120 °C		4820 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.78 MPa
@Strain 0.300 %,
Temperature 0.000 °C		4899 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 33.83 MPa
@Strain 0.800 %,
Temperature 120 °C		4907 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.0 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4930 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 34.39 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4988 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.4 MPa
@Strain 0.800 %,
Temperature 100 °C		4990 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.4 MPa
@Strain 0.600 %,
Temperature 60.0 °C		4990 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.45 MPa
@Strain 0.700 %,
Temperature 100 °C		4997 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.56 MPa
@Strain 0.900 %,
Temperature 150 °C		5013 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.59 MPa
@Strain 0.400 %,
Temperature 0.000 °C		5017 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 35.04 MPa
@Strain 0.900 %,
Temperature 150 °C		5082 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.66 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5172 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.27 MPa
@Strain 0.900 %,
Temperature 120 °C		5261 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.9 MPa
@Strain 0.800 %,
Temperature 80.0 °C		5350 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.1 MPa
@Strain 0.500 %,
Temperature 60.0 °C		5380 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.21 MPa
@Strain 0.900 %,
Temperature 120 °C		5397 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.344 MPa
@Strain 1.00 %,
Temperature 150 °C		5416.3 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.82 MPa
@Strain 1.00 %,
Temperature 150 °C		5485 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.0 MPa
@Strain 0.900 %,
Temperature 100 °C		5510 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.02 MPa
@Strain 0.800 %,
Temperature 100 °C		5514 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.25 MPa
@Strain 0.700 %,
Temperature 80.0 °C		5548 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.21 MPa
@Strain 1.00 %,
Temperature 120 °C		5687 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.3 MPa
@Strain 0.700 %,
Temperature 60.0 °C		5700 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.936 MPa
@Strain 1.10 %,
Temperature 150 °C		5792.2 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.11 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5817 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 40.39 MPa
@Strain 1.00 %,
Temperature 120 °C		5858 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.53 MPa
@Strain 1.10 %,
Temperature 150 °C		5878 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.6 MPa
@Strain 0.900 %,
Temperature 80.0 °C		5890 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.4 MPa
@Strain 1.00 %,
Temperature 100 °C		6000 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.61 MPa
@Strain 0.900 %,
Temperature 100 °C		6035 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.86 MPa
@Strain 1.10 %,
Temperature 120 °C		6071 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.06 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6100 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.23 MPa
@Strain 0.800 %,
Temperature 80.0 °C		6125 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.528 MPa
@Strain 1.20 %,
Temperature 150 °C		6168.2 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.82 MPa
@Strain 0.400 %,
Temperature -40.0 °C		6211 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.16 MPa
@Strain 1.20 %,
Temperature 150 °C		6260 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.46 MPa
@Strain 1.10 %,
Temperature 120 °C		6303 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.56 MPa
@Strain 0.500 %,
Temperature 0.000 °C		6318 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 0.800 %,
Temperature 60.0 °C		6400 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 1.00 %,
Temperature 80.0 °C		6400 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.5 MPa
@Strain 0.600 %,
Temperature 60.0 °C		6450 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.5 MPa
@Strain 1.10 %,
Temperature 100 °C		6450 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.53 MPa
@Strain 1.20 %,
Temperature 120 °C		6459 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.024 MPa
@Strain 1.30 %,
Temperature 150 °C		6530.2 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 45.08 MPa
@Strain 1.00 %,
Temperature 100 °C		6538 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.57 MPa
@Strain 1.30 %,
Temperature 150 °C		6609 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.7 MPa
@Strain 0.400 %,
Temperature 0.000 °C		6630 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 45.82 MPa
@Strain 0.400 %,
Temperature -40.0 °C		6646 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 46.2 MPa
@Strain 0.900 %,
Temperature 80.0 °C		6700 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.33 MPa
@Strain 1.20 %,
Temperature 120 °C		6720 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.0 MPa
@Strain 1.30 %,
Temperature 120 °C		6820 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.232 MPa
@Strain 1.40 %,
Temperature 150 °C		6850.4 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 47.5 MPa
@Strain 1.10 %,
Temperature 80.0 °C		6890 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 1.20 %,
Temperature 100 °C		6900 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.82 MPa
@Strain 1.10 %,
Temperature 100 °C		6936 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.89 MPa
@Strain 1.40 %,
Temperature 150 °C		6946 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.15 MPa
@Strain 0.700 %,
Temperature 23.0 °C		6984 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 0.900 %,
Temperature 60.0 °C		7020 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.2 MPa
@Strain 1.30 %,
Temperature 120 °C		7140 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.37 MPa
@Strain 1.40 %,
Temperature 120 °C		7161 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 49.44 MPa
@Strain 1.50 %,
Temperature 150 °C		7171 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 0.500 %,
Temperature 23.0 °C		7220 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 50.07 MPa
@Strain 1.00 %,
Temperature 80.0 °C		7262 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.11 MPa
@Strain 1.50 %,
Temperature 150 °C		7268 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.4 MPa
@Strain 1.30 %,
Temperature 100 °C		7310 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 50.7 MPa
@Strain 1.20 %,
Temperature 80.0 °C		7350 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.01 MPa
@Strain 1.20 %,
Temperature 100 °C		7398 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.4 MPa
@Strain 0.700 %,
Temperature 60.0 °C		7450 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.46 MPa
@Strain 1.50 %,
Temperature 120 °C		7464 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 51.552 MPa
@Strain 1.60 %,
Temperature 150 °C		7477.0 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 51.87 MPa
@Strain 1.40 %,
Temperature 120 °C		7523 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.15 MPa
@Strain 1.60 %,
Temperature 150 °C		7564 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 1.00 %,
Temperature 60.0 °C		7610 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.73 MPa
@Strain 0.600 %,
Temperature 0.000 °C		7648 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.11 MPa
@Strain 1.10 %,
Temperature 80.0 °C		7703 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 1.40 %,
Temperature 100 °C		7720 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 53.568 MPa
@Strain 1.70 %,
Temperature 150 °C		7769.4 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 53.64 MPa
@Strain 1.60 %,
Temperature 120 °C		7780 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 53.8 MPa
@Strain 1.30 %,
Temperature 80.0 °C		7800 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.9 MPa
@Strain 1.30 %,
Temperature 100 °C		7820 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.15 MPa
@Strain 0.800 %,
Temperature 23.0 °C		7854 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 1.70 %,
Temperature 150 °C		7860 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 54.33 MPa
@Strain 1.50 %,
Temperature 120 °C		7880 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.15 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7999 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 55.488 MPa
@Strain 1.80 %,
Temperature 150 °C		8047.9 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.54 MPa
@Strain 0.500 %,
Temperature 0.000 °C		8055 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 55.73 MPa
@Strain 1.70 %,
Temperature 120 °C		8083 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 55.86 MPa
@Strain 0.500 %,
Temperature -40.0 °C		8102 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.9 MPa
@Strain 1.50 %,
Temperature 100 °C		8110 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 56.17 MPa
@Strain 1.80 %,
Temperature 150 °C		8147 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.4 MPa
@Strain 1.10 %,
Temperature 60.0 °C		8180 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.65 MPa
@Strain 1.20 %,
Temperature 80.0 °C		8216 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.89 MPa
@Strain 1.60 %,
Temperature 120 °C		8251 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.9 MPa
@Strain 1.40 %,
Temperature 80.0 °C		8250 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 56.94 MPa
@Strain 1.40 %,
Temperature 100 °C		8258 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.312 MPa
@Strain 1.90 %,
Temperature 150 °C		8312.4 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.72 MPa
@Strain 1.80 %,
Temperature 120 °C		8372 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 57.9 MPa
@Strain 0.800 %,
Temperature 60.0 °C		8400 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.04 MPa
@Strain 1.90 %,
Temperature 150 °C		8418 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.5 MPa
@Strain 1.60 %,
Temperature 100 °C		8480 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 58.75 MPa
@Strain 0.600 %,
Temperature 23.0 °C		8521 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.944 MPa
@Strain 2.00 %,
Temperature 150 °C		8549.1 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 59.35 MPa
@Strain 1.70 %,
Temperature 120 °C		8608 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 59.62 MPa
@Strain 1.90 %,
Temperature 120 °C		8647 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 59.64 MPa
@Strain 0.900 %,
Temperature 23.0 °C		8650 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.8 MPa
@Strain 1.50 %,
Temperature 80.0 °C		8670 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 59.8 MPa
@Strain 2.00 %,
Temperature 150 °C		8670 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 59.86 MPa
@Strain 1.30 %,
Temperature 80.0 °C		8682 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.93 MPa
@Strain 1.50 %,
Temperature 100 °C		8692 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.0 MPa
@Strain 1.20 %,
Temperature 60.0 °C		8700 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.384 MPa
@Strain 2.10 %,
Temperature 150 °C		8758.0 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 60.8 MPa
@Strain 1.70 %,
Temperature 100 °C		8820 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 61.33 MPa
@Strain 2.00 %,
Temperature 120 °C		8895 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 61.33 MPa
@Strain 0.700 %,
Temperature 0.000 °C		8895 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.4 MPa
@Strain 2.10 %,
Temperature 150 °C		8910 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.6 MPa
@Strain 1.80 %,
Temperature 120 °C		8930 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 62.016 MPa
@Strain 2.20 %,
Temperature 150 °C		8994.7 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 62.47 MPa
@Strain 1.60 %,
Temperature 100 °C		9061 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 62.6 MPa
@Strain 1.60 %,
Temperature 80.0 °C		9080 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 63.04 MPa
@Strain 2.10 %,
Temperature 120 °C		9143 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 63.06 MPa
@Strain 2.20 %,
Temperature 150 °C		9146 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.1 MPa
@Strain 1.80 %,
Temperature 100 °C		9150 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 63.23 MPa
@Strain 1.40 %,
Temperature 80.0 °C		9171 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.36 MPa
@Strain 2.30 %,
Temperature 150 °C		9190 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 63.5 MPa
@Strain 1.30 %,
Temperature 60.0 °C		9210 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.86 MPa
@Strain 1.90 %,
Temperature 120 °C		9262 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 64.0 MPa
@Strain 0.900 %,
Temperature 60.0 °C		9280 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.5 MPa
@Strain 2.30 %,
Temperature 150 °C		9350 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.65 MPa
@Strain 2.20 %,
Temperature 120 °C		9377 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 64.704 MPa
@Strain 2.40 %,
Temperature 150 °C		9384.5 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 64.84 MPa
@Strain 1.00 %,
Temperature 23.0 °C		9404 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.02 MPa
@Strain 1.70 %,
Temperature 100 °C		9430 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 65.3 MPa
@Strain 1.90 %,
Temperature 100 °C		9470 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 65.3 MPa
@Strain 1.70 %,
Temperature 80.0 °C		9470 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 65.81 MPa
@Strain 2.00 %,
Temperature 120 °C		9545 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 65.952 MPa
@Strain 2.50 %,
Temperature 150 °C		9565.5 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 65.97 MPa
@Strain 2.40 %,
Temperature 150 °C		9568 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.21 MPa
@Strain 0.600 %,
Temperature 0.000 °C		9603 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.27 MPa
@Strain 2.30 %,
Temperature 120 °C		9612 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.36 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9625 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 66.5 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9650 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 66.55 MPa
@Strain 1.50 %,
Temperature 80.0 °C		9652 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 1.40 %,
Temperature 60.0 °C		9690 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 67.2 MPa
@Strain 2.60 %,
Temperature 150 °C		9750 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 67.22 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9749 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.31 MPa
@Strain 2.50 %,
Temperature 150 °C		9763 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.4 MPa
@Strain 2.00 %,
Temperature 100 °C		9780 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 67.47 MPa
@Strain 1.80 %,
Temperature 100 °C		9786 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 67.69 MPa
@Strain 2.40 %,
Temperature 120 °C		9818 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 67.75 MPa
@Strain 2.10 %,
Temperature 120 °C		9826 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 67.8 MPa
@Strain 1.80 %,
Temperature 80.0 °C		9830 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 68.256 MPa
@Strain 2.70 %,
Temperature 150 °C		9899.7 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 68.56 MPa
@Strain 2.60 %,
Temperature 150 °C		9944 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.11 MPa
@Strain 2.50 %,
Temperature 120 °C		10020 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.216 MPa
@Strain 2.80 %,
Temperature 150 °C		10039 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 69.38 MPa
@Strain 1.60 %,
Temperature 80.0 °C		10060 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.4 MPa
@Strain 2.10 %,
Temperature 100 °C		10100 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 69.49 MPa
@Strain 0.800 %,
Temperature 0.000 °C		10080 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.6 MPa
@Strain 1.00 %,
Temperature 60.0 °C		10100 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 69.6 MPa
@Strain 2.20 %,
Temperature 120 °C		10100 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 69.7 MPa
@Strain 2.70 %,
Temperature 150 °C		10100 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.72 MPa
@Strain 1.90 %,
Temperature 100 °C		10110 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 69.73 MPa
@Strain 1.10 %,
Temperature 23.0 °C		10110 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.9 MPa
@Strain 1.50 %,
Temperature 60.0 °C		10100 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 70.176 MPa
@Strain 2.90 %,
Temperature 150 °C		10178 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 70.3 MPa
@Strain 1.90 %,
Temperature 80.0 °C		10200 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 70.35 MPa
@Strain 2.60 %,
Temperature 120 °C		10200 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 70.73 MPa
@Strain 2.80 %,
Temperature 150 °C		10260 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 71.04 MPa
@Strain 3.00 %,
Temperature 150 °C		10300 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 71.2 MPa
@Strain 2.20 %,
Temperature 100 °C		10300 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 71.34 MPa
@Strain 2.30 %,
Temperature 120 °C		10350 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 71.68 MPa
@Strain 2.70 %,
Temperature 120 °C		10400 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 71.712 MPa
@Strain 3.10 %,
Temperature 150 °C		10401 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 71.88 MPa
@Strain 2.00 %,
Temperature 100 °C		10430 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 71.92 MPa
@Strain 2.90 %,
Temperature 150 °C		10430 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 72.21 MPa
@Strain 1.70 %,
Temperature 80.0 °C		10470 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 72.384 MPa
@Strain 3.20 %,
Temperature 150 °C		10498 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 72.5 MPa
@Strain 2.00 %,
Temperature 80.0 °C		10500 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 72.82 MPa
@Strain 2.80 %,
Temperature 120 °C		10560 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 72.9 MPa
@Strain 2.30 %,
Temperature 100 °C		10600 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 72.94 MPa
@Strain 3.00 %,
Temperature 150 °C		10580 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 73.0 MPa
@Strain 1.60 %,
Temperature 60.0 °C		10600 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 73.056 MPa
@Strain 3.30 %,
Temperature 150 °C		10596 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 73.08 MPa
@Strain 2.40 %,
Temperature 120 °C		10600 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 73.44 MPa
@Strain 3.40 %,
Temperature 150 °C		10650 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 73.92 MPa
@Strain 3.50 %,
Temperature 150 °C		10720 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 73.92 MPa
@Strain 3.10 %,
Temperature 150 °C		10720 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 73.96 MPa
@Strain 2.90 %,
Temperature 120 °C		10730 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 74.304 MPa
@Strain 3.60 %,
Temperature 150 °C		10777 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.33 MPa
@Strain 2.10 %,
Temperature 100 °C		10780 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 74.53 MPa
@Strain 1.20 %,
Temperature 23.0 °C		10810 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.592 MPa
@Strain 3.70 %,
Temperature 150 °C		10819 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.6 MPa
@Strain 2.40 %,
Temperature 100 °C		10800 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 74.688 MPa
@Strain 3.80 %,
Temperature 150 °C		10833 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 2.10 %,
Temperature 80.0 °C		10800 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 74.72 MPa
@Strain 2.50 %,
Temperature 120 °C		10840 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 74.85 MPa
@Strain 3.20 %,
Temperature 150 °C		10860 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 74.93 MPa
@Strain 1.80 %,
Temperature 80.0 °C		10870 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 75.0 MPa
@Strain 3.00 %,
Temperature 120 °C		10900 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 75.0 MPa
@Strain 1.10 %,
Temperature 60.0 °C		10900 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.62 MPa
@Strain 3.30 %,
Temperature 150 °C		10970 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 75.89 MPa
@Strain 0.800 %,
Temperature 23.0 °C		11010 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.9 MPa
@Strain 1.70 %,
Temperature 60.0 °C		11000 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 75.95 MPa
@Strain 3.10 %,
Temperature 120 °C		11020 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 76.2 MPa
@Strain 2.50 %,
Temperature 100 °C		11100 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 76.44 MPa
@Strain 2.20 %,
Temperature 100 °C		11090 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.44 MPa
@Strain 3.40 %,
Temperature 150 °C		11090 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 76.47 MPa
@Strain 2.60 %,
Temperature 120 °C		11090 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 76.75 MPa
@Strain 0.700 %,
Temperature 0.000 °C		11130 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.8 MPa
@Strain 2.20 %,
Temperature 80.0 °C		11100 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 76.9 MPa
@Strain 3.20 %,
Temperature 120 °C		11200 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 77.0 MPa
@Strain 0.700 %,
Temperature -40.0 °C		11200 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 77.06 MPa
@Strain 0.700 %,
Temperature -40.0 °C		11180 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 77.09 MPa
@Strain 3.50 %,
Temperature 150 °C		11180 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 77.43 MPa
@Strain 1.90 %,
Temperature 80.0 °C		11230 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 77.6 MPa
@Strain 2.60 %,
Temperature 100 °C		11300 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 77.76 MPa
@Strain 3.30 %,
Temperature 120 °C		11280 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 77.77 MPa
@Strain 3.60 %,
Temperature 150 °C		11280 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 77.8 MPa
@Strain 2.70 %,
Temperature 120 °C		11300 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 77.82 MPa
@Strain 0.900 %,
Temperature 0.000 °C		11290 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.38 MPa
@Strain 3.70 %,
Temperature 150 °C		11370 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 78.39 MPa
@Strain 2.30 %,
Temperature 100 °C		11370 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 78.52 MPa
@Strain 3.40 %,
Temperature 120 °C		11390 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 78.6 MPa
@Strain 1.80 %,
Temperature 60.0 °C		11400 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 78.9 MPa
@Strain 2.30 %,
Temperature 80.0 °C		11400 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 78.94 MPa
@Strain 3.80 %,
Temperature 150 °C		11450 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 79.0 MPa
@Strain 2.70 %,
Temperature 100 °C		11500 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 79.02 MPa
@Strain 1.30 %,
Temperature 23.0 °C		11460 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.13 MPa
@Strain 2.80 %,
Temperature 120 °C		11480 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 79.27 MPa
@Strain 3.50 %,
Temperature 120 °C		11500 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 79.43 MPa
@Strain 3.90 %,
Temperature 150 °C		11520 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 79.83 MPa
@Strain 2.00 %,
Temperature 80.0 °C		11580 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 79.9 MPa
@Strain 1.20 %,
Temperature 60.0 °C		11600 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.91 MPa
@Strain 4.00 %,
Temperature 150 °C		11590 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 79.94 MPa
@Strain 3.60 %,
Temperature 120 °C		11590 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 80.2 MPa
@Strain 2.80 %,
Temperature 100 °C		11600 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 80.3 MPa
@Strain 2.40 %,
Temperature 100 °C		11600 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 80.4 MPa
@Strain 4.10 %,
Temperature 150 °C		11700 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 80.5 MPa
@Strain 3.70 %,
Temperature 120 °C		11700 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 80.57 MPa
@Strain 2.90 %,
Temperature 120 °C		11690 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 80.7 MPa
@Strain 2.40 %,
Temperature 80.0 °C		11700 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 80.73 MPa
@Strain 4.20 %,
Temperature 150 °C		11710 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 81.0 MPa
@Strain 3.80 %,
Temperature 120 °C		11700 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.08 MPa
@Strain 4.30 %,
Temperature 150 °C		11760 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 81.2 MPa
@Strain 2.90 %,
Temperature 100 °C		11800 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 81.38 MPa
@Strain 4.40 %,
Temperature 150 °C		11800 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 81.4 MPa
@Strain 3.90 %,
Temperature 120 °C		11800 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.5 MPa
@Strain 1.90 %,
Temperature 60.0 °C		11800 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 81.6 MPa
@Strain 4.00 %,
Temperature 120 °C		11800 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 81.76 MPa
@Strain 4.50 %,
Temperature 150 °C		11860 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 81.8 MPa
@Strain 3.00 %,
Temperature 120 °C		11900 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 81.88 MPa
@Strain 4.60 %,
Temperature 150 °C		11880 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 82.02 MPa
@Strain 4.70 %,
Temperature 150 °C		11900 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 82.04 MPa
@Strain 4.80 %,
Temperature 150 °C		11900 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 82.17 MPa
@Strain 2.50 %,
Temperature 100 °C		11920 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.2 MPa
@Strain 3.00 %,
Temperature 100 °C		11900 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 82.5 MPa
@Strain 2.50 %,
Temperature 80.0 °C		12000 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 82.54 MPa
@Strain 2.10 %,
Temperature 80.0 °C		11970 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 82.92 MPa
@Strain 3.10 %,
Temperature 120 °C		12030 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 3.10 %,
Temperature 100 °C		12100 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 83.22 MPa
@Strain 1.40 %,
Temperature 23.0 °C		12070 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.9 MPa
@Strain 3.20 %,
Temperature 100 °C		12200 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 83.95 MPa
@Strain 3.20 %,
Temperature 120 °C		12180 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 2.00 %,
Temperature 60.0 °C		12200 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 84.02 MPa
@Strain 2.60 %,
Temperature 100 °C		12190 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 84.2 MPa
@Strain 2.60 %,
Temperature 80.0 °C		12200 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 84.4 MPa
@Strain 0.900 %,
Temperature 23.0 °C		12200 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.7 MPa
@Strain 1.30 %,
Temperature 60.0 °C		12300 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.7 MPa
@Strain 3.30 %,
Temperature 100 °C		12300 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 84.89 MPa
@Strain 2.20 %,
Temperature 80.0 °C		12310 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 85.08 MPa
@Strain 3.30 %,
Temperature 120 °C		12340 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 85.16 MPa
@Strain 1.00 %,
Temperature 0.000 °C		12350 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 85.3 MPa
@Strain 3.40 %,
Temperature 100 °C		12400 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 85.69 MPa
@Strain 2.70 %,
Temperature 100 °C		12430 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.7 MPa
@Strain 2.70 %,
Temperature 80.0 °C		12400 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 85.9 MPa
@Strain 3.50 %,
Temperature 100 °C		12500 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 85.9 MPa
@Strain 3.40 %,
Temperature 120 °C		12500 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 86.3 MPa
@Strain 3.60 %,
Temperature 100 °C		12500 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 86.4 MPa
@Strain 2.10 %,
Temperature 60.0 °C		12500 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 86.6 MPa
@Strain 3.70 %,
Temperature 100 °C		12600 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 86.74 MPa
@Strain 0.800 %,
Temperature 0.000 °C		12580 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.82 MPa
@Strain 3.50 %,
Temperature 120 °C		12590 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 86.9 MPa
@Strain 3.80 %,
Temperature 100 °C		12600 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 87.0 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12600 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 87.05 MPa
@Strain 2.30 %,
Temperature 80.0 °C		12630 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 87.1 MPa
@Strain 2.80 %,
Temperature 80.0 °C		12600 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 87.1 MPa
@Strain 3.90 %,
Temperature 100 °C		12600 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 87.26 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12660 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.45 MPa
@Strain 2.80 %,
Temperature 100 °C		12680 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.51 MPa
@Strain 1.50 %,
Temperature 23.0 °C		12690 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 87.64 MPa
@Strain 3.60 %,
Temperature 120 °C		12710 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 87.8 MPa
@Strain 4.00 %,
Temperature 100 °C		12700 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 88.46 MPa
@Strain 3.70 %,
Temperature 120 °C		12830 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.5 MPa
@Strain 2.90 %,
Temperature 80.0 °C		12800 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 88.8 MPa
@Strain 2.20 %,
Temperature 60.0 °C		12900 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 89.1 MPa
@Strain 1.40 %,
Temperature 60.0 °C		12900 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 89.12 MPa
@Strain 2.90 %,
Temperature 100 °C		12930 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.18 MPa
@Strain 2.40 %,
Temperature 80.0 °C		12930 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 89.18 MPa
@Strain 3.80 %,
Temperature 120 °C		12930 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 89.7 MPa
@Strain 3.00 %,
Temperature 80.0 °C		13000 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 89.79 MPa
@Strain 3.90 %,
Temperature 120 °C		13020 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 90.3 MPa
@Strain 4.00 %,
Temperature 120 °C		13100 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 90.59 MPa
@Strain 3.00 %,
Temperature 100 °C		13140 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 90.8 MPa
@Strain 3.10 %,
Temperature 80.0 °C		13200 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 90.92 MPa
@Strain 4.10 %,
Temperature 120 °C		13190 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 91.1 MPa
@Strain 2.30 %,
Temperature 60.0 °C		13200 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 91.25 MPa
@Strain 2.50 %,
Temperature 80.0 °C		13230 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 91.43 MPa
@Strain 4.20 %,
Temperature 120 °C		13260 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 91.61 MPa
@Strain 1.60 %,
Temperature 23.0 °C		13290 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 91.7 MPa
@Strain 3.20 %,
Temperature 80.0 °C		13300 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 91.74 MPa
@Strain 4.30 %,
Temperature 120 °C		13310 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.06 MPa
@Strain 3.10 %,
Temperature 100 °C		13350 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 92.15 MPa
@Strain 4.40 %,
Temperature 120 °C		13370 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.31 MPa
@Strain 1.00 %,
Temperature 23.0 °C		13390 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 92.35 MPa
@Strain 4.50 %,
Temperature 120 °C		13390 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.5 MPa
@Strain 3.30 %,
Temperature 80.0 °C		13400 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 92.56 MPa
@Strain 4.60 %,
Temperature 120 °C		13420 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.67 MPa
@Strain 1.10 %,
Temperature 0.000 °C		13440 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 92.87 MPa
@Strain 4.70 %,
Temperature 120 °C		13470 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.97 MPa
@Strain 4.80 %,
Temperature 120 °C		13480 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 93.07 MPa
@Strain 4.90 %,
Temperature 120 °C		13500 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 93.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		13500 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 93.2 MPa
@Strain 2.40 %,
Temperature 60.0 °C		13500 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 93.3 MPa
@Strain 1.50 %,
Temperature 60.0 °C		13500 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 93.31 MPa
@Strain 2.60 %,
Temperature 80.0 °C		13530 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 93.33 MPa
@Strain 3.20 %,
Temperature 100 °C		13540 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 3.50 %,
Temperature 80.0 °C		13600 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.5 MPa
@Strain 3.60 %,
Temperature 80.0 °C		13700 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 94.55 MPa
@Strain 3.30 %,
Temperature 100 °C		13710 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 94.9 MPa
@Strain 3.70 %,
Temperature 80.0 °C		13800 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.16 MPa
@Strain 2.70 %,
Temperature 80.0 °C		13800 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 95.2 MPa
@Strain 2.50 %,
Temperature 60.0 °C		13800 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 95.3 MPa
@Strain 3.80 %,
Temperature 80.0 °C		13800 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.5 MPa
@Strain 1.70 %,
Temperature 23.0 °C		13900 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 95.6 MPa
@Strain 3.90 %,
Temperature 80.0 °C		13900 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.7 MPa
@Strain 4.00 %,
Temperature 80.0 °C		13900 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 95.78 MPa
@Strain 3.40 %,
Temperature 100 °C		13890 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 96.46 MPa
@Strain 0.900 %,
Temperature 0.000 °C		13990 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.6 MPa
@Strain 0.900 %,
Temperature -40.0 °C		14000 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.86 MPa
@Strain 3.50 %,
Temperature 100 °C		14050 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 96.96 MPa
@Strain 0.900 %,
Temperature -40.0 °C		14060 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.1 MPa
@Strain 2.60 %,
Temperature 60.0 °C		14100 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 97.12 MPa
@Strain 2.80 %,
Temperature 80.0 °C		14090 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 97.4 MPa
@Strain 1.60 %,
Temperature 60.0 °C		14100 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 97.88 MPa
@Strain 3.60 %,
Temperature 100 °C		14200 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 98.36 MPa
@Strain 1.20 %,
Temperature 0.000 °C		14270 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.77 MPa
@Strain 3.70 %,
Temperature 100 °C		14330 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 98.9 MPa
@Strain 2.70 %,
Temperature 60.0 °C		14300 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 98.97 MPa
@Strain 2.90 %,
Temperature 80.0 °C		14350 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 99.1 MPa
@Strain 1.80 %,
Temperature 23.0 °C		14400 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 99.6 MPa
@Strain 3.80 %,
Temperature 100 °C		14400 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 99.83 MPa
@Strain 1.10 %,
Temperature 23.0 °C		14480 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 100.43 MPa
@Strain 3.90 %,
Temperature 100 °C		14566 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 100.6 MPa
@Strain 3.00 %,
Temperature 80.0 °C		14590 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 100.7 MPa
@Strain 2.80 %,
Temperature 60.0 °C		14610 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 101.11 MPa
@Strain 4.00 %,
Temperature 100 °C		14665 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 101.3 MPa
@Strain 1.70 %,
Temperature 60.0 °C		14690 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 101.65 MPa
@Strain 4.10 %,
Temperature 100 °C		14743 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 102.23 MPa
@Strain 3.10 %,
Temperature 80.0 °C		14827 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 102.34 MPa
@Strain 4.20 %,
Temperature 100 °C		14843 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 102.4 MPa
@Strain 2.90 %,
Temperature 60.0 °C		14850 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 102.5 MPa
@Strain 1.90 %,
Temperature 23.0 °C		14870 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 102.83 MPa
@Strain 4.30 %,
Temperature 100 °C		14914 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 103.32 MPa
@Strain 4.40 %,
Temperature 100 °C		14985 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 103.64 MPa
@Strain 3.20 %,
Temperature 80.0 °C		15032 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 103.71 MPa
@Strain 4.50 %,
Temperature 100 °C		15042 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 103.8 MPa
@Strain 3.00 %,
Temperature 60.0 °C		15050 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 104.05 MPa
@Strain 4.60 %,
Temperature 100 °C		15091 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 104.2 MPa
@Strain 4.70 %,
Temperature 100 °C		15110 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 104.44 MPa
@Strain 4.80 %,
Temperature 100 °C		15148 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 104.59 MPa
@Strain 4.90 %,
Temperature 100 °C		15170 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 104.9 MPa
@Strain 1.80 %,
Temperature 60.0 °C		15210 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 105 MPa
@Strain 3.30 %,
Temperature 80.0 °C		15200 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 105.2 MPa
@Strain 3.10 %,
Temperature 60.0 °C		15260 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 105.32 MPa
@Strain 1.30 %,
Temperature 0.000 °C		15275 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 105.99 MPa
@Strain 2.00 %,
Temperature 23.0 °C		15373 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 106.06 MPa
@Strain 1.00 %,
Temperature 0.000 °C		15383 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 106.37 MPa
@Strain 3.40 %,
Temperature 80.0 °C		15428 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 106.4 MPa
@Strain 3.20 %,
Temperature 60.0 °C		15430 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 106.62 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15464 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.96 MPa
@Strain 1.20 %,
Temperature 23.0 °C		15513 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.06 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15528 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.4 MPa
@Strain 3.30 %,
Temperature 60.0 °C		15580 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 107.56 MPa
@Strain 3.50 %,
Temperature 80.0 °C		15600 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 108.2 MPa
@Strain 1.90 %,
Temperature 60.0 °C		15690 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 108.3 MPa
@Strain 3.40 %,
Temperature 60.0 °C		15710 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 108.7 MPa
@Strain 3.60 %,
Temperature 80.0 °C		15770 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 109.39 MPa
@Strain 2.10 %,
Temperature 23.0 °C		15866 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 109.4 MPa
@Strain 3.50 %,
Temperature 60.0 °C		15870 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 109.68 MPa
@Strain 3.70 %,
Temperature 80.0 °C		15908 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 110.2 MPa
@Strain 3.60 %,
Temperature 60.0 °C		15980 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 110.61 MPa
@Strain 3.80 %,
Temperature 80.0 °C		16043 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 110.9 MPa
@Strain 3.70 %,
Temperature 60.0 °C		16080 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 111 MPa
@Strain 2.00 %,
Temperature 60.0 °C		16100 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 111.53 MPa
@Strain 3.90 %,
Temperature 80.0 °C		16176 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 111.56 MPa
@Strain 1.40 %,
Temperature 0.000 °C		16180 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 111.6 MPa
@Strain 3.80 %,
Temperature 60.0 °C		16190 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 112.2 MPa
@Strain 3.90 %,
Temperature 60.0 °C		16270 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 112.29 MPa
@Strain 4.00 %,
Temperature 80.0 °C		16286 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 4.00 %,
Temperature 60.0 °C		16330 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 112.69 MPa
@Strain 2.20 %,
Temperature 23.0 °C		16344 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 112.89 MPa
@Strain 4.10 %,
Temperature 80.0 °C		16373 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 113.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		16480 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 113.65 MPa
@Strain 4.20 %,
Temperature 80.0 °C		16484 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 114.19 MPa
@Strain 4.30 %,
Temperature 80.0 °C		16562 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 114.28 MPa
@Strain 1.30 %,
Temperature 23.0 °C		16575 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.74 MPa
@Strain 4.40 %,
Temperature 80.0 °C		16642 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 114.96 MPa
@Strain 1.10 %,
Temperature 0.000 °C		16674 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 115.17 MPa
@Strain 4.50 %,
Temperature 80.0 °C		16704 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 115.44 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16743 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.55 MPa
@Strain 4.60 %,
Temperature 80.0 °C		16759 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 115.58 MPa
@Strain 2.30 %,
Temperature 23.0 °C		16763 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 115.72 MPa
@Strain 4.70 %,
Temperature 80.0 °C		16784 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 115.99 MPa
@Strain 4.80 %,
Temperature 80.0 °C		16823 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 116.15 MPa
@Strain 4.90 %,
Temperature 80.0 °C		16846 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 116.46 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16891 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.5 MPa
@Strain 2.20 %,
Temperature 60.0 °C		16900 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 117.78 MPa
@Strain 1.50 %,
Temperature 0.000 °C		17083 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.48 MPa
@Strain 2.40 %,
Temperature 23.0 °C		17184 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 119.5 MPa
@Strain 2.30 %,
Temperature 60.0 °C		17330 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 120.7 MPa
@Strain 2.40 %,
Temperature 60.0 °C		17510 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 121.18 MPa
@Strain 2.50 %,
Temperature 23.0 °C		17576 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 121.5 MPa
@Strain 1.40 %,
Temperature 23.0 °C		17620 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 123.11 MPa
@Strain 1.60 %,
Temperature 0.000 °C		17856 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 123.73 MPa
@Strain 1.20 %,
Temperature 0.000 °C		17946 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 123.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		17970 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 123.93 MPa
@Strain 1.20 %,
Temperature -40.0 °C		17975 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 123.98 MPa
@Strain 2.60 %,
Temperature 23.0 °C		17982 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 126.4 MPa
@Strain 2.60 %,
Temperature 60.0 °C		18330 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 126.47 MPa
@Strain 2.70 %,
Temperature 23.0 °C		18343 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 126.6 MPa
@Strain 1.20 %,
Temperature -40.0 °C		18360 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 128.03 MPa
@Strain 1.50 %,
Temperature 23.0 °C		18569 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 128.24 MPa
@Strain 1.70 %,
Temperature 0.000 °C		18600 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 128.3 MPa
@Strain 2.70 %,
Temperature 60.0 °C		18610 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 128.77 MPa
@Strain 2.80 %,
Temperature 23.0 °C		18677 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 129.8 MPa
@Strain 2.80 %,
Temperature 60.0 °C		18830 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 130.77 MPa
@Strain 2.90 %,
Temperature 23.0 °C		18967 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 131.1 MPa
@Strain 2.90 %,
Temperature 60.0 °C		19010 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 131.98 MPa
@Strain 1.30 %,
Temperature 0.000 °C		19142 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 132.1 MPa
@Strain 3.00 %,
Temperature 60.0 °C		19160 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 132.77 MPa
@Strain 3.00 %,
Temperature 23.0 °C		19257 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 132.9 MPa
@Strain 3.10 %,
Temperature 60.0 °C		19280 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 132.92 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19278 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 133.28 MPa
@Strain 1.80 %,
Temperature 0.000 °C		19331 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 133.5 MPa
@Strain 3.20 %,
Temperature 60.0 °C		19360 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 133.8 MPa
@Strain 3.30 %,
Temperature 60.0 °C		19410 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 134.57 MPa
@Strain 3.10 %,
Temperature 23.0 °C		19518 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 134.66 MPa
@Strain 1.60 %,
Temperature 23.0 °C		19531 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 136.06 MPa
@Strain 3.20 %,
Temperature 23.0 °C		19734 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 136.23 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19759 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137.26 MPa
@Strain 3.30 %,
Temperature 23.0 °C		19908 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 137.77 MPa
@Strain 1.90 %,
Temperature 0.000 °C		19982 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 138.36 MPa
@Strain 3.40 %,
Temperature 23.0 °C		20067 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 139.16 MPa
@Strain 3.50 %,
Temperature 23.0 °C		20183 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 139.81 MPa
@Strain 1.40 %,
Temperature 0.000 °C		20278 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 139.86 MPa
@Strain 3.60 %,
Temperature 23.0 °C		20285 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 140.26 MPa
@Strain 3.70 %,
Temperature 23.0 °C		20343 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 140.36 MPa
@Strain 4.00 %,
Temperature 23.0 °C		20358 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 140.46 MPa
@Strain 3.80 %,
Temperature 23.0 °C		20372 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 140.56 MPa
@Strain 3.90 %,
Temperature 23.0 °C		20387 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 140.69 MPa
@Strain 1.70 %,
Temperature 23.0 °C		20405 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 141.1 MPa
@Strain 1.40 %,
Temperature -40.0 °C		20460 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 142.18 MPa
@Strain 2.00 %,
Temperature 0.000 °C		20622 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 145.02 MPa
@Strain 1.40 %,
Temperature -40.0 °C		21033 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 146.24 MPa
@Strain 1.80 %,
Temperature 23.0 °C		21210 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 146.39 MPa
@Strain 2.10 %,
Temperature 0.000 °C		21232 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 147.61 MPa
@Strain 1.50 %,
Temperature 0.000 °C		21409 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 148.98 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21608 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 150.24 MPa
@Strain 2.20 %,
Temperature 0.000 °C		21791 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 151.67 MPa
@Strain 1.90 %,
Temperature 23.0 °C		21998 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 153.1 MPa
@Strain 1.50 %,
Temperature -40.0 °C		22210 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 153.72 MPa
@Strain 2.30 %,
Temperature 0.000 °C		22295 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 155.24 MPa
@Strain 1.60 %,
Temperature 0.000 °C		22516 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 156.55 MPa
@Strain 1.60 %,
Temperature -40.0 °C		22706 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 157.12 MPa
@Strain 2.00 %,
Temperature 23.0 °C		22788 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 157.2 MPa
@Strain 2.40 %,
Temperature 0.000 °C		22800 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 160.51 MPa
@Strain 2.50 %,
Temperature 0.000 °C		23280 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 161.69 MPa
@Strain 1.60 %,
Temperature -40.0 °C		23451 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 162.07 MPa
@Strain 2.10 %,
Temperature 23.0 °C		23506 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 162.3 MPa
@Strain 1.70 %,
Temperature 0.000 °C		23540 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 163.63 MPa
@Strain 2.60 %,
Temperature 0.000 °C		23733 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 164.13 MPa
@Strain 1.70 %,
Temperature -40.0 °C		23805 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 166.37 MPa
@Strain 2.70 %,
Temperature 0.000 °C		24130 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 166.62 MPa
@Strain 2.20 %,
Temperature 23.0 °C		24166 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 168.75 MPa
@Strain 1.80 %,
Temperature 0.000 °C		24475 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 168.94 MPa
@Strain 2.80 %,
Temperature 0.000 °C		24503 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 170.29 MPa
@Strain 1.70 %,
Temperature -40.0 °C		24699 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 170.97 MPa
@Strain 2.30 %,
Temperature 23.0 °C		24797 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 171.2 MPa
@Strain 1.80 %,
Temperature -40.0 °C		24830 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 171.51 MPa
@Strain 2.90 %,
Temperature 0.000 °C		24875 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 173.62 MPa
@Strain 3.00 %,
Temperature 0.000 °C		25181 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 174.83 MPa
@Strain 2.40 %,
Temperature 23.0 °C		25357 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 175.12 MPa
@Strain 1.90 %,
Temperature 0.000 °C		25399 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 175.54 MPa
@Strain 3.10 %,
Temperature 0.000 °C		25460 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 177.28 MPa
@Strain 3.20 %,
Temperature 0.000 °C		25712 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 178.05 MPa
@Strain 1.80 %,
Temperature -40.0 °C		25824 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 178.06 MPa
@Strain 1.90 %,
Temperature -40.0 °C		25825 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 178.57 MPa
@Strain 3.30 %,
Temperature 0.000 °C		25899 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 178.68 MPa
@Strain 2.50 %,
Temperature 23.0 °C		25915 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 179.66 MPa
@Strain 3.40 %,
Temperature 0.000 °C		26058 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 180.4 MPa
@Strain 3.50 %,
Temperature 0.000 °C		26160 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 181.51 MPa
@Strain 2.00 %,
Temperature 0.000 °C		26326 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 182.45 MPa
@Strain 2.60 %,
Temperature 23.0 °C		26462 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 184.83 MPa
@Strain 2.00 %,
Temperature -40.0 °C		26807 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 185.52 MPa
@Strain 2.70 %,
Temperature 23.0 °C		26907 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 185.7 MPa
@Strain 1.90 %,
Temperature -40.0 °C		26930 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 187.36 MPa
@Strain 2.10 %,
Temperature 0.000 °C		27174 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 188.9 MPa
@Strain 2.80 %,
Temperature 23.0 °C		27400 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 191.09 MPa
@Strain 2.10 %,
Temperature -40.0 °C		27715 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 192.07 MPa
@Strain 2.90 %,
Temperature 23.0 °C		27857 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 192.82 MPa
@Strain 2.20 %,
Temperature 0.000 °C		27966 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 193.47 MPa
@Strain 2.00 %,
Temperature -40.0 °C		28061 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 194.94 MPa
@Strain 3.00 %,
Temperature 23.0 °C		28274 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 196.86 MPa
@Strain 3.10 %,
Temperature 23.0 °C		28552 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 197.46 MPa
@Strain 2.20 %,
Temperature -40.0 °C		28639 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 197.92 MPa
@Strain 2.30 %,
Temperature 0.000 °C		28706 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 199.09 MPa
@Strain 3.20 %,
Temperature 23.0 °C		28876 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 200.72 MPa
@Strain 2.10 %,
Temperature -40.0 °C		29112 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 202.65 MPa
@Strain 2.40 %,
Temperature 0.000 °C		29392 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 203.41 MPa
@Strain 2.30 %,
Temperature -40.0 °C		29502 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 207.44 MPa
@Strain 2.50 %,
Temperature 0.000 °C		30087 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 208.48 MPa
@Strain 2.20 %,
Temperature -40.0 °C		30238 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 209.07 MPa
@Strain 2.40 %,
Temperature -40.0 °C		30323 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 211.59 MPa
@Strain 2.60 %,
Temperature 0.000 °C		30689 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 214.63 MPa
@Strain 2.50 %,
Temperature -40.0 °C		31130 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 215.23 MPa
@Strain 2.70 %,
Temperature 0.000 °C		31217 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 215.52 MPa
@Strain 2.30 %,
Temperature -40.0 °C		31259 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 218.83 MPa
@Strain 2.80 %,
Temperature 0.000 °C		31739 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 219.57 MPa
@Strain 2.60 %,
Temperature -40.0 °C		31846 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 221.96 MPa
@Strain 2.90 %,
Temperature 0.000 °C		32193 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 222.46 MPa
@Strain 2.40 %,
Temperature -40.0 °C		32265 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 224.79 MPa
@Strain 3.00 %,
Temperature 0.000 °C		32603 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 225.13 MPa
@Strain 2.70 %,
Temperature -40.0 °C		32652 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 229.39 MPa
@Strain 2.50 %,
Temperature -40.0 °C		33270 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 229.67 MPa
@Strain 2.80 %,
Temperature -40.0 °C		33311 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 235.8 MPa
@Strain 2.60 %,
Temperature -40.0 °C		34200 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 241.91 MPa
@Strain 2.70 %,
Temperature -40.0 °C		35086 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 247.92 MPa
@Strain 2.80 %,
Temperature -40.0 °C		35958 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 251.95 MPa
@Strain 2.90 %,
Temperature -40.0 °C		36542 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  8.00 GPa
@Temperature 23.0 °C		1160 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 10.5 GPa
@Temperature 23.0 °C		1520 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 275 MPa
@Temperature 23.0 °C		39900 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  8.965 GPa
@Temperature 23.0 °C		1300 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 9.30 GPa
@Temperature 23.0 °C		1350 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched 1.07 J/cm
@Temperature 23.0 °C		2.00 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
Izod Impact, Unnotched 10.65 J/cm
@Temperature 23.0 °C		19.95 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 12.0 kJ/m²
@Temperature 23.0 °C		5.71 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Charpy Impact Unnotched  8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm²
@Temperature -40.0 °C		4.28 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index  600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  65.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		36.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 65.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		36.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 83.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		46.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 83.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		46.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 137 µm/m-°C
@Temperature 55.0 - 160 °C		76.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 137 µm/m-°C
@Temperature 55.0 - 160 °C		76.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 260 °C500 °FDAM; ASTM D648
 261 °C502 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 248 °C478 °FDAM; ASTM D648
 252 °C486 °FDAM; ISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 0.710 mm		248 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 0.710 mm		266 °F
@Thickness 0.0280 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesCreep Resistance, GoodDAM
 General PurposeDAM
 LubricatedDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF33<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF33ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Industrial ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45474.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G33L BK031 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4