- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 2.2
- 缺口冲击强度: 4.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.5 % @Temperature 23.0 °C | 6.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 74 | 74 | 50%RH; ISO 2039/2 | ||
| 90 | 90 | DAM; ISO 2039/2 | |||
| Tensile Strength at Break | 67.0 MPa @Temperature 23.0 °C | 9720 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 118 MPa @Temperature 23.0 °C | 17100 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 3.70 GPa @Temperature 23.0 °C | 537 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 5.10 GPa @Temperature 23.0 °C | 740 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 5.40 J/cm² @Temperature -30.0 °C | 25.7 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 5.90 J/cm² @Temperature -30.0 °C | 28.1 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 5.90 J/cm² @Temperature 23.0 °C | 28.1 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 6.70 J/cm² @Temperature 23.0 °C | 31.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 4030 MPa @Temperature 23.0 °C | 585000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 3180 MPa @Temperature 23.0 °C | 461000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 250 V @Temperature 23.0 °C | 250 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 130 µm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 105 °C @Thickness 0.810 mm | 221 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 105 °C @Thickness 0.810 mm | 221 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66-IGF13< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Resin Identification | PA66-IGF13 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||