- 吸水率 [%]: 1.7
- 拉伸强度 [MPa]: 214.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Filler Content | 35 % | 35 % | DAM | ||
| Water Absorption | 1.7 % @Thickness 1.00 mm, Temperature 23.0 °C | 1.7 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 5.5 % @Thickness 1.00 mm, Temperature 23.0 °C | 5.5 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Thickness 2.00 mm | 0.0035 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C | 21800 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 213 MPa @Temperature 23.0 °C | 30900 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength, Yield | 214 MPa @Temperature 23.0 °C | 31000 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 5.5 % @Temperature 23.0 °C | 5.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 11.53 GPa @Temperature 23.0 °C | 1672 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | 8.40 J/cm² @Temperature 23.0 °C | 40.0 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 261 °C | 502 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| 295 °C | 563 °F | DAM; Optimum | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Heat Stabilized | DAM | |||
| Hydrolysis Resistant | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66-GF35< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Hydrolysis Resistant Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-GF35 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||