DuPont Performance Polymers Zytel® 42A NC010 Nylon 66

DuPont Performance Polymers Zytel® 42A NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 42A NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 42A NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 42A NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.2
  • 缺口冲击强度: 0.27
  • 拉伸强度 [MPa]: 32.0
  • 弯曲模量 [MPa]: 0.414
  • 硬度: 108.0
  • 热变形温度 [℃]: 200.0
  • 脆化温度 [℃]: -100.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.14 g/cc1.14 g/ccDAM; ASTM D792
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage 0.015 cm/cm
@Thickness 3.20 mm		0.015 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 606050%RH; ASTM D785
 8080DAM; ASTM D785
Hardness, Rockwell R 10810850%RH; ASTM D785
 121121DAM; ASTM D785
Tensile Strength  32.0 MPa
@Temperature 121 °C		4640 psi
@Temperature 250 °F		50%RH; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		50%RH; ASTM D638
 43.0 MPa
@Temperature 121 °C		6240 psi
@Temperature 250 °F		DAM; ASTM D638
 59.0 MPa
@Temperature 77.0 °C		8560 psi
@Temperature 171 °F		DAM; ASTM D638
 77.0 MPa
@Temperature 23.0 °C		11200 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		DAM; ASTM D638
 111 MPa
@Temperature -40.0 °C		16100 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 117 MPa
@Temperature -40.0 °C		17000 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  0.330 MPa
@Strain 0.100 %,
Temperature 150 °C		47.9 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.370 MPa
@Strain 0.100 %,
Temperature 150 °C		53.7 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.460 MPa
@Strain 0.100 %,
Temperature 120 °C		66.7 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.490 MPa
@Strain 0.100 %,
Temperature 100 °C		71.1 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 0.510 MPa
@Strain 0.100 %,
Temperature 120 °C		74.0 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.530 MPa
@Strain 0.100 %,
Temperature 100 °C		76.9 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 0.550 MPa
@Strain 0.100 %,
Temperature 80.0 °C		79.8 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 0.650 MPa
@Strain 0.200 %,
Temperature 150 °C		94.3 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.680 MPa
@Strain 0.100 %,
Temperature 60.0 °C		98.6 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.740 MPa
@Strain 0.200 %,
Temperature 150 °C		107 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.870 MPa
@Strain 0.100 %,
Temperature 80.0 °C		126 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 0.920 MPa
@Strain 0.200 %,
Temperature 120 °C		133 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.960 MPa
@Strain 0.300 %,
Temperature 150 °C		139 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.970 MPa
@Strain 0.200 %,
Temperature 120 °C		141 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.970 MPa
@Strain 0.200 %,
Temperature 100 °C		141 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.05 MPa
@Strain 0.200 %,
Temperature 100 °C		152 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.09 MPa
@Strain 0.300 %,
Temperature 150 °C		158 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.11 MPa
@Strain 0.200 %,
Temperature 80.0 °C		161 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.26 MPa
@Strain 0.100 %,
Temperature 23.0 °C		183 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.27 MPa
@Strain 0.400 %,
Temperature 150 °C		184 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.34 MPa
@Strain 0.400 %,
Temperature 150 °C		194 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.36 MPa
@Strain 0.300 %,
Temperature 120 °C		197 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.37 MPa
@Strain 0.200 %,
Temperature 60.0 °C		199 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.44 MPa
@Strain 0.300 %,
Temperature 100 °C		209 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.44 MPa
@Strain 0.500 %,
Temperature 150 °C		209 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.45 MPa
@Strain 0.300 %,
Temperature 120 °C		210 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.58 MPa
@Strain 0.300 %,
Temperature 100 °C		229 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.70 MPa
@Strain 0.500 %,
Temperature 150 °C		247 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.70 MPa
@Strain 0.300 %,
Temperature 80.0 °C		247 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.70 MPa
@Strain 0.200 %,
Temperature 80.0 °C		247 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 1.72 MPa
@Strain 0.400 %,
Temperature 120 °C		249 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.73 MPa
@Strain 0.100 %,
Temperature 60.0 °C		251 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 1.78 MPa
@Strain 0.600 %,
Temperature 150 °C		258 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.81 MPa
@Strain 0.400 %,
Temperature 100 °C		263 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.83 MPa
@Strain 0.400 %,
Temperature 120 °C		265 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.92 MPa
@Strain 0.400 %,
Temperature 100 °C		278 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.99 MPa
@Strain 0.300 %,
Temperature 60.0 °C		289 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.11 MPa
@Strain 0.600 %,
Temperature 150 °C		306 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.12 MPa
@Strain 0.400 %,
Temperature 80.0 °C		307 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.16 MPa
@Strain 0.700 %,
Temperature 150 °C		313 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.23 MPa
@Strain 0.500 %,
Temperature 120 °C		323 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.42 MPa
@Strain 0.300 %,
Temperature 80.0 °C		351 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.43 MPa
@Strain 0.500 %,
Temperature 120 °C		352 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.44 MPa
@Strain 0.400 %,
Temperature 60.0 °C		354 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.48 MPa
@Strain 0.500 %,
Temperature 100 °C		360 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.48 MPa
@Strain 0.800 %,
Temperature 150 °C		360 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.55 MPa
@Strain 0.700 %,
Temperature 150 °C		370 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.55 MPa
@Strain 0.500 %,
Temperature 100 °C		370 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.58 MPa
@Strain 0.200 %,
Temperature 23.0 °C		374 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 2.67 MPa
@Strain 0.600 %,
Temperature 120 °C		387 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.80 MPa
@Strain 0.400 %,
Temperature 80.0 °C		406 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.80 MPa
@Strain 0.500 %,
Temperature 80.0 °C		406 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.89 MPa
@Strain 0.100 %,
Temperature 23.0 °C		419 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.93 MPa
@Strain 0.900 %,
Temperature 150 °C		425 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.94 MPa
@Strain 0.600 %,
Temperature 120 °C		426 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.99 MPa
@Strain 0.600 %,
Temperature 100 °C		434 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.00 MPa
@Strain 0.800 %,
Temperature 150 °C		435 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.02 MPa
@Strain 0.100 %,
Temperature 0.000 °C		438 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 3.04 MPa
@Strain 0.100 %,
Temperature 0.000 °C		441 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 3.12 MPa
@Strain 0.700 %,
Temperature 120 °C		453 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.15 MPa
@Strain 0.100 %,
Temperature -40.0 °C		457 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.18 MPa
@Strain 1.00 %,
Temperature 150 °C		461 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.19 MPa
@Strain 0.600 %,
Temperature 100 °C		463 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.26 MPa
@Strain 0.900 %,
Temperature 150 °C		473 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.31 MPa
@Strain 0.500 %,
Temperature 60.0 °C		480 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.37 MPa
@Strain 0.600 %,
Temperature 80.0 °C		489 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.44 MPa
@Strain 0.700 %,
Temperature 100 °C		499 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.45 MPa
@Strain 0.700 %,
Temperature 120 °C		500 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.45 MPa
@Strain 0.200 %,
Temperature 60.0 °C		500 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.56 MPa
@Strain 0.800 %,
Temperature 120 °C		516 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.56 MPa
@Strain 1.10 %,
Temperature 150 °C		516 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.57 MPa
@Strain 0.700 %,
Temperature 100 °C		518 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.64 MPa
@Strain 1.00 %,
Temperature 150 °C		528 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.70 MPa
@Strain 0.800 %,
Temperature 120 °C		537 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.70 MPa
@Strain 0.500 %,
Temperature 80.0 °C		537 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.88 MPa
@Strain 0.600 %,
Temperature 60.0 °C		563 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.88 MPa
@Strain 0.300 %,
Temperature 23.0 °C		563 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.88 MPa
@Strain 0.900 %,
Temperature 120 °C		563 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.88 MPa
@Strain 1.30 %,
Temperature 150 °C		563 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.92 MPa
@Strain 0.100 %,
Temperature -40.0 °C		569 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 3.95 MPa
@Strain 0.900 %,
Temperature 100 °C		573 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.96 MPa
@Strain 0.900 %,
Temperature 120 °C		574 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.01 MPa
@Strain 0.700 %,
Temperature 80.0 °C		582 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.09 MPa
@Strain 1.10 %,
Temperature 150 °C		593 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.15 MPa
@Strain 0.800 %,
Temperature 100 °C		602 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.20 MPa
@Strain 1.40 %,
Temperature 150 °C		609 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.23 MPa
@Strain 1.00 %,
Temperature 120 °C		614 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.34 MPa
@Strain 1.00 %,
Temperature 120 °C		629 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.39 MPa
@Strain 1.00 %,
Temperature 100 °C		637 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.45 MPa
@Strain 0.800 %,
Temperature 80.0 °C		645 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.47 MPa
@Strain 0.600 %,
Temperature 80.0 °C		648 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.47 MPa
@Strain 1.20 %,
Temperature 150 °C		648 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.52 MPa
@Strain 1.50 %,
Temperature 150 °C		656 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.52 MPa
@Strain 0.700 %,
Temperature 60.0 °C		656 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.59 MPa
@Strain 0.900 %,
Temperature 100 °C		666 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.61 MPa
@Strain 0.400 %,
Temperature 23.0 °C		669 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.65 MPa
@Strain 1.10 %,
Temperature 120 °C		674 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.79 MPa
@Strain 1.30 %,
Temperature 150 °C		695 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.84 MPa
@Strain 1.60 %,
Temperature 150 °C		702 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.84 MPa
@Strain 1.10 %,
Temperature 100 °C		702 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.90 MPa
@Strain 0.700 %,
Temperature 80.0 °C		711 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.92 MPa
@Strain 1.10 %,
Temperature 120 °C		714 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.96 MPa
@Strain 0.900 %,
Temperature 80.0 °C		719 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.09 MPa
@Strain 0.800 %,
Temperature 60.0 °C		738 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.09 MPa
@Strain 1.20 %,
Temperature 120 °C		738 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.09 MPa
@Strain 1.70 %,
Temperature 150 °C		738 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.13 MPa
@Strain 0.300 %,
Temperature 60.0 °C		744 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.17 MPa
@Strain 1.00 %,
Temperature 100 °C		750 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.23 MPa
@Strain 0.800 %,
Temperature 80.0 °C		759 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.24 MPa
@Strain 1.20 %,
Temperature 120 °C		760 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.24 MPa
@Strain 1.40 %,
Temperature 150 °C		760 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.40 MPa
@Strain 1.10 %,
Temperature 100 °C		783 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.41 MPa
@Strain 1.20 %,
Temperature 100 °C		785 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.47 MPa
@Strain 1.80 %,
Temperature 150 °C		793 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.49 MPa
@Strain 1.50 %,
Temperature 150 °C		796 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 1.30 %,
Temperature 120 °C		798 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.54 MPa
@Strain 1.10 %,
Temperature 80.0 °C		804 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.61 MPa
@Strain 1.20 %,
Temperature 100 °C		814 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.70 MPa
@Strain 1.60 %,
Temperature 150 °C		827 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.73 MPa
@Strain 0.900 %,
Temperature 60.0 °C		831 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.75 MPa
@Strain 1.30 %,
Temperature 120 °C		834 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.79 MPa
@Strain 1.30 %,
Temperature 100 °C		840 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.79 MPa
@Strain 1.90 %,
Temperature 150 °C		840 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.85 MPa
@Strain 1.40 %,
Temperature 120 °C		848 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.87 MPa
@Strain 0.900 %,
Temperature 80.0 °C		851 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.94 MPa
@Strain 1.70 %,
Temperature 150 °C		862 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.04 MPa
@Strain 0.400 %,
Temperature 60.0 °C		876 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 6.04 MPa
@Strain 0.500 %,
Temperature 23.0 °C		876 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 6.05 MPa
@Strain 1.20 %,
Temperature 80.0 °C		877 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.06 MPa
@Strain 1.30 %,
Temperature 100 °C		879 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.06 MPa
@Strain 0.200 %,
Temperature 0.000 °C		879 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 6.11 MPa
@Strain 2.00 %,
Temperature 150 °C		886 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.17 MPa
@Strain 1.40 %,
Temperature 100 °C		895 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.24 MPa
@Strain 1.50 %,
Temperature 120 °C		905 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.26 MPa
@Strain 1.40 %,
Temperature 120 °C		908 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.32 MPa
@Strain 1.80 %,
Temperature 150 °C		917 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.35 MPa
@Strain 0.200 %,
Temperature 23.0 °C		921 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 6.36 MPa
@Strain 2.20 %,
Temperature 150 °C		922 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.43 MPa
@Strain 1.00 %,
Temperature 60.0 °C		933 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.55 MPa
@Strain 1.30 %,
Temperature 80.0 °C		950 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.57 MPa
@Strain 1.40 %,
Temperature 100 °C		953 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.58 MPa
@Strain 1.90 %,
Temperature 150 °C		954 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.68 MPa
@Strain 2.30 %,
Temperature 150 °C		969 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.70 MPa
@Strain 1.00 %,
Temperature 80.0 °C		972 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.71 MPa
@Strain 1.50 %,
Temperature 120 °C		973 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.71 MPa
@Strain 1.60 %,
Temperature 120 °C		973 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.75 MPa
@Strain 1.50 %,
Temperature 100 °C		979 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.83 MPa
@Strain 2.00 %,
Temperature 150 °C		991 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.84 MPa
@Strain 0.200 %,
Temperature 0.000 °C		992 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.90 MPa
@Strain 1.60 %,
Temperature 120 °C		1000 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.94 MPa
@Strain 2.40 %,
Temperature 150 °C		1010 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.94 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1010 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.00 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1020 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.03 MPa
@Strain 1.70 %,
Temperature 120 °C		1020 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.06 MPa
@Strain 1.60 %,
Temperature 100 °C		1020 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.08 MPa
@Strain 1.50 %,
Temperature 100 °C		1030 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.09 MPa
@Strain 1.70 %,
Temperature 120 °C		1030 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.12 MPa
@Strain 0.600 %,
Temperature 23.0 °C		1030 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 7.21 MPa
@Strain 2.10 %,
Temperature 150 °C		1050 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.25 MPa
@Strain 2.50 %,
Temperature 150 °C		1050 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.25 MPa
@Strain 1.80 %,
Temperature 120 °C		1050 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.32 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1060 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 7.34 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1060 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.45 MPa
@Strain 1.20 %,
Temperature 60.0 °C		1080 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.45 MPa
@Strain 2.60 %,
Temperature 150 °C		1080 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.47 MPa
@Strain 1.80 %,
Temperature 120 °C		1080 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.51 MPa
@Strain 1.80 %,
Temperature 100 °C		1090 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.53 MPa
@Strain 1.60 %,
Temperature 100 °C		1090 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.53 MPa
@Strain 2.20 %,
Temperature 150 °C		1090 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.60 MPa
@Strain 1.90 %,
Temperature 120 °C		1100 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.60 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1100 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.64 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1110 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 2.70 %,
Temperature 150 °C		1110 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.80 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1130 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.86 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1140 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 7.86 MPa
@Strain 1.90 %,
Temperature 120 °C		1140 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.91 MPa
@Strain 1.70 %,
Temperature 100 °C		1150 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.92 MPa
@Strain 2.30 %,
Temperature 150 °C		1150 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.95 MPa
@Strain 2.80 %,
Temperature 150 °C		1150 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.95 MPa
@Strain 2.00 %,
Temperature 120 °C		1150 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.02 MPa
@Strain 1.90 %,
Temperature 100 °C		1160 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.02 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1160 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.02 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1160 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.10 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1170 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.15 MPa
@Strain 3.00 %,
Temperature 150 °C		1180 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.17 MPa
@Strain 2.40 %,
Temperature 150 °C		1180 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.21 MPa
@Strain 0.700 %,
Temperature 23.0 °C		1190 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.24 MPa
@Strain 2.00 %,
Temperature 120 °C		1200 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.30 MPa
@Strain 2.10 %,
Temperature 120 °C		1200 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.34 MPa
@Strain 2.00 %,
Temperature 100 °C		1210 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.36 MPa
@Strain 1.80 %,
Temperature 100 °C		1210 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.40 MPa
@Strain 2.50 %,
Temperature 150 °C		1220 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.40 MPa
@Strain 3.10 %,
Temperature 150 °C		1220 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.46 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1230 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.56 MPa
@Strain 2.60 %,
Temperature 150 °C		1240 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.59 MPa
@Strain 1.50 %,
Temperature 60.0 °C		1250 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.60 MPa
@Strain 1.90 %,
Temperature 100 °C		1250 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.61 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1250 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.62 MPa
@Strain 2.20 %,
Temperature 120 °C		1250 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.62 MPa
@Strain 2.10 %,
Temperature 120 °C		1250 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.62 MPa
@Strain 2.70 %,
Temperature 150 °C		1250 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.72 MPa
@Strain 3.20 %,
Temperature 150 °C		1260 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.72 MPa
@Strain 2.10 %,
Temperature 100 °C		1260 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.80 MPa
@Strain 2.00 %,
Temperature 100 °C		1280 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.91 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1290 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.94 MPa
@Strain 2.20 %,
Temperature 120 °C		1300 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.94 MPa
@Strain 2.30 %,
Temperature 120 °C		1300 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.97 MPa
@Strain 3.30 %,
Temperature 150 °C		1300 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.01 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1310 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 9.07 MPa
@Strain 2.80 %,
Temperature 150 °C		1320 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.10 MPa
@Strain 1.60 %,
Temperature 60.0 °C		1320 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.16 MPa
@Strain 0.600 %,
Temperature 60.0 °C		1330 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.16 MPa
@Strain 3.40 %,
Temperature 150 °C		1330 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.19 MPa
@Strain 2.10 %,
Temperature 100 °C		1330 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.23 MPa
@Strain 2.20 %,
Temperature 100 °C		1340 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.23 MPa
@Strain 2.40 %,
Temperature 120 °C		1340 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.26 MPa
@Strain 2.90 %,
Temperature 150 °C		1340 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.35 MPa
@Strain 3.50 %,
Temperature 150 °C		1360 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.38 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1360 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.41 MPa
@Strain 0.800 %,
Temperature 23.0 °C		1360 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.42 MPa
@Strain 1.90 %,
Temperature 80.0 °C		1370 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.45 MPa
@Strain 2.50 %,
Temperature 120 °C		1370 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.45 MPa
@Strain 2.30 %,
Temperature 120 °C		1370 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.55 MPa
@Strain 2.30 %,
Temperature 100 °C		1390 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.55 MPa
@Strain 3.70 %,
Temperature 150 °C		1390 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.57 MPa
@Strain 2.20 %,
Temperature 100 °C		1390 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.60 MPa
@Strain 2.40 %,
Temperature 120 °C		1390 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.60 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1390 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.61 MPa
@Strain 1.70 %,
Temperature 60.0 °C		1390 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.64 MPa
@Strain 3.00 %,
Temperature 150 °C		1400 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.66 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1400 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 9.71 MPa
@Strain 2.50 %,
Temperature 120 °C		1410 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.74 MPa
@Strain 2.60 %,
Temperature 120 °C		1410 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.74 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1410 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.80 MPa
@Strain 3.80 %,
Temperature 150 °C		1420 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.83 MPa
@Strain 3.10 %,
Temperature 150 °C		1430 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.89 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1430 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.93 MPa
@Strain 2.40 %,
Temperature 100 °C		1440 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.95 MPa
@Strain 2.30 %,
Temperature 100 °C		1440 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.05 MPa
@Strain 3.90 %,
Temperature 150 °C		1458 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.09 MPa
@Strain 2.70 %,
Temperature 120 °C		1463 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.15 MPa
@Strain 3.20 %,
Temperature 150 °C		1472 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.16 MPa
@Strain 2.60 %,
Temperature 120 °C		1474 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.18 MPa
@Strain 1.80 %,
Temperature 60.0 °C		1476 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.25 MPa
@Strain 4.00 %,
Temperature 150 °C		1487 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.26 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1488 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 10.31 MPa
@Strain 2.10 %,
Temperature 80.0 °C		1495 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.34 MPa
@Strain 3.30 %,
Temperature 150 °C		1500 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.34 MPa
@Strain 2.80 %,
Temperature 120 °C		1500 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.34 MPa
@Strain 2.40 %,
Temperature 100 °C		1500 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.37 MPa
@Strain 2.60 %,
Temperature 100 °C		1504 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.37 MPa
@Strain 4.10 %,
Temperature 150 °C		1504 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1510 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.41 MPa
@Strain 2.70 %,
Temperature 120 °C		1510 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.5 MPa
@Strain 2.90 %,
Temperature 120 °C		1520 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.5 MPa
@Strain 3.40 %,
Temperature 150 °C		1520 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.5 MPa
@Strain 0.900 %,
Temperature 23.0 °C		1520 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 10.63 MPa
@Strain 1.90 %,
Temperature 60.0 °C		1542 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.63 MPa
@Strain 4.20 %,
Temperature 150 °C		1542 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.65 MPa
@Strain 2.50 %,
Temperature 100 °C		1545 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.66 MPa
@Strain 3.50 %,
Temperature 150 °C		1546 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.69 MPa
@Strain 2.30 %,
Temperature 80.0 °C		1550 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.7 MPa
@Strain 0.700 %,
Temperature 60.0 °C		1550 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 10.73 MPa
@Strain 3.60 %,
Temperature 150 °C		1556 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.73 MPa
@Strain 2.80 %,
Temperature 120 °C		1556 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.76 MPa
@Strain 2.70 %,
Temperature 100 °C		1561 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.82 MPa
@Strain 4.30 %,
Temperature 150 °C		1569 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.85 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1574 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.89 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1579 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 10.95 MPa
@Strain 4.50 %,
Temperature 150 °C		1588 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.95 MPa
@Strain 3.00 %,
Temperature 120 °C		1588 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.98 MPa
@Strain 3.70 %,
Temperature 150 °C		1593 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.98 MPa
@Strain 1.90 %,
Temperature 80.0 °C		1593 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.04 MPa
@Strain 2.60 %,
Temperature 100 °C		1601 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.07 MPa
@Strain 2.80 %,
Temperature 100 °C		1606 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.07 MPa
@Strain 3.10 %,
Temperature 120 °C		1606 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.08 MPa
@Strain 2.00 %,
Temperature 60.0 °C		1607 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.12 MPa
@Strain 2.90 %,
Temperature 120 °C		1613 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.14 MPa
@Strain 4.60 %,
Temperature 150 °C		1616 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.17 MPa
@Strain 3.80 %,
Temperature 150 °C		1620 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 2.70 %,
Temperature 100 °C		1620 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 2.40 %,
Temperature 80.0 °C		1620 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.3 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1640 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.3 MPa
@Strain 3.00 %,
Temperature 120 °C		1640 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.33 MPa
@Strain 2.90 %,
Temperature 100 °C		1643 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.39 MPa
@Strain 3.20 %,
Temperature 120 °C		1652 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.39 MPa
@Strain 4.70 %,
Temperature 150 °C		1652 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.42 MPa
@Strain 2.80 %,
Temperature 100 °C		1656 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.43 MPa
@Strain 3.10 %,
Temperature 120 °C		1658 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.43 MPa
@Strain 3.90 %,
Temperature 150 °C		1658 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.46 MPa
@Strain 2.50 %,
Temperature 80.0 °C		1662 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.49 MPa
@Strain 2.10 %,
Temperature 80.0 °C		1666 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.51 MPa
@Strain 1.00 %,
Temperature 23.0 °C		1669 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.52 MPa
@Strain 2.10 %,
Temperature 60.0 °C		1671 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.58 MPa
@Strain 3.30 %,
Temperature 120 °C		1680 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.65 MPa
@Strain 4.80 %,
Temperature 150 °C		1690 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.67 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1693 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 11.68 MPa
@Strain 4.00 %,
Temperature 150 °C		1694 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.74 MPa
@Strain 2.90 %,
Temperature 100 °C		1703 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.75 MPa
@Strain 3.20 %,
Temperature 120 °C		1704 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.77 MPa
@Strain 4.90 %,
Temperature 150 °C		1707 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.77 MPa
@Strain 3.00 %,
Temperature 100 °C		1707 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.81 MPa
@Strain 3.40 %,
Temperature 120 °C		1713 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.81 MPa
@Strain 4.10 %,
Temperature 150 °C		1713 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.9 MPa
@Strain 2.60 %,
Temperature 80.0 °C		1730 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.96 MPa
@Strain 3.10 %,
Temperature 100 °C		1735 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.0 MPa
@Strain 2.20 %,
Temperature 80.0 °C		1740 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.03 MPa
@Strain 2.20 %,
Temperature 60.0 °C		1745 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.06 MPa
@Strain 3.00 %,
Temperature 100 °C		1749 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.07 MPa
@Strain 3.30 %,
Temperature 120 °C		1751 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.09 MPa
@Strain 0.800 %,
Temperature 60.0 °C		1754 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 12.16 MPa
@Strain 3.50 %,
Temperature 120 °C		1764 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.19 MPa
@Strain 4.20 %,
Temperature 150 °C		1768 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 2.30 %,
Temperature 80.0 °C		1770 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.28 MPa
@Strain 2.70 %,
Temperature 80.0 °C		1781 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.32 MPa
@Strain 4.30 %,
Temperature 150 °C		1787 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.32 MPa
@Strain 5.40 %,
Temperature 150 °C		1787 psi
@Strain 5.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.33 MPa
@Strain 3.40 %,
Temperature 120 °C		1788 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.35 MPa
@Strain 3.60 %,
Temperature 120 °C		1791 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.4 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1800 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 12.44 MPa
@Strain 2.40 %,
Temperature 80.0 °C		1804 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.47 MPa
@Strain 3.20 %,
Temperature 100 °C		1809 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.48 MPa
@Strain 2.30 %,
Temperature 60.0 °C		1810 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.5 MPa
@Strain 3.10 %,
Temperature 100 °C		1810 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.5 MPa
@Strain 4.40 %,
Temperature 150 °C		1810 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.54 MPa
@Strain 3.70 %,
Temperature 120 °C		1819 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.58 MPa
@Strain 4.50 %,
Temperature 150 °C		1825 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.6 MPa
@Strain 1.10 %,
Temperature 23.0 °C		1830 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 12.65 MPa
@Strain 3.50 %,
Temperature 120 °C		1835 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.66 MPa
@Strain 2.80 %,
Temperature 80.0 °C		1836 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.7 MPa
@Strain 3.20 %,
Temperature 100 °C		1840 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.73 MPa
@Strain 3.40 %,
Temperature 100 °C		1846 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.73 MPa
@Strain 3.80 %,
Temperature 120 °C		1846 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.77 MPa
@Strain 4.60 %,
Temperature 150 °C		1852 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.78 MPa
@Strain 3.60 %,
Temperature 120 °C		1854 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.88 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1868 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 12.89 MPa
@Strain 2.50 %,
Temperature 80.0 °C		1870 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 4.70 %,
Temperature 150 °C		1870 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.95 MPa
@Strain 3.90 %,
Temperature 120 °C		1878 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.98 MPa
@Strain 3.50 %,
Temperature 100 °C		1883 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.99 MPa
@Strain 2.40 %,
Temperature 60.0 °C		1884 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.02 MPa
@Strain 3.30 %,
Temperature 100 °C		1888 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.09 MPa
@Strain 4.80 %,
Temperature 150 °C		1899 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.11 MPa
@Strain 2.90 %,
Temperature 80.0 °C		1901 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.12 MPa
@Strain 5.90 %,
Temperature 150 °C		1903 psi
@Strain 5.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.16 MPa
@Strain 3.70 %,
Temperature 120 °C		1909 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.24 MPa
@Strain 3.60 %,
Temperature 100 °C		1920 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.24 MPa
@Strain 4.00 %,
Temperature 120 °C		1920 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.24 MPa
@Strain 2.50 %,
Temperature 60.0 °C		1920 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.28 MPa
@Strain 4.90 %,
Temperature 150 °C		1926 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.3 MPa
@Strain 0.900 %,
Temperature 60.0 °C		1930 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 13.35 MPa
@Strain 3.80 %,
Temperature 120 °C		1936 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.36 MPa
@Strain 0.400 %,
Temperature -40.0 °C		1938 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 13.4 MPa
@Strain 2.60 %,
Temperature 80.0 °C		1940 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.42 MPa
@Strain 1.20 %,
Temperature 23.0 °C		1946 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.43 MPa
@Strain 3.00 %,
Temperature 80.0 °C		1948 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.46 MPa
@Strain 3.40 %,
Temperature 100 °C		1952 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.49 MPa
@Strain 4.10 %,
Temperature 120 °C		1957 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.56 MPa
@Strain 3.70 %,
Temperature 100 °C		1967 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.6 MPa
@Strain 3.50 %,
Temperature 100 °C		1970 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.6 MPa
@Strain 3.90 %,
Temperature 120 °C		1970 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.6 MPa
@Strain 2.70 %,
Temperature 80.0 °C		1970 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.62 MPa
@Strain 6.40 %,
Temperature 150 °C		1975 psi
@Strain 6.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.65 MPa
@Strain 3.60 %,
Temperature 100 °C		1980 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.68 MPa
@Strain 4.20 %,
Temperature 120 °C		1984 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.73 MPa
@Strain 4.00 %,
Temperature 120 °C		1991 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.75 MPa
@Strain 2.60 %,
Temperature 60.0 °C		1994 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.78 MPa
@Strain 2.80 %,
Temperature 80.0 °C		1999 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.78 MPa
@Strain 4.30 %,
Temperature 120 °C		1999 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.81 MPa
@Strain 3.80 %,
Temperature 100 °C		2003 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.81 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2003 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.91 MPa
@Strain 3.70 %,
Temperature 100 °C		2017 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.91 MPa
@Strain 5.40 %,
Temperature 150 °C		2017 psi
@Strain 5.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.93 MPa
@Strain 4.10 %,
Temperature 120 °C		2020 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.94 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2022 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 13.97 MPa
@Strain 4.40 %,
Temperature 120 °C		2026 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.13 MPa
@Strain 2.70 %,
Temperature 60.0 °C		2049 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.18 MPa
@Strain 4.20 %,
Temperature 120 °C		2057 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.19 MPa
@Strain 4.50 %,
Temperature 120 °C		2058 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.19 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2058 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.24 MPa
@Strain 6.90 %,
Temperature 150 °C		2065 psi
@Strain 6.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.26 MPa
@Strain 3.90 %,
Temperature 100 °C		2068 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.29 MPa
@Strain 3.80 %,
Temperature 100 °C		2073 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.29 MPa
@Strain 2.90 %,
Temperature 80.0 °C		2073 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.32 MPa
@Strain 4.60 %,
Temperature 120 °C		2077 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.38 MPa
@Strain 4.00 %,
Temperature 100 °C		2086 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.38 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2086 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 14.44 MPa
@Strain 4.30 %,
Temperature 120 °C		2094 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.45 MPa
@Strain 4.70 %,
Temperature 120 °C		2096 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.45 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2096 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.55 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2110 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.55 MPa
@Strain 3.90 %,
Temperature 100 °C		2110 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.57 MPa
@Strain 4.80 %,
Temperature 120 °C		2113 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.63 MPa
@Strain 4.40 %,
Temperature 120 °C		2122 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.64 MPa
@Strain 2.90 %,
Temperature 60.0 °C		2123 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.7 MPa
@Strain 4.20 %,
Temperature 100 °C		2130 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.73 MPa
@Strain 5.00 %,
Temperature 120 °C		2136 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.74 MPa
@Strain 4.00 %,
Temperature 100 °C		2138 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.76 MPa
@Strain 5.90 %,
Temperature 150 °C		2141 psi
@Strain 5.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.76 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2141 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.8 MPa
@Strain 4.50 %,
Temperature 120 °C		2150 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.8 MPa
@Strain 7.40 %,
Temperature 150 °C		2150 psi
@Strain 7.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.89 MPa
@Strain 1.00 %,
Temperature 60.0 °C		2160 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.95 MPa
@Strain 4.60 %,
Temperature 120 °C		2168 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.96 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2170 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.0 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2180 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.02 MPa
@Strain 4.30 %,
Temperature 100 °C		2178 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.06 MPa
@Strain 4.10 %,
Temperature 100 °C		2184 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.08 MPa
@Strain 3.60 %,
Temperature 80.0 °C		2187 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.14 MPa
@Strain 4.70 %,
Temperature 120 °C		2196 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.2 MPa
@Strain 4.20 %,
Temperature 100 °C		2200 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.2 MPa
@Strain 1.40 %,
Temperature 23.0 °C		2200 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.24 MPa
@Strain 7.90 %,
Temperature 150 °C		2210 psi
@Strain 7.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.32 MPa
@Strain 6.40 %,
Temperature 150 °C		2222 psi
@Strain 6.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.34 MPa
@Strain 4.40 %,
Temperature 100 °C		2225 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.36 MPa
@Strain 5.50 %,
Temperature 120 °C		2228 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.38 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2231 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.4 MPa
@Strain 3.10 %,
Temperature 60.0 °C		2230 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 4.80 %,
Temperature 120 °C		2230 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.44 MPa
@Strain 4.30 %,
Temperature 100 °C		2239 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.46 MPa
@Strain 3.70 %,
Temperature 80.0 °C		2242 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.53 MPa
@Strain 4.50 %,
Temperature 100 °C		2252 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.63 MPa
@Strain 4.40 %,
Temperature 100 °C		2267 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.64 MPa
@Strain 8.40 %,
Temperature 150 °C		2268 psi
@Strain 8.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.65 MPa
@Strain 4.90 %,
Temperature 120 °C		2270 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.72 MPa
@Strain 4.60 %,
Temperature 100 °C		2280 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.72 MPa
@Strain 3.20 %,
Temperature 60.0 °C		2280 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.76 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2286 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.78 MPa
@Strain 3.80 %,
Temperature 80.0 °C		2289 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.97 MPa
@Strain 1.50 %,
Temperature 23.0 °C		2316 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.97 MPa
@Strain 6.90 %,
Temperature 150 °C		2316 psi
@Strain 6.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.99 MPa
@Strain 8.90 %,
Temperature 150 °C		2319 psi
@Strain 8.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.01 MPa
@Strain 4.50 %,
Temperature 100 °C		2322 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.04 MPa
@Strain 4.70 %,
Temperature 100 °C		2326 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.04 MPa
@Strain 0.400 %,
Temperature -40.0 °C		2326 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 3.90 %,
Temperature 80.0 °C		2340 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 3.30 %,
Temperature 60.0 °C		2340 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 1.10 %,
Temperature 60.0 °C		2340 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 16.14 MPa
@Strain 4.60 %,
Temperature 100 °C		2341 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.16 MPa
@Strain 4.80 %,
Temperature 100 °C		2344 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.17 MPa
@Strain 6.00 %,
Temperature 120 °C		2345 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.21 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2351 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.32 MPa
@Strain 9.40 %,
Temperature 150 °C		2367 psi
@Strain 9.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.41 MPa
@Strain 5.40 %,
Temperature 120 °C		2380 psi
@Strain 5.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.46 MPa
@Strain 4.70 %,
Temperature 100 °C		2387 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.48 MPa
@Strain 5.00 %,
Temperature 100 °C		2390 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.48 MPa
@Strain 4.00 %,
Temperature 80.0 °C		2390 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.49 MPa
@Strain 3.40 %,
Temperature 60.0 °C		2392 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.55 MPa
@Strain 7.40 %,
Temperature 150 °C		2400 psi
@Strain 7.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.59 MPa
@Strain 4.80 %,
Temperature 100 °C		2406 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.59 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2406 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.66 MPa
@Strain 9.90 %,
Temperature 150 °C		2416 psi
@Strain 9.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.7 MPa
@Strain 3.60 %,
Temperature 80.0 °C		2420 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.73 MPa
@Strain 1.60 %,
Temperature 23.0 °C		2426 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.74 MPa
@Strain 4.10 %,
Temperature 80.0 °C		2428 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.76 MPa
@Strain 6.50 %,
Temperature 120 °C		2431 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.8 MPa
@Strain 0.600 %,
Temperature 0.000 °C		2440 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 16.85 MPa
@Strain 3.70 %,
Temperature 80.0 °C		2444 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.87 MPa
@Strain 3.50 %,
Temperature 60.0 °C		2447 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.91 MPa
@Strain 4.90 %,
Temperature 100 °C		2453 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.97 MPa
@Strain 7.90 %,
Temperature 150 °C		2461 psi
@Strain 7.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.99 MPa
@Strain 4.20 %,
Temperature 80.0 °C		2464 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.1 MPa
@Strain 3.80 %,
Temperature 80.0 °C		2480 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.19 MPa
@Strain 3.60 %,
Temperature 60.0 °C		2493 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.21 MPa
@Strain 10.9 %,
Temperature 150 °C		2496 psi
@Strain 10.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.25 MPa
@Strain 4.40 %,
Temperature 80.0 °C		2502 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.27 MPa
@Strain 5.50 %,
Temperature 100 °C		2505 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.31 MPa
@Strain 7.00 %,
Temperature 120 °C		2511 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.36 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2518 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 17.37 MPa
@Strain 8.40 %,
Temperature 150 °C		2519 psi
@Strain 8.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.42 MPa
@Strain 3.90 %,
Temperature 80.0 °C		2527 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.43 MPa
@Strain 1.20 %,
Temperature 60.0 °C		2528 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.46 MPa
@Strain 5.90 %,
Temperature 120 °C		2532 psi
@Strain 5.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.5 MPa
@Strain 3.70 %,
Temperature 60.0 °C		2540 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.56 MPa
@Strain 4.50 %,
Temperature 80.0 °C		2547 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.61 MPa
@Strain 5.40 %,
Temperature 100 °C		2554 psi
@Strain 5.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.62 MPa
@Strain 1.70 %,
Temperature 23.0 °C		2556 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.7 MPa
@Strain 7.50 %,
Temperature 120 °C		2570 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.74 MPa
@Strain 11.9 %,
Temperature 150 °C		2573 psi
@Strain 11.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.78 MPa
@Strain 8.90 %,
Temperature 150 °C		2579 psi
@Strain 8.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.8 MPa
@Strain 4.00 %,
Temperature 80.0 °C		2580 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.88 MPa
@Strain 4.60 %,
Temperature 80.0 °C		2593 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.89 MPa
@Strain 3.80 %,
Temperature 60.0 °C		2595 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.91 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2598 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 18.09 MPa
@Strain 8.00 %,
Temperature 120 °C		2624 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.14 MPa
@Strain 4.70 %,
Temperature 80.0 °C		2631 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.16 MPa
@Strain 9.40 %,
Temperature 150 °C		2634 psi
@Strain 9.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.17 MPa
@Strain 6.40 %,
Temperature 120 °C		2635 psi
@Strain 6.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.18 MPa
@Strain 12.9 %,
Temperature 150 °C		2637 psi
@Strain 12.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.19 MPa
@Strain 4.10 %,
Temperature 80.0 °C		2638 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.21 MPa
@Strain 4.00 %,
Temperature 60.0 °C		2641 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.26 MPa
@Strain 1.80 %,
Temperature 23.0 °C		2648 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.39 MPa
@Strain 4.80 %,
Temperature 80.0 °C		2667 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.44 MPa
@Strain 4.20 %,
Temperature 80.0 °C		2675 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.46 MPa
@Strain 6.00 %,
Temperature 100 °C		2677 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.46 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2677 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 18.49 MPa
@Strain 8.50 %,
Temperature 120 °C		2682 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.5 MPa
@Strain 9.90 %,
Temperature 150 °C		2680 psi
@Strain 9.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.52 MPa
@Strain 4.10 %,
Temperature 60.0 °C		2686 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.54 MPa
@Strain 13.9 %,
Temperature 150 °C		2689 psi
@Strain 13.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.6 MPa
@Strain 1.30 %,
Temperature 60.0 °C		2700 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 18.6 MPa
@Strain 4.30 %,
Temperature 80.0 °C		2700 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.71 MPa
@Strain 4.90 %,
Temperature 80.0 °C		2714 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.72 MPa
@Strain 5.90 %,
Temperature 100 °C		2715 psi
@Strain 5.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.82 MPa
@Strain 4.40 %,
Temperature 80.0 °C		2730 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.83 MPa
@Strain 9.00 %,
Temperature 120 °C		2731 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.84 MPa
@Strain 4.20 %,
Temperature 60.0 °C		2733 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.88 MPa
@Strain 14.9 %,
Temperature 150 °C		2738 psi
@Strain 14.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.89 MPa
@Strain 6.90 %,
Temperature 120 °C		2740 psi
@Strain 6.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.89 MPa
@Strain 1.90 %,
Temperature 23.0 °C		2740 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.08 MPa
@Strain 4.50 %,
Temperature 80.0 °C		2767 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.1 MPa
@Strain 10.9 %,
Temperature 150 °C		2770 psi
@Strain 10.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.16 MPa
@Strain 4.30 %,
Temperature 60.0 °C		2779 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.17 MPa
@Strain 15.9 %,
Temperature 150 °C		2780 psi
@Strain 15.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.17 MPa
@Strain 9.50 %,
Temperature 120 °C		2780 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.34 MPa
@Strain 4.60 %,
Temperature 80.0 °C		2805 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.35 MPa
@Strain 6.50 %,
Temperature 100 °C		2806 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.43 MPa
@Strain 16.9 %,
Temperature 150 °C		2818 psi
@Strain 16.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.49 MPa
@Strain 10.0 %,
Temperature 120 °C		2827 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.52 MPa
@Strain 7.40 %,
Temperature 120 °C		2831 psi
@Strain 7.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.54 MPa
@Strain 5.40 %,
Temperature 80.0 °C		2834 psi
@Strain 5.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.54 MPa
@Strain 4.40 %,
Temperature 60.0 °C		2834 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.59 MPa
@Strain 2.00 %,
Temperature 23.0 °C		2841 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.6 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2840 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.63 MPa
@Strain 6.40 %,
Temperature 100 °C		2847 psi
@Strain 6.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 19.65 MPa
@Strain 4.70 %,
Temperature 80.0 °C		2850 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.69 MPa
@Strain 17.9 %,
Temperature 150 °C		2856 psi
@Strain 17.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.74 MPa
@Strain 11.9 %,
Temperature 150 °C		2863 psi
@Strain 11.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.79 MPa
@Strain 1.40 %,
Temperature 60.0 °C		2870 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.8 MPa
@Strain 4.50 %,
Temperature 60.0 °C		2870 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.8 MPa
@Strain 4.80 %,
Temperature 80.0 °C		2870 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.89 MPa
@Strain 18.9 %,
Temperature 150 °C		2885 psi
@Strain 18.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.91 MPa
@Strain 4.90 %,
Temperature 80.0 °C		2888 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.94 MPa
@Strain 11.0 %,
Temperature 120 °C		2892 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.05 MPa
@Strain 7.00 %,
Temperature 100 °C		2908 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.08 MPa
@Strain 19.9 %,
Temperature 150 °C		2912 psi
@Strain 19.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.1 MPa
@Strain 2.20 %,
Temperature 23.0 °C		2920 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.16 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2924 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 20.16 MPa
@Strain 5.00 %,
Temperature 80.0 °C		2924 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.18 MPa
@Strain 12.9 %,
Temperature 150 °C		2927 psi
@Strain 12.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.18 MPa
@Strain 4.60 %,
Temperature 60.0 °C		2927 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.25 MPa
@Strain 7.90 %,
Temperature 120 °C		2937 psi
@Strain 7.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.28 MPa
@Strain 20.9 %,
Temperature 150 °C		2941 psi
@Strain 20.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.42 MPa
@Strain 6.90 %,
Temperature 100 °C		2962 psi
@Strain 6.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.43 MPa
@Strain 4.80 %,
Temperature 60.0 °C		2963 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.46 MPa
@Strain 21.9 %,
Temperature 150 °C		2967 psi
@Strain 21.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.5 MPa
@Strain 12.0 %,
Temperature 120 °C		2970 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.58 MPa
@Strain 13.9 %,
Temperature 150 °C		2985 psi
@Strain 13.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.62 MPa
@Strain 0.700 %,
Temperature 0.000 °C		2991 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 20.63 MPa
@Strain 22.9 %,
Temperature 150 °C		2992 psi
@Strain 22.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.67 MPa
@Strain 2.30 %,
Temperature 23.0 °C		2998 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.69 MPa
@Strain 4.90 %,
Temperature 60.0 °C		3001 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.71 MPa
@Strain 7.50 %,
Temperature 100 °C		3004 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.78 MPa
@Strain 5.90 %,
Temperature 80.0 °C		3014 psi
@Strain 5.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.82 MPa
@Strain 23.9 %,
Temperature 150 °C		3020 psi
@Strain 23.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.82 MPa
@Strain 8.40 %,
Temperature 120 °C		3020 psi
@Strain 8.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.9 MPa
@Strain 1.50 %,
Temperature 60.0 °C		3030 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.91 MPa
@Strain 24.9 %,
Temperature 150 °C		3033 psi
@Strain 24.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.93 MPa
@Strain 13.0 %,
Temperature 120 °C		3036 psi
@Strain 13.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.94 MPa
@Strain 5.00 %,
Temperature 60.0 °C		3037 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.94 MPa
@Strain 0.600 %,
Temperature 0.000 °C		3037 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 20.97 MPa
@Strain 14.9 %,
Temperature 150 °C		3041 psi
@Strain 14.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.09 MPa
@Strain 25.9 %,
Temperature 150 °C		3059 psi
@Strain 25.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.12 MPa
@Strain 5.50 %,
Temperature 80.0 °C		3063 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.21 MPa
@Strain 26.9 %,
Temperature 150 °C		3076 psi
@Strain 26.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.22 MPa
@Strain 7.40 %,
Temperature 100 °C		3078 psi
@Strain 7.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.31 MPa
@Strain 2.40 %,
Temperature 23.0 °C		3091 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.32 MPa
@Strain 27.9 %,
Temperature 150 °C		3092 psi
@Strain 27.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.33 MPa
@Strain 15.9 %,
Temperature 150 °C		3094 psi
@Strain 15.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.37 MPa
@Strain 8.90 %,
Temperature 120 °C		3099 psi
@Strain 8.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.38 MPa
@Strain 14.0 %,
Temperature 120 °C		3101 psi
@Strain 14.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.41 MPa
@Strain 8.00 %,
Temperature 100 °C		3105 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.43 MPa
@Strain 28.9 %,
Temperature 150 °C		3108 psi
@Strain 28.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.55 MPa
@Strain 29.9 %,
Temperature 150 °C		3126 psi
@Strain 29.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.62 MPa
@Strain 16.9 %,
Temperature 150 °C		3136 psi
@Strain 16.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.64 MPa
@Strain 30.9 %,
Temperature 150 °C		3139 psi
@Strain 30.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.69 MPa
@Strain 6.40 %,
Temperature 80.0 °C		3146 psi
@Strain 6.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.71 MPa
@Strain 0.600 %,
Temperature -40.0 °C		3149 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 21.74 MPa
@Strain 15.0 %,
Temperature 120 °C		3153 psi
@Strain 15.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.75 MPa
@Strain 31.9 %,
Temperature 150 °C		3155 psi
@Strain 31.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.76 MPa
@Strain 2.50 %,
Temperature 23.0 °C		3156 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.85 MPa
@Strain 32.9 %,
Temperature 150 °C		3169 psi
@Strain 32.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.85 MPa
@Strain 9.40 %,
Temperature 120 °C		3169 psi
@Strain 9.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.88 MPa
@Strain 17.9 %,
Temperature 150 °C		3173 psi
@Strain 17.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.95 MPa
@Strain 7.90 %,
Temperature 100 °C		3184 psi
@Strain 7.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.96 MPa
@Strain 33.9 %,
Temperature 150 °C		3185 psi
@Strain 33.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.96 MPa
@Strain 5.50 %,
Temperature 60.0 °C		3185 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.01 MPa
@Strain 1.60 %,
Temperature 60.0 °C		3192 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.03 MPa
@Strain 34.9 %,
Temperature 150 °C		3195 psi
@Strain 34.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.05 MPa
@Strain 8.50 %,
Temperature 100 °C		3198 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.08 MPa
@Strain 16.0 %,
Temperature 120 °C		3202 psi
@Strain 16.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.09 MPa
@Strain 35.9 %,
Temperature 150 °C		3204 psi
@Strain 35.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.13 MPa
@Strain 18.9 %,
Temperature 150 °C		3210 psi
@Strain 18.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.17 MPa
@Strain 36.9 %,
Temperature 150 °C		3215 psi
@Strain 36.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.23 MPa
@Strain 37.9 %,
Temperature 150 °C		3224 psi
@Strain 37.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.26 MPa
@Strain 2.60 %,
Temperature 23.0 °C		3229 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.29 MPa
@Strain 9.90 %,
Temperature 120 °C		3233 psi
@Strain 9.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.32 MPa
@Strain 38.9 %,
Temperature 150 °C		3237 psi
@Strain 38.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.39 MPa
@Strain 39.9 %,
Temperature 150 °C		3247 psi
@Strain 39.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.39 MPa
@Strain 19.9 %,
Temperature 150 °C		3247 psi
@Strain 19.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.4 MPa
@Strain 17.0 %,
Temperature 120 °C		3250 psi
@Strain 17.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.44 MPa
@Strain 40.9 %,
Temperature 150 °C		3255 psi
@Strain 40.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.51 MPa
@Strain 41.9 %,
Temperature 150 °C		3265 psi
@Strain 41.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.55 MPa
@Strain 8.40 %,
Temperature 100 °C		3271 psi
@Strain 8.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.57 MPa
@Strain 42.9 %,
Temperature 150 °C		3274 psi
@Strain 42.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.58 MPa
@Strain 9.00 %,
Temperature 100 °C		3275 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.59 MPa
@Strain 20.9 %,
Temperature 150 °C		3276 psi
@Strain 20.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.65 MPa
@Strain 43.9 %,
Temperature 150 °C		3285 psi
@Strain 43.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.66 MPa
@Strain 6.90 %,
Temperature 80.0 °C		3287 psi
@Strain 6.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.69 MPa
@Strain 44.9 %,
Temperature 150 °C		3291 psi
@Strain 44.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.75 MPa
@Strain 45.9 %,
Temperature 150 °C		3300 psi
@Strain 45.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.77 MPa
@Strain 2.70 %,
Temperature 23.0 °C		3303 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.79 MPa
@Strain 46.9 %,
Temperature 150 °C		3305 psi
@Strain 46.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 18.0 %,
Temperature 120 °C		3310 psi
@Strain 18.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.83 MPa
@Strain 47.9 %,
Temperature 150 °C		3311 psi
@Strain 47.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.83 MPa
@Strain 21.9 %,
Temperature 150 °C		3311 psi
@Strain 21.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.84 MPa
@Strain 6.00 %,
Temperature 80.0 °C		3313 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.86 MPa
@Strain 48.9 %,
Temperature 150 °C		3316 psi
@Strain 48.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.89 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3320 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 22.9 MPa
@Strain 50.0 %,
Temperature 150 °C		3320 psi
@Strain 50.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.91 MPa
@Strain 49.9 %,
Temperature 150 °C		3323 psi
@Strain 49.9 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.98 MPa
@Strain 10.9 %,
Temperature 120 °C		3333 psi
@Strain 10.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.99 MPa
@Strain 22.9 %,
Temperature 150 °C		3334 psi
@Strain 22.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.0 MPa
@Strain 1.70 %,
Temperature 60.0 °C		3340 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.07 MPa
@Strain 9.50 %,
Temperature 100 °C		3346 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.1 MPa
@Strain 0.600 %,
Temperature -40.0 °C		3350 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 23.18 MPa
@Strain 23.9 %,
Temperature 150 °C		3362 psi
@Strain 23.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.18 MPa
@Strain 19.0 %,
Temperature 120 °C		3362 psi
@Strain 19.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.21 MPa
@Strain 8.90 %,
Temperature 100 °C		3366 psi
@Strain 8.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.22 MPa
@Strain 2.80 %,
Temperature 23.0 °C		3368 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.28 MPa
@Strain 6.00 %,
Temperature 60.0 °C		3376 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.32 MPa
@Strain 24.9 %,
Temperature 150 °C		3382 psi
@Strain 24.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.48 MPa
@Strain 7.40 %,
Temperature 80.0 °C		3405 psi
@Strain 7.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.5 MPa
@Strain 25.9 %,
Temperature 150 °C		3410 psi
@Strain 25.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.52 MPa
@Strain 20.0 %,
Temperature 120 °C		3411 psi
@Strain 20.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.53 MPa
@Strain 10.0 %,
Temperature 100 °C		3413 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.65 MPa
@Strain 26.9 %,
Temperature 150 °C		3430 psi
@Strain 26.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.73 MPa
@Strain 9.40 %,
Temperature 100 °C		3442 psi
@Strain 9.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.73 MPa
@Strain 2.90 %,
Temperature 23.0 °C		3442 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.79 MPa
@Strain 27.9 %,
Temperature 150 °C		3450 psi
@Strain 27.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.82 MPa
@Strain 21.0 %,
Temperature 120 °C		3455 psi
@Strain 21.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.84 MPa
@Strain 11.9 %,
Temperature 120 °C		3458 psi
@Strain 11.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.86 MPa
@Strain 0.700 %,
Temperature 0.000 °C		3461 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.92 MPa
@Strain 28.9 %,
Temperature 150 °C		3469 psi
@Strain 28.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.04 MPa
@Strain 29.9 %,
Temperature 150 °C		3487 psi
@Strain 29.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.05 MPa
@Strain 1.80 %,
Temperature 60.0 °C		3488 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.16 MPa
@Strain 30.9 %,
Temperature 150 °C		3504 psi
@Strain 30.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.17 MPa
@Strain 22.0 %,
Temperature 120 °C		3506 psi
@Strain 22.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.17 MPa
@Strain 3.10 %,
Temperature 23.0 °C		3506 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.2 MPa
@Strain 6.50 %,
Temperature 80.0 °C		3510 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.25 MPa
@Strain 31.9 %,
Temperature 150 °C		3517 psi
@Strain 31.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.25 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3517 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 24.28 MPa
@Strain 7.90 %,
Temperature 80.0 °C		3522 psi
@Strain 7.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.32 MPa
@Strain 6.50 %,
Temperature 60.0 °C		3527 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.32 MPa
@Strain 11.0 %,
Temperature 100 °C		3527 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.32 MPa
@Strain 9.90 %,
Temperature 100 °C		3527 psi
@Strain 9.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.41 MPa
@Strain 32.9 %,
Temperature 150 °C		3540 psi
@Strain 32.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.44 MPa
@Strain 23.0 %,
Temperature 120 °C		3545 psi
@Strain 23.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.46 MPa
@Strain 12.9 %,
Temperature 120 °C		3548 psi
@Strain 12.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.49 MPa
@Strain 33.9 %,
Temperature 150 °C		3552 psi
@Strain 33.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.61 MPa
@Strain 34.9 %,
Temperature 150 °C		3569 psi
@Strain 34.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.62 MPa
@Strain 3.20 %,
Temperature 23.0 °C		3571 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.67 MPa
@Strain 24.0 %,
Temperature 120 °C		3578 psi
@Strain 24.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.7 MPa
@Strain 35.9 %,
Temperature 150 °C		3580 psi
@Strain 35.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.81 MPa
@Strain 36.9 %,
Temperature 150 °C		3598 psi
@Strain 36.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.83 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3601 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 24.88 MPa
@Strain 37.9 %,
Temperature 150 °C		3609 psi
@Strain 37.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.9 MPa
@Strain 25.0 %,
Temperature 120 °C		3610 psi
@Strain 25.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.9 MPa
@Strain 1.90 %,
Temperature 60.0 °C		3610 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.93 MPa
@Strain 7.00 %,
Temperature 80.0 °C		3616 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.96 MPa
@Strain 38.9 %,
Temperature 150 °C		3620 psi
@Strain 38.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.05 MPa
@Strain 13.9 %,
Temperature 120 °C		3633 psi
@Strain 13.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.06 MPa
@Strain 39.9 %,
Temperature 150 °C		3635 psi
@Strain 39.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.06 MPa
@Strain 3.30 %,
Temperature 23.0 °C		3635 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.07 MPa
@Strain 8.40 %,
Temperature 80.0 °C		3636 psi
@Strain 8.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.08 MPa
@Strain 40.9 %,
Temperature 150 °C		3638 psi
@Strain 40.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.13 MPa
@Strain 26.0 %,
Temperature 120 °C		3645 psi
@Strain 26.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.18 MPa
@Strain 41.9 %,
Temperature 150 °C		3652 psi
@Strain 41.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.19 MPa
@Strain 12.0 %,
Temperature 100 °C		3654 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.23 MPa
@Strain 10.9 %,
Temperature 100 °C		3659 psi
@Strain 10.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.25 MPa
@Strain 42.9 %,
Temperature 150 °C		3662 psi
@Strain 42.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.29 MPa
@Strain 27.0 %,
Temperature 120 °C		3668 psi
@Strain 27.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.29 MPa
@Strain 7.00 %,
Temperature 60.0 °C		3668 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.35 MPa
@Strain 43.9 %,
Temperature 150 °C		3677 psi
@Strain 43.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.4 MPa
@Strain 44.9 %,
Temperature 150 °C		3680 psi
@Strain 44.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.43 MPa
@Strain 28.0 %,
Temperature 120 °C		3688 psi
@Strain 28.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.44 MPa
@Strain 3.40 %,
Temperature 23.0 °C		3690 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.46 MPa
@Strain 45.9 %,
Temperature 150 °C		3693 psi
@Strain 45.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.5 MPa
@Strain 46.9 %,
Temperature 150 °C		3700 psi
@Strain 46.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.54 MPa
@Strain 14.9 %,
Temperature 120 °C		3704 psi
@Strain 14.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.55 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3706 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.58 MPa
@Strain 29.0 %,
Temperature 120 °C		3710 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.59 MPa
@Strain 7.50 %,
Temperature 80.0 °C		3712 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.59 MPa
@Strain 47.9 %,
Temperature 150 °C		3712 psi
@Strain 47.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.63 MPa
@Strain 8.90 %,
Temperature 80.0 °C		3717 psi
@Strain 8.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.64 MPa
@Strain 48.9 %,
Temperature 150 °C		3719 psi
@Strain 48.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.69 MPa
@Strain 49.9 %,
Temperature 150 °C		3726 psi
@Strain 49.9 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.7 MPa
@Strain 50.0 %,
Temperature 150 °C		3730 psi
@Strain 50.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.73 MPa
@Strain 30.0 %,
Temperature 120 °C		3732 psi
@Strain 30.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.77 MPa
@Strain 13.0 %,
Temperature 100 °C		3738 psi
@Strain 13.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.77 MPa
@Strain 2.00 %,
Temperature 60.0 °C		3738 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.83 MPa
@Strain 3.50 %,
Temperature 23.0 °C		3746 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.88 MPa
@Strain 31.0 %,
Temperature 120 °C		3754 psi
@Strain 31.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.99 MPa
@Strain 32.0 %,
Temperature 120 °C		3770 psi
@Strain 32.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.04 MPa
@Strain 15.9 %,
Temperature 120 °C		3777 psi
@Strain 15.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.13 MPa
@Strain 33.0 %,
Temperature 120 °C		3790 psi
@Strain 33.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.21 MPa
@Strain 11.9 %,
Temperature 100 °C		3801 psi
@Strain 11.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.21 MPa
@Strain 3.60 %,
Temperature 23.0 °C		3801 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.23 MPa
@Strain 34.0 %,
Temperature 120 °C		3804 psi
@Strain 34.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.28 MPa
@Strain 7.50 %,
Temperature 60.0 °C		3812 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.28 MPa
@Strain 9.40 %,
Temperature 80.0 °C		3812 psi
@Strain 9.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.31 MPa
@Strain 14.0 %,
Temperature 100 °C		3816 psi
@Strain 14.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.31 MPa
@Strain 8.00 %,
Temperature 80.0 °C		3816 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.31 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3816 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 26.35 MPa
@Strain 35.0 %,
Temperature 120 °C		3822 psi
@Strain 35.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.39 MPa
@Strain 16.9 %,
Temperature 120 °C		3828 psi
@Strain 16.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.44 MPa
@Strain 36.0 %,
Temperature 120 °C		3835 psi
@Strain 36.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 2.10 %,
Temperature 60.0 °C		3840 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.54 MPa
@Strain 37.0 %,
Temperature 120 °C		3849 psi
@Strain 37.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.62 MPa
@Strain 38.0 %,
Temperature 120 °C		3861 psi
@Strain 38.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.65 MPa
@Strain 3.80 %,
Temperature 23.0 °C		3865 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.71 MPa
@Strain 39.0 %,
Temperature 120 °C		3874 psi
@Strain 39.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.74 MPa
@Strain 17.9 %,
Temperature 120 °C		3878 psi
@Strain 17.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.75 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3880 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 26.77 MPa
@Strain 15.0 %,
Temperature 100 °C		3883 psi
@Strain 15.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.79 MPa
@Strain 40.0 %,
Temperature 120 °C		3886 psi
@Strain 40.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.87 MPa
@Strain 41.0 %,
Temperature 120 °C		3897 psi
@Strain 41.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.92 MPa
@Strain 0.900 %,
Temperature 0.000 °C		3904 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 26.94 MPa
@Strain 42.0 %,
Temperature 120 °C		3907 psi
@Strain 42.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.94 MPa
@Strain 9.90 %,
Temperature 80.0 °C		3907 psi
@Strain 9.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.97 MPa
@Strain 3.90 %,
Temperature 23.0 °C		3912 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.0 MPa
@Strain 12.9 %,
Temperature 100 °C		3920 psi
@Strain 12.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.01 MPa
@Strain 8.50 %,
Temperature 80.0 °C		3917 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.02 MPa
@Strain 43.0 %,
Temperature 120 °C		3919 psi
@Strain 43.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.09 MPa
@Strain 44.0 %,
Temperature 120 °C		3929 psi
@Strain 44.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.11 MPa
@Strain 18.9 %,
Temperature 120 °C		3932 psi
@Strain 18.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.15 MPa
@Strain 8.00 %,
Temperature 60.0 °C		3938 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.16 MPa
@Strain 45.0 %,
Temperature 120 °C		3939 psi
@Strain 45.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.17 MPa
@Strain 16.0 %,
Temperature 100 °C		3941 psi
@Strain 16.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.2 MPa
@Strain 46.0 %,
Temperature 120 °C		3950 psi
@Strain 46.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.26 MPa
@Strain 47.0 %,
Temperature 120 °C		3954 psi
@Strain 47.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.3 MPa
@Strain 48.0 %,
Temperature 120 °C		3960 psi
@Strain 48.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.35 MPa
@Strain 4.00 %,
Temperature 23.0 °C		3967 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.36 MPa
@Strain 2.20 %,
Temperature 60.0 °C		3968 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.37 MPa
@Strain 49.0 %,
Temperature 120 °C		3970 psi
@Strain 49.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.41 MPa
@Strain 19.9 %,
Temperature 120 °C		3975 psi
@Strain 19.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.42 MPa
@Strain 50.0 %,
Temperature 120 °C		3977 psi
@Strain 50.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.56 MPa
@Strain 17.0 %,
Temperature 100 °C		3997 psi
@Strain 17.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.61 MPa
@Strain 9.00 %,
Temperature 80.0 °C		4004 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.64 MPa
@Strain 13.9 %,
Temperature 100 °C		4009 psi
@Strain 13.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.67 MPa
@Strain 4.10 %,
Temperature 23.0 °C		4013 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.69 MPa
@Strain 20.9 %,
Temperature 120 °C		4016 psi
@Strain 20.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.83 MPa
@Strain 10.9 %,
Temperature 80.0 °C		4036 psi
@Strain 10.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.85 MPa
@Strain 8.50 %,
Temperature 60.0 °C		4039 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.86 MPa
@Strain 18.0 %,
Temperature 100 °C		4041 psi
@Strain 18.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.95 MPa
@Strain 0.800 %,
Temperature -40.0 °C		4054 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 27.96 MPa
@Strain 21.9 %,
Temperature 120 °C		4055 psi
@Strain 21.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.0 MPa
@Strain 2.30 %,
Temperature 60.0 °C		4060 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.05 MPa
@Strain 4.20 %,
Temperature 23.0 °C		4068 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.15 MPa
@Strain 19.0 %,
Temperature 100 °C		4083 psi
@Strain 19.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.19 MPa
@Strain 22.9 %,
Temperature 120 °C		4089 psi
@Strain 22.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.23 MPa
@Strain 9.50 %,
Temperature 80.0 °C		4094 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.27 MPa
@Strain 14.9 %,
Temperature 100 °C		4100 psi
@Strain 14.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.28 MPa
@Strain 0.900 %,
Temperature 23.0 °C		4102 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.43 MPa
@Strain 4.30 %,
Temperature 23.0 °C		4123 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.43 MPa
@Strain 20.0 %,
Temperature 100 °C		4123 psi
@Strain 20.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.43 MPa
@Strain 23.9 %,
Temperature 120 °C		4123 psi
@Strain 23.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.61 MPa
@Strain 9.00 %,
Temperature 60.0 °C		4150 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.67 MPa
@Strain 24.9 %,
Temperature 120 °C		4158 psi
@Strain 24.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.67 MPa
@Strain 21.0 %,
Temperature 100 °C		4158 psi
@Strain 21.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.69 MPa
@Strain 2.40 %,
Temperature 60.0 °C		4161 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.79 MPa
@Strain 11.9 %,
Temperature 80.0 °C		4176 psi
@Strain 11.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.82 MPa
@Strain 22.0 %,
Temperature 100 °C		4180 psi
@Strain 22.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.83 MPa
@Strain 10.0 %,
Temperature 80.0 °C		4181 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.84 MPa
@Strain 15.9 %,
Temperature 100 °C		4183 psi
@Strain 15.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.86 MPa
@Strain 25.9 %,
Temperature 120 °C		4186 psi
@Strain 25.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.88 MPa
@Strain 4.40 %,
Temperature 23.0 °C		4189 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.01 MPa
@Strain 4.60 %,
Temperature 23.0 °C		4208 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.05 MPa
@Strain 26.9 %,
Temperature 120 °C		4213 psi
@Strain 26.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.06 MPa
@Strain 23.0 %,
Temperature 100 °C		4215 psi
@Strain 23.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 27.9 %,
Temperature 120 °C		4240 psi
@Strain 27.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.21 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4237 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 29.23 MPa
@Strain 24.0 %,
Temperature 100 °C		4239 psi
@Strain 24.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.34 MPa
@Strain 16.9 %,
Temperature 100 °C		4255 psi
@Strain 16.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.37 MPa
@Strain 25.0 %,
Temperature 100 °C		4260 psi
@Strain 25.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.38 MPa
@Strain 9.50 %,
Temperature 60.0 °C		4261 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.39 MPa
@Strain 28.9 %,
Temperature 120 °C		4263 psi
@Strain 28.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.4 MPa
@Strain 2.50 %,
Temperature 60.0 °C		4260 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.45 MPa
@Strain 4.70 %,
Temperature 23.0 °C		4271 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.5 MPa
@Strain 29.9 %,
Temperature 120 °C		4280 psi
@Strain 29.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.51 MPa
@Strain 26.0 %,
Temperature 100 °C		4280 psi
@Strain 26.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.54 MPa
@Strain 12.9 %,
Temperature 80.0 °C		4284 psi
@Strain 12.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.62 MPa
@Strain 27.0 %,
Temperature 100 °C		4296 psi
@Strain 27.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.68 MPa
@Strain 30.9 %,
Temperature 120 °C		4305 psi
@Strain 30.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.75 MPa
@Strain 28.0 %,
Temperature 100 °C		4315 psi
@Strain 28.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.75 MPa
@Strain 17.9 %,
Temperature 100 °C		4315 psi
@Strain 17.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.77 MPa
@Strain 11.0 %,
Temperature 80.0 °C		4318 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.77 MPa
@Strain 4.80 %,
Temperature 23.0 °C		4318 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.84 MPa
@Strain 2.60 %,
Temperature 60.0 °C		4328 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.85 MPa
@Strain 29.0 %,
Temperature 100 °C		4329 psi
@Strain 29.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.85 MPa
@Strain 31.9 %,
Temperature 120 °C		4329 psi
@Strain 31.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.93 MPa
@Strain 32.9 %,
Temperature 120 °C		4341 psi
@Strain 32.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.93 MPa
@Strain 30.0 %,
Temperature 100 °C		4341 psi
@Strain 30.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.97 MPa
@Strain 10.0 %,
Temperature 60.0 °C		4347 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.99 MPa
@Strain 0.900 %,
Temperature 0.000 °C		4350 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 30.02 MPa
@Strain 4.90 %,
Temperature 23.0 °C		4354 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.03 MPa
@Strain 31.0 %,
Temperature 100 °C		4355 psi
@Strain 31.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.08 MPa
@Strain 33.9 %,
Temperature 120 °C		4363 psi
@Strain 33.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.1 MPa
@Strain 32.0 %,
Temperature 100 °C		4370 psi
@Strain 32.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.17 MPa
@Strain 33.0 %,
Temperature 100 °C		4376 psi
@Strain 33.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.2 MPa
@Strain 18.9 %,
Temperature 100 °C		4380 psi
@Strain 18.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.22 MPa
@Strain 34.9 %,
Temperature 120 °C		4383 psi
@Strain 34.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.24 MPa
@Strain 13.9 %,
Temperature 80.0 °C		4386 psi
@Strain 13.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.25 MPa
@Strain 34.0 %,
Temperature 100 °C		4387 psi
@Strain 34.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.3 MPa
@Strain 2.70 %,
Temperature 60.0 °C		4390 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.31 MPa
@Strain 35.0 %,
Temperature 100 °C		4396 psi
@Strain 35.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.33 MPa
@Strain 36.0 %,
Temperature 100 °C		4399 psi
@Strain 36.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.33 MPa
@Strain 35.9 %,
Temperature 120 °C		4399 psi
@Strain 35.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.42 MPa
@Strain 37.0 %,
Temperature 100 °C		4412 psi
@Strain 37.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.42 MPa
@Strain 0.800 %,
Temperature -40.0 °C		4412 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 30.43 MPa
@Strain 36.9 %,
Temperature 120 °C		4414 psi
@Strain 36.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.47 MPa
@Strain 38.0 %,
Temperature 100 °C		4419 psi
@Strain 38.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 39.0 %,
Temperature 100 °C		4420 psi
@Strain 39.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.53 MPa
@Strain 40.0 %,
Temperature 100 °C		4428 psi
@Strain 40.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.56 MPa
@Strain 37.9 %,
Temperature 120 °C		4432 psi
@Strain 37.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.57 MPa
@Strain 41.0 %,
Temperature 100 °C		4434 psi
@Strain 41.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.57 MPa
@Strain 19.9 %,
Temperature 100 °C		4434 psi
@Strain 19.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.59 MPa
@Strain 42.0 %,
Temperature 100 °C		4437 psi
@Strain 42.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.63 MPa
@Strain 43.0 %,
Temperature 100 °C		4443 psi
@Strain 43.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.63 MPa
@Strain 44.0 %,
Temperature 100 °C		4443 psi
@Strain 44.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.66 MPa
@Strain 38.9 %,
Temperature 120 °C		4447 psi
@Strain 38.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.67 MPa
@Strain 45.0 %,
Temperature 100 °C		4448 psi
@Strain 45.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.7 MPa
@Strain 2.80 %,
Temperature 60.0 °C		4450 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.73 MPa
@Strain 46.0 %,
Temperature 100 °C		4457 psi
@Strain 46.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.73 MPa
@Strain 47.0 %,
Temperature 100 °C		4457 psi
@Strain 47.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.74 MPa
@Strain 48.0 %,
Temperature 100 °C		4458 psi
@Strain 48.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.77 MPa
@Strain 49.0 %,
Temperature 100 °C		4463 psi
@Strain 49.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.77 MPa
@Strain 39.9 %,
Temperature 120 °C		4463 psi
@Strain 39.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.78 MPa
@Strain 50.0 %,
Temperature 100 °C		4464 psi
@Strain 50.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.85 MPa
@Strain 14.9 %,
Temperature 80.0 °C		4474 psi
@Strain 14.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.86 MPa
@Strain 2.90 %,
Temperature 60.0 °C		4476 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.87 MPa
@Strain 40.9 %,
Temperature 120 °C		4477 psi
@Strain 40.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.88 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4479 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.89 MPa
@Strain 12.0 %,
Temperature 80.0 °C		4480 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.9 MPa
@Strain 20.9 %,
Temperature 100 °C		4480 psi
@Strain 20.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.92 MPa
@Strain 41.9 %,
Temperature 120 °C		4485 psi
@Strain 41.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.99 MPa
@Strain 11.0 %,
Temperature 60.0 °C		4495 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.05 MPa
@Strain 42.9 %,
Temperature 120 °C		4503 psi
@Strain 42.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.1 MPa
@Strain 43.9 %,
Temperature 120 °C		4510 psi
@Strain 43.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.15 MPa
@Strain 5.40 %,
Temperature 23.0 °C		4518 psi
@Strain 5.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.19 MPa
@Strain 21.9 %,
Temperature 100 °C		4524 psi
@Strain 21.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.2 MPa
@Strain 44.9 %,
Temperature 120 °C		4530 psi
@Strain 44.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.22 MPa
@Strain 45.9 %,
Temperature 120 °C		4528 psi
@Strain 45.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.36 MPa
@Strain 46.9 %,
Temperature 120 °C		4548 psi
@Strain 46.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.38 MPa
@Strain 15.9 %,
Temperature 80.0 °C		4551 psi
@Strain 15.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 47.9 %,
Temperature 120 °C		4550 psi
@Strain 47.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.47 MPa
@Strain 48.9 %,
Temperature 120 °C		4564 psi
@Strain 48.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 50.0 %,
Temperature 120 °C		4570 psi
@Strain 50.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 3.00 %,
Temperature 60.0 °C		4570 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 1.10 %,
Temperature 0.000 °C		4570 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 31.51 MPa
@Strain 22.9 %,
Temperature 100 °C		4570 psi
@Strain 22.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.54 MPa
@Strain 49.9 %,
Temperature 120 °C		4574 psi
@Strain 49.9 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.7 MPa
@Strain 0.900 %,
Temperature -40.0 °C		4600 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 31.77 MPa
@Strain 23.9 %,
Temperature 100 °C		4608 psi
@Strain 23.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.77 MPa
@Strain 16.9 %,
Temperature 80.0 °C		4608 psi
@Strain 16.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.84 MPa
@Strain 13.0 %,
Temperature 80.0 °C		4618 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.0 MPa
@Strain 3.10 %,
Temperature 60.0 °C		4640 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.03 MPa
@Strain 24.9 %,
Temperature 100 °C		4646 psi
@Strain 24.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.16 MPa
@Strain 12.0 %,
Temperature 60.0 °C		4664 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.16 MPa
@Strain 17.9 %,
Temperature 80.0 °C		4664 psi
@Strain 17.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.25 MPa
@Strain 25.9 %,
Temperature 100 °C		4677 psi
@Strain 25.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 3.20 %,
Temperature 60.0 °C		4680 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.47 MPa
@Strain 26.9 %,
Temperature 100 °C		4709 psi
@Strain 26.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.5 MPa
@Strain 18.9 %,
Temperature 80.0 °C		4710 psi
@Strain 18.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.57 MPa
@Strain 3.30 %,
Temperature 60.0 °C		4724 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.62 MPa
@Strain 5.90 %,
Temperature 23.0 °C		4731 psi
@Strain 5.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.64 MPa
@Strain 14.0 %,
Temperature 80.0 °C		4734 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.66 MPa
@Strain 27.9 %,
Temperature 100 °C		4737 psi
@Strain 27.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.8 MPa
@Strain 3.40 %,
Temperature 60.0 °C		4760 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.8 MPa
@Strain 19.9 %,
Temperature 80.0 °C		4760 psi
@Strain 19.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.86 MPa
@Strain 28.9 %,
Temperature 100 °C		4766 psi
@Strain 28.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 3.50 %,
Temperature 60.0 °C		4770 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.01 MPa
@Strain 29.9 %,
Temperature 100 °C		4788 psi
@Strain 29.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.04 MPa
@Strain 13.0 %,
Temperature 60.0 °C		4792 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.08 MPa
@Strain 3.60 %,
Temperature 60.0 °C		4798 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.08 MPa
@Strain 20.9 %,
Temperature 80.0 °C		4798 psi
@Strain 20.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.14 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4807 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 33.21 MPa
@Strain 30.9 %,
Temperature 100 °C		4817 psi
@Strain 30.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.27 MPa
@Strain 21.9 %,
Temperature 80.0 °C		4825 psi
@Strain 21.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 3.70 %,
Temperature 60.0 °C		4830 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.3 MPa
@Strain 31.9 %,
Temperature 100 °C		4830 psi
@Strain 31.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.45 MPa
@Strain 15.0 %,
Temperature 80.0 °C		4852 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.5 MPa
@Strain 32.9 %,
Temperature 100 °C		4860 psi
@Strain 32.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.5 MPa
@Strain 22.9 %,
Temperature 80.0 °C		4860 psi
@Strain 22.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.54 MPa
@Strain 1.20 %,
Temperature 0.000 °C		4865 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.59 MPa
@Strain 3.80 %,
Temperature 60.0 °C		4872 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.64 MPa
@Strain 33.9 %,
Temperature 100 °C		4879 psi
@Strain 33.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.66 MPa
@Strain 23.9 %,
Temperature 80.0 °C		4882 psi
@Strain 23.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.7 MPa
@Strain 3.90 %,
Temperature 60.0 °C		4890 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.74 MPa
@Strain 14.0 %,
Temperature 60.0 °C		4894 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.74 MPa
@Strain 34.9 %,
Temperature 100 °C		4894 psi
@Strain 34.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.77 MPa
@Strain 24.9 %,
Temperature 80.0 °C		4898 psi
@Strain 24.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.8 MPa
@Strain 4.00 %,
Temperature 60.0 °C		4900 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.85 MPa
@Strain 6.40 %,
Temperature 23.0 °C		4910 psi
@Strain 6.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.92 MPa
@Strain 35.9 %,
Temperature 100 °C		4920 psi
@Strain 35.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.98 MPa
@Strain 25.9 %,
Temperature 80.0 °C		4928 psi
@Strain 25.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.04 MPa
@Strain 4.10 %,
Temperature 60.0 °C		4937 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.04 MPa
@Strain 36.9 %,
Temperature 100 °C		4937 psi
@Strain 36.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.05 MPa
@Strain 26.9 %,
Temperature 80.0 °C		4939 psi
@Strain 26.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.09 MPa
@Strain 16.0 %,
Temperature 80.0 °C		4944 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.14 MPa
@Strain 37.9 %,
Temperature 100 °C		4952 psi
@Strain 37.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.18 MPa
@Strain 27.9 %,
Temperature 80.0 °C		4957 psi
@Strain 27.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.23 MPa
@Strain 38.9 %,
Temperature 100 °C		4965 psi
@Strain 38.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.27 MPa
@Strain 28.9 %,
Temperature 80.0 °C		4970 psi
@Strain 28.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.3 MPa
@Strain 4.20 %,
Temperature 60.0 °C		4970 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.33 MPa
@Strain 0.900 %,
Temperature -40.0 °C		4979 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 34.36 MPa
@Strain 39.9 %,
Temperature 100 °C		4984 psi
@Strain 39.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.37 MPa
@Strain 29.9 %,
Temperature 80.0 °C		4985 psi
@Strain 29.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.44 MPa
@Strain 30.9 %,
Temperature 80.0 °C		4995 psi
@Strain 30.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.44 MPa
@Strain 40.9 %,
Temperature 100 °C		4995 psi
@Strain 40.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.47 MPa
@Strain 31.9 %,
Temperature 80.0 °C		4999 psi
@Strain 31.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.48 MPa
@Strain 15.0 %,
Temperature 60.0 °C		5001 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.48 MPa
@Strain 41.9 %,
Temperature 100 °C		5001 psi
@Strain 41.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.54 MPa
@Strain 4.30 %,
Temperature 60.0 °C		5010 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.55 MPa
@Strain 32.9 %,
Temperature 80.0 °C		5011 psi
@Strain 32.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.57 MPa
@Strain 33.9 %,
Temperature 80.0 °C		5014 psi
@Strain 33.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 4.40 %,
Temperature 60.0 °C		5020 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.6 MPa
@Strain 42.9 %,
Temperature 100 °C		5020 psi
@Strain 42.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.62 MPa
@Strain 34.9 %,
Temperature 80.0 °C		5021 psi
@Strain 34.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.63 MPa
@Strain 43.9 %,
Temperature 100 °C		5023 psi
@Strain 43.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.65 MPa
@Strain 35.9 %,
Temperature 80.0 °C		5026 psi
@Strain 35.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.65 MPa
@Strain 36.9 %,
Temperature 80.0 °C		5026 psi
@Strain 36.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.7 MPa
@Strain 37.9 %,
Temperature 80.0 °C		5030 psi
@Strain 37.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.7 MPa
@Strain 4.50 %,
Temperature 60.0 °C		5030 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.72 MPa
@Strain 38.9 %,
Temperature 80.0 °C		5036 psi
@Strain 38.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.74 MPa
@Strain 39.9 %,
Temperature 80.0 °C		5039 psi
@Strain 39.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.74 MPa
@Strain 40.9 %,
Temperature 80.0 °C		5039 psi
@Strain 40.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.74 MPa
@Strain 17.0 %,
Temperature 80.0 °C		5039 psi
@Strain 17.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.76 MPa
@Strain 44.9 %,
Temperature 80.0 °C		5042 psi
@Strain 44.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.76 MPa
@Strain 1.10 %,
Temperature 23.0 °C		5042 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 34.77 MPa
@Strain 41.9 %,
Temperature 80.0 °C		5043 psi
@Strain 41.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.77 MPa
@Strain 42.9 %,
Temperature 80.0 °C		5043 psi
@Strain 42.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.77 MPa
@Strain 47.9 %,
Temperature 80.0 °C		5043 psi
@Strain 47.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.77 MPa
@Strain 44.9 %,
Temperature 100 °C		5043 psi
@Strain 44.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.78 MPa
@Strain 43.9 %,
Temperature 80.0 °C		5044 psi
@Strain 43.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.78 MPa
@Strain 45.9 %,
Temperature 80.0 °C		5044 psi
@Strain 45.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 50.0 %,
Temperature 80.0 °C		5050 psi
@Strain 50.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 48.9 %,
Temperature 80.0 °C		5050 psi
@Strain 48.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 46.9 %,
Temperature 80.0 °C		5050 psi
@Strain 46.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.83 MPa
@Strain 49.9 %,
Temperature 80.0 °C		5052 psi
@Strain 49.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.84 MPa
@Strain 45.9 %,
Temperature 100 °C		5053 psi
@Strain 45.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.86 MPa
@Strain 4.60 %,
Temperature 60.0 °C		5056 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.94 MPa
@Strain 46.9 %,
Temperature 100 °C		5068 psi
@Strain 46.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.95 MPa
@Strain 6.90 %,
Temperature 23.0 °C		5069 psi
@Strain 6.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.98 MPa
@Strain 47.9 %,
Temperature 100 °C		5073 psi
@Strain 47.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.03 MPa
@Strain 48.9 %,
Temperature 100 °C		5081 psi
@Strain 48.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.06 MPa
@Strain 16.0 %,
Temperature 60.0 °C		5085 psi
@Strain 16.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.1 MPa
@Strain 50.0 %,
Temperature 100 °C		5090 psi
@Strain 50.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.11 MPa
@Strain 49.9 %,
Temperature 100 °C		5092 psi
@Strain 49.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.2 MPa
@Strain 4.70 %,
Temperature 60.0 °C		5110 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.39 MPa
@Strain 1.00 %,
Temperature -40.0 °C		5133 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 35.44 MPa
@Strain 4.80 %,
Temperature 60.0 °C		5140 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.56 MPa
@Strain 17.0 %,
Temperature 60.0 °C		5158 psi
@Strain 17.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.64 MPa
@Strain 1.30 %,
Temperature 0.000 °C		5169 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 35.97 MPa
@Strain 7.40 %,
Temperature 23.0 °C		5217 psi
@Strain 7.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.0 MPa
@Strain 18.0 %,
Temperature 60.0 °C		5220 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.05 MPa
@Strain 5.30 %,
Temperature 60.0 °C		5229 psi
@Strain 5.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.13 MPa
@Strain 18.0 %,
Temperature 80.0 °C		5240 psi
@Strain 18.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.39 MPa
@Strain 19.0 %,
Temperature 60.0 °C		5278 psi
@Strain 19.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.5 MPa
@Strain 1.10 %,
Temperature 0.000 °C		5290 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 36.71 MPa
@Strain 20.0 %,
Temperature 60.0 °C		5324 psi
@Strain 20.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.95 MPa
@Strain 7.90 %,
Temperature 23.0 °C		5359 psi
@Strain 7.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.99 MPa
@Strain 5.80 %,
Temperature 60.0 °C		5365 psi
@Strain 5.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.01 MPa
@Strain 21.0 %,
Temperature 60.0 °C		5368 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.28 MPa
@Strain 19.0 %,
Temperature 80.0 °C		5407 psi
@Strain 19.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.29 MPa
@Strain 1.00 %,
Temperature -40.0 °C		5408 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.33 MPa
@Strain 22.0 %,
Temperature 60.0 °C		5414 psi
@Strain 22.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.51 MPa
@Strain 23.0 %,
Temperature 60.0 °C		5440 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.61 MPa
@Strain 1.40 %,
Temperature 0.000 °C		5455 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.67 MPa
@Strain 24.0 %,
Temperature 60.0 °C		5464 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.69 MPa
@Strain 6.30 %,
Temperature 60.0 °C		5466 psi
@Strain 6.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.73 MPa
@Strain 20.0 %,
Temperature 80.0 °C		5472 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.86 MPa
@Strain 25.0 %,
Temperature 60.0 °C		5491 psi
@Strain 25.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.98 MPa
@Strain 8.40 %,
Temperature 23.0 °C		5509 psi
@Strain 8.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.0 MPa
@Strain 26.0 %,
Temperature 60.0 °C		5510 psi
@Strain 26.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.14 MPa
@Strain 27.0 %,
Temperature 60.0 °C		5532 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.16 MPa
@Strain 21.0 %,
Temperature 80.0 °C		5535 psi
@Strain 21.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.23 MPa
@Strain 1.10 %,
Temperature -40.0 °C		5545 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 38.24 MPa
@Strain 28.0 %,
Temperature 60.0 °C		5546 psi
@Strain 28.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.33 MPa
@Strain 29.0 %,
Temperature 60.0 °C		5559 psi
@Strain 29.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.36 MPa
@Strain 6.80 %,
Temperature 60.0 °C		5564 psi
@Strain 6.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.37 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5565 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 38.42 MPa
@Strain 30.0 %,
Temperature 60.0 °C		5572 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.46 MPa
@Strain 31.0 %,
Temperature 60.0 °C		5578 psi
@Strain 31.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.49 MPa
@Strain 32.0 %,
Temperature 60.0 °C		5583 psi
@Strain 32.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.53 MPa
@Strain 22.0 %,
Temperature 80.0 °C		5588 psi
@Strain 22.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.57 MPa
@Strain 33.0 %,
Temperature 60.0 °C		5594 psi
@Strain 33.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.61 MPa
@Strain 34.0 %,
Temperature 60.0 °C		5600 psi
@Strain 34.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.61 MPa
@Strain 35.0 %,
Temperature 60.0 °C		5600 psi
@Strain 35.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.66 MPa
@Strain 37.0 %,
Temperature 60.0 °C		5607 psi
@Strain 37.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.68 MPa
@Strain 38.0 %,
Temperature 60.0 °C		5610 psi
@Strain 38.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.68 MPa
@Strain 36.0 %,
Temperature 60.0 °C		5610 psi
@Strain 36.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 39.0 %,
Temperature 60.0 °C		5610 psi
@Strain 39.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 40.0 %,
Temperature 60.0 °C		5610 psi
@Strain 40.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 50.0 %,
Temperature 60.0 °C		5610 psi
@Strain 50.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.72 MPa
@Strain 49.0 %,
Temperature 60.0 °C		5616 psi
@Strain 49.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.72 MPa
@Strain 44.0 %,
Temperature 60.0 °C		5616 psi
@Strain 44.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.73 MPa
@Strain 45.0 %,
Temperature 60.0 °C		5617 psi
@Strain 45.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.73 MPa
@Strain 43.0 %,
Temperature 60.0 °C		5617 psi
@Strain 43.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.73 MPa
@Strain 47.0 %,
Temperature 60.0 °C		5617 psi
@Strain 47.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.74 MPa
@Strain 48.0 %,
Temperature 60.0 °C		5619 psi
@Strain 48.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.74 MPa
@Strain 46.0 %,
Temperature 60.0 °C		5619 psi
@Strain 46.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.74 MPa
@Strain 41.0 %,
Temperature 60.0 °C		5619 psi
@Strain 41.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.75 MPa
@Strain 42.0 %,
Temperature 60.0 °C		5620 psi
@Strain 42.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.76 MPa
@Strain 8.90 %,
Temperature 23.0 °C		5622 psi
@Strain 8.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.87 MPa
@Strain 23.0 %,
Temperature 80.0 °C		5638 psi
@Strain 23.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.06 MPa
@Strain 7.30 %,
Temperature 60.0 °C		5665 psi
@Strain 7.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.19 MPa
@Strain 24.0 %,
Temperature 80.0 °C		5684 psi
@Strain 24.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.49 MPa
@Strain 25.0 %,
Temperature 80.0 °C		5728 psi
@Strain 25.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 9.40 %,
Temperature 23.0 °C		5740 psi
@Strain 9.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 7.80 %,
Temperature 60.0 °C		5760 psi
@Strain 7.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.83 MPa
@Strain 26.0 %,
Temperature 80.0 °C		5777 psi
@Strain 26.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.04 MPa
@Strain 1.20 %,
Temperature 0.000 °C		5807 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.12 MPa
@Strain 27.0 %,
Temperature 80.0 °C		5819 psi
@Strain 27.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.27 MPa
@Strain 8.30 %,
Temperature 60.0 °C		5841 psi
@Strain 8.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.29 MPa
@Strain 1.50 %,
Temperature 0.000 °C		5844 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 9.90 %,
Temperature 23.0 °C		5850 psi
@Strain 9.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.42 MPa
@Strain 28.0 %,
Temperature 80.0 °C		5862 psi
@Strain 28.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.68 MPa
@Strain 29.0 %,
Temperature 80.0 °C		5900 psi
@Strain 29.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.74 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5909 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 40.83 MPa
@Strain 1.10 %,
Temperature -40.0 °C		5922 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 40.94 MPa
@Strain 8.80 %,
Temperature 60.0 °C		5938 psi
@Strain 8.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.96 MPa
@Strain 30.0 %,
Temperature 80.0 °C		5941 psi
@Strain 30.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.17 MPa
@Strain 31.0 %,
Temperature 80.0 °C		5971 psi
@Strain 31.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.38 MPa
@Strain 32.0 %,
Temperature 80.0 °C		6002 psi
@Strain 32.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.51 MPa
@Strain 9.30 %,
Temperature 60.0 °C		6021 psi
@Strain 9.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.56 MPa
@Strain 10.9 %,
Temperature 23.0 °C		6028 psi
@Strain 10.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.58 MPa
@Strain 33.0 %,
Temperature 80.0 °C		6031 psi
@Strain 33.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.71 MPa
@Strain 1.20 %,
Temperature -40.0 °C		6050 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.82 MPa
@Strain 34.0 %,
Temperature 80.0 °C		6065 psi
@Strain 34.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.96 MPa
@Strain 9.80 %,
Temperature 60.0 °C		6086 psi
@Strain 9.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.14 MPa
@Strain 35.0 %,
Temperature 80.0 °C		6112 psi
@Strain 35.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.4 MPa
@Strain 36.0 %,
Temperature 80.0 °C		6150 psi
@Strain 36.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.54 MPa
@Strain 37.0 %,
Temperature 80.0 °C		6170 psi
@Strain 37.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.66 MPa
@Strain 38.0 %,
Temperature 80.0 °C		6187 psi
@Strain 38.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.75 MPa
@Strain 39.0 %,
Temperature 80.0 °C		6200 psi
@Strain 39.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.77 MPa
@Strain 1.60 %,
Temperature 0.000 °C		6203 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 42.87 MPa
@Strain 40.0 %,
Temperature 80.0 °C		6218 psi
@Strain 40.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.9 MPa
@Strain 10.8 %,
Temperature 60.0 °C		6220 psi
@Strain 10.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.91 MPa
@Strain 41.0 %,
Temperature 80.0 °C		6224 psi
@Strain 41.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.96 MPa
@Strain 1.30 %,
Temperature 0.000 °C		6231 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 43.01 MPa
@Strain 11.9 %,
Temperature 23.0 °C		6238 psi
@Strain 11.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.03 MPa
@Strain 42.0 %,
Temperature 80.0 °C		6241 psi
@Strain 42.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.08 MPa
@Strain 43.0 %,
Temperature 80.0 °C		6248 psi
@Strain 43.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.17 MPa
@Strain 44.0 %,
Temperature 80.0 °C		6261 psi
@Strain 44.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.24 MPa
@Strain 45.0 %,
Temperature 80.0 °C		6271 psi
@Strain 45.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.3 MPa
@Strain 46.0 %,
Temperature 80.0 °C		6280 psi
@Strain 46.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.33 MPa
@Strain 47.0 %,
Temperature 80.0 °C		6284 psi
@Strain 47.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.4 MPa
@Strain 48.0 %,
Temperature 80.0 °C		6290 psi
@Strain 48.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.48 MPa
@Strain 49.0 %,
Temperature 80.0 °C		6306 psi
@Strain 49.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.52 MPa
@Strain 50.0 %,
Temperature 80.0 °C		6312 psi
@Strain 50.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.04 MPa
@Strain 12.9 %,
Temperature 23.0 °C		6387 psi
@Strain 12.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.04 MPa
@Strain 11.8 %,
Temperature 60.0 °C		6387 psi
@Strain 11.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.18 MPa
@Strain 1.40 %,
Temperature 23.0 °C		6408 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.2 MPa
@Strain 1.20 %,
Temperature -40.0 °C		6410 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 44.36 MPa
@Strain 1.70 %,
Temperature 0.000 °C		6434 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 44.91 MPa
@Strain 12.8 %,
Temperature 60.0 °C		6514 psi
@Strain 12.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.06 MPa
@Strain 13.9 %,
Temperature 23.0 °C		6535 psi
@Strain 13.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.17 MPa
@Strain 1.30 %,
Temperature -40.0 °C		6551 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.69 MPa
@Strain 13.8 %,
Temperature 60.0 °C		6627 psi
@Strain 13.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.89 MPa
@Strain 1.80 %,
Temperature 0.000 °C		6656 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 45.94 MPa
@Strain 14.9 %,
Temperature 23.0 °C		6663 psi
@Strain 14.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.03 MPa
@Strain 1.40 %,
Temperature 0.000 °C		6676 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 46.47 MPa
@Strain 14.8 %,
Temperature 60.0 °C		6740 psi
@Strain 14.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.7 MPa
@Strain 15.9 %,
Temperature 23.0 °C		6770 psi
@Strain 15.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.22 MPa
@Strain 1.90 %,
Temperature 0.000 °C		6849 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.32 MPa
@Strain 1.30 %,
Temperature -40.0 °C		6863 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.37 MPa
@Strain 16.9 %,
Temperature 23.0 °C		6870 psi
@Strain 16.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 1.50 %,
Temperature 23.0 °C		6870 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 47.58 MPa
@Strain 15.8 %,
Temperature 60.0 °C		6901 psi
@Strain 15.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.88 MPa
@Strain 1.40 %,
Temperature -40.0 °C		6944 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 47.96 MPa
@Strain 17.9 %,
Temperature 23.0 °C		6956 psi
@Strain 17.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.2 MPa
@Strain 16.8 %,
Temperature 60.0 °C		6990 psi
@Strain 16.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.51 MPa
@Strain 18.9 %,
Temperature 23.0 °C		7036 psi
@Strain 18.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.69 MPa
@Strain 2.00 %,
Temperature 0.000 °C		7062 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.92 MPa
@Strain 17.8 %,
Temperature 60.0 °C		7095 psi
@Strain 17.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.97 MPa
@Strain 19.9 %,
Temperature 23.0 °C		7103 psi
@Strain 19.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.25 MPa
@Strain 1.50 %,
Temperature 0.000 °C		7143 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 49.34 MPa
@Strain 18.8 %,
Temperature 60.0 °C		7156 psi
@Strain 18.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.37 MPa
@Strain 20.9 %,
Temperature 23.0 °C		7161 psi
@Strain 20.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.42 MPa
@Strain 1.60 %,
Temperature 23.0 °C		7168 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.68 MPa
@Strain 21.9 %,
Temperature 23.0 °C		7205 psi
@Strain 21.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 19.8 %,
Temperature 60.0 °C		7210 psi
@Strain 19.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 2.10 %,
Temperature 0.000 °C		7240 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 50.04 MPa
@Strain 22.9 %,
Temperature 23.0 °C		7258 psi
@Strain 22.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.07 MPa
@Strain 20.8 %,
Temperature 60.0 °C		7262 psi
@Strain 20.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.28 MPa
@Strain 23.9 %,
Temperature 23.0 °C		7293 psi
@Strain 23.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.37 MPa
@Strain 21.8 %,
Temperature 60.0 °C		7306 psi
@Strain 21.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.43 MPa
@Strain 1.40 %,
Temperature -40.0 °C		7314 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 50.53 MPa
@Strain 24.9 %,
Temperature 23.0 °C		7329 psi
@Strain 24.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.59 MPa
@Strain 22.8 %,
Temperature 60.0 °C		7337 psi
@Strain 22.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.72 MPa
@Strain 25.9 %,
Temperature 23.0 °C		7356 psi
@Strain 25.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.87 MPa
@Strain 26.9 %,
Temperature 23.0 °C		7378 psi
@Strain 26.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.92 MPa
@Strain 23.8 %,
Temperature 60.0 °C		7385 psi
@Strain 23.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.01 MPa
@Strain 27.9 %,
Temperature 23.0 °C		7398 psi
@Strain 27.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.04 MPa
@Strain 2.20 %,
Temperature 0.000 °C		7403 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 51.09 MPa
@Strain 1.50 %,
Temperature -40.0 °C		7410 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 51.15 MPa
@Strain 28.9 %,
Temperature 23.0 °C		7419 psi
@Strain 28.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.15 MPa
@Strain 24.8 %,
Temperature 60.0 °C		7419 psi
@Strain 24.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.24 MPa
@Strain 29.9 %,
Temperature 23.0 °C		7432 psi
@Strain 29.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.29 MPa
@Strain 30.9 %,
Temperature 23.0 °C		7439 psi
@Strain 30.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.3 MPa
@Strain 50.0 %,
Temperature 23.0 °C		7440 psi
@Strain 50.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.31 MPa
@Strain 49.9 %,
Temperature 23.0 °C		7442 psi
@Strain 49.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.33 MPa
@Strain 47.9 %,
Temperature 23.0 °C		7445 psi
@Strain 47.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.35 MPa
@Strain 48.9 %,
Temperature 23.0 °C		7448 psi
@Strain 48.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.36 MPa
@Strain 31.9 %,
Temperature 23.0 °C		7449 psi
@Strain 31.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.39 MPa
@Strain 25.8 %,
Temperature 60.0 °C		7454 psi
@Strain 25.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.4 MPa
@Strain 32.9 %,
Temperature 23.0 °C		7450 psi
@Strain 32.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.43 MPa
@Strain 45.9 %,
Temperature 23.0 °C		7459 psi
@Strain 45.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.43 MPa
@Strain 46.9 %,
Temperature 23.0 °C		7459 psi
@Strain 46.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.45 MPa
@Strain 34.9 %,
Temperature 23.0 °C		7462 psi
@Strain 34.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.46 MPa
@Strain 33.9 %,
Temperature 23.0 °C		7464 psi
@Strain 33.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.47 MPa
@Strain 44.9 %,
Temperature 23.0 °C		7465 psi
@Strain 44.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.48 MPa
@Strain 43.9 %,
Temperature 23.0 °C		7467 psi
@Strain 43.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.49 MPa
@Strain 35.9 %,
Temperature 23.0 °C		7468 psi
@Strain 35.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.51 MPa
@Strain 41.9 %,
Temperature 23.0 °C		7471 psi
@Strain 41.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.52 MPa
@Strain 39.9 %,
Temperature 23.0 °C		7472 psi
@Strain 39.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.53 MPa
@Strain 40.9 %,
Temperature 23.0 °C		7474 psi
@Strain 40.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.53 MPa
@Strain 38.9 %,
Temperature 23.0 °C		7474 psi
@Strain 38.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.54 MPa
@Strain 42.9 %,
Temperature 23.0 °C		7475 psi
@Strain 42.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.55 MPa
@Strain 36.9 %,
Temperature 23.0 °C		7477 psi
@Strain 36.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.55 MPa
@Strain 26.8 %,
Temperature 60.0 °C		7477 psi
@Strain 26.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.58 MPa
@Strain 37.9 %,
Temperature 23.0 °C		7481 psi
@Strain 37.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.6 MPa
@Strain 1.70 %,
Temperature 23.0 °C		7480 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 51.71 MPa
@Strain 27.8 %,
Temperature 60.0 °C		7500 psi
@Strain 27.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.79 MPa
@Strain 1.60 %,
Temperature 0.000 °C		7512 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 51.87 MPa
@Strain 28.8 %,
Temperature 60.0 °C		7523 psi
@Strain 28.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.01 MPa
@Strain 29.8 %,
Temperature 60.0 °C		7543 psi
@Strain 29.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.13 MPa
@Strain 30.8 %,
Temperature 60.0 °C		7561 psi
@Strain 30.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.25 MPa
@Strain 31.8 %,
Temperature 60.0 °C		7578 psi
@Strain 31.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.25 MPa
@Strain 2.30 %,
Temperature 0.000 °C		7578 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.34 MPa
@Strain 32.8 %,
Temperature 60.0 °C		7591 psi
@Strain 32.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.41 MPa
@Strain 33.8 %,
Temperature 60.0 °C		7601 psi
@Strain 33.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.47 MPa
@Strain 34.8 %,
Temperature 60.0 °C		7610 psi
@Strain 34.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.53 MPa
@Strain 35.8 %,
Temperature 60.0 °C		7619 psi
@Strain 35.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.58 MPa
@Strain 36.8 %,
Temperature 60.0 °C		7626 psi
@Strain 36.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.61 MPa
@Strain 38.8 %,
Temperature 60.0 °C		7630 psi
@Strain 38.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.63 MPa
@Strain 37.8 %,
Temperature 60.0 °C		7633 psi
@Strain 37.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.65 MPa
@Strain 50.0 %,
Temperature 60.0 °C		7636 psi
@Strain 50.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.66 MPa
@Strain 39.8 %,
Temperature 60.0 °C		7638 psi
@Strain 39.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.68 MPa
@Strain 40.8 %,
Temperature 60.0 °C		7641 psi
@Strain 40.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 41.8 %,
Temperature 60.0 °C		7640 psi
@Strain 41.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 48.8 %,
Temperature 60.0 °C		7640 psi
@Strain 48.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.71 MPa
@Strain 43.8 %,
Temperature 60.0 °C		7645 psi
@Strain 43.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.71 MPa
@Strain 44.8 %,
Temperature 60.0 °C		7645 psi
@Strain 44.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.72 MPa
@Strain 49.8 %,
Temperature 60.0 °C		7646 psi
@Strain 49.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.72 MPa
@Strain 46.8 %,
Temperature 60.0 °C		7646 psi
@Strain 46.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.74 MPa
@Strain 47.8 %,
Temperature 60.0 °C		7649 psi
@Strain 47.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.74 MPa
@Strain 45.8 %,
Temperature 60.0 °C		7649 psi
@Strain 45.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.76 MPa
@Strain 42.8 %,
Temperature 60.0 °C		7652 psi
@Strain 42.8 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.27 MPa
@Strain 2.40 %,
Temperature 0.000 °C		7726 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 1.50 %,
Temperature -40.0 °C		7760 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 54.15 MPa
@Strain 1.60 %,
Temperature -40.0 °C		7854 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 54.29 MPa
@Strain 2.50 %,
Temperature 0.000 °C		7874 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 54.43 MPa
@Strain 1.70 %,
Temperature 0.000 °C		7894 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 54.47 MPa
@Strain 1.80 %,
Temperature 23.0 °C		7900 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 55.05 MPa
@Strain 2.60 %,
Temperature 0.000 °C		7984 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 55.69 MPa
@Strain 2.70 %,
Temperature 0.000 °C		8077 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.45 MPa
@Strain 2.80 %,
Temperature 0.000 °C		8187 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.08 MPa
@Strain 1.60 %,
Temperature -40.0 °C		8279 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 57.09 MPa
@Strain 2.90 %,
Temperature 0.000 °C		8280 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.26 MPa
@Strain 1.70 %,
Temperature -40.0 °C		8305 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.33 MPa
@Strain 1.80 %,
Temperature 0.000 °C		8315 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 57.41 MPa
@Strain 1.90 %,
Temperature 23.0 °C		8327 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 57.6 MPa
@Strain 3.00 %,
Temperature 0.000 °C		8350 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.98 MPa
@Strain 3.10 %,
Temperature 0.000 °C		8409 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.23 MPa
@Strain 3.20 %,
Temperature 0.000 °C		8446 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.84 MPa
@Strain 3.40 %,
Temperature 0.000 °C		8534 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.25 MPa
@Strain 3.50 %,
Temperature 0.000 °C		8594 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.37 MPa
@Strain 2.00 %,
Temperature 23.0 °C		8611 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 59.51 MPa
@Strain 3.60 %,
Temperature 0.000 °C		8631 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.76 MPa
@Strain 3.70 %,
Temperature 0.000 °C		8667 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.95 MPa
@Strain 1.70 %,
Temperature -40.0 °C		8695 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 60.19 MPa
@Strain 1.80 %,
Temperature -40.0 °C		8730 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.27 MPa
@Strain 3.90 %,
Temperature 0.000 °C		8741 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.29 MPa
@Strain 1.90 %,
Temperature 0.000 °C		8744 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 60.42 MPa
@Strain 4.00 %,
Temperature 0.000 °C		8763 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.65 MPa
@Strain 4.10 %,
Temperature 0.000 °C		8797 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.65 MPa
@Strain 4.20 %,
Temperature 0.000 °C		8797 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.91 MPa
@Strain 4.30 %,
Temperature 0.000 °C		8834 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.16 MPa
@Strain 4.50 %,
Temperature 0.000 °C		8871 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.22 MPa
@Strain 4.60 %,
Temperature 0.000 °C		8879 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.29 MPa
@Strain 4.70 %,
Temperature 0.000 °C		8889 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.54 MPa
@Strain 4.90 %,
Temperature 0.000 °C		8926 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.67 MPa
@Strain 5.00 %,
Temperature 0.000 °C		8944 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.1 MPa
@Strain 2.10 %,
Temperature 23.0 °C		9010 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.28 MPa
@Strain 5.50 %,
Temperature 0.000 °C		9033 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.69 MPa
@Strain 2.00 %,
Temperature 0.000 °C		9092 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 62.72 MPa
@Strain 1.80 %,
Temperature -40.0 °C		9097 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 63.01 MPa
@Strain 6.00 %,
Temperature 0.000 °C		9139 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.16 MPa
@Strain 1.90 %,
Temperature -40.0 °C		9161 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.52 MPa
@Strain 6.50 %,
Temperature 0.000 °C		9213 psi
@Strain 6.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.18 MPa
@Strain 7.00 %,
Temperature 0.000 °C		9309 psi
@Strain 7.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.76 MPa
@Strain 7.50 %,
Temperature 0.000 °C		9393 psi
@Strain 7.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.83 MPa
@Strain 2.20 %,
Temperature 23.0 °C		9403 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.04 MPa
@Strain 48.9 %,
Temperature 23.0 °C		9433 psi
@Strain 48.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.08 MPa
@Strain 49.9 %,
Temperature 23.0 °C		9439 psi
@Strain 49.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.12 MPa
@Strain 50.0 %,
Temperature 23.0 °C		9445 psi
@Strain 50.0 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.14 MPa
@Strain 45.9 %,
Temperature 23.0 °C		9448 psi
@Strain 45.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.19 MPa
@Strain 47.9 %,
Temperature 23.0 °C		9455 psi
@Strain 47.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.22 MPa
@Strain 43.9 %,
Temperature 23.0 °C		9459 psi
@Strain 43.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.23 MPa
@Strain 8.00 %,
Temperature 0.000 °C		9461 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.25 MPa
@Strain 42.9 %,
Temperature 23.0 °C		9464 psi
@Strain 42.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.29 MPa
@Strain 46.9 %,
Temperature 23.0 °C		9470 psi
@Strain 46.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.29 MPa
@Strain 44.9 %,
Temperature 23.0 °C		9470 psi
@Strain 44.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.34 MPa
@Strain 41.9 %,
Temperature 23.0 °C		9477 psi
@Strain 41.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.4 MPa
@Strain 39.9 %,
Temperature 23.0 °C		9490 psi
@Strain 39.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.4 MPa
@Strain 40.9 %,
Temperature 23.0 °C		9490 psi
@Strain 40.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.42 MPa
@Strain 1.90 %,
Temperature -40.0 °C		9488 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 65.43 MPa
@Strain 38.9 %,
Temperature 23.0 °C		9490 psi
@Strain 38.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.45 MPa
@Strain 2.10 %,
Temperature 0.000 °C		9493 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 65.64 MPa
@Strain 36.9 %,
Temperature 23.0 °C		9520 psi
@Strain 36.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.64 MPa
@Strain 37.9 %,
Temperature 23.0 °C		9520 psi
@Strain 37.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.67 MPa
@Strain 35.9 %,
Temperature 23.0 °C		9525 psi
@Strain 35.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.71 MPa
@Strain 8.50 %,
Temperature 0.000 °C		9530 psi
@Strain 8.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.78 MPa
@Strain 34.9 %,
Temperature 23.0 °C		9541 psi
@Strain 34.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.99 MPa
@Strain 33.9 %,
Temperature 23.0 °C		9571 psi
@Strain 33.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.01 MPa
@Strain 2.00 %,
Temperature -40.0 °C		9574 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 66.17 MPa
@Strain 32.9 %,
Temperature 23.0 °C		9597 psi
@Strain 32.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.32 MPa
@Strain 9.00 %,
Temperature 0.000 °C		9619 psi
@Strain 9.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.37 MPa
@Strain 31.9 %,
Temperature 23.0 °C		9626 psi
@Strain 31.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.6 MPa
@Strain 48.0 %,
Temperature 0.000 °C		9660 psi
@Strain 48.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.62 MPa
@Strain 30.9 %,
Temperature 23.0 °C		9662 psi
@Strain 30.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.65 MPa
@Strain 2.30 %,
Temperature 23.0 °C		9667 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.68 MPa
@Strain 9.50 %,
Temperature 0.000 °C		9671 psi
@Strain 9.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.75 MPa
@Strain 26.9 %,
Temperature 23.0 °C		9681 psi
@Strain 26.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.88 MPa
@Strain 29.9 %,
Temperature 23.0 °C		9700 psi
@Strain 29.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.05 MPa
@Strain 10.0 %,
Temperature 0.000 °C		9725 psi
@Strain 10.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.27 MPa
@Strain 28.9 %,
Temperature 23.0 °C		9757 psi
@Strain 28.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.58 MPa
@Strain 27.9 %,
Temperature 23.0 °C		9802 psi
@Strain 27.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.8 MPa
@Strain 25.9 %,
Temperature 23.0 °C		9830 psi
@Strain 25.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.89 MPa
@Strain 11.0 %,
Temperature 0.000 °C		9847 psi
@Strain 11.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.07 MPa
@Strain 2.00 %,
Temperature -40.0 °C		9873 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 68.14 MPa
@Strain 2.20 %,
Temperature 0.000 °C		9883 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 68.33 MPa
@Strain 2.40 %,
Temperature 23.0 °C		9910 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.69 MPa
@Strain 47.0 %,
Temperature 0.000 °C		9963 psi
@Strain 47.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.71 MPa
@Strain 12.0 %,
Temperature 0.000 °C		9966 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.79 MPa
@Strain 2.10 %,
Temperature -40.0 °C		9977 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.36 MPa
@Strain 13.0 %,
Temperature 0.000 °C		10060 psi
@Strain 13.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.62 MPa
@Strain 2.30 %,
Temperature 0.000 °C		10100 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.87 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10130 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 70.21 MPa
@Strain 14.0 %,
Temperature 0.000 °C		10180 psi
@Strain 14.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.57 MPa
@Strain 2.10 %,
Temperature -40.0 °C		10240 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 70.8 MPa
@Strain 15.0 %,
Temperature 0.000 °C		10300 psi
@Strain 15.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.0 MPa
@Strain 2.40 %,
Temperature 0.000 °C		10300 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 71.04 MPa
@Strain 2.20 %,
Temperature -40.0 °C		10300 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 71.28 MPa
@Strain 46.0 %,
Temperature 0.000 °C		10340 psi
@Strain 46.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.56 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10380 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.76 MPa
@Strain 16.0 %,
Temperature 0.000 °C		10410 psi
@Strain 16.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.94 MPa
@Strain 45.0 %,
Temperature 0.000 °C		10430 psi
@Strain 45.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.07 MPa
@Strain 41.0 %,
Temperature 0.000 °C		10450 psi
@Strain 41.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.16 MPa
@Strain 43.0 %,
Temperature 0.000 °C		10470 psi
@Strain 43.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.33 MPa
@Strain 39.0 %,
Temperature 0.000 °C		10490 psi
@Strain 39.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.33 MPa
@Strain 40.0 %,
Temperature 0.000 °C		10490 psi
@Strain 40.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.34 MPa
@Strain 42.0 %,
Temperature 0.000 °C		10490 psi
@Strain 42.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.36 MPa
@Strain 2.50 %,
Temperature 0.000 °C		10490 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.38 MPa
@Strain 17.0 %,
Temperature 0.000 °C		10500 psi
@Strain 17.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.39 MPa
@Strain 44.0 %,
Temperature 0.000 °C		10500 psi
@Strain 44.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.54 MPa
@Strain 38.0 %,
Temperature 0.000 °C		10520 psi
@Strain 38.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.58 MPa
@Strain 2.30 %,
Temperature -40.0 °C		10530 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.74 MPa
@Strain 37.0 %,
Temperature 0.000 °C		10550 psi
@Strain 37.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.98 MPa
@Strain 36.0 %,
Temperature 0.000 °C		10580 psi
@Strain 36.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.11 MPa
@Strain 18.0 %,
Temperature 0.000 °C		10600 psi
@Strain 18.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.16 MPa
@Strain 2.20 %,
Temperature -40.0 °C		10610 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 73.17 MPa
@Strain 35.0 %,
Temperature 0.000 °C		10610 psi
@Strain 35.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.34 MPa
@Strain 34.0 %,
Temperature 0.000 °C		10640 psi
@Strain 34.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.44 MPa
@Strain 19.0 %,
Temperature 0.000 °C		10650 psi
@Strain 19.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.49 MPa
@Strain 33.0 %,
Temperature 0.000 °C		10660 psi
@Strain 33.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.65 MPa
@Strain 32.0 %,
Temperature 0.000 °C		10680 psi
@Strain 32.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.65 MPa
@Strain 20.0 %,
Temperature 0.000 °C		10680 psi
@Strain 20.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.79 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10700 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.95 MPa
@Strain 31.0 %,
Temperature 0.000 °C		10730 psi
@Strain 31.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.96 MPa
@Strain 2.40 %,
Temperature -40.0 °C		10730 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 74.05 MPa
@Strain 2.60 %,
Temperature 0.000 °C		10740 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.09 MPa
@Strain 30.0 %,
Temperature 0.000 °C		10750 psi
@Strain 30.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.33 MPa
@Strain 29.0 %,
Temperature 0.000 °C		10780 psi
@Strain 29.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.51 MPa
@Strain 21.0 %,
Temperature 0.000 °C		10810 psi
@Strain 21.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.51 MPa
@Strain 28.0 %,
Temperature 0.000 °C		10810 psi
@Strain 28.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.84 MPa
@Strain 27.0 %,
Temperature 0.000 °C		10850 psi
@Strain 27.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.91 MPa
@Strain 26.0 %,
Temperature 0.000 °C		10860 psi
@Strain 26.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 22.0 %,
Temperature 0.000 °C		10900 psi
@Strain 22.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.34 MPa
@Strain 25.0 %,
Temperature 0.000 °C		10930 psi
@Strain 25.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.35 MPa
@Strain 2.50 %,
Temperature -40.0 °C		10930 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.44 MPa
@Strain 24.0 %,
Temperature 0.000 °C		10940 psi
@Strain 24.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.47 MPa
@Strain 23.0 %,
Temperature 0.000 °C		10950 psi
@Strain 23.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.5 MPa
@Strain 50.0 %,
Temperature 0.000 °C		11000 psi
@Strain 50.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.5 MPa
@Strain 45.8 %,
Temperature 0.000 °C		11000 psi
@Strain 45.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.6 MPa
@Strain 49.9 %,
Temperature 0.000 °C		11000 psi
@Strain 49.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.63 MPa
@Strain 36.8 %,
Temperature 0.000 °C		10970 psi
@Strain 36.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.63 MPa
@Strain 37.8 %,
Temperature 0.000 °C		10970 psi
@Strain 37.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.63 MPa
@Strain 33.8 %,
Temperature 0.000 °C		10970 psi
@Strain 33.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.63 MPa
@Strain 28.8 %,
Temperature 0.000 °C		10970 psi
@Strain 28.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.7 MPa
@Strain 40.8 %,
Temperature 0.000 °C		11000 psi
@Strain 40.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.73 MPa
@Strain 2.30 %,
Temperature -40.0 °C		10980 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 75.76 MPa
@Strain 44.8 %,
Temperature 0.000 °C		10990 psi
@Strain 44.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.82 MPa
@Strain 23.8 %,
Temperature 0.000 °C		11000 psi
@Strain 23.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.89 MPa
@Strain 31.8 %,
Temperature 0.000 °C		11010 psi
@Strain 31.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.95 MPa
@Strain 41.8 %,
Temperature 0.000 °C		11020 psi
@Strain 41.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.02 MPa
@Strain 34.8 %,
Temperature 0.000 °C		11030 psi
@Strain 34.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.03 MPa
@Strain 2.80 %,
Temperature 23.0 °C		11030 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.1 MPa
@Strain 32.8 %,
Temperature 0.000 °C		11000 psi
@Strain 32.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.14 MPa
@Strain 39.8 %,
Temperature 0.000 °C		11040 psi
@Strain 39.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.14 MPa
@Strain 2.70 %,
Temperature 0.000 °C		11040 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.21 MPa
@Strain 26.8 %,
Temperature 0.000 °C		11050 psi
@Strain 26.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.27 MPa
@Strain 27.8 %,
Temperature 0.000 °C		11060 psi
@Strain 27.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.27 MPa
@Strain 48.8 %,
Temperature 0.000 °C		11060 psi
@Strain 48.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 48.9 %,
Temperature 0.000 °C		11100 psi
@Strain 48.9 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 43.8 %,
Temperature 0.000 °C		11100 psi
@Strain 43.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.46 MPa
@Strain 38.8 %,
Temperature 0.000 °C		11090 psi
@Strain 38.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.59 MPa
@Strain 29.8 %,
Temperature 0.000 °C		11110 psi
@Strain 29.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.72 MPa
@Strain 35.8 %,
Temperature 0.000 °C		11130 psi
@Strain 35.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.78 MPa
@Strain 30.8 %,
Temperature 0.000 °C		11140 psi
@Strain 30.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.83 MPa
@Strain 19.8 %,
Temperature 0.000 °C		11140 psi
@Strain 19.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.93 MPa
@Strain 2.60 %,
Temperature -40.0 °C		11160 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 76.98 MPa
@Strain 22.8 %,
Temperature 0.000 °C		11170 psi
@Strain 22.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.04 MPa
@Strain 46.8 %,
Temperature 0.000 °C		11170 psi
@Strain 46.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.04 MPa
@Strain 47.8 %,
Temperature 0.000 °C		11170 psi
@Strain 47.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.04 MPa
@Strain 42.8 %,
Temperature 0.000 °C		11170 psi
@Strain 42.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.15 MPa
@Strain 2.90 %,
Temperature 23.0 °C		11190 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 24.8 %,
Temperature 0.000 °C		11200 psi
@Strain 24.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.55 MPa
@Strain 25.8 %,
Temperature 0.000 °C		11250 psi
@Strain 25.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.57 MPa
@Strain 2.40 %,
Temperature -40.0 °C		11250 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 77.64 MPa
@Strain 21.8 %,
Temperature 0.000 °C		11260 psi
@Strain 21.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.3 MPa
@Strain 2.80 %,
Temperature 0.000 °C		11400 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.41 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11370 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.87 MPa
@Strain 24.9 %,
Temperature 23.0 °C		11440 psi
@Strain 24.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.98 MPa
@Strain 2.70 %,
Temperature -40.0 °C		11460 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 79.1 MPa
@Strain 20.8 %,
Temperature 0.000 °C		11500 psi
@Strain 20.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 79.35 MPa
@Strain 23.9 %,
Temperature 23.0 °C		11510 psi
@Strain 23.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.43 MPa
@Strain 8.90 %,
Temperature 23.0 °C		11520 psi
@Strain 8.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.44 MPa
@Strain 9.90 %,
Temperature 23.0 °C		11520 psi
@Strain 9.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.46 MPa
@Strain 10.9 %,
Temperature 23.0 °C		11520 psi
@Strain 10.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.48 MPa
@Strain 2.50 %,
Temperature -40.0 °C		11530 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.49 MPa
@Strain 9.40 %,
Temperature 23.0 °C		11530 psi
@Strain 9.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.51 MPa
@Strain 11.9 %,
Temperature 23.0 °C		11530 psi
@Strain 11.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.53 MPa
@Strain 8.40 %,
Temperature 23.0 °C		11530 psi
@Strain 8.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.53 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11530 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.59 MPa
@Strain 7.90 %,
Temperature 23.0 °C		11540 psi
@Strain 7.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.63 MPa
@Strain 2.90 %,
Temperature 0.000 °C		11550 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 79.67 MPa
@Strain 12.9 %,
Temperature 23.0 °C		11560 psi
@Strain 12.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.72 MPa
@Strain 7.40 %,
Temperature 23.0 °C		11560 psi
@Strain 7.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.72 MPa
@Strain 22.9 %,
Temperature 23.0 °C		11560 psi
@Strain 22.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.79 MPa
@Strain 21.9 %,
Temperature 23.0 °C		11570 psi
@Strain 21.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.79 MPa
@Strain 13.9 %,
Temperature 23.0 °C		11570 psi
@Strain 13.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.86 MPa
@Strain 14.9 %,
Temperature 23.0 °C		11580 psi
@Strain 14.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.92 MPa
@Strain 15.9 %,
Temperature 23.0 °C		11590 psi
@Strain 15.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.95 MPa
@Strain 19.9 %,
Temperature 23.0 °C		11600 psi
@Strain 19.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.95 MPa
@Strain 20.9 %,
Temperature 23.0 °C		11600 psi
@Strain 20.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.97 MPa
@Strain 18.9 %,
Temperature 23.0 °C		11600 psi
@Strain 18.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.98 MPa
@Strain 16.9 %,
Temperature 23.0 °C		11600 psi
@Strain 16.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.99 MPa
@Strain 17.9 %,
Temperature 23.0 °C		11600 psi
@Strain 17.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.03 MPa
@Strain 6.90 %,
Temperature 23.0 °C		11610 psi
@Strain 6.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.19 MPa
@Strain 6.40 %,
Temperature 23.0 °C		11630 psi
@Strain 6.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.51 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11680 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.56 MPa
@Strain 5.90 %,
Temperature 23.0 °C		11680 psi
@Strain 5.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.56 MPa
@Strain 2.80 %,
Temperature -40.0 °C		11680 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.92 MPa
@Strain 3.00 %,
Temperature 0.000 °C		11740 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 80.96 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11740 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.36 MPa
@Strain 3.40 %,
Temperature 23.0 °C		11800 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.36 MPa
@Strain 5.40 %,
Temperature 23.0 °C		11800 psi
@Strain 5.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.69 MPa
@Strain 2.60 %,
Temperature -40.0 °C		11850 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 81.92 MPa
@Strain 3.50 %,
Temperature 23.0 °C		11880 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.05 MPa
@Strain 4.90 %,
Temperature 23.0 °C		11900 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.1 MPa
@Strain 2.90 %,
Temperature -40.0 °C		11900 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 82.19 MPa
@Strain 4.80 %,
Temperature 23.0 °C		11920 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.39 MPa
@Strain 4.70 %,
Temperature 23.0 °C		11950 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.48 MPa
@Strain 4.60 %,
Temperature 23.0 °C		11960 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.49 MPa
@Strain 3.10 %,
Temperature 0.000 °C		11960 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.61 MPa
@Strain 3.60 %,
Temperature 23.0 °C		11980 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		12000 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.50 %,
Temperature 23.0 °C		12000 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.94 MPa
@Strain 4.40 %,
Temperature 23.0 °C		12030 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.04 MPa
@Strain 4.20 %,
Temperature 23.0 °C		12040 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.04 MPa
@Strain 4.30 %,
Temperature 23.0 °C		12040 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.05 MPa
@Strain 3.80 %,
Temperature 23.0 °C		12050 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.16 MPa
@Strain 4.10 %,
Temperature 23.0 °C		12060 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.17 MPa
@Strain 3.90 %,
Temperature 23.0 °C		12060 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.17 MPa
@Strain 4.00 %,
Temperature 23.0 °C		12060 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.43 MPa
@Strain 3.00 %,
Temperature -40.0 °C		12100 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.87 MPa
@Strain 2.70 %,
Temperature -40.0 °C		12160 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 83.98 MPa
@Strain 3.20 %,
Temperature 0.000 °C		12180 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.7 MPa
@Strain 33.0 %,
Temperature -40.0 °C		12300 psi
@Strain 33.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 84.8 MPa
@Strain 3.30 %,
Temperature 0.000 °C		12300 psi
@Strain 3.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.4 MPa
@Strain 2.80 %,
Temperature -40.0 °C		12400 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 85.45 MPa
@Strain 3.10 %,
Temperature -40.0 °C		12390 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.62 MPa
@Strain 17.9 %,
Temperature -40.0 °C		12420 psi
@Strain 17.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.13 MPa
@Strain 3.40 %,
Temperature 0.000 °C		12490 psi
@Strain 3.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.16 MPa
@Strain 18.9 %,
Temperature -40.0 °C		12500 psi
@Strain 18.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.99 MPa
@Strain 2.90 %,
Temperature -40.0 °C		12620 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.0 MPa
@Strain 3.50 %,
Temperature 0.000 °C		12600 psi
@Strain 3.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.3 MPa
@Strain 18.8 %,
Temperature 0.000 °C		12700 psi
@Strain 18.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.45 MPa
@Strain 3.20 %,
Temperature -40.0 °C		12680 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 88.0 MPa
@Strain 3.60 %,
Temperature 0.000 °C		12800 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.37 MPa
@Strain 17.0 %,
Temperature 0.000 °C		12820 psi
@Strain 17.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.45 MPa
@Strain 3.00 %,
Temperature -40.0 °C		12830 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.64 MPa
@Strain 16.0 %,
Temperature 0.000 °C		12860 psi
@Strain 16.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.69 MPa
@Strain 3.70 %,
Temperature 0.000 °C		12860 psi
@Strain 3.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.98 MPa
@Strain 15.0 %,
Temperature 0.000 °C		12910 psi
@Strain 15.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.24 MPa
@Strain 14.0 %,
Temperature 0.000 °C		12940 psi
@Strain 14.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.33 MPa
@Strain 3.30 %,
Temperature -40.0 °C		12960 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.55 MPa
@Strain 13.0 %,
Temperature 0.000 °C		12990 psi
@Strain 13.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.92 MPa
@Strain 3.10 %,
Temperature -40.0 °C		13040 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.0 MPa
@Strain 3.80 %,
Temperature 0.000 °C		13100 psi
@Strain 3.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.09 MPa
@Strain 12.0 %,
Temperature 0.000 °C		13070 psi
@Strain 12.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.29 MPa
@Strain 26.9 %,
Temperature -40.0 °C		13100 psi
@Strain 26.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.61 MPa
@Strain 11.0 %,
Temperature 0.000 °C		13140 psi
@Strain 11.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.76 MPa
@Strain 25.9 %,
Temperature -40.0 °C		13160 psi
@Strain 25.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.77 MPa
@Strain 29.9 %,
Temperature -40.0 °C		13170 psi
@Strain 29.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.86 MPa
@Strain 3.90 %,
Temperature 0.000 °C		13180 psi
@Strain 3.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.9 MPa
@Strain 23.9 %,
Temperature -40.0 °C		13200 psi
@Strain 23.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.99 MPa
@Strain 22.9 %,
Temperature -40.0 °C		13200 psi
@Strain 22.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.13 MPa
@Strain 27.9 %,
Temperature -40.0 °C		13220 psi
@Strain 27.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.16 MPa
@Strain 10.0 %,
Temperature 0.000 °C		13220 psi
@Strain 10.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.28 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13240 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.31 MPa
@Strain 28.9 %,
Temperature -40.0 °C		13240 psi
@Strain 28.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.36 MPa
@Strain 24.9 %,
Temperature -40.0 °C		13250 psi
@Strain 24.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.38 MPa
@Strain 3.20 %,
Temperature -40.0 °C		13250 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 91.5 MPa
@Strain 35.9 %,
Temperature -40.0 °C		13300 psi
@Strain 35.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.53 MPa
@Strain 33.9 %,
Temperature -40.0 °C		13280 psi
@Strain 33.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.54 MPa
@Strain 39.9 %,
Temperature -40.0 °C		13280 psi
@Strain 39.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.61 MPa
@Strain 36.9 %,
Temperature -40.0 °C		13290 psi
@Strain 36.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.69 MPa
@Strain 46.9 %,
Temperature -40.0 °C		13300 psi
@Strain 46.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.74 MPa
@Strain 19.9 %,
Temperature -40.0 °C		13310 psi
@Strain 19.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.81 MPa
@Strain 30.9 %,
Temperature -40.0 °C		13320 psi
@Strain 30.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.9 MPa
@Strain 42.9 %,
Temperature -40.0 °C		13300 psi
@Strain 42.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.0 MPa
@Strain 4.00 %,
Temperature 0.000 °C		13300 psi
@Strain 4.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.01 MPa
@Strain 9.00 %,
Temperature 0.000 °C		13340 psi
@Strain 9.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.1 MPa
@Strain 34.9 %,
Temperature -40.0 °C		13400 psi
@Strain 34.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.27 MPa
@Strain 8.50 %,
Temperature 0.000 °C		13380 psi
@Strain 8.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.52 MPa
@Strain 8.00 %,
Temperature 0.000 °C		13420 psi
@Strain 8.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.54 MPa
@Strain 32.9 %,
Temperature -40.0 °C		13420 psi
@Strain 32.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.72 MPa
@Strain 3.30 %,
Temperature -40.0 °C		13450 psi
@Strain 3.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.78 MPa
@Strain 4.10 %,
Temperature 0.000 °C		13460 psi
@Strain 4.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.85 MPa
@Strain 43.9 %,
Temperature -40.0 °C		13470 psi
@Strain 43.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 92.86 MPa
@Strain 21.9 %,
Temperature -40.0 °C		13470 psi
@Strain 21.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.04 MPa
@Strain 40.9 %,
Temperature -40.0 °C		13490 psi
@Strain 40.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.04 MPa
@Strain 7.50 %,
Temperature 0.000 °C		13490 psi
@Strain 7.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.16 MPa
@Strain 3.50 %,
Temperature -40.0 °C		13510 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.36 MPa
@Strain 47.9 %,
Temperature -40.0 °C		13540 psi
@Strain 47.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.61 MPa
@Strain 7.00 %,
Temperature 0.000 °C		13580 psi
@Strain 7.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.63 MPa
@Strain 41.9 %,
Temperature -40.0 °C		13580 psi
@Strain 41.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.77 MPa
@Strain 50.0 %,
Temperature -40.0 °C		13600 psi
@Strain 50.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.8 MPa
@Strain 49.9 %,
Temperature -40.0 °C		13600 psi
@Strain 49.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.81 MPa
@Strain 31.9 %,
Temperature -40.0 °C		13610 psi
@Strain 31.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.86 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13610 psi
@Strain 3.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 94.06 MPa
@Strain 20.9 %,
Temperature -40.0 °C		13640 psi
@Strain 20.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.32 MPa
@Strain 6.50 %,
Temperature 0.000 °C		13680 psi
@Strain 6.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.44 MPa
@Strain 4.60 %,
Temperature 0.000 °C		13700 psi
@Strain 4.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.96 MPa
@Strain 6.00 %,
Temperature 0.000 °C		13770 psi
@Strain 6.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.01 MPa
@Strain 3.50 %,
Temperature -40.0 °C		13780 psi
@Strain 3.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 95.04 MPa
@Strain 3.60 %,
Temperature -40.0 °C		13780 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.21 MPa
@Strain 48.9 %,
Temperature -40.0 °C		13810 psi
@Strain 48.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.34 MPa
@Strain 5.00 %,
Temperature 0.000 °C		13830 psi
@Strain 5.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.4 MPa
@Strain 5.50 %,
Temperature 0.000 °C		13800 psi
@Strain 5.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.63 MPa
@Strain 38.9 %,
Temperature -40.0 °C		13870 psi
@Strain 38.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.09 MPa
@Strain 3.60 %,
Temperature -40.0 °C		13940 psi
@Strain 3.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.31 MPa
@Strain 3.70 %,
Temperature -40.0 °C		13970 psi
@Strain 3.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.6 MPa
@Strain 32.0 %,
Temperature -40.0 °C		14000 psi
@Strain 32.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.9 MPa
@Strain 37.9 %,
Temperature -40.0 °C		14100 psi
@Strain 37.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.92 MPa
@Strain 3.70 %,
Temperature -40.0 °C		14060 psi
@Strain 3.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.36 MPa
@Strain 45.9 %,
Temperature -40.0 °C		14120 psi
@Strain 45.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 97.71 MPa
@Strain 3.80 %,
Temperature -40.0 °C		14170 psi
@Strain 3.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 97.87 MPa
@Strain 3.80 %,
Temperature -40.0 °C		14190 psi
@Strain 3.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 98.55 MPa
@Strain 16.9 %,
Temperature -40.0 °C		14290 psi
@Strain 16.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 98.64 MPa
@Strain 44.9 %,
Temperature -40.0 °C		14310 psi
@Strain 44.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 98.95 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14350 psi
@Strain 3.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.39 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14420 psi
@Strain 3.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.29 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14546 psi
@Strain 4.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14600 psi
@Strain 4.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.5 MPa
@Strain 4.10 %,
Temperature -40.0 °C		14720 psi
@Strain 4.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.58 MPa
@Strain 4.20 %,
Temperature -40.0 °C		14878 psi
@Strain 4.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.61 MPa
@Strain 4.10 %,
Temperature -40.0 °C		14882 psi
@Strain 4.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.54 MPa
@Strain 4.30 %,
Temperature -40.0 °C		15017 psi
@Strain 4.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.81 MPa
@Strain 4.20 %,
Temperature -40.0 °C		15056 psi
@Strain 4.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.96 MPa
@Strain 31.0 %,
Temperature -40.0 °C		15078 psi
@Strain 31.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.17 MPa
@Strain 4.40 %,
Temperature -40.0 °C		15109 psi
@Strain 4.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 105 MPa
@Strain 4.50 %,
Temperature -40.0 °C		15200 psi
@Strain 4.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 105.02 MPa
@Strain 4.30 %,
Temperature -40.0 °C		15232 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.7 MPa
@Strain 4.60 %,
Temperature -40.0 °C		15330 psi
@Strain 4.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.17 MPa
@Strain 30.0 %,
Temperature -40.0 °C		15399 psi
@Strain 30.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.27 MPa
@Strain 4.70 %,
Temperature -40.0 °C		15413 psi
@Strain 4.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.49 MPa
@Strain 4.40 %,
Temperature -40.0 °C		15445 psi
@Strain 4.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.97 MPa
@Strain 4.80 %,
Temperature -40.0 °C		15515 psi
@Strain 4.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.14 MPa
@Strain 29.0 %,
Temperature -40.0 °C		15539 psi
@Strain 29.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.23 MPa
@Strain 4.90 %,
Temperature -40.0 °C		15552 psi
@Strain 4.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.56 MPa
@Strain 4.50 %,
Temperature -40.0 °C		15600 psi
@Strain 4.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.67 MPa
@Strain 5.00 %,
Temperature -40.0 °C		15616 psi
@Strain 5.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.84 MPa
@Strain 15.9 %,
Temperature -40.0 °C		15641 psi
@Strain 15.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.71 MPa
@Strain 4.60 %,
Temperature -40.0 °C		15767 psi
@Strain 4.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.87 MPa
@Strain 5.50 %,
Temperature -40.0 °C		15790 psi
@Strain 5.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.42 MPa
@Strain 28.0 %,
Temperature -40.0 °C		15870 psi
@Strain 28.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.61 MPa
@Strain 24.0 %,
Temperature -40.0 °C		15898 psi
@Strain 24.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.82 MPa
@Strain 6.00 %,
Temperature -40.0 °C		15928 psi
@Strain 6.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.95 MPa
@Strain 25.0 %,
Temperature -40.0 °C		15947 psi
@Strain 25.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.97 MPa
@Strain 23.0 %,
Temperature -40.0 °C		15950 psi
@Strain 23.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.05 MPa
@Strain 6.50 %,
Temperature -40.0 °C		15961 psi
@Strain 6.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.08 MPa
@Strain 7.00 %,
Temperature -40.0 °C		15966 psi
@Strain 7.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.11 MPa
@Strain 4.70 %,
Temperature -40.0 °C		15970 psi
@Strain 4.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.27 MPa
@Strain 22.0 %,
Temperature -40.0 °C		15993 psi
@Strain 22.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.39 MPa
@Strain 7.50 %,
Temperature -40.0 °C		16011 psi
@Strain 7.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.46 MPa
@Strain 20.0 %,
Temperature -40.0 °C		16021 psi
@Strain 20.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.63 MPa
@Strain 21.0 %,
Temperature -40.0 °C		16046 psi
@Strain 21.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.86 MPa
@Strain 9.50 %,
Temperature -40.0 °C		16079 psi
@Strain 9.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.92 MPa
@Strain 27.0 %,
Temperature -40.0 °C		16088 psi
@Strain 27.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.97 MPa
@Strain 8.00 %,
Temperature -40.0 °C		16095 psi
@Strain 8.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.01 MPa
@Strain 9.00 %,
Temperature -40.0 °C		16101 psi
@Strain 9.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.02 MPa
@Strain 19.0 %,
Temperature -40.0 °C		16102 psi
@Strain 19.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.05 MPa
@Strain 4.80 %,
Temperature -40.0 °C		16106 psi
@Strain 4.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.11 MPa
@Strain 8.50 %,
Temperature -40.0 °C		16115 psi
@Strain 8.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.11 MPa
@Strain 14.0 %,
Temperature -40.0 °C		16115 psi
@Strain 14.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.29 MPa
@Strain 16.0 %,
Temperature -40.0 °C		16141 psi
@Strain 16.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.36 MPa
@Strain 18.0 %,
Temperature -40.0 °C		16151 psi
@Strain 18.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.37 MPa
@Strain 13.0 %,
Temperature -40.0 °C		16153 psi
@Strain 13.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.49 MPa
@Strain 26.0 %,
Temperature -40.0 °C		16170 psi
@Strain 26.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.49 MPa
@Strain 15.0 %,
Temperature -40.0 °C		16170 psi
@Strain 15.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.74 MPa
@Strain 10.0 %,
Temperature -40.0 °C		16207 psi
@Strain 10.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.79 MPa
@Strain 17.0 %,
Temperature -40.0 °C		16214 psi
@Strain 17.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.06 MPa
@Strain 12.0 %,
Temperature -40.0 °C		16253 psi
@Strain 12.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.54 MPa
@Strain 11.0 %,
Temperature -40.0 °C		16323 psi
@Strain 11.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.91 MPa
@Strain 4.90 %,
Temperature -40.0 °C		16376 psi
@Strain 4.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.31 MPa
@Strain 14.9 %,
Temperature -40.0 °C		16434 psi
@Strain 14.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.84 MPa
@Strain 13.9 %,
Temperature -40.0 °C		16946 psi
@Strain 13.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.31 MPa
@Strain 5.40 %,
Temperature -40.0 °C		17014 psi
@Strain 5.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.57 MPa
@Strain 12.9 %,
Temperature -40.0 °C		17342 psi
@Strain 12.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 121.11 MPa
@Strain 5.90 %,
Temperature -40.0 °C		17566 psi
@Strain 5.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 121.43 MPa
@Strain 11.9 %,
Temperature -40.0 °C		17612 psi
@Strain 11.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.04 MPa
@Strain 10.9 %,
Temperature -40.0 °C		17845 psi
@Strain 10.9 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.09 MPa
@Strain 6.40 %,
Temperature -40.0 °C		17853 psi
@Strain 6.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.94 MPa
@Strain 9.90 %,
Temperature -40.0 °C		17976 psi
@Strain 9.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.24 MPa
@Strain 9.40 %,
Temperature -40.0 °C		18020 psi
@Strain 9.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.26 MPa
@Strain 6.90 %,
Temperature -40.0 °C		18022 psi
@Strain 6.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.56 MPa
@Strain 8.90 %,
Temperature -40.0 °C		18066 psi
@Strain 8.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.82 MPa
@Strain 8.40 %,
Temperature -40.0 °C		18104 psi
@Strain 8.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.86 MPa
@Strain 7.40 %,
Temperature -40.0 °C		18109 psi
@Strain 7.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.99 MPa
@Strain 7.90 %,
Temperature -40.0 °C		18128 psi
@Strain 7.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Tensile Strength, Yield  32.0 MPa
@Temperature 121 °C		4640 psi
@Temperature 250 °F		50%RH; ASTM D638
 35.0 MPa
@Temperature 121 °C		5080 psi
@Temperature 250 °F		DAM; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		50%RH; ASTM D638
 55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 59.0 MPa
@Temperature 23.0 °C		8560 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 59.0 MPa
@Temperature 77.0 °C		8560 psi
@Temperature 171 °F		DAM; ASTM D638
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ISO 527
 85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		DAM; ASTM D638
 111 MPa
@Temperature -40.0 °C		16100 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 117 MPa
@Temperature -40.0 °C		17000 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  15 %
@Temperature -40.0 °C		15 %
@Temperature -40.0 °F		DAM; ASTM D638
 35 %
@Temperature -40.0 °C		35 %
@Temperature -40.0 °F		50%RH; ASTM D638
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 90 %
@Temperature 23.0 °C		90 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 100 %
@Temperature 23.0 °C		>= 100 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 155 %
@Temperature 77.0 °C		155 %
@Temperature 171 °F		DAM; ASTM D638
 200 %
@Temperature 121 °C		200 %
@Temperature 250 °F		DAM; ASTM D638
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 121 °C		>= 300 %
@Temperature 250 °F		50%RH; ASTM D638
Elongation at Yield  4.4 %
@Temperature 23.0 °C		4.4 %
@Temperature 73.4 °F		DAM; ISO 527
 5.0 %
@Temperature -40.0 °C		5.0 %
@Temperature -40.0 °F		50%RH; ASTM D638
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 27 %
@Temperature 23.0 °C		27 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 23.0 °C		30 %
@Temperature 73.4 °F		50%RH; ASTM D638
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		50%RH; ASTM D638
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 30 %
@Temperature 121 °C		30 %
@Temperature 250 °F		DAM; ASTM D638
 30 %
@Temperature 121 °C		30 %
@Temperature 250 °F		50%RH; ASTM D638
Tensile Modulus  1.30 GPa
@Temperature 23.0 °C		189 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.414 GPa
@Temperature 121 °C		60.0 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.538 GPa
@Temperature 121 °C		78.0 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.565 GPa
@Temperature 77.0 °C		81.9 ksi
@Temperature 171 °F		50%RH; ASTM D790
 0.690 GPa
@Temperature 77.0 °C		100 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.07 GPa
@Temperature 23.0 °C		155 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 1.21 GPa
@Temperature 23.0 °C		175 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.83 GPa
@Temperature 23.0 °C		410 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 3.24 GPa
@Temperature -40.0 °C		470 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 3.45 GPa
@Temperature -40.0 °C		500 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Strength  63.0 MPa
@Temperature 23.0 °C		9140 psi
@Temperature 73.4 °F		50%RH; ASTM D732
 66.0 MPa
@Temperature 23.0 °C		9570 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.270 J/cm
@Temperature -40.0 °C		0.506 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.640 J/cm
@Temperature 23.0 °C		1.20 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 6.00 kJ/m²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 7.00 kJ/m²
@Temperature -30.0 °C		3.33 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 23.0 kJ/m²
@Temperature 23.0 °C		10.9 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 180/1U
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 2.00 J/cm²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Impact Strength 535 kJ/m²
@Temperature 23.0 °C		255 ft-lb/in²
@Temperature 73.4 °F		DAM; Long specimen; ASTM D1822
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 100 Hz,
Temperature 23.0 °C		4.0
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 4.3
@Frequency 100 Hz,
Temperature 23.0 °C		4.3
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 7.0
@Frequency 1000 Hz,
Temperature 23.0 °C		7.0
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 8.0
@Frequency 100 Hz,
Temperature 23.0 °C		8.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 10.3
@Frequency 100 Hz,
Temperature 23.0 °C		10.3
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 30.5 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		775 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.015
@Frequency 100 Hz,
Temperature 23.0 °C		0.015
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.024
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.024
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.075
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.075
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 1000 Hz,
Temperature 23.0 °C		0.20
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FDAM; ASTM D648
 70.0 °C158 °FDAM; ISO 75-1/-2
Brittleness Temperature -100 °C-148 °FDAM; ASTM D746
 -85.0 °C-121 °F50%RH; ASTM D746
Glass Transition Temp, Tg 70.0 °C158 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  125 °C
@Thickness 0.710 mm		257 °F
@Thickness 0.0280 in		DAM; UL 746B
 125 °C
@Thickness 6.00 mm		257 °F
@Thickness 0.236 in		DAM; UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
 125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 0.710 mm		149 °F
@Thickness 0.0280 in		DAM; UL 746B
 75.0 °C
@Thickness 6.00 mm		167 °F
@Thickness 0.236 in		DAM; UL 746B
 75.0 °C
@Thickness 3.00 mm		167 °F
@Thickness 0.118 in		DAM; UL 746B
 75.0 °C
@Thickness 1.50 mm		167 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 0.710 mm		149 °F
@Thickness 0.0280 in		DAM; UL 746B
 85.0 °C
@Thickness 1.50 mm		185 °F
@Thickness 0.0591 in		DAM; UL 746B
 85.0 °C
@Thickness 3.00 mm		185 °F
@Thickness 0.118 in		DAM; UL 746B
 85.0 °C
@Thickness 6.00 mm		185 °F
@Thickness 0.236 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 V-2
@Thickness 6.00 mm		V-2
@Thickness 0.236 in		DAM; UL94
Oxygen Index 28 %28 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 285 °C545 °FDAM; Optimum; Extrusion
 280 - 290 °C536 - 554 °FDAM; Extrusion
 280 - 300 °C536 - 572 °FDAM; Injection Molding
 290 °C554 °FDAM; Optimum; Injection Molding
Mold Temperature 70.0 °C158 °FDAM; optimum; Injection Molding
 50.0 - 90.0 °C122 - 194 °FDAM; Injection Molding
Drying Temperature 80.0 °C176 °FDAM; Extrusion
 80.0 °C176 °FDAM; Injection Molding
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM; Injection Molding
 4.00 - 6.00 hour4.00 - 6.00 hourDAM; Extrusion
Moisture Content <= 0.050 %<= 0.050 %DAM; Extrusion
 <= 0.050 %<= 0.050 %DAM; Injection Molding
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
Extrudable - CoatingYesDAM
Extrudable - FilamentYesDAM
Extrudable - SheetYesDAM
Extrudable - TubingYesDAM
FeaturesMolecular Wt., HighDAM
 Viscosity, HighDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodExtrusionDAM
 ExtrusionDAM
 Injection MoldingDAM
Product CategoryExtrusion ResinsDAM
 Unreinforced ResinsDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesGearsDAM
 Stock Material for MachiningDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45458.html

免责声明: 本文 DuPont Performance Polymers Zytel® 42A NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4