- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 2.0
- 缺口冲击强度: 8.0
- 硬度: 116.0
- 热变形温度 [℃]: 263.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.4 % @Temperature 23.0 °C | 6.4 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 87 | 87 | 50%RH; ISO 2039/2 | ||
| 103 | 103 | DAM; ISO 2039/2 | |||
| Hardness, Rockwell R | 116 | 116 | 50%RH; ISO 2039/2 | ||
| 123 | 123 | DAM; ISO 2039/2 | |||
| Tensile Strength at Break | 115 MPa @Temperature 23.0 °C | 16700 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 188 MPa @Temperature 23.0 °C | 27300 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.1 % @Temperature 23.0 °C | 3.1 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.10 GPa @Temperature 23.0 °C | 885 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 8.60 GPa @Temperature 23.0 °C | 1250 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 240 MPa @Temperature 23.0 °C | 34800 psi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Shear Modulus | 0.265 GPa @Temperature 250 °C | 38.4 ksi @Temperature 482 °F | DAM; ISO 6721 | ||
| 0.348 GPa @Temperature 240 °C | 50.5 ksi @Temperature 464 °F | DAM; ISO 6721 | |||
| 0.395 GPa @Temperature 230 °C | 57.3 ksi @Temperature 446 °F | DAM; ISO 6721 | |||
| 0.426 GPa @Temperature 220 °C | 61.8 ksi @Temperature 428 °F | DAM; ISO 6721 | |||
| 0.448 GPa @Temperature 210 °C | 65.0 ksi @Temperature 410 °F | DAM; ISO 6721 | |||
| 0.464 GPa @Temperature 200 °C | 67.3 ksi @Temperature 392 °F | DAM; ISO 6721 | |||
| 0.479 GPa @Temperature 190 °C | 69.5 ksi @Temperature 374 °F | DAM; ISO 6721 | |||
| 0.495 GPa @Temperature 180 °C | 71.8 ksi @Temperature 356 °F | DAM; ISO 6721 | |||
| 0.510 GPa @Temperature 170 °C | 74.0 ksi @Temperature 338 °F | DAM; ISO 6721 | |||
| 0.524 GPa @Temperature 160 °C | 76.0 ksi @Temperature 320 °F | DAM; ISO 6721 | |||
| 0.539 GPa @Temperature 150 °C | 78.2 ksi @Temperature 302 °F | DAM; ISO 6721 | |||
| 0.556 GPa @Temperature 140 °C | 80.6 ksi @Temperature 284 °F | DAM; ISO 6721 | |||
| 0.575 GPa @Temperature 130 °C | 83.4 ksi @Temperature 266 °F | DAM; ISO 6721 | |||
| 0.597 GPa @Temperature 120 °C | 86.6 ksi @Temperature 248 °F | DAM; ISO 6721 | |||
| 0.628 GPa @Temperature 110 °C | 91.1 ksi @Temperature 230 °F | DAM; ISO 6721 | |||
| 0.676 GPa @Temperature 100 °C | 98.0 ksi @Temperature 212 °F | DAM; ISO 6721 | |||
| 0.754 GPa @Temperature 90.0 °C | 109 ksi @Temperature 194 °F | DAM; ISO 6721 | |||
| 0.878 GPa @Temperature 80.0 °C | 127 ksi @Temperature 176 °F | DAM; ISO 6721 | |||
| 1.05 GPa @Temperature 70.0 °C | 152 ksi @Temperature 158 °F | DAM; ISO 6721 | |||
| 1.29 GPa @Temperature 60.0 °C | 187 ksi @Temperature 140 °F | DAM; ISO 6721 | |||
| 1.60 GPa @Temperature 50.0 °C | 232 ksi @Temperature 122 °F | DAM; ISO 6721 | |||
| 1.72 GPa @Temperature 40.0 °C | 249 ksi @Temperature 104 °F | DAM; ISO 6721 | |||
| 1.78 GPa @Temperature 30.0 °C | 258 ksi @Temperature 86.0 °F | DAM; ISO 6721 | |||
| 1.83 GPa @Temperature 20.0 °C | 265 ksi @Temperature 68.0 °F | DAM; ISO 6721 | |||
| 1.87 GPa @Temperature 10.0 °C | 271 ksi @Temperature 50.0 °F | DAM; ISO 6721 | |||
| 1.90 GPa @Temperature 0.000 °C | 276 ksi @Temperature 32.0 °F | DAM; ISO 6721 | |||
| 1.91 GPa @Temperature -10.0 °C | 277 ksi @Temperature 14.0 °F | DAM; ISO 6721 | |||
| 1.92 GPa @Temperature -20.0 °C | 278 ksi @Temperature -4.00 °F | DAM; ISO 6721 | |||
| 1.93 GPa @Temperature -30.0 °C | 280 ksi @Temperature -22.0 °F | DAM; ISO 6721 | |||
| 1.96 GPa @Temperature -40.0 °C | 284 ksi @Temperature -40.0 °F | DAM; ISO 6721 | |||
| 1.99 GPa @Temperature -50.0 °C | 289 ksi @Temperature -58.0 °F | DAM; ISO 6721 | |||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.70 J/cm² @Temperature -30.0 °C | 22.4 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 5.30 J/cm² @Temperature -30.0 °C | 25.2 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 8.50 J/cm² @Temperature 23.0 °C | 40.4 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.10 J/cm² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 5000 MPa @Temperature 23.0 °C | 725000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 4100 MPa @Temperature 23.0 °C | 595000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 23.0 °C | 1.00e+11 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm @Temperature 23.0 °C | >= 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| 1.00e+17 ohm-cm @Temperature 23.0 °C | 1.00e+17 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm @Temperature 23.0 °C | >= 1.00e+15 ohm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.1 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 4.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.5 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.073 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.073 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature 23.0 - 55.0 °C | 62.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 112 µm/m-°C @Temperature 23.0 - 55.0 °C | 62.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C | 505 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 125 °C @Thickness 0.710 mm | 257 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF25< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Resin Identification | PA66-GF25 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||