- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.95
- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 0.690
- 硬度: 121.0
- 热变形温度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | DAM; ASTM D792 | ||
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 0.95 % @Temperature 23.0 °C | 0.95 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | ||
| 2.7 % @Temperature 23.0 °C | 2.7 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | |||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | Saturation; DAM; ASTM D570 | |||
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.20 mm | 0.012 in/in @Thickness 0.126 in | Flow; DAM | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | DAM; ASTM D785 | ||
| Tensile Strength | 41.4 MPa @Temperature 77.0 °C | 6000 psi @Temperature 171 °F | 50%RH; ASTM D638 | ||
| 48.3 MPa @Temperature 77.0 °C | 7010 psi @Temperature 171 °F | DAM; ASTM D638 | |||
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 111 MPa @Temperature -40.0 °C | 16100 psi @Temperature -40.0 °F | 50%RH; ASTM D638 | |||
| 114 MPa @Temperature -40.0 °C | 16500 psi @Temperature -40.0 °F | DAM; ASTM D638 | |||
| Tensile Strength, Yield | 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 85.0 MPa @Temperature 23.0 °C | 12300 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 10 % @Temperature -40.0 °C | 10 % @Temperature -40.0 °F | 50%RH; ASTM D638 | ||
| 10 % @Temperature -40.0 °C | 10 % @Temperature -40.0 °F | DAM; ASTM D638 | |||
| 24 % @Temperature 23.0 °C | 24 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| >= 25 % @Temperature 23.0 °C | >= 25 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| >= 120 % @Temperature 23.0 °C | >= 120 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| >= 120 % @Temperature 77.0 °C | >= 120 % @Temperature 171 °F | DAM; ASTM D638 | |||
| >= 200 % @Temperature 77.0 °C | >= 200 % @Temperature 171 °F | 50%RH; ASTM D638 | |||
| Elongation at Yield | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.20 GPa @Temperature 23.0 °C | 464 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 0.690 GPa @Temperature 77.0 °C | 100 ksi @Temperature 171 °F | DAM; ASTM D790 | ||
| 0.690 GPa @Temperature 77.0 °C | 100 ksi @Temperature 171 °F | 50%RH; ASTM D790 | |||
| 1.38 GPa @Temperature 23.0 °C | 200 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | |||
| 2.83 GPa @Temperature 23.0 °C | 410 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| 3.93 GPa @Temperature -40.0 °C | 570 ksi @Temperature -40.0 °F | 50%RH; ASTM D790 | |||
| 4.48 GPa @Temperature -40.0 °C | 650 ksi @Temperature -40.0 °F | DAM; ASTM D790 | |||
| Shear Strength | 65.5 MPa @Temperature 23.0 °C | 9500 psi @Temperature 73.4 °F | 50%RH; ASTM D732 | ||
| 72.4 MPa @Temperature 23.0 °C | 10500 psi @Temperature 73.4 °F | DAM; ASTM D732 | |||
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C | 0.899 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 0.590 J/cm @Temperature -40.0 °C | 1.11 ft-lb/in @Temperature -40.0 °F | 50%RH; ASTM D256 | |||
| 0.590 J/cm @Temperature -40.0 °C | 1.11 ft-lb/in @Temperature -40.0 °F | DAM; ASTM D256 | |||
| 0.640 J/cm @Temperature 77.0 °C | 1.20 ft-lb/in @Temperature 171 °F | DAM; ASTM D256 | |||
| 1.10 J/cm @Temperature 23.0 °C | 2.06 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| 2.70 J/cm @Temperature 77.0 °C | 5.06 ft-lb/in @Temperature 171 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Impact Strength | 340 kJ/m² @Temperature 23.0 °C | 162 ft-lb/in² @Temperature 73.4 °F | DAM; Long specimen; ASTM D1822 | ||
| 920 kJ/m² @Temperature 23.0 °C | 438 ft-lb/in² @Temperature 73.4 °F | 50%RH; Long specimen; ASTM D1822 | |||
| Tensile Creep Modulus, 1 hour | 1340 MPa @Temperature 23.0 °C | 194000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 600 MPa @Temperature 23.0 °C | 87000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm @Temperature 23.0 °C | 1.00e+12 ohm-cm @Temperature 73.4 °F | 50%RH; ASTM D257 | ||
| 1.00e+14 ohm-cm @Temperature 23.0 °C | 1.00e+14 ohm-cm @Temperature 73.4 °F | DAM; ASTM D257 | |||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.4 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 3.7 @Frequency 100 Hz, Temperature 23.0 °C | 3.7 @Frequency 100 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| 3.7 @Frequency 1000 Hz, Temperature 23.0 °C | 3.7 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| 4.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 5.4 @Frequency 1000 Hz, Temperature 23.0 °C | 5.4 @Frequency 1000 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| 6.5 @Frequency 100 Hz, Temperature 23.0 °C | 6.5 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| Dissipation Factor | 0.010 @Frequency 100 Hz, Temperature 23.0 °C | 0.010 @Frequency 100 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 0.010 @Frequency 1000 Hz, Temperature 23.0 °C | 0.010 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| 0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.020 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| 0.030 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.030 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 0.050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| 0.060 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.060 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 0.12 @Frequency 1000 Hz, Temperature 23.0 °C | 0.12 @Frequency 1000 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| 0.13 @Frequency 100 Hz, Temperature 23.0 °C | 0.13 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C | 278 µin/in-°F | DAM; ASTM E 228 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 | ||
| 210 °C | 410 °F | DAM; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ASTM D648 | ||
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 125 °C @Thickness 0.710 mm | 257 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 125 °C @Thickness 6.00 mm | 257 °F @Thickness 0.236 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.710 mm | 149 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 75.0 °C @Thickness 1.50 mm | 167 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 6.00 mm | 167 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.710 mm | 149 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 6.00 mm | 185 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; UL94 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; UL94 | |||
| Oxygen Index | 27 % | 27 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Molding Cycle, Fast | DAM | |||
| Wear Resistance, Good | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| UV Resistant/Weatherable Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||