塑胶原料之家
  1. 首页
  2. 英文物性
  3. PA66
  4. DuPont Performance Polymers Minlon® 22C NC010 Nylon 66

DuPont Performance Polymers Minlon® 22C NC010 Nylon 66

DuPont Performance Polymers Minlon® 22C NC010 Nylon 66 物性表: DuPont Performance Polymers Minlon® 22C NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® 22C NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® 22C NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.45
  • 吸水率 [%]: 0.7
  • 成型收缩率 [%]: 0.006
  • 缺口冲击强度: 0.32
  • 弯曲模量 [MPa]: 1.38
  • 硬度: 122.0
  • 热变形温度 [℃]: 255.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.45 g/cc1.45 g/ccDAM; ASTM D792
Density 1.45 g/cc0.0524 lb/in³DAM; ISO 1183
Filler Content 38 %38 %DAM
Water Absorption  0.70 %
@Temperature 23.0 °C		0.70 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.0 %
@Temperature 23.0 °C		1.0 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 1.4 %
@Temperature 23.0 °C		1.4 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 4.7 %
@Temperature 23.0 °C		4.7 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 5.4 %
@Temperature 23.0 °C		5.4 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0060 cm/cm
@Thickness 1.60 mm		0.0060 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0070 cm/cm
@Thickness 3.20 mm		0.0070 in/in
@Thickness 0.126 in		Flow; DAM
 0.0080 cm/cm
@Thickness 6.40 mm		0.0080 in/in
@Thickness 0.252 in		Flow; DAM
 0.0080 cm/cm
@Thickness 1.60 mm		0.0080 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.0090 cm/cm
@Thickness 3.20 mm		0.0090 in/in
@Thickness 0.126 in		Transverse; DAM
 0.011 cm/cm
@Thickness 6.40 mm		0.011 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 9797DAM; ASTM D785
Hardness, Rockwell R 122122DAM; ASTM D785
Tensile Strength at Break  82.0 MPa
@Temperature 23.0 °C		11900 psi
@Temperature 73.4 °F		50%RH; ISO 527
 130 MPa
@Temperature 23.0 °C		18900 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  44.0 MPa
@Temperature 121 °C		6380 psi
@Temperature 250 °F		50%RH; ASTM D638
 52.0 MPa
@Temperature 121 °C		7540 psi
@Temperature 250 °F		DAM; ASTM D638
 56.0 MPa
@Temperature 77.0 °C		8120 psi
@Temperature 171 °F		50%RH; ASTM D638
 66.0 MPa
@Temperature 77.0 °C		9570 psi
@Temperature 171 °F		DAM; ASTM D638
 86.0 MPa
@Temperature 23.0 °C		12500 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 128 MPa
@Temperature 23.0 °C		18600 psi
@Temperature 73.4 °F		DAM; ASTM D638
 134 MPa
@Temperature -40.0 °C		19400 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 145 MPa
@Temperature -40.0 °C		21000 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  2.10 MPa
@Strain 0.100 %,
Temperature 150 °C		305 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.10 MPa
@Strain 0.100 %,
Temperature 150 °C		305 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.30 MPa
@Strain 0.100 %,
Temperature 120 °C		334 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.30 MPa
@Strain 0.100 %,
Temperature 120 °C		334 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.40 MPa
@Strain 0.100 %,
Temperature 100 °C		348 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.60 MPa
@Strain 0.100 %,
Temperature 100 °C		377 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.80 MPa
@Strain 0.100 %,
Temperature 80.0 °C		406 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.00 MPa
@Strain 0.100 %,
Temperature 60.0 °C		435 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.26 MPa
@Strain 0.100 %,
Temperature 80.0 °C		473 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.30 MPa
@Strain 0.200 %,
Temperature 150 °C		624 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.30 MPa
@Strain 0.200 %,
Temperature 150 °C		624 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.50 MPa
@Strain 0.200 %,
Temperature 120 °C		653 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.60 MPa
@Strain 0.200 %,
Temperature 120 °C		667 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.60 MPa
@Strain 0.100 %,
Temperature 23.0 °C		667 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.80 MPa
@Strain 0.100 %,
Temperature 60.0 °C		696 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 4.80 MPa
@Strain 0.200 %,
Temperature 100 °C		696 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.30 MPa
@Strain 0.200 %,
Temperature 100 °C		769 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.60 MPa
@Strain 0.200 %,
Temperature 80.0 °C		812 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.00 MPa
@Strain 0.200 %,
Temperature 60.0 °C		870 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.30 MPa
@Strain 0.300 %,
Temperature 150 °C		914 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.50 MPa
@Strain 0.300 %,
Temperature 150 °C		943 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.53 MPa
@Strain 0.200 %,
Temperature 80.0 °C		947 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 0.300 %,
Temperature 120 °C		957 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.80 MPa
@Strain 0.300 %,
Temperature 120 °C		986 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.90 MPa
@Strain 0.300 %,
Temperature 100 °C		1000 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.20 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1040 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 7.60 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1100 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 7.70 MPa
@Strain 0.400 %,
Temperature 150 °C		1120 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.80 MPa
@Strain 0.300 %,
Temperature 100 °C		1130 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.979 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1157 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 8.50 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1230 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.50 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1230 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.90 MPa
@Strain 0.400 %,
Temperature 150 °C		1290 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.00 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1310 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 9.10 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1320 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.20 MPa
@Strain 0.400 %,
Temperature 120 °C		1330 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.40 MPa
@Strain 0.400 %,
Temperature 120 °C		1360 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.50 MPa
@Strain 0.400 %,
Temperature 100 °C		1380 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.60 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1390 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.74 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1410 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.89 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1430 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 10.3 MPa
@Strain 0.500 %,
Temperature 150 °C		1490 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.5 MPa
@Strain 0.400 %,
Temperature 100 °C		1520 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.8 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1570 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.9 MPa
@Strain 0.500 %,
Temperature 150 °C		1580 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1620 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.5 MPa
@Strain 0.500 %,
Temperature 120 °C		1670 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 0.500 %,
Temperature 120 °C		1700 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.7 MPa
@Strain 0.500 %,
Temperature 100 °C		1700 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 0.600 %,
Temperature 150 °C		1770 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.6 MPa
@Strain 0.600 %,
Temperature 150 °C		1830 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.7 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1840 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 0.500 %,
Temperature 100 °C		1870 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.0 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1890 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.3 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1930 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.6 MPa
@Strain 0.600 %,
Temperature 120 °C		1970 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.7 MPa
@Strain 0.600 %,
Temperature 120 °C		1990 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.99 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2029 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 14.0 MPa
@Strain 0.700 %,
Temperature 150 °C		2030 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.0 MPa
@Strain 0.600 %,
Temperature 100 °C		2030 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.1 MPa
@Strain 0.700 %,
Temperature 150 °C		2050 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.1 MPa
@Strain 0.300 %,
Temperature 60.0 °C		2050 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.2 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2060 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.8 MPa
@Strain 0.600 %,
Temperature 100 °C		2150 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.9 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2160 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 15.4 MPa
@Strain 0.700 %,
Temperature 120 °C		2230 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.6 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2260 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 0.800 %,
Temperature 150 °C		2280 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 0.500 %,
Temperature 80.0 °C		2281 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.8 MPa
@Strain 0.800 %,
Temperature 150 °C		2290 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.8 MPa
@Strain 0.700 %,
Temperature 120 °C		2290 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.2 MPa
@Strain 0.700 %,
Temperature 100 °C		2350 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.7 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2420 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.9 MPa
@Strain 0.700 %,
Temperature 100 °C		2450 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.1 MPa
@Strain 0.400 %,
Temperature 60.0 °C		2480 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.3 MPa
@Strain 0.900 %,
Temperature 150 °C		2510 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 0.800 %,
Temperature 120 °C		2520 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.4 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2520 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.452 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2531.2 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 17.6 MPa
@Strain 0.900 %,
Temperature 150 °C		2550 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.6 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2550 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.8 MPa
@Strain 0.800 %,
Temperature 120 °C		2580 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.2 MPa
@Strain 0.800 %,
Temperature 100 °C		2640 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.3 MPa
@Strain 0.200 %,
Temperature 0.000 °C		2650 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 18.7 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2710 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 0.800 %,
Temperature 100 °C		2730 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.8 MPa
@Strain 1.00 %,
Temperature 150 °C		2730 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.9 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2740 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.1 MPa
@Strain 1.00 %,
Temperature 150 °C		2770 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 0.900 %,
Temperature 120 °C		2800 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.5 MPa
@Strain 0.900 %,
Temperature 120 °C		2830 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.6 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2840 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.87 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2882 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 20.1 MPa
@Strain 0.900 %,
Temperature 100 °C		2920 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.1 MPa
@Strain 1.10 %,
Temperature 150 °C		2920 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.5 MPa
@Strain 1.10 %,
Temperature 150 °C		2970 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.9 MPa
@Strain 0.900 %,
Temperature 100 °C		3030 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.0 MPa
@Strain 1.00 %,
Temperature 120 °C		3050 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.1 MPa
@Strain 1.00 %,
Temperature 120 °C		3060 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.23 MPa
@Strain 0.700 %,
Temperature 80.0 °C		3079 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.23 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3079 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 21.6 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3130 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 1.20 %,
Temperature 150 °C		3130 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.7 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3150 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.9 MPa
@Strain 1.00 %,
Temperature 100 °C		3180 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.9 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3180 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 1.20 %,
Temperature 150 °C		3190 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.7 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3290 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 22.8 MPa
@Strain 1.10 %,
Temperature 120 °C		3310 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.8 MPa
@Strain 1.10 %,
Temperature 120 °C		3310 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 1.00 %,
Temperature 100 °C		3310 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.9 MPa
@Strain 1.30 %,
Temperature 150 °C		3320 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.1 MPa
@Strain 0.500 %,
Temperature 60.0 °C		3350 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.3 MPa
@Strain 1.30 %,
Temperature 150 °C		3380 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.6 MPa
@Strain 1.10 %,
Temperature 100 °C		3420 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.63 MPa
@Strain 0.800 %,
Temperature 80.0 °C		3427 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.7 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3440 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.0 MPa
@Strain 0.900 %,
Temperature 60.0 °C		3480 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.0 MPa
@Strain 1.40 %,
Temperature 150 °C		3480 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.3 MPa
@Strain 1.20 %,
Temperature 120 °C		3520 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.4 MPa
@Strain 1.20 %,
Temperature 120 °C		3540 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.5 MPa
@Strain 1.40 %,
Temperature 150 °C		3550 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.5 MPa
@Strain 1.10 %,
Temperature 100 °C		3550 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.2 MPa
@Strain 1.20 %,
Temperature 100 °C		3650 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.3 MPa
@Strain 1.50 %,
Temperature 150 °C		3670 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3710 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.7 MPa
@Strain 1.30 %,
Temperature 120 °C		3730 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.7 MPa
@Strain 1.50 %,
Temperature 150 °C		3730 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.855 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3750.0 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 25.9 MPa
@Strain 1.30 %,
Temperature 120 °C		3760 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		3770 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.1 MPa
@Strain 1.20 %,
Temperature 100 °C		3790 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.1 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3790 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.3 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3810 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.4 MPa
@Strain 1.60 %,
Temperature 150 °C		3830 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.9 MPa
@Strain 1.60 %,
Temperature 150 °C		3900 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.9 MPa
@Strain 1.30 %,
Temperature 100 °C		3900 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.9 MPa
@Strain 0.300 %,
Temperature 0.000 °C		3900 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 27.0 MPa
@Strain 1.40 %,
Temperature 120 °C		3920 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.4 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3970 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.4 MPa
@Strain 1.70 %,
Temperature 150 °C		3970 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.4 MPa
@Strain 1.40 %,
Temperature 120 °C		3970 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.4 MPa
@Strain 0.600 %,
Temperature 60.0 °C		3970 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.6 MPa
@Strain 1.30 %,
Temperature 100 °C		4000 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.1 MPa
@Strain 1.70 %,
Temperature 150 °C		4080 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.3 MPa
@Strain 1.80 %,
Temperature 150 °C		4100 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.3 MPa
@Strain 1.50 %,
Temperature 120 °C		4100 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.37 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4115 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.42 MPa
@Strain 1.00 %,
Temperature 80.0 °C		4122 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.5 MPa
@Strain 1.40 %,
Temperature 100 °C		4130 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.5 MPa
@Strain 1.10 %,
Temperature 60.0 °C		4130 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.8 MPa
@Strain 1.50 %,
Temperature 120 °C		4180 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 1.40 %,
Temperature 100 °C		4190 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.0 MPa
@Strain 0.400 %,
Temperature 0.000 °C		4210 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 29.1 MPa
@Strain 1.80 %,
Temperature 150 °C		4220 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.2 MPa
@Strain 1.90 %,
Temperature 150 °C		4240 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.4 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4260 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.6 MPa
@Strain 1.60 %,
Temperature 120 °C		4290 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.7 MPa
@Strain 0.700 %,
Temperature 23.0 °C		4310 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.76 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4316 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 1.50 %,
Temperature 100 °C		4350 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.1 MPa
@Strain 1.90 %,
Temperature 150 °C		4370 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.1 MPa
@Strain 2.00 %,
Temperature 150 °C		4370 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.2 MPa
@Strain 1.60 %,
Temperature 120 °C		4380 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.24 MPa
@Strain 1.10 %,
Temperature 80.0 °C		4386 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.4 MPa
@Strain 1.20 %,
Temperature 60.0 °C		4410 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.6 MPa
@Strain 1.50 %,
Temperature 100 °C		4440 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.7 MPa
@Strain 1.70 %,
Temperature 120 °C		4450 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.9 MPa
@Strain 2.10 %,
Temperature 150 °C		4480 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.1 MPa
@Strain 2.00 %,
Temperature 150 °C		4510 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.3 MPa
@Strain 1.60 %,
Temperature 100 °C		4540 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.3 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4540 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 0.700 %,
Temperature 60.0 °C		4550 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 1.70 %,
Temperature 120 °C		4570 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.6 MPa
@Strain 2.20 %,
Temperature 150 °C		4580 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.9 MPa
@Strain 1.80 %,
Temperature 120 °C		4630 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.0 MPa
@Strain 1.60 %,
Temperature 100 °C		4640 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.2 MPa
@Strain 2.10 %,
Temperature 150 °C		4670 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.27 MPa
@Strain 1.20 %,
Temperature 80.0 °C		4680 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.5 MPa
@Strain 2.30 %,
Temperature 150 °C		4710 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.7 MPa
@Strain 1.80 %,
Temperature 120 °C		4740 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.7 MPa
@Strain 1.30 %,
Temperature 60.0 °C		4740 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.7 MPa
@Strain 1.70 %,
Temperature 100 °C		4740 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.0 MPa
@Strain 1.90 %,
Temperature 120 °C		4790 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.0 MPa
@Strain 2.20 %,
Temperature 150 °C		4790 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.1 MPa
@Strain 2.40 %,
Temperature 150 °C		4800 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 1.70 %,
Temperature 100 °C		4800 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		4800 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.461 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4853.1 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 33.6 MPa
@Strain 2.50 %,
Temperature 150 °C		4870 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.9 MPa
@Strain 2.30 %,
Temperature 150 °C		4920 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.9 MPa
@Strain 1.90 %,
Temperature 120 °C		4920 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.0 MPa
@Strain 2.00 %,
Temperature 120 °C		4930 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.0 MPa
@Strain 1.80 %,
Temperature 100 °C		4930 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.1 MPa
@Strain 1.60 %,
Temperature 80.0 °C		4950 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.3 MPa
@Strain 1.80 %,
Temperature 100 °C		4970 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.3 MPa
@Strain 2.60 %,
Temperature 150 °C		4970 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.4 MPa
@Strain 1.40 %,
Temperature 60.0 °C		4990 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.54 MPa
@Strain 1.30 %,
Temperature 80.0 °C		5010 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.7 MPa
@Strain 0.400 %,
Temperature 0.000 °C		5030 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 2.70 %,
Temperature 150 °C		5050 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.8 MPa
@Strain 2.40 %,
Temperature 150 °C		5050 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.9 MPa
@Strain 2.10 %,
Temperature 120 °C		5060 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.0 MPa
@Strain 2.00 %,
Temperature 120 °C		5080 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.2 MPa
@Strain 1.90 %,
Temperature 100 °C		5110 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.4 MPa
@Strain 2.80 %,
Temperature 150 °C		5130 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 0.800 %,
Temperature 60.0 °C		5130 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.5 MPa
@Strain 2.50 %,
Temperature 150 °C		5150 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.51 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5150 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 35.6 MPa
@Strain 2.20 %,
Temperature 120 °C		5160 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 1.90 %,
Temperature 100 °C		5160 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.7 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5180 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 1.50 %,
Temperature 60.0 °C		5190 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 2.90 %,
Temperature 150 °C		5210 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.1 MPa
@Strain 2.60 %,
Temperature 150 °C		5240 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.1 MPa
@Strain 2.10 %,
Temperature 120 °C		5240 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.2 MPa
@Strain 3.00 %,
Temperature 150 °C		5250 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.3 MPa
@Strain 0.900 %,
Temperature 23.0 °C		5260 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.36 MPa
@Strain 1.40 %,
Temperature 80.0 °C		5274 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.5 MPa
@Strain 2.00 %,
Temperature 100 °C		5290 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.5 MPa
@Strain 2.30 %,
Temperature 120 °C		5290 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 2.00 %,
Temperature 100 °C		5310 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 3.10 %,
Temperature 150 °C		5310 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 2.70 %,
Temperature 150 °C		5340 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.0 MPa
@Strain 3.20 %,
Temperature 150 °C		5370 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5370 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.2 MPa
@Strain 2.40 %,
Temperature 120 °C		5400 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.2 MPa
@Strain 2.20 %,
Temperature 120 °C		5400 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 0.500 %,
Temperature 0.000 °C		5410 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 37.5 MPa
@Strain 3.30 %,
Temperature 150 °C		5440 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.5 MPa
@Strain 2.10 %,
Temperature 100 °C		5440 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.5 MPa
@Strain 1.60 %,
Temperature 60.0 °C		5440 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 2.10 %,
Temperature 100 °C		5450 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.6 MPa
@Strain 2.80 %,
Temperature 150 °C		5450 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.8 MPa
@Strain 3.40 %,
Temperature 150 °C		5480 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.0 MPa
@Strain 2.50 %,
Temperature 120 °C		5510 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.1 MPa
@Strain 1.50 %,
Temperature 80.0 °C		5530 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.1 MPa
@Strain 3.50 %,
Temperature 150 °C		5530 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.1 MPa
@Strain 2.30 %,
Temperature 120 °C		5530 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.2 MPa
@Strain 2.90 %,
Temperature 150 °C		5540 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.5 MPa
@Strain 3.60 %,
Temperature 150 °C		5580 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.5 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5580 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.6 MPa
@Strain 2.60 %,
Temperature 120 °C		5600 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.7 MPa
@Strain 2.20 %,
Temperature 100 °C		5610 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.8 MPa
@Strain 2.20 %,
Temperature 100 °C		5630 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.8 MPa
@Strain 3.70 %,
Temperature 150 °C		5630 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.9 MPa
@Strain 3.00 %,
Temperature 150 °C		5640 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.9 MPa
@Strain 3.80 %,
Temperature 150 °C		5640 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.9 MPa
@Strain 0.900 %,
Temperature 60.0 °C		5640 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.98 MPa
@Strain 0.400 %,
Temperature -40.0 °C		5654 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 39.0 MPa
@Strain 1.70 %,
Temperature 60.0 °C		5660 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.1 MPa
@Strain 2.40 %,
Temperature 120 °C		5670 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 3.90 %,
Temperature 150 °C		5670 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 2.70 %,
Temperature 120 °C		5690 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 1.00 %,
Temperature 23.0 °C		5690 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.4 MPa
@Strain 4.00 %,
Temperature 150 °C		5710 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.5 MPa
@Strain 4.10 %,
Temperature 150 °C		5730 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 3.10 %,
Temperature 150 °C		5740 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 2.30 %,
Temperature 100 °C		5740 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.73 MPa
@Strain 1.60 %,
Temperature 80.0 °C		5762 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 4.20 %,
Temperature 150 °C		5770 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.8 MPa
@Strain 2.80 %,
Temperature 120 °C		5770 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 4.30 %,
Temperature 150 °C		5790 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 2.30 %,
Temperature 100 °C		5790 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.9 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5790 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.0 MPa
@Strain 2.50 %,
Temperature 120 °C		5800 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.2 MPa
@Strain 4.40 %,
Temperature 150 °C		5830 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.2 MPa
@Strain 3.20 %,
Temperature 150 °C		5830 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.3 MPa
@Strain 4.50 %,
Temperature 150 °C		5850 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 2.90 %,
Temperature 120 °C		5850 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 2.40 %,
Temperature 100 °C		5860 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 1.80 %,
Temperature 60.0 °C		5860 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.5 MPa
@Strain 4.60 %,
Temperature 150 °C		5870 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.6 MPa
@Strain 3.30 %,
Temperature 150 °C		5890 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.7 MPa
@Strain 4.70 %,
Temperature 150 °C		5900 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.7 MPa
@Strain 3.00 %,
Temperature 120 °C		5900 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.9 MPa
@Strain 4.80 %,
Temperature 150 °C		5930 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.9 MPa
@Strain 2.40 %,
Temperature 100 °C		5930 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.0 MPa
@Strain 2.10 %,
Temperature 80.0 °C		5950 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.0 MPa
@Strain 2.60 %,
Temperature 120 °C		5950 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.005 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5947.3 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 3.40 %,
Temperature 150 °C		5960 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 4.90 %,
Temperature 150 °C		5960 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.1 MPa
@Strain 5.00 %,
Temperature 150 °C		5960 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.2 MPa
@Strain 3.10 %,
Temperature 120 °C		5980 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.3 MPa
@Strain 2.50 %,
Temperature 100 °C		5990 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.47 MPa
@Strain 1.70 %,
Temperature 80.0 °C		6015 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.5 MPa
@Strain 0.500 %,
Temperature 0.000 °C		6020 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 41.6 MPa
@Strain 5.50 %,
Temperature 150 °C		6030 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 41.6 MPa
@Strain 3.50 %,
Temperature 150 °C		6030 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.7 MPa
@Strain 3.20 %,
Temperature 120 °C		6050 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 2.50 %,
Temperature 100 °C		6060 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.9 MPa
@Strain 3.30 %,
Temperature 120 °C		6080 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.9 MPa
@Strain 2.70 %,
Temperature 120 °C		6080 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.9 MPa
@Strain 1.10 %,
Temperature 23.0 °C		6080 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.0 MPa
@Strain 6.00 %,
Temperature 150 °C		6090 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.0 MPa
@Strain 3.60 %,
Temperature 150 °C		6090 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.0 MPa
@Strain 1.90 %,
Temperature 60.0 °C		6090 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.1 MPa
@Strain 2.60 %,
Temperature 100 °C		6110 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.1 MPa
@Strain 1.00 %,
Temperature 60.0 °C		6110 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.2 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6120 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.27 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6131 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 42.3 MPa
@Strain 6.50 %,
Temperature 150 °C		6140 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.3 MPa
@Strain 7.00 %,
Temperature 150 °C		6140 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.3 MPa
@Strain 3.40 %,
Temperature 120 °C		6140 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.5 MPa
@Strain 7.50 %,
Temperature 150 °C		6160 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.5 MPa
@Strain 8.00 %,
Temperature 150 °C		6160 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.5 MPa
@Strain 3.70 %,
Temperature 150 °C		6160 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.6 MPa
@Strain 8.50 %,
Temperature 150 °C		6180 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 9.00 %,
Temperature 150 °C		6180 psi
@Strain 9.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 3.50 %,
Temperature 120 °C		6180 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.68 MPa
@Strain 1.80 %,
Temperature 80.0 °C		6190 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.7 MPa
@Strain 2.70 %,
Temperature 100 °C		6190 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 9.50 %,
Temperature 150 °C		6190 psi
@Strain 9.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 10.0 %,
Temperature 150 °C		6190 psi
@Strain 10.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 2.80 %,
Temperature 120 °C		6190 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.8 MPa
@Strain 11.0 %,
Temperature 150 °C		6210 psi
@Strain 11.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 3.60 %,
Temperature 120 °C		6220 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 3.80 %,
Temperature 150 °C		6220 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.9 MPa
@Strain 2.60 %,
Temperature 100 °C		6220 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.3 MPa
@Strain 2.80 %,
Temperature 100 °C		6280 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 3.90 %,
Temperature 150 °C		6280 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.3 MPa
@Strain 3.70 %,
Temperature 120 °C		6280 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 3.80 %,
Temperature 120 °C		6290 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 2.90 %,
Temperature 120 °C		6290 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.4 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6290 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 2.00 %,
Temperature 60.0 °C		6290 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.6 MPa
@Strain 4.00 %,
Temperature 150 °C		6320 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 3.90 %,
Temperature 120 °C		6350 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.9 MPa
@Strain 4.10 %,
Temperature 150 °C		6370 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 2.70 %,
Temperature 100 °C		6370 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.0 MPa
@Strain 2.90 %,
Temperature 100 °C		6380 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.0 MPa
@Strain 4.00 %,
Temperature 120 °C		6380 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.1 MPa
@Strain 3.00 %,
Temperature 120 °C		6400 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.2 MPa
@Strain 4.10 %,
Temperature 120 °C		6410 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.2 MPa
@Strain 4.20 %,
Temperature 150 °C		6410 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.3 MPa
@Strain 1.20 %,
Temperature 23.0 °C		6430 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.33 MPa
@Strain 1.90 %,
Temperature 80.0 °C		6430 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 3.00 %,
Temperature 100 °C		6440 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6440 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.4 MPa
@Strain 4.30 %,
Temperature 150 °C		6440 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 4.20 %,
Temperature 120 °C		6440 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.6 MPa
@Strain 4.30 %,
Temperature 120 °C		6470 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		6470 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.7 MPa
@Strain 4.40 %,
Temperature 120 °C		6480 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.8 MPa
@Strain 4.50 %,
Temperature 120 °C		6500 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.8 MPa
@Strain 3.10 %,
Temperature 120 °C		6500 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.8 MPa
@Strain 4.40 %,
Temperature 150 °C		6500 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.8 MPa
@Strain 2.80 %,
Temperature 100 °C		6500 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.8 MPa
@Strain 0.600 %,
Temperature 0.000 °C		6500 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 3.10 %,
Temperature 100 °C		6510 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.9 MPa
@Strain 4.60 %,
Temperature 120 °C		6510 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.0 MPa
@Strain 4.50 %,
Temperature 150 °C		6530 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.2 MPa
@Strain 4.60 %,
Temperature 150 °C		6560 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.2 MPa
@Strain 1.10 %,
Temperature 60.0 °C		6560 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 4.70 %,
Temperature 120 °C		6570 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.3 MPa
@Strain 3.20 %,
Temperature 100 °C		6570 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.4 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6580 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.4 MPa
@Strain 4.80 %,
Temperature 120 °C		6580 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.5 MPa
@Strain 3.20 %,
Temperature 120 °C		6600 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.5 MPa
@Strain 4.70 %,
Temperature 150 °C		6600 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.6 MPa
@Strain 4.90 %,
Temperature 120 °C		6610 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.7 MPa
@Strain 5.00 %,
Temperature 120 °C		6630 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.7 MPa
@Strain 4.80 %,
Temperature 150 °C		6630 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.7 MPa
@Strain 2.90 %,
Temperature 100 °C		6630 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.7 MPa
@Strain 3.30 %,
Temperature 100 °C		6630 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.9 MPa
@Strain 2.20 %,
Temperature 60.0 °C		6660 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.9 MPa
@Strain 4.90 %,
Temperature 150 °C		6660 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.0 MPa
@Strain 5.00 %,
Temperature 150 °C		6670 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.0 MPa
@Strain 3.40 %,
Temperature 100 °C		6670 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.03 MPa
@Strain 2.00 %,
Temperature 80.0 °C		6676 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 5.50 %,
Temperature 120 °C		6690 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 46.2 MPa
@Strain 3.30 %,
Temperature 120 °C		6700 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.2 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6700 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.3 MPa
@Strain 3.50 %,
Temperature 100 °C		6720 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.4 MPa
@Strain 3.00 %,
Temperature 100 °C		6730 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.6 MPa
@Strain 6.00 %,
Temperature 120 °C		6760 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 46.7 MPa
@Strain 3.40 %,
Temperature 120 °C		6770 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.8 MPa
@Strain 5.50 %,
Temperature 150 °C		6790 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.8 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6790 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 3.60 %,
Temperature 100 °C		6790 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 1.30 %,
Temperature 23.0 °C		6790 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 2.30 %,
Temperature 60.0 °C		6820 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 6.50 %,
Temperature 120 °C		6820 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.1 MPa
@Strain 3.70 %,
Temperature 100 °C		6830 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.2 MPa
@Strain 3.10 %,
Temperature 100 °C		6850 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 7.00 %,
Temperature 120 °C		6850 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.2 MPa
@Strain 3.50 %,
Temperature 120 °C		6850 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.4 MPa
@Strain 7.50 %,
Temperature 120 °C		6870 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 3.80 %,
Temperature 100 °C		6870 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.5 MPa
@Strain 8.00 %,
Temperature 120 °C		6890 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.5 MPa
@Strain 8.50 %,
Temperature 120 °C		6890 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 9.00 %,
Temperature 120 °C		6900 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 9.50 %,
Temperature 120 °C		6900 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 10.0 %,
Temperature 120 °C		6900 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 11.0 %,
Temperature 120 °C		6900 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 47.642 MPa
@Strain 0.600 %,
Temperature -40.0 °C		6909.9 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 47.68 MPa
@Strain 2.10 %,
Temperature 80.0 °C		6915 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.7 MPa
@Strain 2.40 %,
Temperature 60.0 °C		6920 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 3.90 %,
Temperature 100 °C		6920 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 2.80 %,
Temperature 80.0 °C		6920 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 6.00 %,
Temperature 150 °C		6920 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.7 MPa
@Strain 3.60 %,
Temperature 120 °C		6920 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.9 MPa
@Strain 4.00 %,
Temperature 100 °C		6950 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.0 MPa
@Strain 3.20 %,
Temperature 100 °C		6960 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.0 MPa
@Strain 0.600 %,
Temperature 0.000 °C		6960 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.1 MPa
@Strain 1.20 %,
Temperature 60.0 °C		6980 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.1 MPa
@Strain 4.10 %,
Temperature 100 °C		6980 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.2 MPa
@Strain 3.70 %,
Temperature 120 °C		6990 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.2 MPa
@Strain 6.50 %,
Temperature 150 °C		6990 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.3 MPa
@Strain 4.20 %,
Temperature 100 °C		7010 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7020 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 4.30 %,
Temperature 100 °C		7030 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.58 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7046 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 48.6 MPa
@Strain 3.30 %,
Temperature 100 °C		7050 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.6 MPa
@Strain 3.80 %,
Temperature 120 °C		7050 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 7.00 %,
Temperature 150 °C		7060 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 4.40 %,
Temperature 100 °C		7060 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.0 MPa
@Strain 4.50 %,
Temperature 100 °C		7110 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.0 MPa
@Strain 2.20 %,
Temperature 80.0 °C		7110 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.0 MPa
@Strain 3.90 %,
Temperature 120 °C		7110 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.1 MPa
@Strain 7.50 %,
Temperature 150 °C		7120 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.1 MPa
@Strain 2.50 %,
Temperature 60.0 °C		7120 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.1 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7120 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.2 MPa
@Strain 4.60 %,
Temperature 100 °C		7140 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.22 MPa
@Strain 0.700 %,
Temperature 23.0 °C		7139 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.3 MPa
@Strain 3.40 %,
Temperature 100 °C		7150 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.3 MPa
@Strain 4.00 %,
Temperature 120 °C		7150 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.4 MPa
@Strain 8.00 %,
Temperature 150 °C		7160 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.4 MPa
@Strain 4.70 %,
Temperature 100 °C		7160 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.4 MPa
@Strain 1.40 %,
Temperature 23.0 °C		7160 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7180 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 4.80 %,
Temperature 100 °C		7190 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 8.50 %,
Temperature 150 °C		7210 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.7 MPa
@Strain 4.10 %,
Temperature 120 °C		7210 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 4.90 %,
Temperature 100 °C		7220 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.9 MPa
@Strain 5.00 %,
Temperature 100 °C		7240 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.9 MPa
@Strain 4.20 %,
Temperature 120 °C		7240 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 9.00 %,
Temperature 150 °C		7250 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 3.50 %,
Temperature 100 °C		7250 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 2.60 %,
Temperature 60.0 °C		7250 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.14 MPa
@Strain 2.30 %,
Temperature 80.0 °C		7272 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.2 MPa
@Strain 9.50 %,
Temperature 150 °C		7280 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.3 MPa
@Strain 10.0 %,
Temperature 150 °C		7300 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.3 MPa
@Strain 4.30 %,
Temperature 120 °C		7300 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.3 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7300 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.4 MPa
@Strain 5.50 %,
Temperature 100 °C		7310 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 50.5 MPa
@Strain 3.60 %,
Temperature 100 °C		7320 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 11.0 %,
Temperature 150 °C		7320 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.6 MPa
@Strain 4.40 %,
Temperature 120 °C		7340 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.6 MPa
@Strain 1.30 %,
Temperature 60.0 °C		7340 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 15.0 %,
Temperature 150 °C		7350 psi
@Strain 15.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 12.0 %,
Temperature 150 °C		7350 psi
@Strain 12.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 13.0 %,
Temperature 150 °C		7370 psi
@Strain 13.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 14.0 %,
Temperature 150 °C		7370 psi
@Strain 14.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7370 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 2.70 %,
Temperature 60.0 °C		7380 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 4.50 %,
Temperature 120 °C		7380 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.0 MPa
@Strain 6.00 %,
Temperature 100 °C		7400 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 4.60 %,
Temperature 120 °C		7410 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 3.70 %,
Temperature 100 °C		7410 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.3 MPa
@Strain 6.50 %,
Temperature 100 °C		7440 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.4 MPa
@Strain 4.70 %,
Temperature 120 °C		7450 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.4 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7450 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.42 MPa
@Strain 2.40 %,
Temperature 80.0 °C		7458 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 3.80 %,
Temperature 100 °C		7480 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 4.80 %,
Temperature 120 °C		7480 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 7.00 %,
Temperature 100 °C		7480 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 7.50 %,
Temperature 100 °C		7500 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 1.50 %,
Temperature 23.0 °C		7500 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.8 MPa
@Strain 4.90 %,
Temperature 120 °C		7510 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.8 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7510 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 2.80 %,
Temperature 60.0 °C		7530 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 8.50 %,
Temperature 100 °C		7530 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 8.00 %,
Temperature 100 °C		7530 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 10.0 %,
Temperature 100 °C		7540 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 9.50 %,
Temperature 100 °C		7540 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 9.00 %,
Temperature 100 °C		7540 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.0 MPa
@Strain 3.90 %,
Temperature 100 °C		7540 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.1 MPa
@Strain 11.0 %,
Temperature 100 °C		7560 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 5.00 %,
Temperature 120 °C		7560 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.2 MPa
@Strain 12.0 %,
Temperature 100 °C		7570 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 52.2 MPa
@Strain 3.60 %,
Temperature 80.0 °C		7570 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.5 MPa
@Strain 3.70 %,
Temperature 80.0 °C		7610 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.5 MPa
@Strain 4.00 %,
Temperature 100 °C		7610 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 5.50 %,
Temperature 120 °C		7640 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		7640 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 52.86 MPa
@Strain 2.50 %,
Temperature 80.0 °C		7667 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.9 MPa
@Strain 2.90 %,
Temperature 60.0 °C		7670 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.9 MPa
@Strain 4.10 %,
Temperature 100 °C		7670 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.9 MPa
@Strain 3.80 %,
Temperature 80.0 °C		7670 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 4.20 %,
Temperature 100 °C		7700 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 0.700 %,
Temperature 0.000 °C		7720 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.3 MPa
@Strain 3.90 %,
Temperature 80.0 °C		7730 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 1.40 %,
Temperature 60.0 °C		7750 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.5 MPa
@Strain 4.30 %,
Temperature 100 °C		7760 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.5 MPa
@Strain 4.00 %,
Temperature 80.0 °C		7760 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.6 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7770 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.6 MPa
@Strain 6.00 %,
Temperature 120 °C		7770 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.8 MPa
@Strain 4.10 %,
Temperature 80.0 °C		7800 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.8 MPa
@Strain 1.60 %,
Temperature 23.0 °C		7800 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.9 MPa
@Strain 4.20 %,
Temperature 80.0 °C		7820 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.9 MPa
@Strain 4.40 %,
Temperature 100 °C		7820 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.14 MPa
@Strain 2.60 %,
Temperature 80.0 °C		7852 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7860 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 4.50 %,
Temperature 100 °C		7860 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.2 MPa
@Strain 4.30 %,
Temperature 80.0 °C		7860 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 6.50 %,
Temperature 120 °C		7860 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 4.40 %,
Temperature 80.0 °C		7900 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 4.60 %,
Temperature 100 °C		7900 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.6 MPa
@Strain 4.50 %,
Temperature 80.0 °C		7920 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7920 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 7.00 %,
Temperature 120 °C		7920 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.7 MPa
@Strain 4.70 %,
Temperature 100 °C		7930 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 4.80 %,
Temperature 100 °C		7960 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 4.60 %,
Temperature 80.0 °C		7960 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.0 MPa
@Strain 4.70 %,
Temperature 80.0 °C		7980 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.0 MPa
@Strain 7.50 %,
Temperature 120 °C		7980 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.05 MPa
@Strain 2.70 %,
Temperature 80.0 °C		7984 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 4.90 %,
Temperature 100 °C		8010 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.3 MPa
@Strain 4.80 %,
Temperature 80.0 °C		8020 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.3 MPa
@Strain 3.30 %,
Temperature 60.0 °C		8020 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.4 MPa
@Strain 8.00 %,
Temperature 120 °C		8040 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.5 MPa
@Strain 4.90 %,
Temperature 80.0 °C		8050 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		8050 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 55.5 MPa
@Strain 5.00 %,
Temperature 100 °C		8050 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.505 MPa
@Strain 0.700 %,
Temperature -40.0 °C		8050.3 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.7 MPa
@Strain 1.70 %,
Temperature 23.0 °C		8080 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 1.50 %,
Temperature 60.0 °C		8080 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.7 MPa
@Strain 3.40 %,
Temperature 60.0 °C		8080 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 8.50 %,
Temperature 120 °C		8080 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.9 MPa
@Strain 9.00 %,
Temperature 120 °C		8110 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.1 MPa
@Strain 5.50 %,
Temperature 80.0 °C		8140 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 56.16 MPa
@Strain 0.800 %,
Temperature 23.0 °C		8145 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 5.50 %,
Temperature 100 °C		8150 psi
@Strain 5.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 3.50 %,
Temperature 60.0 °C		8150 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.2 MPa
@Strain 9.50 %,
Temperature 120 °C		8150 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.22 MPa
@Strain 2.80 %,
Temperature 80.0 °C		8154 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.4 MPa
@Strain 10.0 %,
Temperature 120 °C		8180 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.6 MPa
@Strain 11.0 %,
Temperature 120 °C		8210 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 56.6 MPa
@Strain 3.60 %,
Temperature 60.0 °C		8210 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.8 MPa
@Strain 6.00 %,
Temperature 80.0 °C		8240 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 56.9 MPa
@Strain 12.0 %,
Temperature 120 °C		8250 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 3.70 %,
Temperature 60.0 °C		8270 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 6.50 %,
Temperature 80.0 °C		8280 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 13.0 %,
Temperature 120 °C		8280 psi
@Strain 13.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 57.1 MPa
@Strain 14.0 %,
Temperature 120 °C		8280 psi
@Strain 14.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 57.1 MPa
@Strain 15.0 %,
Temperature 120 °C		8280 psi
@Strain 15.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 57.12 MPa
@Strain 0.600 %,
Temperature -40.0 °C		8285 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 57.2 MPa
@Strain 6.00 %,
Temperature 100 °C		8300 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.4 MPa
@Strain 3.80 %,
Temperature 60.0 °C		8330 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.45 MPa
@Strain 2.90 %,
Temperature 80.0 °C		8332 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.5 MPa
@Strain 7.00 %,
Temperature 80.0 °C		8340 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.7 MPa
@Strain 7.50 %,
Temperature 80.0 °C		8370 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.7 MPa
@Strain 3.90 %,
Temperature 60.0 °C		8370 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.8 MPa
@Strain 1.60 %,
Temperature 60.0 °C		8380 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.8 MPa
@Strain 6.50 %,
Temperature 100 °C		8380 psi
@Strain 6.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.8 MPa
@Strain 1.80 %,
Temperature 23.0 °C		8380 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 57.9 MPa
@Strain 8.00 %,
Temperature 80.0 °C		8400 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 57.9 MPa
@Strain 8.50 %,
Temperature 80.0 °C		8400 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 58.0 MPa
@Strain 9.00 %,
Temperature 80.0 °C		8410 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 58.0 MPa
@Strain 9.50 %,
Temperature 80.0 °C		8410 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 58.0 MPa
@Strain 10.0 %,
Temperature 80.0 °C		8410 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 58.0 MPa
@Strain 4.00 %,
Temperature 60.0 °C		8410 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.28 MPa
@Strain 3.00 %,
Temperature 80.0 °C		8453 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.3 MPa
@Strain 4.10 %,
Temperature 60.0 °C		8460 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.3 MPa
@Strain 7.00 %,
Temperature 100 °C		8460 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.6 MPa
@Strain 4.20 %,
Temperature 60.0 °C		8500 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.8 MPa
@Strain 4.30 %,
Temperature 60.0 °C		8530 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.8 MPa
@Strain 7.50 %,
Temperature 100 °C		8530 psi
@Strain 7.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.0 MPa
@Strain 3.10 %,
Temperature 80.0 °C		8560 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.1 MPa
@Strain 4.40 %,
Temperature 60.0 °C		8570 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.1 MPa
@Strain 0.800 %,
Temperature 0.000 °C		8570 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.2 MPa
@Strain 8.00 %,
Temperature 100 °C		8590 psi
@Strain 8.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.3 MPa
@Strain 4.50 %,
Temperature 60.0 °C		8600 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 4.60 %,
Temperature 60.0 °C		8630 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 8.50 %,
Temperature 100 °C		8630 psi
@Strain 8.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.6 MPa
@Strain 1.90 %,
Temperature 23.0 °C		8640 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 1.70 %,
Temperature 60.0 °C		8660 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 59.7 MPa
@Strain 4.70 %,
Temperature 60.0 °C		8660 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.8 MPa
@Strain 9.00 %,
Temperature 100 °C		8670 psi
@Strain 9.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.84 MPa
@Strain 3.20 %,
Temperature 80.0 °C		8679 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.0 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8700 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.0 MPa
@Strain 9.50 %,
Temperature 100 °C		8700 psi
@Strain 9.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.1 MPa
@Strain 4.90 %,
Temperature 60.0 °C		8720 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.1 MPa
@Strain 0.800 %,
Temperature 0.000 °C		8720 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 60.2 MPa
@Strain 5.00 %,
Temperature 60.0 °C		8730 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 60.3 MPa
@Strain 10.0 %,
Temperature 100 °C		8750 psi
@Strain 10.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.6 MPa
@Strain 11.0 %,
Temperature 100 °C		8790 psi
@Strain 11.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.66 MPa
@Strain 3.30 %,
Temperature 80.0 °C		8798 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		8830 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 61.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		8880 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.3 MPa
@Strain 2.00 %,
Temperature 23.0 °C		8890 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.5 MPa
@Strain 6.00 %,
Temperature 60.0 °C		8920 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 61.8 MPa
@Strain 1.80 %,
Temperature 60.0 °C		8960 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.0 MPa
@Strain 6.50 %,
Temperature 60.0 °C		8990 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 62.03 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8997 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.24 MPa
@Strain 0.900 %,
Temperature 23.0 °C		9027 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.268 MPa
@Strain 0.800 %,
Temperature -40.0 °C		9031.2 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 7.00 %,
Temperature 60.0 °C		9050 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 62.57 MPa
@Strain 3.60 %,
Temperature 80.0 °C		9075 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.6 MPa
@Strain 7.50 %,
Temperature 60.0 °C		9080 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 62.9 MPa
@Strain 8.00 %,
Temperature 60.0 °C		9120 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.0 MPa
@Strain 8.50 %,
Temperature 60.0 °C		9140 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.11 MPa
@Strain 3.70 %,
Temperature 80.0 °C		9153 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.2 MPa
@Strain 9.00 %,
Temperature 60.0 °C		9170 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.2 MPa
@Strain 9.50 %,
Temperature 60.0 °C		9170 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.2 MPa
@Strain 10.0 %,
Temperature 60.0 °C		9170 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 63.2 MPa
@Strain 2.10 %,
Temperature 23.0 °C		9170 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.5 MPa
@Strain 1.90 %,
Temperature 60.0 °C		9210 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.52 MPa
@Strain 3.80 %,
Temperature 80.0 °C		9213 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.02 MPa
@Strain 3.90 %,
Temperature 80.0 °C		9285 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.1 MPa
@Strain 0.900 %,
Temperature 0.000 °C		9300 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.32 MPa
@Strain 4.00 %,
Temperature 80.0 °C		9329 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.69 MPa
@Strain 4.10 %,
Temperature 80.0 °C		9383 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 2.20 %,
Temperature 23.0 °C		9400 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.92 MPa
@Strain 4.20 %,
Temperature 80.0 °C		9416 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.1 MPa
@Strain 2.00 %,
Temperature 60.0 °C		9440 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.18 MPa
@Strain 0.700 %,
Temperature -40.0 °C		9454 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 65.24 MPa
@Strain 4.30 %,
Temperature 80.0 °C		9462 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.58 MPa
@Strain 4.40 %,
Temperature 80.0 °C		9512 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.93 MPa
@Strain 4.50 %,
Temperature 80.0 °C		9562 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.11 MPa
@Strain 4.60 %,
Temperature 80.0 °C		9588 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.38 MPa
@Strain 4.70 %,
Temperature 80.0 °C		9628 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.4 MPa
@Strain 2.30 %,
Temperature 23.0 °C		9630 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 66.59 MPa
@Strain 4.80 %,
Temperature 80.0 °C		9658 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		9660 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.71 MPa
@Strain 4.90 %,
Temperature 80.0 °C		9675 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 0.900 %,
Temperature 0.000 °C		9690 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.94 MPa
@Strain 5.00 %,
Temperature 80.0 °C		9709 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 67.44 MPa
@Strain 5.50 %,
Temperature 80.0 °C		9781 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 67.9 MPa
@Strain 2.40 %,
Temperature 23.0 °C		9850 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.1 MPa
@Strain 2.20 %,
Temperature 60.0 °C		9880 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.13 MPa
@Strain 1.00 %,
Temperature 23.0 °C		9881 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.21 MPa
@Strain 6.00 %,
Temperature 80.0 °C		9893 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.6 MPa
@Strain 1.00 %,
Temperature 0.000 °C		9950 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.66 MPa
@Strain 6.50 %,
Temperature 80.0 °C		9958 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.771 MPa
@Strain 0.900 %,
Temperature -40.0 °C		9974.4 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.0 MPa
@Strain 7.00 %,
Temperature 80.0 °C		10000 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.25 MPa
@Strain 7.50 %,
Temperature 80.0 °C		10040 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.4 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10100 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.56 MPa
@Strain 8.00 %,
Temperature 80.0 °C		10090 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.6 MPa
@Strain 2.30 %,
Temperature 60.0 °C		10100 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 69.67 MPa
@Strain 8.50 %,
Temperature 80.0 °C		10100 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.75 MPa
@Strain 9.00 %,
Temperature 80.0 °C		10120 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.88 MPa
@Strain 10.0 %,
Temperature 80.0 °C		10140 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.89 MPa
@Strain 9.50 %,
Temperature 80.0 °C		10140 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.8 MPa
@Strain 2.40 %,
Temperature 60.0 °C		10300 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 70.8 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10300 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.9 MPa
@Strain 2.50 %,
Temperature 60.0 °C		10400 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.1 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10500 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.77 MPa
@Strain 0.800 %,
Temperature -40.0 °C		10550 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 72.8 MPa
@Strain 1.10 %,
Temperature 0.000 °C		10600 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.1 MPa
@Strain 2.60 %,
Temperature 60.0 °C		10600 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.3 MPa
@Strain 2.80 %,
Temperature 23.0 °C		10600 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.6 MPa
@Strain 1.00 %,
Temperature 0.000 °C		10700 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.11 MPa
@Strain 1.10 %,
Temperature 23.0 °C		10750 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.3 MPa
@Strain 2.90 %,
Temperature 23.0 °C		10800 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.3 MPa
@Strain 2.70 %,
Temperature 60.0 °C		10800 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.206 MPa
@Strain 1.00 %,
Temperature -40.0 °C		10908 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.3 MPa
@Strain 3.00 %,
Temperature 23.0 °C		10900 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.3 MPa
@Strain 2.80 %,
Temperature 60.0 °C		10900 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 2.90 %,
Temperature 60.0 °C		11100 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11100 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.7 MPa
@Strain 1.20 %,
Temperature 0.000 °C		11100 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.2 MPa
@Strain 3.00 %,
Temperature 60.0 °C		11200 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11200 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.0 MPa
@Strain 3.10 %,
Temperature 60.0 °C		11300 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.1 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11300 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.7 MPa
@Strain 3.40 %,
Temperature 23.0 °C		11400 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 78.8 MPa
@Strain 3.20 %,
Temperature 60.0 °C		11400 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.3 MPa
@Strain 3.50 %,
Temperature 23.0 °C		11500 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.52 MPa
@Strain 1.20 %,
Temperature 23.0 °C		11530 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.6 MPa
@Strain 3.30 %,
Temperature 60.0 °C		11500 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.8 MPa
@Strain 3.60 %,
Temperature 23.0 °C		11600 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 79.97 MPa
@Strain 0.900 %,
Temperature -40.0 °C		11600 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 80.1 MPa
@Strain 3.40 %,
Temperature 60.0 °C		11600 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.2 MPa
@Strain 1.10 %,
Temperature 0.000 °C		11600 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 80.3 MPa
@Strain 1.30 %,
Temperature 0.000 °C		11600 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 80.3 MPa
@Strain 3.70 %,
Temperature 23.0 °C		11600 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 80.5 MPa
@Strain 3.50 %,
Temperature 60.0 °C		11700 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.7 MPa
@Strain 3.80 %,
Temperature 23.0 °C		11700 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.0 MPa
@Strain 3.60 %,
Temperature 60.0 °C		11700 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.1 MPa
@Strain 3.90 %,
Temperature 23.0 °C		11800 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.4 MPa
@Strain 4.00 %,
Temperature 23.0 °C		11800 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.4 MPa
@Strain 3.70 %,
Temperature 60.0 °C		11800 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.595 MPa
@Strain 1.10 %,
Temperature -40.0 °C		11834 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 81.6 MPa
@Strain 4.10 %,
Temperature 23.0 °C		11800 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 81.6 MPa
@Strain 3.80 %,
Temperature 60.0 °C		11800 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.9 MPa
@Strain 3.90 %,
Temperature 60.0 °C		11900 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.9 MPa
@Strain 4.20 %,
Temperature 23.0 °C		11900 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.1 MPa
@Strain 4.30 %,
Temperature 23.0 °C		11900 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.2 MPa
@Strain 4.40 %,
Temperature 23.0 °C		11900 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.2 MPa
@Strain 4.00 %,
Temperature 60.0 °C		11900 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.3 MPa
@Strain 4.10 %,
Temperature 60.0 °C		11900 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.4 MPa
@Strain 4.50 %,
Temperature 23.0 °C		12000 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.5 MPa
@Strain 4.60 %,
Temperature 23.0 °C		12000 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.5 MPa
@Strain 4.20 %,
Temperature 60.0 °C		12000 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.6 MPa
@Strain 4.30 %,
Temperature 60.0 °C		12000 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.7 MPa
@Strain 4.40 %,
Temperature 60.0 °C		12000 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.7 MPa
@Strain 4.70 %,
Temperature 23.0 °C		12000 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.8 MPa
@Strain 4.80 %,
Temperature 23.0 °C		12000 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 82.8 MPa
@Strain 4.50 %,
Temperature 60.0 °C		12000 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.8 MPa
@Strain 4.70 %,
Temperature 60.0 °C		12000 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.80 %,
Temperature 60.0 °C		12000 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.60 %,
Temperature 60.0 °C		12000 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.90 %,
Temperature 23.0 °C		12000 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.0 MPa
@Strain 5.00 %,
Temperature 23.0 °C		12000 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.0 MPa
@Strain 9.50 %,
Temperature 60.0 °C		12000 psi
@Strain 9.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.0 MPa
@Strain 5.00 %,
Temperature 60.0 °C		12000 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.0 MPa
@Strain 4.90 %,
Temperature 60.0 °C		12000 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.1 MPa
@Strain 9.00 %,
Temperature 60.0 °C		12100 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.1 MPa
@Strain 5.50 %,
Temperature 60.0 °C		12100 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 8.50 %,
Temperature 60.0 °C		12100 psi
@Strain 8.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 8.00 %,
Temperature 60.0 °C		12100 psi
@Strain 8.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 7.50 %,
Temperature 60.0 °C		12100 psi
@Strain 7.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 7.00 %,
Temperature 60.0 °C		12100 psi
@Strain 7.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 6.50 %,
Temperature 60.0 °C		12100 psi
@Strain 6.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 6.00 %,
Temperature 60.0 °C		12100 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.3 MPa
@Strain 5.50 %,
Temperature 23.0 °C		12100 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.5 MPa
@Strain 1.40 %,
Temperature 0.000 °C		12100 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 83.7 MPa
@Strain 6.00 %,
Temperature 23.0 °C		12100 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.8 MPa
@Strain 6.50 %,
Temperature 23.0 °C		12200 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.9 MPa
@Strain 7.00 %,
Temperature 23.0 °C		12200 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 83.9 MPa
@Strain 7.50 %,
Temperature 23.0 °C		12200 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 84.0 MPa
@Strain 8.00 %,
Temperature 23.0 °C		12200 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 84.1 MPa
@Strain 8.50 %,
Temperature 23.0 °C		12200 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 84.53 MPa
@Strain 1.30 %,
Temperature 23.0 °C		12260 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 86.6 MPa
@Strain 1.50 %,
Temperature 0.000 °C		12600 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.6 MPa
@Strain 1.20 %,
Temperature 0.000 °C		12600 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.69 MPa
@Strain 1.00 %,
Temperature -40.0 °C		12570 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.59 MPa
@Strain 1.20 %,
Temperature -40.0 °C		12700 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.17 MPa
@Strain 1.40 %,
Temperature 23.0 °C		12930 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.5 MPa
@Strain 1.60 %,
Temperature 0.000 °C		13000 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 92.3 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13400 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 92.4 MPa
@Strain 1.30 %,
Temperature 0.000 °C		13400 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.02 MPa
@Strain 1.10 %,
Temperature -40.0 °C		13490 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.493 MPa
@Strain 1.30 %,
Temperature -40.0 °C		13560 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.7 MPa
@Strain 1.50 %,
Temperature 23.0 °C		13600 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 94.6 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13700 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 96.8 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14000 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.76 MPa
@Strain 1.60 %,
Temperature 23.0 °C		14180 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 97.8 MPa
@Strain 1.40 %,
Temperature 0.000 °C		14200 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.8 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14300 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.88 MPa
@Strain 1.20 %,
Temperature -40.0 °C		14340 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.02 MPa
@Strain 1.40 %,
Temperature -40.0 °C		14360 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.9 MPa
@Strain 2.10 %,
Temperature 0.000 °C		14630 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.13 MPa
@Strain 1.70 %,
Temperature 23.0 °C		14668 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 102.8 MPa
@Strain 2.20 %,
Temperature 0.000 °C		14910 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 103 MPa
@Strain 1.50 %,
Temperature 0.000 °C		14900 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 104.12 MPa
@Strain 1.80 %,
Temperature 23.0 °C		15101 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 104.5 MPa
@Strain 2.30 %,
Temperature 0.000 °C		15160 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.519 MPa
@Strain 1.50 %,
Temperature -40.0 °C		15159.2 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 104.54 MPa
@Strain 1.30 %,
Temperature -40.0 °C		15162 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.1 MPa
@Strain 2.40 %,
Temperature 0.000 °C		15390 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 107.2 MPa
@Strain 1.60 %,
Temperature 0.000 °C		15550 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 107.5 MPa
@Strain 1.90 %,
Temperature 23.0 °C		15590 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.9 MPa
@Strain 2.50 %,
Temperature 0.000 °C		15650 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.3 MPa
@Strain 2.60 %,
Temperature 0.000 °C		15850 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.73 MPa
@Strain 1.40 %,
Temperature -40.0 °C		15915 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.745 MPa
@Strain 1.60 %,
Temperature -40.0 °C		15917.2 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.3 MPa
@Strain 2.00 %,
Temperature 23.0 °C		16000 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 110.7 MPa
@Strain 2.70 %,
Temperature 0.000 °C		16060 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 111.9 MPa
@Strain 2.80 %,
Temperature 0.000 °C		16230 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 112.33 MPa
@Strain 2.10 %,
Temperature 23.0 °C		16292 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 112.4 MPa
@Strain 1.70 %,
Temperature 0.000 °C		16300 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 113 MPa
@Strain 2.90 %,
Temperature 0.000 °C		16400 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 114 MPa
@Strain 3.00 %,
Temperature 0.000 °C		16500 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 114.55 MPa
@Strain 2.20 %,
Temperature 23.0 °C		16614 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.62 MPa
@Strain 1.50 %,
Temperature -40.0 °C		16624 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.745 MPa
@Strain 1.70 %,
Temperature -40.0 °C		16642.4 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.9 MPa
@Strain 3.10 %,
Temperature 0.000 °C		16660 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.6 MPa
@Strain 3.20 %,
Temperature 0.000 °C		16770 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 116 MPa
@Strain 1.80 %,
Temperature 0.000 °C		16800 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 116.1 MPa
@Strain 3.30 %,
Temperature 0.000 °C		16840 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 116.6 MPa
@Strain 3.40 %,
Temperature 0.000 °C		16910 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 116.9 MPa
@Strain 3.50 %,
Temperature 0.000 °C		16950 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 116.96 MPa
@Strain 2.30 %,
Temperature 23.0 °C		16964 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 117 MPa
@Strain 3.60 %,
Temperature 0.000 °C		17000 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.1 MPa
@Strain 3.70 %,
Temperature 0.000 °C		16980 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.2 MPa
@Strain 3.80 %,
Temperature 0.000 °C		17000 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.2 MPa
@Strain 3.90 %,
Temperature 0.000 °C		17000 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.89 MPa
@Strain 2.40 %,
Temperature 23.0 °C		17244 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 119.14 MPa
@Strain 1.60 %,
Temperature -40.0 °C		17280 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.465 MPa
@Strain 1.80 %,
Temperature -40.0 °C		17327.0 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 120.4 MPa
@Strain 1.90 %,
Temperature 0.000 °C		17460 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 120.43 MPa
@Strain 2.50 %,
Temperature 23.0 °C		17467 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 121.69 MPa
@Strain 2.60 %,
Temperature 23.0 °C		17650 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 122.84 MPa
@Strain 2.70 %,
Temperature 23.0 °C		17816 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 123.26 MPa
@Strain 1.70 %,
Temperature -40.0 °C		17877 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 123.81 MPa
@Strain 2.80 %,
Temperature 23.0 °C		17957 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 124.066 MPa
@Strain 1.90 %,
Temperature -40.0 °C		17994.3 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.2 MPa
@Strain 2.00 %,
Temperature 0.000 °C		18010 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 124.77 MPa
@Strain 2.90 %,
Temperature 23.0 °C		18096 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.45 MPa
@Strain 3.00 %,
Temperature 23.0 °C		18195 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.84 MPa
@Strain 3.10 %,
Temperature 23.0 °C		18252 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 126.13 MPa
@Strain 3.20 %,
Temperature 23.0 °C		18294 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 126.42 MPa
@Strain 3.30 %,
Temperature 23.0 °C		18336 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 127.2 MPa
@Strain 1.80 %,
Temperature -40.0 °C		18450 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 127.5 MPa
@Strain 2.10 %,
Temperature 0.000 °C		18490 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 128.377 MPa
@Strain 2.00 %,
Temperature -40.0 °C		18619.5 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 130.5 MPa
@Strain 2.20 %,
Temperature 0.000 °C		18930 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 131.04 MPa
@Strain 1.90 %,
Temperature -40.0 °C		19006 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 132.297 MPa
@Strain 2.10 %,
Temperature -40.0 °C		19188.1 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 133.3 MPa
@Strain 2.30 %,
Temperature 0.000 °C		19330 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 134.59 MPa
@Strain 2.00 %,
Temperature -40.0 °C		19521 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 136 MPa
@Strain 2.40 %,
Temperature 0.000 °C		19700 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 136.215 MPa
@Strain 2.20 %,
Temperature -40.0 °C		19756.3 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 137.86 MPa
@Strain 2.10 %,
Temperature -40.0 °C		19995 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 138.3 MPa
@Strain 2.50 %,
Temperature 0.000 °C		20060 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 140.167 MPa
@Strain 2.30 %,
Temperature -40.0 °C		20329.5 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.5 MPa
@Strain 2.60 %,
Temperature 0.000 °C		20380 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 140.83 MPa
@Strain 2.20 %,
Temperature -40.0 °C		20426 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 142.5 MPa
@Strain 2.70 %,
Temperature 0.000 °C		20670 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 143.62 MPa
@Strain 2.30 %,
Temperature -40.0 °C		20830 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 143.778 MPa
@Strain 2.40 %,
Temperature -40.0 °C		20853.3 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 144.3 MPa
@Strain 2.80 %,
Temperature 0.000 °C		20930 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 145.8 MPa
@Strain 2.90 %,
Temperature 0.000 °C		21150 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 146.3 MPa
@Strain 2.40 %,
Temperature -40.0 °C		21220 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 147.113 MPa
@Strain 2.50 %,
Temperature -40.0 °C		21337.0 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 147.3 MPa
@Strain 3.00 %,
Temperature 0.000 °C		21360 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 148.6 MPa
@Strain 3.10 %,
Temperature 0.000 °C		21550 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 148.61 MPa
@Strain 2.50 %,
Temperature -40.0 °C		21554 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 149.8 MPa
@Strain 3.20 %,
Temperature 0.000 °C		21730 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 150.315 MPa
@Strain 2.60 %,
Temperature -40.0 °C		21801.4 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 150.82 MPa
@Strain 2.60 %,
Temperature -40.0 °C		21875 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 152.93 MPa
@Strain 2.70 %,
Temperature -40.0 °C		22181 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 153.224 MPa
@Strain 2.70 %,
Temperature -40.0 °C		22223.3 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 154.85 MPa
@Strain 2.80 %,
Temperature -40.0 °C		22459 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 156.115 MPa
@Strain 2.80 %,
Temperature -40.0 °C		22642.6 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 156.77 MPa
@Strain 2.90 %,
Temperature -40.0 °C		22738 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 158.4 MPa
@Strain 3.00 %,
Temperature -40.0 °C		22970 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 158.831 MPa
@Strain 2.90 %,
Temperature -40.0 °C		23036.5 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 159.74 MPa
@Strain 3.10 %,
Temperature -40.0 °C		23168 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 160.7 MPa
@Strain 3.20 %,
Temperature -40.0 °C		23310 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 161.298 MPa
@Strain 3.00 %,
Temperature -40.0 °C		23394.3 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 163.594 MPa
@Strain 3.10 %,
Temperature -40.0 °C		23727.3 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 165.852 MPa
@Strain 3.20 %,
Temperature -40.0 °C		24054.8 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature -40.0 °C		3.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature -40.0 °C		4.0 %
@Temperature -40.0 °F		50%RH; ASTM D638
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 10 %
@Temperature 23.0 °C		10 %
@Temperature 73.4 °F		50%RH; ISO 527
 12 %
@Temperature 23.0 °C		12 %
@Temperature 73.4 °F		50%RH; ASTM D638
 13 %
@Temperature 77.0 °C		13 %
@Temperature 171 °F		DAM; ASTM D638
 16 %
@Temperature 77.0 °C		16 %
@Temperature 171 °F		50%RH; ASTM D638
 17 %
@Temperature 121 °C		17 %
@Temperature 250 °F		DAM; ASTM D638
 18 %
@Temperature 121 °C		18 %
@Temperature 250 °F		50%RH; ASTM D638
Tensile Modulus  5.00 GPa
@Temperature 23.0 °C		725 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 7.50 GPa
@Temperature 23.0 °C		1090 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 193 MPa
@Temperature 23.0 °C		28000 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  1.38 GPa
@Temperature 121 °C		200 ksi
@Temperature 250 °F		50%RH; ASTM D790
 1.38 GPa
@Temperature 121 °C		200 ksi
@Temperature 250 °F		DAM; ASTM D790
 1.86 GPa
@Temperature 77.0 °C		270 ksi
@Temperature 171 °F		50%RH; ASTM D790
 1.895 GPa
@Temperature 77.0 °C		274.8 ksi
@Temperature 171 °F		DAM; ASTM D790
 4.135 GPa
@Temperature 23.0 °C		599.7 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 5.00 GPa
@Temperature 23.0 °C		725 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 6.50 GPa
@Temperature 23.0 °C		943 ksi
@Temperature 73.4 °F		DAM; ISO 178
 6.55 GPa
@Temperature -40.0 °C		950 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
 6.895 GPa
@Temperature -40.0 °C		1000 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 6.895 GPa
@Temperature 23.0 °C		1000 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Strength 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.380 J/cm
@Temperature -40.0 °C		0.712 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.480 J/cm
@Temperature 23.0 °C		0.899 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.590 J/cm
@Temperature 23.0 °C		1.11 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched 6.90 J/cm
@Temperature 23.0 °C		12.9 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.00 kJ/m²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 6.00 kJ/m²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  40.0 kJ/m²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 40.0 kJ/m²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
 50.0 kJ/m²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 50.0 kJ/m²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched  3.50 J/cm²
@Temperature -30.0 °C		16.7 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 4.50 J/cm²
@Temperature 23.0 °C		21.4 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 5.00 J/cm²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.400 J/cm²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+9 ohm-cm
@Temperature 23.0 °C		1.00e+9 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+9 ohm-cm
@Temperature 23.0 °C		1.00e+9 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.8
@Frequency 1000 Hz,
Temperature 23.0 °C		3.8
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 100 Hz,
Temperature 23.0 °C		4.0
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 4.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 7.0
@Frequency 100 Hz,
Temperature 23.0 °C		7.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 7.3
@Frequency 1000 Hz,
Temperature 23.0 °C		7.3
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Dielectric Strength  15.7 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		399 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		50%RH; Short Time; ASTM D149
 17.3 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		439 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		DAM; Short Time; ASTM D149
 18.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		457 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		50%RH; IEC 60243-1
 20.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		508 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.010
@Frequency 1000 Hz,
Temperature 23.0 °C		0.010
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.010
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.010
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 100 Hz,
Temperature 23.0 °C		0.020
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.050
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.050
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.070
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.070
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 1000 Hz,
Temperature 23.0 °C		0.20
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Comparative Tracking Index 475 V
@Temperature 23.0 °C		475 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 62.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 62.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		34.4 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 100 µm/m-°C
@Temperature 55.0 - 160 °C		55.6 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 100 µm/m-°C
@Temperature 55.0 - 160 °C		55.6 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 255 °C491 °FDAM; ISO 75-1/-2
 255 °C491 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 230 °C446 °FDAM; ISO 75-1/-2
 235 °C455 °FDAM; ASTM D648
UL RTI, Electrical  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.810 mm		149 °F
@Thickness 0.0319 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 24 %24 %DAM; ASTM D2863
 24 %24 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesStiffness, GoodDAM
 Strength, GoodDAM
 Warpage, LowDAM
FillerMineral/GlassDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-(MD+GF)38<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass/Mineral Reinforced ResinsDAM
 Low Warp ResinsDAM
Resin IdentificationPA66-(MD+GF)38ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Industrial ApplicationsDAM
 Parts, EngineeringDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45445.html

免责声明: 本文 DuPont Performance Polymers Minlon® 22C NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4