DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66 物性表: DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66物性表及特性介绍,DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66注塑参数详情,如需DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.47
  • 吸水率 [%]: 1.5
  • 缺口冲击强度: 4.0
  • 弯曲模量 [MPa]: 9.90
  • 热变形温度 [℃]: 256.0
 
Physical PropertiesMetricEnglishComments
Density 1.47 g/cc0.0531 lb/in³DAM; ISO 1183
Filler Content 40 %40 %DAM
Water Absorption  1.5 %
@Temperature 23.0 °C		1.5 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0040 cm/cm
@Thickness 2.00 mm		0.0040 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
@Thickness 2.00 mm		0.011 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  97.0 MPa
@Temperature 23.0 °C		14100 psi
@Temperature 73.4 °F		50%RH; ISO 527
 160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  4.10 MPa
@Strain 0.100 %,
Temperature 100 °C		595 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.50 MPa
@Strain 0.100 %,
Temperature 150 °C		653 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.20 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1190 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 8.50 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1230 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.8 MPa
@Strain 0.200 %,
Temperature 100 °C		1570 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.9 MPa
@Strain 0.200 %,
Temperature 150 °C		1580 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.2 MPa
@Strain 0.300 %,
Temperature 150 °C		2200 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.7 MPa
@Strain 0.300 %,
Temperature 100 °C		2280 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.2 MPa
@Strain 0.400 %,
Temperature 150 °C		2640 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 0.400 %,
Temperature 100 °C		2800 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.5 MPa
@Strain 0.200 %,
Temperature -40.0 °C		3120 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 21.5 MPa
@Strain 0.600 %,
Temperature 120 °C		3120 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 527
 21.7 MPa
@Strain 0.200 %,
Temperature 23.0 °C		3150 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 22.4 MPa
@Strain 0.500 %,
Temperature 150 °C		3250 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.4 MPa
@Strain 0.570 %,
Temperature 90.0 °C		3390 psi
@Strain 0.570 %,
Temperature 194 °F		50%RH; ISO 527
 23.7 MPa
@Strain 0.440 %,
Temperature 40.0 °C		3440 psi
@Strain 0.440 %,
Temperature 104 °F		50%RH; ISO 527
 23.9 MPa
@Strain 0.530 %,
Temperature 60.0 °C		3470 psi
@Strain 0.530 %,
Temperature 140 °F		50%RH; ISO 527
 25.0 MPa
@Strain 0.500 %,
Temperature 100 °C		3630 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.0 MPa
@Strain 0.240 %,
Temperature 0.000 °C		3630 psi
@Strain 0.240 %,
Temperature 32.0 °F		50%RH; ISO 527
 25.1 MPa
@Strain 0.310 %,
Temperature 60.0 °C		3640 psi
@Strain 0.310 %,
Temperature 140 °F		DAM; ISO 527
 25.2 MPa
@Strain 0.700 %,
Temperature 120 °C		3650 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 527
 25.4 MPa
@Strain 0.350 %,
Temperature 23.0 °C		3680 psi
@Strain 0.350 %,
Temperature 73.4 °F		50%RH; ISO 527
 25.7 MPa
@Strain 0.600 %,
Temperature 150 °C		3730 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.2 MPa
@Strain 0.220 %,
Temperature 40.0 °C		3800 psi
@Strain 0.220 %,
Temperature 104 °F		DAM; ISO 527
 26.9 MPa
@Strain 0.640 %,
Temperature 90.0 °C		3900 psi
@Strain 0.640 %,
Temperature 194 °F		DAM; ISO 527
 27.3 MPa
@Strain 0.220 %,
Temperature -20.0 °C		3960 psi
@Strain 0.220 %,
Temperature -4.00 °F		50%RH; ISO 527
 28.2 MPa
@Strain 0.220 %,
Temperature 23.0 °C		4090 psi
@Strain 0.220 %,
Temperature 73.4 °F		DAM; ISO 527
 28.8 MPa
@Strain 0.700 %,
Temperature 150 °C		4180 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.1 MPa
@Strain 0.600 %,
Temperature 100 °C		4220 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.6 MPa
@Strain 0.230 %,
Temperature 0.000 °C		4440 psi
@Strain 0.230 %,
Temperature 32.0 °F		DAM; ISO 527
 31.5 MPa
@Strain 0.800 %,
Temperature 150 °C		4570 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.5 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4570 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.2 MPa
@Strain 0.300 %,
Temperature 23.0 °C		4670 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 0.220 %,
Temperature -20.0 °C		4680 psi
@Strain 0.220 %,
Temperature -4.00 °F		DAM; ISO 527
 33.0 MPa
@Strain 0.700 %,
Temperature 100 °C		4790 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.8 MPa
@Strain 1.20 %,
Temperature 120 °C		4900 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 527
 34.0 MPa
@Strain 0.900 %,
Temperature 150 °C		4930 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.1 MPa
@Strain 1.00 %,
Temperature 150 °C		5240 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.6 MPa
@Strain 0.800 %,
Temperature 100 °C		5310 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.0 MPa
@Strain 1.14 %,
Temperature 90.0 °C		5510 psi
@Strain 1.14 %,
Temperature 194 °F		50%RH; ISO 527
 38.2 MPa
@Strain 1.10 %,
Temperature 150 °C		5540 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 0.900 %,
Temperature 100 °C		5770 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.2 MPa
@Strain 1.20 %,
Temperature 150 °C		5830 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.5 MPa
@Strain 1.06 %,
Temperature 60.0 °C		5870 psi
@Strain 1.06 %,
Temperature 140 °F		50%RH; ISO 527
 41.3 MPa
@Strain 1.80 %,
Temperature 120 °C		5990 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 527
 41.9 MPa
@Strain 1.40 %,
Temperature 120 °C		6080 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 527
 41.9 MPa
@Strain 0.880 %,
Temperature 40.0 °C		6080 psi
@Strain 0.880 %,
Temperature 104 °F		50%RH; ISO 527
 42.1 MPa
@Strain 1.30 %,
Temperature 150 °C		6110 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.4 MPa
@Strain 0.400 %,
Temperature -40.0 °C		6150 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 1.00 %,
Temperature 100 °C		6240 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 0.400 %,
Temperature 23.0 °C		6240 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 1.40 %,
Temperature 150 °C		6370 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 0.700 %,
Temperature 23.0 °C		6440 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 527
 44.6 MPa
@Strain 0.620 %,
Temperature 60.0 °C		6470 psi
@Strain 0.620 %,
Temperature 140 °F		DAM; ISO 527
 45.2 MPa
@Strain 1.28 %,
Temperature 90.0 °C		6560 psi
@Strain 1.28 %,
Temperature 194 °F		DAM; ISO 527
 45.4 MPa
@Strain 1.50 %,
Temperature 150 °C		6580 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.9 MPa
@Strain 1.10 %,
Temperature 100 °C		6660 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.0 MPa
@Strain 2.40 %,
Temperature 120 °C		6670 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 527
 46.1 MPa
@Strain 0.480 %,
Temperature 0.000 °C		6690 psi
@Strain 0.480 %,
Temperature 32.0 °F		50%RH; ISO 527
 47.1 MPa
@Strain 1.60 %,
Temperature 150 °C		6830 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.2 MPa
@Strain 1.71 %,
Temperature 90.0 °C		6850 psi
@Strain 1.71 %,
Temperature 194 °F		50%RH; ISO 527
 48.6 MPa
@Strain 1.70 %,
Temperature 150 °C		7050 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 1.20 %,
Temperature 100 °C		7060 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.8 MPa
@Strain 3.00 %,
Temperature 120 °C		7080 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 527
 49.1 MPa
@Strain 0.440 %,
Temperature 40.0 °C		7120 psi
@Strain 0.440 %,
Temperature 104 °F		DAM; ISO 527
 50.0 MPa
@Strain 1.80 %,
Temperature 150 °C		7250 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.4 MPa
@Strain 0.440 %,
Temperature -20.0 °C		7310 psi
@Strain 0.440 %,
Temperature -4.00 °F		50%RH; ISO 527
 50.5 MPa
@Strain 3.60 %,
Temperature 120 °C		7320 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 527
 51.2 MPa
@Strain 4.20 %,
Temperature 120 °C		7430 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 527
 51.3 MPa
@Strain 1.90 %,
Temperature 150 °C		7440 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 51.4 MPa
@Strain 1.30 %,
Temperature 100 °C		7450 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.5 MPa
@Strain 4.80 %,
Temperature 120 °C		7470 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 527
 51.7 MPa
@Strain 5.40 %,
Temperature 120 °C		7500 psi
@Strain 5.40 %,
Temperature 248 °F		50%RH; ISO 527
 51.8 MPa
@Strain 1.59 %,
Temperature 60.0 °C		7510 psi
@Strain 1.59 %,
Temperature 140 °F		50%RH; ISO 527
 51.9 MPa
@Strain 6.00 %,
Temperature 120 °C		7530 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 527
 52.6 MPa
@Strain 2.10 %,
Temperature 120 °C		7630 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 527
 52.6 MPa
@Strain 2.00 %,
Temperature 150 °C		7630 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 52.7 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7640 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 53.0 MPa
@Strain 2.28 %,
Temperature 90.0 °C		7690 psi
@Strain 2.28 %,
Temperature 194 °F		50%RH; ISO 527
 53.0 MPa
@Strain 0.440 %,
Temperature 23.0 °C		7690 psi
@Strain 0.440 %,
Temperature 73.4 °F		DAM; ISO 527
 53.4 MPa
@Strain 0.500 %,
Temperature 23.0 °C		7750 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.7 MPa
@Strain 2.10 %,
Temperature 150 °C		7790 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 53.8 MPa
@Strain 1.40 %,
Temperature 100 °C		7800 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 2.20 %,
Temperature 150 °C		7960 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 55.3 MPa
@Strain 1.32 %,
Temperature 40.0 °C		8020 psi
@Strain 1.32 %,
Temperature 104 °F		50%RH; ISO 527
 55.9 MPa
@Strain 2.30 %,
Temperature 150 °C		8110 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.1 MPa
@Strain 1.50 %,
Temperature 100 °C		8140 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.6 MPa
@Strain 2.85 %,
Temperature 90.0 °C		8210 psi
@Strain 2.85 %,
Temperature 194 °F		50%RH; ISO 527
 56.8 MPa
@Strain 2.40 %,
Temperature 150 °C		8240 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 0.460 %,
Temperature 0.000 °C		8270 psi
@Strain 0.460 %,
Temperature 32.0 °F		DAM; ISO 527
 57.2 MPa
@Strain 1.92 %,
Temperature 90.0 °C		8300 psi
@Strain 1.92 %,
Temperature 194 °F		DAM; ISO 527
 57.7 MPa
@Strain 2.50 %,
Temperature 150 °C		8370 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.3 MPa
@Strain 1.60 %,
Temperature 100 °C		8460 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.4 MPa
@Strain 1.05 %,
Temperature 23.0 °C		8470 psi
@Strain 1.05 %,
Temperature 73.4 °F		50%RH; ISO 527
 58.5 MPa
@Strain 2.60 %,
Temperature 150 °C		8480 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.6 MPa
@Strain 0.440 %,
Temperature -20.0 °C		8500 psi
@Strain 0.440 %,
Temperature -4.00 °F		DAM; ISO 527
 58.6 MPa
@Strain 3.42 %,
Temperature 90.0 °C		8500 psi
@Strain 3.42 %,
Temperature 194 °F		50%RH; ISO 527
 59.2 MPa
@Strain 2.70 %,
Temperature 150 °C		8590 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 59.3 MPa
@Strain 2.12 %,
Temperature 60.0 °C		8600 psi
@Strain 2.12 %,
Temperature 140 °F		50%RH; ISO 527
 59.4 MPa
@Strain 3.99 %,
Temperature 90.0 °C		8620 psi
@Strain 3.99 %,
Temperature 194 °F		50%RH; ISO 527
 59.4 MPa
@Strain 0.930 %,
Temperature 60.0 °C		8620 psi
@Strain 0.930 %,
Temperature 140 °F		DAM; ISO 527
 59.5 MPa
@Strain 2.80 %,
Temperature 120 °C		8630 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 527
 59.6 MPa
@Strain 4.56 %,
Temperature 90.0 °C		8640 psi
@Strain 4.56 %,
Temperature 194 °F		50%RH; ISO 527
 59.7 MPa
@Strain 5.13 %,
Temperature 90.0 °C		8660 psi
@Strain 5.13 %,
Temperature 194 °F		50%RH; ISO 527
 59.8 MPa
@Strain 5.70 %,
Temperature 90.0 °C		8670 psi
@Strain 5.70 %,
Temperature 194 °F		50%RH; ISO 527
 59.9 MPa
@Strain 2.80 %,
Temperature 150 °C		8690 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.4 MPa
@Strain 1.70 %,
Temperature 100 °C		8760 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.5 MPa
@Strain 2.90 %,
Temperature 150 °C		8770 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.0 MPa
@Strain 3.00 %,
Temperature 150 °C		8850 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.5 MPa
@Strain 3.10 %,
Temperature 150 °C		8920 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.9 MPa
@Strain 3.20 %,
Temperature 150 °C		8980 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 3.30 %,
Temperature 150 °C		9050 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 1.80 %,
Temperature 100 °C		9050 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 62.8 MPa
@Strain 3.40 %,
Temperature 150 °C		9110 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.1 MPa
@Strain 3.50 %,
Temperature 150 °C		9150 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.4 MPa
@Strain 3.60 %,
Temperature 150 °C		9200 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.5 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9210 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.6 MPa
@Strain 3.50 %,
Temperature 120 °C		9220 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 527
 63.7 MPa
@Strain 3.70 %,
Temperature 150 °C		9240 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.8 MPa
@Strain 0.720 %,
Temperature 0.000 °C		9250 psi
@Strain 0.720 %,
Temperature 32.0 °F		50%RH; ISO 527
 63.9 MPa
@Strain 3.80 %,
Temperature 150 °C		9270 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 0.600 %,
Temperature 23.0 °C		9270 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.0 MPa
@Strain 2.65 %,
Temperature 60.0 °C		9280 psi
@Strain 2.65 %,
Temperature 140 °F		50%RH; ISO 527
 64.1 MPa
@Strain 1.90 %,
Temperature 100 °C		9300 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 64.2 MPa
@Strain 3.90 %,
Temperature 150 °C		9310 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.5 MPa
@Strain 4.00 %,
Temperature 150 °C		9350 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.7 MPa
@Strain 4.10 %,
Temperature 150 °C		9380 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.7 MPa
@Strain 4.20 %,
Temperature 150 °C		9380 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.9 MPa
@Strain 1.76 %,
Temperature 40.0 °C		9410 psi
@Strain 1.76 %,
Temperature 104 °F		50%RH; ISO 527
 65.0 MPa
@Strain 2.56 %,
Temperature 90.0 °C		9430 psi
@Strain 2.56 %,
Temperature 194 °F		DAM; ISO 527
 65.0 MPa
@Strain 4.30 %,
Temperature 150 °C		9430 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.1 MPa
@Strain 4.40 %,
Temperature 150 °C		9440 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.2 MPa
@Strain 4.60 %,
Temperature 150 °C		9460 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.3 MPa
@Strain 4.50 %,
Temperature 150 °C		9470 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.5 MPa
@Strain 4.70 %,
Temperature 150 °C		9500 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.6 MPa
@Strain 4.80 %,
Temperature 150 °C		9510 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.6 MPa
@Strain 4.90 %,
Temperature 150 °C		9510 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.7 MPa
@Strain 5.00 %,
Temperature 150 °C		9530 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.7 MPa
@Strain 5.50 %,
Temperature 150 °C		9530 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.8 MPa
@Strain 2.00 %,
Temperature 100 °C		9540 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 65.9 MPa
@Strain 4.20 %,
Temperature 120 °C		9560 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 527
 66.8 MPa
@Strain 3.18 %,
Temperature 60.0 °C		9690 psi
@Strain 3.18 %,
Temperature 140 °F		50%RH; ISO 527
 66.8 MPa
@Strain 6.30 %,
Temperature 120 °C		9690 psi
@Strain 6.30 %,
Temperature 248 °F		DAM; ISO 527
 67.0 MPa
@Strain 4.90 %,
Temperature 120 °C		9720 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 527
 67.2 MPa
@Strain 5.60 %,
Temperature 120 °C		9750 psi
@Strain 5.60 %,
Temperature 248 °F		DAM; ISO 527
 67.3 MPa
@Strain 2.10 %,
Temperature 100 °C		9760 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 68.3 MPa
@Strain 3.71 %,
Temperature 60.0 °C		9910 psi
@Strain 3.71 %,
Temperature 140 °F		50%RH; ISO 527
 68.5 MPa
@Strain 4.24 %,
Temperature 60.0 °C		9940 psi
@Strain 4.24 %,
Temperature 140 °F		50%RH; ISO 527
 68.5 MPa
@Strain 0.660 %,
Temperature 40.0 °C		9940 psi
@Strain 0.660 %,
Temperature 104 °F		DAM; ISO 527
 68.5 MPa
@Strain 2.20 %,
Temperature 100 °C		9940 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 68.8 MPa
@Strain 1.40 %,
Temperature 23.0 °C		9980 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 527
 69.7 MPa
@Strain 2.30 %,
Temperature 100 °C		10100 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 69.9 MPa
@Strain 3.20 %,
Temperature 90.0 °C		10100 psi
@Strain 3.20 %,
Temperature 194 °F		DAM; ISO 527
 70.2 MPa
@Strain 0.660 %,
Temperature -20.0 °C		10200 psi
@Strain 0.660 %,
Temperature -4.00 °F		50%RH; ISO 527
 70.5 MPa
@Strain 1.24 %,
Temperature 60.0 °C		10200 psi
@Strain 1.24 %,
Temperature 140 °F		DAM; ISO 527
 70.8 MPa
@Strain 2.40 %,
Temperature 100 °C		10300 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 71.5 MPa
@Strain 2.20 %,
Temperature 40.0 °C		10400 psi
@Strain 2.20 %,
Temperature 104 °F		50%RH; ISO 527
 71.6 MPa
@Strain 2.50 %,
Temperature 100 °C		10400 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 72.1 MPa
@Strain 3.84 %,
Temperature 90.0 °C		10500 psi
@Strain 3.84 %,
Temperature 194 °F		DAM; ISO 527
 72.4 MPa
@Strain 2.60 %,
Temperature 100 °C		10500 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 72.8 MPa
@Strain 4.48 %,
Temperature 90.0 °C		10600 psi
@Strain 4.48 %,
Temperature 194 °F		DAM; ISO 527
 73.0 MPa
@Strain 2.70 %,
Temperature 100 °C		10600 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.3 MPa
@Strain 5.12 %,
Temperature 90.0 °C		10600 psi
@Strain 5.12 %,
Temperature 194 °F		DAM; ISO 527
 73.6 MPa
@Strain 2.80 %,
Temperature 100 °C		10700 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.7 MPa
@Strain 5.76 %,
Temperature 90.0 °C		10700 psi
@Strain 5.76 %,
Temperature 194 °F		DAM; ISO 527
 74.1 MPa
@Strain 2.90 %,
Temperature 100 °C		10700 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 74.2 MPa
@Strain 0.700 %,
Temperature 23.0 °C		10800 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.2 MPa
@Strain 0.700 %,
Temperature -40.0 °C		10800 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 74.2 MPa
@Strain 6.40 %,
Temperature 90.0 °C		10800 psi
@Strain 6.40 %,
Temperature 194 °F		DAM; ISO 527
 74.4 MPa
@Strain 0.660 %,
Temperature 23.0 °C		10800 psi
@Strain 0.660 %,
Temperature 73.4 °F		DAM; ISO 527
 74.5 MPa
@Strain 3.00 %,
Temperature 100 °C		10800 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 74.8 MPa
@Strain 3.10 %,
Temperature 100 °C		10800 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.1 MPa
@Strain 3.20 %,
Temperature 100 °C		10900 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.4 MPa
@Strain 3.30 %,
Temperature 100 °C		10900 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.6 MPa
@Strain 3.40 %,
Temperature 100 °C		11000 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.8 MPa
@Strain 3.50 %,
Temperature 100 °C		11000 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.8 MPa
@Strain 2.64 %,
Temperature 40.0 °C		11000 psi
@Strain 2.64 %,
Temperature 104 °F		50%RH; ISO 527
 75.9 MPa
@Strain 3.60 %,
Temperature 100 °C		11000 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.1 MPa
@Strain 3.70 %,
Temperature 100 °C		11000 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.2 MPa
@Strain 3.80 %,
Temperature 100 °C		11100 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 3.90 %,
Temperature 100 °C		11100 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 4.00 %,
Temperature 100 °C		11100 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 1.75 %,
Temperature 23.0 °C		11100 psi
@Strain 1.75 %,
Temperature 73.4 °F		50%RH; ISO 527
 76.4 MPa
@Strain 4.10 %,
Temperature 100 °C		11100 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 4.20 %,
Temperature 100 °C		11100 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 4.30 %,
Temperature 100 °C		11100 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.08 %,
Temperature 40.0 °C		11400 psi
@Strain 3.08 %,
Temperature 104 °F		50%RH; ISO 527
 78.5 MPa
@Strain 1.55 %,
Temperature 60.0 °C		11400 psi
@Strain 1.55 %,
Temperature 140 °F		DAM; ISO 527
 78.5 MPa
@Strain 0.960 %,
Temperature 0.000 °C		11400 psi
@Strain 0.960 %,
Temperature 32.0 °F		50%RH; ISO 527
 79.7 MPa
@Strain 0.690 %,
Temperature 0.000 °C		11600 psi
@Strain 0.690 %,
Temperature 32.0 °F		DAM; ISO 527
 79.7 MPa
@Strain 3.52 %,
Temperature 40.0 °C		11600 psi
@Strain 3.52 %,
Temperature 104 °F		50%RH; ISO 527
 80.1 MPa
@Strain 3.96 %,
Temperature 40.0 °C		11600 psi
@Strain 3.96 %,
Temperature 104 °F		50%RH; ISO 527
 80.4 MPa
@Strain 0.660 %,
Temperature -20.0 °C		11700 psi
@Strain 0.660 %,
Temperature -4.00 °F		DAM; ISO 527
 81.7 MPa
@Strain 2.10 %,
Temperature 23.0 °C		11800 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 527
 83.9 MPa
@Strain 0.800 %,
Temperature 23.0 °C		12200 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 1.86 %,
Temperature 60.0 °C		12200 psi
@Strain 1.86 %,
Temperature 140 °F		DAM; ISO 527
 84.6 MPa
@Strain 0.880 %,
Temperature 40.0 °C		12300 psi
@Strain 0.880 %,
Temperature 104 °F		DAM; ISO 527
 84.7 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12300 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.4 MPa
@Strain 2.45 %,
Temperature 23.0 °C		12400 psi
@Strain 2.45 %,
Temperature 73.4 °F		50%RH; ISO 527
 87.5 MPa
@Strain 0.880 %,
Temperature -20.0 °C		12700 psi
@Strain 0.880 %,
Temperature -4.00 °F		50%RH; ISO 527
 88.0 MPa
@Strain 2.80 %,
Temperature 23.0 °C		12800 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 527
 88.0 MPa
@Strain 2.17 %,
Temperature 60.0 °C		12800 psi
@Strain 2.17 %,
Temperature 140 °F		DAM; ISO 527
 89.5 MPa
@Strain 3.15 %,
Temperature 23.0 °C		13000 psi
@Strain 3.15 %,
Temperature 73.4 °F		50%RH; ISO 527
 90.4 MPa
@Strain 3.50 %,
Temperature 23.0 °C		13100 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 527
 90.4 MPa
@Strain 2.48 %,
Temperature 60.0 °C		13100 psi
@Strain 2.48 %,
Temperature 140 °F		DAM; ISO 527
 90.8 MPa
@Strain 1.20 %,
Temperature 0.000 °C		13200 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 527
 91.9 MPa
@Strain 2.79 %,
Temperature 60.0 °C		13300 psi
@Strain 2.79 %,
Temperature 140 °F		DAM; ISO 527
 92.5 MPa
@Strain 3.10 %,
Temperature 60.0 °C		13400 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 527
 92.6 MPa
@Strain 0.880 %,
Temperature 23.0 °C		13400 psi
@Strain 0.880 %,
Temperature 73.4 °F		DAM; ISO 527
 93.3 MPa
@Strain 0.900 %,
Temperature 23.0 °C		13500 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.1 MPa
@Strain 0.900 %,
Temperature -40.0 °C		13800 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 97.7 MPa
@Strain 1.10 %,
Temperature 40.0 °C		14200 psi
@Strain 1.10 %,
Temperature 104 °F		DAM; ISO 527
 98.7 MPa
@Strain 0.880 %,
Temperature -20.0 °C		14300 psi
@Strain 0.880 %,
Temperature -4.00 °F		DAM; ISO 527
 99.0 MPa
@Strain 0.920 %,
Temperature 0.000 °C		14400 psi
@Strain 0.920 %,
Temperature 32.0 °F		DAM; ISO 527
 101 MPa
@Strain 1.44 %,
Temperature 0.000 °C		14600 psi
@Strain 1.44 %,
Temperature 32.0 °F		50%RH; ISO 527
 102 MPa
@Strain 1.00 %,
Temperature 23.0 °C		14800 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103 MPa
@Strain 1.10 %,
Temperature -20.0 °C		14900 psi
@Strain 1.10 %,
Temperature -4.00 °F		50%RH; ISO 527
 105 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15200 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108 MPa
@Strain 1.32 %,
Temperature 40.0 °C		15700 psi
@Strain 1.32 %,
Temperature 104 °F		DAM; ISO 527
 108 MPa
@Strain 1.10 %,
Temperature 23.0 °C		15700 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 527
 109 MPa
@Strain 1.68 %,
Temperature 0.000 °C		15800 psi
@Strain 1.68 %,
Temperature 32.0 °F		50%RH; ISO 527
 110.3 MPa
@Strain 1.10 %,
Temperature 23.0 °C		16000 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114 MPa
@Strain 1.10 %,
Temperature -20.0 °C		16500 psi
@Strain 1.10 %,
Temperature -4.00 °F		DAM; ISO 527
 114.7 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16640 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115 MPa
@Strain 1.15 %,
Temperature 0.000 °C		16700 psi
@Strain 1.15 %,
Temperature 32.0 °F		DAM; ISO 527
 116 MPa
@Strain 1.32 %,
Temperature -20.0 °C		16800 psi
@Strain 1.32 %,
Temperature -4.00 °F		50%RH; ISO 527
 116 MPa
@Strain 1.92 %,
Temperature 0.000 °C		16800 psi
@Strain 1.92 %,
Temperature 32.0 °F		50%RH; ISO 527
 116 MPa
@Strain 1.54 %,
Temperature 40.0 °C		16800 psi
@Strain 1.54 %,
Temperature 104 °F		DAM; ISO 527
 118.2 MPa
@Strain 1.20 %,
Temperature 23.0 °C		17140 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120 MPa
@Strain 1.32 %,
Temperature 23.0 °C		17400 psi
@Strain 1.32 %,
Temperature 73.4 °F		DAM; ISO 527
 122 MPa
@Strain 2.16 %,
Temperature 0.000 °C		17700 psi
@Strain 2.16 %,
Temperature 32.0 °F		50%RH; ISO 527
 123 MPa
@Strain 1.76 %,
Temperature 40.0 °C		17800 psi
@Strain 1.76 %,
Temperature 104 °F		DAM; ISO 527
 123.9 MPa
@Strain 1.20 %,
Temperature -40.0 °C		17970 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 125.5 MPa
@Strain 1.30 %,
Temperature 23.0 °C		18200 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 126 MPa
@Strain 2.40 %,
Temperature 0.000 °C		18300 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 527
 127 MPa
@Strain 1.98 %,
Temperature 40.0 °C		18400 psi
@Strain 1.98 %,
Temperature 104 °F		DAM; ISO 527
 128 MPa
@Strain 1.32 %,
Temperature -20.0 °C		18600 psi
@Strain 1.32 %,
Temperature -4.00 °F		DAM; ISO 527
 129 MPa
@Strain 1.54 %,
Temperature -20.0 °C		18700 psi
@Strain 1.54 %,
Temperature -4.00 °F		50%RH; ISO 527
 129 MPa
@Strain 1.38 %,
Temperature 0.000 °C		18700 psi
@Strain 1.38 %,
Temperature 32.0 °F		DAM; ISO 527
 130 MPa
@Strain 2.20 %,
Temperature 40.0 °C		18900 psi
@Strain 2.20 %,
Temperature 104 °F		DAM; ISO 527
 130 MPa
@Strain 1.54 %,
Temperature 23.0 °C		18900 psi
@Strain 1.54 %,
Temperature 73.4 °F		DAM; ISO 527
 132.2 MPa
@Strain 1.40 %,
Temperature 23.0 °C		19170 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 132.9 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19280 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 138 MPa
@Strain 1.76 %,
Temperature 23.0 °C		20000 psi
@Strain 1.76 %,
Temperature 73.4 °F		DAM; ISO 527
 138.5 MPa
@Strain 1.50 %,
Temperature 23.0 °C		20090 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 140 MPa
@Strain 1.76 %,
Temperature -20.0 °C		20300 psi
@Strain 1.76 %,
Temperature -4.00 °F		50%RH; ISO 527
 140 MPa
@Strain 1.54 %,
Temperature -20.0 °C		20300 psi
@Strain 1.54 %,
Temperature -4.00 °F		DAM; ISO 527
 141 MPa
@Strain 1.61 %,
Temperature 0.000 °C		20500 psi
@Strain 1.61 %,
Temperature 32.0 °F		DAM; ISO 527
 141.5 MPa
@Strain 1.40 %,
Temperature -40.0 °C		20520 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 144.2 MPa
@Strain 1.60 %,
Temperature 23.0 °C		20910 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 145 MPa
@Strain 1.98 %,
Temperature 23.0 °C		21000 psi
@Strain 1.98 %,
Temperature 73.4 °F		DAM; ISO 527
 149 MPa
@Strain 2.20 %,
Temperature 23.0 °C		21600 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 527
 149 MPa
@Strain 1.84 %,
Temperature 0.000 °C		21600 psi
@Strain 1.84 %,
Temperature 32.0 °F		DAM; ISO 527
 149.4 MPa
@Strain 1.70 %,
Temperature 23.0 °C		21670 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 149.8 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21730 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 150 MPa
@Strain 1.76 %,
Temperature -20.0 °C		21800 psi
@Strain 1.76 %,
Temperature -4.00 °F		DAM; ISO 527
 151 MPa
@Strain 1.98 %,
Temperature -20.0 °C		21900 psi
@Strain 1.98 %,
Temperature -4.00 °F		50%RH; ISO 527
 154.3 MPa
@Strain 1.80 %,
Temperature 23.0 °C		22380 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 156 MPa
@Strain 2.07 %,
Temperature 0.000 °C		22600 psi
@Strain 2.07 %,
Temperature 32.0 °F		DAM; ISO 527
 157.7 MPa
@Strain 1.60 %,
Temperature -40.0 °C		22870 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 158.3 MPa
@Strain 1.90 %,
Temperature 23.0 °C		22960 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 159 MPa
@Strain 1.98 %,
Temperature -20.0 °C		23100 psi
@Strain 1.98 %,
Temperature -4.00 °F		DAM; ISO 527
 160 MPa
@Strain 2.20 %,
Temperature -20.0 °C		23200 psi
@Strain 2.20 %,
Temperature -4.00 °F		50%RH; ISO 527
 162 MPa
@Strain 2.30 %,
Temperature 0.000 °C		23500 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 527
 165.2 MPa
@Strain 1.70 %,
Temperature -40.0 °C		23960 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 167 MPa
@Strain 2.20 %,
Temperature -20.0 °C		24200 psi
@Strain 2.20 %,
Temperature -4.00 °F		DAM; ISO 527
 172.4 MPa
@Strain 1.80 %,
Temperature -40.0 °C		25000 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 179.2 MPa
@Strain 1.90 %,
Temperature -40.0 °C		25990 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 185.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		26900 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 191.7 MPa
@Strain 2.10 %,
Temperature -40.0 °C		27800 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 197.7 MPa
@Strain 2.20 %,
Temperature -40.0 °C		28670 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 202.6 MPa
@Strain 2.30 %,
Temperature -40.0 °C		29380 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.2 %
@Temperature 23.0 °C		2.2 %
@Temperature 73.4 °F		DAM; ISO 527
 4.6 %
@Temperature 23.0 °C		4.6 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  6.50 GPa
@Temperature 23.0 °C		943 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 10.0 GPa
@Temperature 23.0 °C		1450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 9.90 GPa
@Temperature 23.0 °C		1440 ksi
@Temperature 73.4 °F		DAM; ISO 178
Shear Modulus  0.249 GPa
@Temperature 250 °C		36.1 ksi
@Temperature 482 °F		DAM; ISO 6721
 0.345 GPa
@Temperature 240 °C		50.0 ksi
@Temperature 464 °F		DAM; ISO 6721
 0.416 GPa
@Temperature 230 °C		60.3 ksi
@Temperature 446 °F		DAM; ISO 6721
 0.466 GPa
@Temperature 220 °C		67.6 ksi
@Temperature 428 °F		DAM; ISO 6721
 0.499 GPa
@Temperature 210 °C		72.4 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.531 GPa
@Temperature 200 °C		77.0 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.553 GPa
@Temperature 190 °C		80.2 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.575 GPa
@Temperature 180 °C		83.4 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.598 GPa
@Temperature 170 °C		86.7 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.620 GPa
@Temperature 160 °C		89.9 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.642 GPa
@Temperature 150 °C		93.1 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.665 GPa
@Temperature 140 °C		96.5 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.690 GPa
@Temperature 130 °C		100 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.718 GPa
@Temperature 120 °C		104 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.754 GPa
@Temperature 110 °C		109 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.808 GPa
@Temperature 100 °C		117 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.898 GPa
@Temperature 90.0 °C		130 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.980 GPa
@Temperature 84.0 °C		142 ksi
@Temperature 183 °F		DAM; ISO 6721
 1.135 GPa
@Temperature 76.0 °C		164.6 ksi
@Temperature 169 °F		DAM; ISO 6721
 1.296 GPa
@Temperature 70.0 °C		188.0 ksi
@Temperature 158 °F		DAM; ISO 6721
 1.664 GPa
@Temperature 60.0 °C		241.3 ksi
@Temperature 140 °F		DAM; ISO 6721
 2.098 GPa
@Temperature 50.0 °C		304.3 ksi
@Temperature 122 °F		DAM; ISO 6721
 2.27 GPa
@Temperature 40.0 °C		329 ksi
@Temperature 104 °F		DAM; ISO 6721
 2.366 GPa
@Temperature 30.0 °C		343.2 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 2.421 GPa
@Temperature 20.0 °C		351.1 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 2.447 GPa
@Temperature 10.0 °C		354.9 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 2.463 GPa
@Temperature 0.000 °C		357.2 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 2.474 GPa
@Temperature -10.0 °C		358.8 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 2.485 GPa
@Temperature -20.0 °C		360.4 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 2.50 GPa
@Temperature -30.0 °C		363 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 2.527 GPa
@Temperature -40.0 °C		366.5 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 2.569 GPa
@Temperature -50.0 °C		372.6 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 4.50 J/cm²
@Temperature 23.0 °C		21.4 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 5.00 J/cm²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.450 J/cm²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.650 J/cm²
@Temperature 23.0 °C		3.09 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Dielectric Constant  4.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.9
@Frequency 100 Hz,
Temperature 23.0 °C		4.9
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 5.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		5.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 13.9
@Frequency 100 Hz,
Temperature 23.0 °C		13.9
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 28.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		711 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.013
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.013
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.014
@Frequency 100 Hz,
Temperature 23.0 °C		0.014
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.070
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.070
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.54
@Frequency 100 Hz,
Temperature 23.0 °C		0.54
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  87.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		48.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 87.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		48.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 256 °C493 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 240 °C464 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesWarp ResistantDAM
 Warpage, LowDAM
FillerGlass/MineralDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-(GF+MD)40<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass/Mineral Reinforced ResinsDAM
 Low Warp ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-(GF+MD)40ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive Under the HoodDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45446.html

免责声明: 本文 DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4