- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.9
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 42.0
- 弯曲模量 [MPa]: 1.063
- 硬度: 69.0
- 热变形温度 [℃]: 187.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | DAM; ASTM D792 | ||
| Density | 1.11 g/cc | 0.0401 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 0.90 % @Temperature 23.0 °C | 0.90 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | |||
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Thickness 2.00 mm | 0.017 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Thickness 2.00 mm | 0.017 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 69 | 69 | 50%RH; ASTM D785 | ||
| 113 | 113 | DAM; ASTM D785 | |||
| Tensile Strength | 42.0 MPa @Temperature 23.0 °C | 6090 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 61.0 MPa @Temperature 23.0 °C | 8850 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Stress | 24.0 MPa @Strain 50.0 %, Temperature 150 °C | 3480 psi @Strain 50.0 %, Temperature 302 °F | 50%RH; ISO 527 | ||
| 27.0 MPa @Strain 50.0 %, Temperature 120 °C | 3920 psi @Strain 50.0 %, Temperature 248 °F | 50%RH; ISO 527 | |||
| 27.0 MPa @Strain 50.0 %, Temperature 150 °C | 3920 psi @Strain 50.0 %, Temperature 302 °F | DAM; ISO 527 | |||
| 29.0 MPa @Strain 50.0 %, Temperature 120 °C | 4210 psi @Strain 50.0 %, Temperature 248 °F | DAM; ISO 527 | |||
| 31.0 MPa @Strain 50.0 %, Temperature 100 °C | 4500 psi @Strain 50.0 %, Temperature 212 °F | 50%RH; ISO 527 | |||
| 33.0 MPa @Strain 50.0 %, Temperature 80.0 °C | 4790 psi @Strain 50.0 %, Temperature 176 °F | 50%RH; ISO 527 | |||
| 33.0 MPa @Strain 50.0 %, Temperature 100 °C | 4790 psi @Strain 50.0 %, Temperature 212 °F | DAM; ISO 527 | |||
| 36.0 MPa @Strain 50.0 %, Temperature 60.0 °C | 5220 psi @Strain 50.0 %, Temperature 140 °F | 50%RH; ISO 527 | |||
| 37.0 MPa @Strain 50.0 %, Temperature 80.0 °C | 5370 psi @Strain 50.0 %, Temperature 176 °F | DAM; ISO 527 | |||
| 43.0 MPa @Strain 50.0 %, Temperature 23.0 °C | 6240 psi @Strain 50.0 %, Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 43.0 MPa @Strain 50.0 %, Temperature 60.0 °C | 6240 psi @Strain 50.0 %, Temperature 140 °F | DAM; ISO 527 | |||
| 56.0 MPa @Strain 50.0 %, Temperature 0.000 °C | 8120 psi @Strain 50.0 %, Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 61.0 MPa @Strain 50.0 %, Temperature 23.0 °C | 8850 psi @Strain 50.0 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| 70.0 MPa @Strain 50.0 %, Temperature 0.000 °C | 10200 psi @Strain 50.0 %, Temperature 32.0 °F | DAM; ISO 527 | |||
| 86.0 MPa @Strain 50.0 %, Temperature -40.0 °C | 12500 psi @Strain 50.0 %, Temperature -40.0 °F | 50%RH; ISO 527 | |||
| 94.0 MPa @Strain 50.0 %, Temperature -40.0 °C | 13600 psi @Strain 50.0 %, Temperature -40.0 °F | DAM; ISO 527 | |||
| Tensile Strength, Yield | 42.0 MPa @Temperature 23.0 °C | 6090 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 28 % @Temperature 0.000 °C | 28 % @Temperature 32.0 °F | DAM; nominal; ISO 527 | ||
| 29 % @Temperature 23.0 °C | 29 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 35 % @Temperature 23.0 °C | 35 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 36 % @Temperature 23.0 °C | 36 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| >= 50 % @Temperature -40.0 °C | >= 50 % @Temperature -40.0 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 0.000 °C | >= 50 % @Temperature 32.0 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 100 °C | >= 50 % @Temperature 212 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 120 °C | >= 50 % @Temperature 248 °F | DAM; nominal; ISO 527 | |||
| >= 50 % @Temperature 120 °C | >= 50 % @Temperature 248 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 150 °C | >= 50 % @Temperature 302 °F | DAM; nominal; ISO 527 | |||
| >= 50 % @Temperature 150 °C | >= 50 % @Temperature 302 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 60.0 °C | >= 50 % @Temperature 140 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 60.0 °C | >= 50 % @Temperature 140 °F | DAM; nominal; ISO 527 | |||
| >= 50 % @Temperature 80.0 °C | >= 50 % @Temperature 176 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 80.0 °C | >= 50 % @Temperature 176 °F | DAM; nominal; ISO 527 | |||
| >= 50 % @Temperature 100 °C | >= 50 % @Temperature 212 °F | DAM; nominal; ISO 527 | |||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 7.1 % @Temperature 0.000 °C | 7.1 % @Temperature 32.0 °F | DAM; ISO 527 | |||
| 8.7 % @Temperature -40.0 °C | 8.7 % @Temperature -40.0 °F | 50%RH; ISO 527 | |||
| 9.7 % @Temperature -40.0 °C | 9.7 % @Temperature -40.0 °F | DAM; ISO 527 | |||
| 22.4 % @Temperature 0.000 °C | 22.4 % @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 27 % @Temperature 23.0 °C | 27 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 30.1 % @Temperature 80.0 °C | 30.1 % @Temperature 176 °F | 50%RH; ISO 527 | |||
| 31 % @Temperature 60.0 °C | 31 % @Temperature 140 °F | 50%RH; ISO 527 | |||
| 45.1 % @Temperature 60.0 °C | 45.1 % @Temperature 140 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 80.0 °C | >= 50 % @Temperature 176 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 100 °C | >= 50 % @Temperature 212 °F | 50%RH; ISO 527 | |||
| >= 50 % @Temperature 100 °C | >= 50 % @Temperature 212 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 120 °C | >= 50 % @Temperature 248 °F | 50%RH; ISO 527 | |||
| >= 50 % @Temperature 120 °C | >= 50 % @Temperature 248 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 150 °C | >= 50 % @Temperature 302 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 150 °C | >= 50 % @Temperature 302 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.344 GPa @Temperature 150 °C | 49.9 ksi @Temperature 302 °F | 50%RH; ISO 527 | ||
| 0.358 GPa @Temperature 150 °C | 51.9 ksi @Temperature 302 °F | DAM; ISO 527 | |||
| 0.443 GPa @Temperature 120 °C | 64.3 ksi @Temperature 248 °F | 50%RH; ISO 527 | |||
| 0.476 GPa @Temperature 120 °C | 69.0 ksi @Temperature 248 °F | DAM; ISO 527 | |||
| 0.489 GPa @Temperature 100 °C | 70.9 ksi @Temperature 212 °F | 50%RH; ISO 527 | |||
| 0.513 GPa @Temperature 80.0 °C | 74.4 ksi @Temperature 176 °F | 50%RH; ISO 527 | |||
| 0.639 GPa @Temperature 60.0 °C | 92.7 ksi @Temperature 140 °F | 50%RH; ISO 527 | |||
| 0.640 GPa @Temperature 100 °C | 92.8 ksi @Temperature 212 °F | DAM; ISO 527 | |||
| 0.894 GPa @Temperature 80.0 °C | 130 ksi @Temperature 176 °F | DAM; ISO 527 | |||
| 1.075 GPa @Temperature 23.0 °C | 155.9 ksi @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 1.075 GPa @Temperature 23.0 °C | 155.9 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 1.777 GPa @Temperature 60.0 °C | 257.7 ksi @Temperature 140 °F | DAM; ISO 527 | |||
| 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 2.426 GPa @Temperature 0.000 °C | 351.9 ksi @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 2.443 GPa @Temperature 0.000 °C | 354.3 ksi @Temperature 32.0 °F | DAM; ISO 527 | |||
| 2.70 GPa @Temperature 23.0 °C | 392 ksi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| 2.795 GPa @Temperature -40.0 °C | 405.4 ksi @Temperature -40.0 °F | DAM; ISO 527 | |||
| 3.171 GPa @Temperature -40.0 °C | 459.9 ksi @Temperature -40.0 °F | 50%RH; ISO 527 | |||
| Flexural Modulus | 1.063 GPa @Temperature 23.0 °C | 154.2 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 1.075 GPa @Temperature 23.0 °C | 155.9 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | |||
| 2.20 GPa @Temperature 23.0 °C | 319 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 1.33 J/cm @Temperature 23.0 °C | 2.49 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -40.0 °C | 5.23 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 13.0 kJ/m² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 13.0 kJ/m² @Temperature -20.0 °C | 6.19 ft-lb/in² @Temperature -4.00 °F | DAM; ISO 180/1A | |||
| 17.0 kJ/m² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 9.70e+11 ohm-cm @Temperature 23.0 °C | 9.70e+11 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 2.00e+15 ohm-cm @Temperature 23.0 °C | 2.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 4.70e+11 ohm @Temperature 23.0 °C | 4.70e+11 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 3.00e+15 ohm @Temperature 23.0 °C | 3.00e+15 ohm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 3.9 @Frequency 100 Hz, Temperature 23.0 °C | 3.9 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 4.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 9.8 @Frequency 100 Hz, Temperature 23.0 °C | 9.8 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C | 559 kV/in @Thickness 0.0787 in, Temperature 73.4 °F | 50%RH; IEC 60243-1 | ||
| 25.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C | 635 kV/in @Thickness 0.0787 in, Temperature 73.4 °F | DAM; IEC 60243-1 | |||
| Dissipation Factor | 0.0060 @Frequency 100 Hz, Temperature 23.0 °C | 0.0060 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.013 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.013 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 0.435 @Frequency 100 Hz, Temperature 23.0 °C | 0.435 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 0.51 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.51 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 525 V @Temperature 23.0 °C | 525 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| 600 V @Thickness 3.00 mm, Temperature 23.0 °C | 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -30.0 - 30.0 °C | 278 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -30.0 - 30.0 °C | 278 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.6 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | ||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 100 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.6 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 140 µm/m-°C @Temperature 55.0 - 160 °C | 77.8 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 140 µm/m-°C @Temperature 55.0 - 160 °C | 77.8 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 260 °C | 500 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 187 °C | 369 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | DAM; UL 746B | ||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 95.0 °C @Thickness 0.800 mm | 203 °F @Thickness 0.0315 in | DAM; UL 746B | ||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | DAM; Optimum | |||
| 270 - 300 °C | 518 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Impact Modifier | DAM | ||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Resistance, Good | DAM | ||||
| Oil Resistant | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Toughness, Good | DAM | ||||
| UV Resistance, Good | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-I< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Toughened Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| UV Resistant/Weatherable Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-I | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||
| Sporting Goods | DAM | ||||