DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66 物性表: DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.6
  • 弯曲模量 [MPa]: 9.41
 
Physical PropertiesMetricEnglishComments
Density 1.60 g/cc0.0578 lb/in³DAM; ISO 1183
Filler Content 25 %25 %DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 158 MPa
@Temperature 23.0 °C		22900 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  4.42 MPa
@Strain 0.100 %,
Temperature 150 °C		641 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.20 MPa
@Strain 0.100 %,
Temperature 100 °C		754 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.40 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1220 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 9.76 MPa
@Strain 0.200 %,
Temperature 150 °C		1420 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.16 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1474 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.97 MPa
@Strain 0.200 %,
Temperature 100 °C		1591 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.75 MPa
@Strain 0.300 %,
Temperature 150 °C		2284 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.7 MPa
@Strain 0.300 %,
Temperature 100 °C		2420 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.47 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2534 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 19.44 MPa
@Strain 0.400 %,
Temperature 150 °C		2820 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.52 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2976 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 21.95 MPa
@Strain 0.400 %,
Temperature 100 °C		3184 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.92 MPa
@Strain 0.500 %,
Temperature 150 °C		3469 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.09 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3929 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 27.47 MPa
@Strain 0.500 %,
Temperature 100 °C		3984 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.22 MPa
@Strain 0.600 %,
Temperature 150 °C		4093 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.98 MPa
@Strain 0.300 %,
Temperature -40.0 °C		4493 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.04 MPa
@Strain 0.700 %,
Temperature 150 °C		4647 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.21 MPa
@Strain 0.600 %,
Temperature 100 °C		4672 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.38 MPa
@Strain 0.800 %,
Temperature 150 °C		5131 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.44 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5285 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 36.93 MPa
@Strain 0.700 %,
Temperature 100 °C		5356 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.48 MPa
@Strain 0.900 %,
Temperature 150 °C		5581 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.75 MPa
@Strain 0.400 %,
Temperature -40.0 °C		5910 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 0.800 %,
Temperature 100 °C		5960 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.33 MPa
@Strain 1.00 %,
Temperature 150 °C		5994 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.05 MPa
@Strain 1.10 %,
Temperature 150 °C		6389 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.99 MPa
@Strain 0.900 %,
Temperature 100 °C		6525 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 47.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6820 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 48.87 MPa
@Strain 1.00 %,
Temperature 100 °C		7088 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.01 MPa
@Strain 1.30 %,
Temperature 150 °C		7108 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 50.95 MPa
@Strain 1.40 %,
Temperature 150 °C		7390 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 52.33 MPa
@Strain 0.500 %,
Temperature -40.0 °C		7590 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 52.33 MPa
@Strain 1.10 %,
Temperature 100 °C		7590 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.67 MPa
@Strain 1.50 %,
Temperature 150 °C		7639 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 54.57 MPa
@Strain 1.60 %,
Temperature 150 °C		7915 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 55.69 MPa
@Strain 1.20 %,
Temperature 100 °C		8077 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.86 MPa
@Strain 1.70 %,
Temperature 150 °C		8102 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 57.43 MPa
@Strain 1.80 %,
Temperature 150 °C		8330 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.4 MPa
@Strain 0.600 %,
Temperature 23.0 °C		8470 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.8 MPa
@Strain 1.90 %,
Temperature 150 °C		8530 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 59.03 MPa
@Strain 1.30 %,
Temperature 100 °C		8562 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.09 MPa
@Strain 2.00 %,
Temperature 150 °C		8715 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.13 MPa
@Strain 2.10 %,
Temperature 150 °C		8866 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.91 MPa
@Strain 1.40 %,
Temperature 100 °C		8979 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 62.1 MPa
@Strain 2.20 %,
Temperature 150 °C		9010 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.87 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9119 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.12 MPa
@Strain 2.30 %,
Temperature 150 °C		9155 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.81 MPa
@Strain 2.40 %,
Temperature 150 °C		9255 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.58 MPa
@Strain 1.50 %,
Temperature 100 °C		9367 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 64.75 MPa
@Strain 2.50 %,
Temperature 150 °C		9391 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.42 MPa
@Strain 2.60 %,
Temperature 150 °C		9488 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.96 MPa
@Strain 2.70 %,
Temperature 150 °C		9567 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.65 MPa
@Strain 2.80 %,
Temperature 150 °C		9667 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.96 MPa
@Strain 1.60 %,
Temperature 100 °C		9712 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 66.99 MPa
@Strain 2.90 %,
Temperature 150 °C		9716 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.46 MPa
@Strain 3.00 %,
Temperature 150 °C		9784 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.95 MPa
@Strain 3.10 %,
Temperature 150 °C		9855 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.0 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9860 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.15 MPa
@Strain 3.20 %,
Temperature 150 °C		9884 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.55 MPa
@Strain 3.30 %,
Temperature 150 °C		9942 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.86 MPa
@Strain 3.40 %,
Temperature 150 °C		9987 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.96 MPa
@Strain 3.50 %,
Temperature 150 °C		10000 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.28 MPa
@Strain 3.60 %,
Temperature 150 °C		10050 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.35 MPa
@Strain 1.70 %,
Temperature 100 °C		10060 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 69.48 MPa
@Strain 3.70 %,
Temperature 150 °C		10080 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.52 MPa
@Strain 3.80 %,
Temperature 150 °C		10080 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.77 MPa
@Strain 3.90 %,
Temperature 150 °C		10120 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.81 MPa
@Strain 4.10 %,
Temperature 150 °C		10130 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.82 MPa
@Strain 4.70 %,
Temperature 150 °C		10130 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.85 MPa
@Strain 4.00 %,
Temperature 150 °C		10130 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.93 MPa
@Strain 4.40 %,
Temperature 150 °C		10140 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.95 MPa
@Strain 4.20 %,
Temperature 150 °C		10150 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.99 MPa
@Strain 4.50 %,
Temperature 150 °C		10150 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 70.01 MPa
@Strain 4.60 %,
Temperature 150 °C		10150 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 70.03 MPa
@Strain 4.30 %,
Temperature 150 °C		10160 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 71.47 MPa
@Strain 1.80 %,
Temperature 100 °C		10370 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.68 MPa
@Strain 1.90 %,
Temperature 100 °C		10690 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.97 MPa
@Strain 0.700 %,
Temperature -40.0 °C		10730 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.61 MPa
@Strain 2.00 %,
Temperature 100 °C		10970 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 77.48 MPa
@Strain 0.800 %,
Temperature 23.0 °C		11240 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.5 MPa
@Strain 2.10 %,
Temperature 100 °C		11200 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.12 MPa
@Strain 2.20 %,
Temperature 100 °C		11480 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 80.69 MPa
@Strain 2.30 %,
Temperature 100 °C		11700 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.08 MPa
@Strain 2.40 %,
Temperature 100 °C		11900 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 83.41 MPa
@Strain 2.50 %,
Temperature 100 °C		12100 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 84.45 MPa
@Strain 2.60 %,
Temperature 100 °C		12250 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 84.68 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12280 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 85.56 MPa
@Strain 2.70 %,
Temperature 100 °C		12410 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.3 MPa
@Strain 2.80 %,
Temperature 100 °C		12500 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 86.73 MPa
@Strain 0.900 %,
Temperature 23.0 °C		12580 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 87.14 MPa
@Strain 2.90 %,
Temperature 100 °C		12640 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.79 MPa
@Strain 3.00 %,
Temperature 100 °C		12730 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 88.25 MPa
@Strain 3.10 %,
Temperature 100 °C		12800 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 88.81 MPa
@Strain 3.20 %,
Temperature 100 °C		12880 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.05 MPa
@Strain 3.30 %,
Temperature 100 °C		12920 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.3 MPa
@Strain 3.40 %,
Temperature 100 °C		13000 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.63 MPa
@Strain 3.50 %,
Temperature 100 °C		13000 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.67 MPa
@Strain 4.00 %,
Temperature 100 °C		13010 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.68 MPa
@Strain 3.60 %,
Temperature 100 °C		13010 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.74 MPa
@Strain 3.70 %,
Temperature 100 °C		13020 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.85 MPa
@Strain 3.90 %,
Temperature 100 °C		13030 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 89.92 MPa
@Strain 3.80 %,
Temperature 100 °C		13040 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 95.4 MPa
@Strain 0.900 %,
Temperature -40.0 °C		13800 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.42 MPa
@Strain 1.00 %,
Temperature 23.0 °C		13840 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.73 MPa
@Strain 1.10 %,
Temperature 23.0 °C		15045 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 105.72 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15333 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.45 MPa
@Strain 1.20 %,
Temperature 23.0 °C		16164 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 115.63 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16771 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.37 MPa
@Strain 1.30 %,
Temperature 23.0 °C		17168 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 124.87 MPa
@Strain 1.40 %,
Temperature 23.0 °C		18111 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.3 MPa
@Strain 1.20 %,
Temperature -40.0 °C		18170 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 130.77 MPa
@Strain 1.50 %,
Temperature 23.0 °C		18967 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 134.05 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19442 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 136.15 MPa
@Strain 1.60 %,
Temperature 23.0 °C		19747 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 140.98 MPa
@Strain 1.70 %,
Temperature 23.0 °C		20447 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 142.58 MPa
@Strain 1.40 %,
Temperature -40.0 °C		20680 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 145.2 MPa
@Strain 1.80 %,
Temperature 23.0 °C		21060 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 150.63 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21847 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 158.53 MPa
@Strain 1.60 %,
Temperature -40.0 °C		22993 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 165.44 MPa
@Strain 1.70 %,
Temperature -40.0 °C		23995 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 171.84 MPa
@Strain 1.80 %,
Temperature -40.0 °C		24923 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 178.11 MPa
@Strain 1.90 %,
Temperature -40.0 °C		25833 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 183.63 MPa
@Strain 2.00 %,
Temperature -40.0 °C		26633 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 187.59 MPa
@Strain 2.10 %,
Temperature -40.0 °C		27208 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break 2.1 %
@Temperature 23.0 °C		2.1 %
@Temperature 73.4 °F		DAM; ISO 527
Tensile Modulus 10.64 GPa
@Temperature 23.0 °C		1543 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 9.41 GPa
@Temperature 23.0 °C		1360 ksi
@Temperature 73.4 °F		DAM; ISO 178
Charpy Impact, Notched  0.790 J/cm²
@Temperature -40.0 °C		3.76 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.840 J/cm²
@Temperature 23.0 °C		4.00 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 250 - 400 V
@Temperature 23.0 °C		250 - 400 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 242 °C468 °FDAM; ISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		DAM; UL 746B
UL RTI, Mechanical with Impact  105 °C
@Thickness 0.750 mm		221 °F
@Thickness 0.0295 in		DAM; UL 746B
 115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		DAM; UL 746B
 115 °C
@Thickness 3.00 mm		239 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  105 °C
@Thickness 0.750 mm		221 °F
@Thickness 0.0295 in		DAM; UL 746B
 115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  V-0
@Thickness 0.350 mm		V-0
@Thickness 0.0138 in		DAM; IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		DAM; UL94
 V-0
@Thickness 0.350 mm		V-0
@Thickness 0.0138 in		DAM; UL94
 5VA
@Thickness 1.50 mm		5VA
@Thickness 0.0591 in		DAM; IEC 60695-11-20
 5VA
@Thickness 1.50 mm		5VA
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 5VA
@Thickness 3.00 mm		5VA
@Thickness 0.118 in		DAM; IEC 60695-11-10
 5VA
@Thickness 3.00 mm		5VA
@Thickness 0.118 in		DAM; UL94
 5VA
@Thickness 1.50 mm		5VA
@Thickness 0.0591 in		DAM; UL94
Glow Wire Test  900 °C
@Thickness 1.50 mm		1650 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 900 °C
@Thickness 0.750 mm		1650 °F
@Thickness 0.0295 in		DAM; Ignition; IEC 60695-2-13
 930 °C
@Thickness 3.00 mm		1710 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 960 °C
@Thickness 0.750 mm		1760 °F
@Thickness 0.0295 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 260 °C500 °FDAM; ISO 11357-1/-3
 280 °C536 °FDAM; Optimum
 270 - 290 °C518 - 554 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceBlack ColorDAM
FeaturesFlame RetardantDAM
 Flame RetardantDAM
FillerGlass ReinforcedDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF25FR(17)<ISO 11469; DAM
Processing MethodInjection MoldingDAM
Product CategoryFlame Retardant ResinsDAM
 Glass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF25FR(17)ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesConnectorsDAM
 ConnectorsDAM
 Electrical PartsDAM
 Electrical PartsDAM
 Electrical/Electronic ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Housing, ElectricalDAM
 Housing, ElectricalDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45521.html

免责声明: 本文 DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4