- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 20.0
- 弯曲模量 [MPa]: 1.05
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa @Temperature 23.0 °C | 5800 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 125 % @Temperature 23.0 °C | 125 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 150 % @Temperature 23.0 °C | 150 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Modulus | 1.05 GPa @Temperature 23.0 °C | 152 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 1.05 GPa @Temperature 23.0 °C | 152 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -40.0 °C | 9.52 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 35.0 kJ/m² @Temperature -20.0 °C | 16.7 ft-lb/in² @Temperature -4.00 °F | DAM; ISO 180/1A | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -40.0 °C | 9.52 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | DAM; Optimum; Injection Molding | |||
| 275 - 295 °C | 527 - 563 °F | DAM; Injection Molding | |||
| Mold Temperature | 60.0 °C | 140 °F | DAM; optimum; Injection Molding | ||
| 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM; Injection Molding | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-F< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-F | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||