- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.07
- 缺口冲击强度: 18.0
- 拉伸强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 1.80
- 热变形温度 [℃]: 162.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.07 % @Temperature 23.0 °C | 1.07 % @Temperature 73.4 °F | DAM; Immersion 24h; ISO 62, Similar to | ||
| Linear Mold Shrinkage, Flow | 0.022 cm/cm @Thickness 2.00 mm | 0.022 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm @Thickness 2.00 mm | 0.020 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 45.0 MPa @Temperature 23.0 °C | 6530 psi @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | ||
| Tensile Stress | 41.0 MPa @Strain 50.0 %, Temperature 23.0 °C | 5950 psi @Strain 50.0 %, Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 50.0 MPa @Strain 50.0 %, Temperature 23.0 °C | 7250 psi @Strain 50.0 %, Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength, Yield | 47.0 MPa @Temperature 23.0 °C | 6820 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 48 % @Temperature 23.0 °C | 48 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 75 % @Temperature 23.0 °C | 75 % @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | |||
| Elongation at Yield | 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 1.237 GPa @Temperature 23.0 °C | 179.4 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 1.90 GPa @Temperature 23.0 °C | 276 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C | 261 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -40.0 °C | 8.57 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 76.0 kJ/m² @Temperature 23.0 °C | 36.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -40.0 °C | 9.04 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 7.90 J/cm² @Temperature 23.0 °C | 37.6 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.40e+12 ohm-cm @Temperature 23.0 °C | 7.40e+12 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 2.00e+16 ohm-cm @Temperature 23.0 °C | 2.00e+16 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 3.00e+12 ohm @Temperature 23.0 °C | 3.00e+12 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 2.40e+16 ohm @Temperature 23.0 °C | 2.40e+16 ohm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 3.9 @Frequency 100 Hz, Temperature 23.0 °C | 3.9 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 4.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 6.7 @Frequency 100 Hz, Temperature 23.0 °C | 6.7 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dielectric Strength | 22.0 kV/mm @Temperature 23.0 °C | 559 kV/in @Temperature 73.4 °F | 50%RH; IEC 60243-1 | ||
| 25.0 kV/mm @Temperature 23.0 °C | 635 kV/in @Temperature 73.4 °F | DAM; IEC 60243-1 | |||
| Dissipation Factor | 0.0060 @Frequency 100 Hz, Temperature 23.0 °C | 0.0060 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.012 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.012 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 0.044 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.044 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 0.159 @Frequency 100 Hz, Temperature 23.0 °C | 0.159 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature -40.0 - 23.0 °C | 61.1 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 110 µm/m-°C @Temperature -40.0 - 23.0 °C | 61.1 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 120 µm/m-°C @Temperature -30.0 - 30.0 °C | 66.7 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | |||
| 120 µm/m-°C @Temperature -30.0 - 30.0 °C | 66.7 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 150 µm/m-°C @Temperature 55.0 - 160 °C | 83.3 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| 150 µm/m-°C @Temperature 55.0 - 160 °C | 83.3 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 150 µm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 150 µm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 110 µm/m-°C @Temperature -30.0 - 30.0 °C | 61.1 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | |||
| 110 µm/m-°C @Temperature -30.0 - 30.0 °C | 61.1 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 130 µm/m-°C @Temperature 55.0 - 160 °C | 72.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 130 µm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 130 µm/m-°C @Temperature 55.0 - 160 °C | 72.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| 130 µm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 125 °C @Thickness 0.750 mm | 257 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.750 mm | 185 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | DAM | ||
| 290 °C | 554 °F | DAM; optimum | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Impact Modifier | ||||
| UV Stabilizer | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | ||||
| Features | Chemical Resistance, Good | ||||
| Fuel Resistant | |||||
| Grease Resistant | |||||
| Impact Modified | |||||
| Impact Resistance, High | |||||
| Oil Resistant | |||||
| Toughness, Low Temperature | |||||
| Toughness, Ultra High | |||||
| UV Resistance, Good | |||||
| Forms | Pellets | ||||
| Generic | Nylon 66 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA66-HI< | ISO 11469 | |||
| Polymer Family | Polyamide | ||||
| Polymer Type | PA66 | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Toughened Resins | ||||
| Unreinforced Resins | |||||
| UV Resistant/Weatherable Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA66-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Ultrasonic Weldable | Yes | ||||
| Uses | Appliance Components | ||||
| Automotive Applications | |||||
| Electrical/Electronic Applications | |||||
| Industrial Applications | |||||
| Sporting Goods | |||||