- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.6
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 1.07
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.20 mm | 0.015 in/in @Thickness 0.126 in | Flow; DAM | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.4 % @Temperature 23.0 °C | 4.4 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 27 % @Temperature 23.0 °C | 27 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.30 GPa @Temperature 23.0 °C | 189 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.07 GPa @Temperature 23.0 °C | 155 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 23.0 kJ/m² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 180/1U | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 180/1U | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1U | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 180/1U | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |||
| 280 - 290 °C | 536 - 554 °F | DAM; Extrusion | |||
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |||
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Features | Food Contact Acceptable | DAM | |||
| Viscosity, High | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Food Contact Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Food Applications, Non-specific | DAM | |||