  4. DuPont Performance Polymers Zytel® E42A NC010 Nylon 66

DuPont Performance Polymers Zytel® E42A NC010 Nylon 66

DuPont Performance Polymers Zytel® E42A NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® E42A NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® E42A NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® E42A NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 2.7
  • 缺口冲击强度: 4.0
  • 拉伸强度 [MPa]: 52.0
  • 热变形温度 [℃]: 205.0
 
Physical PropertiesMetricEnglishComments
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  2.7 %
@Temperature 23.0 °C		2.7 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Viscosity  109000 cP
@Shear Rate 7000 1/s,
Temperature 305 °C		109000 cP
@Shear Rate 7000 1/s,
Temperature 581 °F		DAM; ISO 11443
 119000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		119000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		DAM; ISO 11443
 136000 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		136000 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		DAM; ISO 11443
 144000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		144000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		DAM; ISO 11443
 150000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		150000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		DAM; ISO 11443
 182000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		182000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		DAM; ISO 11443
 243000 cP
@Shear Rate 2000 1/s,
Temperature 305 °C		243000 cP
@Shear Rate 2000 1/s,
Temperature 581 °F		DAM; ISO 11443
 274000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		274000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		DAM; ISO 11443
 342000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		342000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		DAM; ISO 11443
 360000 cP
@Shear Rate 1000 1/s,
Temperature 305 °C		360000 cP
@Shear Rate 1000 1/s,
Temperature 581 °F		DAM; ISO 11443
 413000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		413000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		DAM; ISO 11443
 431000 cP
@Shear Rate 700 1/s,
Temperature 305 °C		431000 cP
@Shear Rate 700 1/s,
Temperature 581 °F		DAM; ISO 11443
 501000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		501000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		DAM; ISO 11443
 504000 cP
@Shear Rate 500 1/s,
Temperature 305 °C		504000 cP
@Shear Rate 500 1/s,
Temperature 581 °F		DAM; ISO 11443
 535000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		535000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		DAM; ISO 11443
 593000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		593000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		DAM; ISO 11443
 664000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		664000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		DAM; ISO 11443
 806000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		806000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		DAM; ISO 11443
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Stress  13.4 MPa
@Strain 3.00 %,
Temperature 90.0 °C		1940 psi
@Strain 3.00 %,
Temperature 194 °F		50%RH; ISO 527
 14.5 MPa
@Strain 5.00 %,
Temperature 120 °C		2100 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 527
 15.9 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2310 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 527
 17.6 MPa
@Strain 5.00 %,
Temperature 120 °C		2550 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 527
 19.7 MPa
@Strain 3.00 %,
Temperature 40.0 °C		2860 psi
@Strain 3.00 %,
Temperature 104 °F		50%RH; ISO 527
 20.9 MPa
@Strain 10.0 %,
Temperature 120 °C		3030 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 527
 21.1 MPa
@Strain 6.00 %,
Temperature 90.0 °C		3060 psi
@Strain 6.00 %,
Temperature 194 °F		50%RH; ISO 527
 21.8 MPa
@Strain 5.00 %,
Temperature 90.0 °C		3160 psi
@Strain 5.00 %,
Temperature 194 °F		DAM; ISO 527
 22.4 MPa
@Strain 0.800 %,
Temperature 40.0 °C		3250 psi
@Strain 0.800 %,
Temperature 104 °F		DAM; ISO 527
 23.5 MPa
@Strain 10.0 %,
Temperature 120 °C		3410 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 527
 24.2 MPa
@Strain 15.0 %,
Temperature 120 °C		3510 psi
@Strain 15.0 %,
Temperature 248 °F		50%RH; ISO 527
 24.8 MPa
@Strain 6.00 %,
Temperature 60.0 °C		3600 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 527
 24.9 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3610 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 527
 25.8 MPa
@Strain 9.00 %,
Temperature 90.0 °C		3740 psi
@Strain 9.00 %,
Temperature 194 °F		50%RH; ISO 527
 26.1 MPa
@Strain 20.0 %,
Temperature 120 °C		3790 psi
@Strain 20.0 %,
Temperature 248 °F		50%RH; ISO 527
 26.3 MPa
@Strain 15.0 %,
Temperature 120 °C		3810 psi
@Strain 15.0 %,
Temperature 248 °F		DAM; ISO 527
 27.2 MPa
@Strain 25.0 %,
Temperature 120 °C		3950 psi
@Strain 25.0 %,
Temperature 248 °F		50%RH; ISO 527
 27.2 MPa
@Strain 3.00 %,
Temperature 60.0 °C		3950 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 527
 27.9 MPa
@Strain 30.0 %,
Temperature 120 °C		4050 psi
@Strain 30.0 %,
Temperature 248 °F		50%RH; ISO 527
 27.9 MPa
@Strain 20.0 %,
Temperature 120 °C		4050 psi
@Strain 20.0 %,
Temperature 248 °F		DAM; ISO 527
 28.2 MPa
@Strain 35.0 %,
Temperature 120 °C		4090 psi
@Strain 35.0 %,
Temperature 248 °F		50%RH; ISO 527
 28.3 MPa
@Strain 40.0 %,
Temperature 120 °C		4100 psi
@Strain 40.0 %,
Temperature 248 °F		50%RH; ISO 527
 28.4 MPa
@Strain 45.0 %,
Temperature 120 °C		4120 psi
@Strain 45.0 %,
Temperature 248 °F		50%RH; ISO 527
 28.5 MPa
@Strain 50.0 %,
Temperature 120 °C		4130 psi
@Strain 50.0 %,
Temperature 248 °F		50%RH; ISO 527
 28.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		4130 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 28.8 MPa
@Strain 12.0 %,
Temperature 90.0 °C		4180 psi
@Strain 12.0 %,
Temperature 194 °F		50%RH; ISO 527
 28.9 MPa
@Strain 25.0 %,
Temperature 120 °C		4190 psi
@Strain 25.0 %,
Temperature 248 °F		DAM; ISO 527
 29.6 MPa
@Strain 30.0 %,
Temperature 120 °C		4290 psi
@Strain 30.0 %,
Temperature 248 °F		DAM; ISO 527
 29.6 MPa
@Strain 10.0 %,
Temperature 90.0 °C		4290 psi
@Strain 10.0 %,
Temperature 194 °F		DAM; ISO 527
 30.0 MPa
@Strain 35.0 %,
Temperature 120 °C		4350 psi
@Strain 35.0 %,
Temperature 248 °F		DAM; ISO 527
 30.1 MPa
@Strain 6.00 %,
Temperature 40.0 °C		4370 psi
@Strain 6.00 %,
Temperature 104 °F		50%RH; ISO 527
 30.3 MPa
@Strain 9.00 %,
Temperature 60.0 °C		4390 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 527
 30.4 MPa
@Strain 40.0 %,
Temperature 120 °C		4410 psi
@Strain 40.0 %,
Temperature 248 °F		DAM; ISO 527
 30.6 MPa
@Strain 45.0 %,
Temperature 120 °C		4440 psi
@Strain 45.0 %,
Temperature 248 °F		DAM; ISO 527
 30.7 MPa
@Strain 50.0 %,
Temperature 120 °C		4450 psi
@Strain 50.0 %,
Temperature 248 °F		DAM; ISO 527
 30.7 MPa
@Strain 15.0 %,
Temperature 90.0 °C		4450 psi
@Strain 15.0 %,
Temperature 194 °F		50%RH; ISO 527
 31.9 MPa
@Strain 18.0 %,
Temperature 90.0 °C		4630 psi
@Strain 18.0 %,
Temperature 194 °F		50%RH; ISO 527
 32.7 MPa
@Strain 21.0 %,
Temperature 90.0 °C		4740 psi
@Strain 21.0 %,
Temperature 194 °F		50%RH; ISO 527
 33.1 MPa
@Strain 24.0 %,
Temperature 90.0 °C		4800 psi
@Strain 24.0 %,
Temperature 194 °F		50%RH; ISO 527
 33.3 MPa
@Strain 27.0 %,
Temperature 90.0 °C		4830 psi
@Strain 27.0 %,
Temperature 194 °F		50%RH; ISO 527
 33.4 MPa
@Strain 15.0 %,
Temperature 90.0 °C		4840 psi
@Strain 15.0 %,
Temperature 194 °F		DAM; ISO 527
 33.4 MPa
@Strain 30.0 %,
Temperature 90.0 °C		4840 psi
@Strain 30.0 %,
Temperature 194 °F		50%RH; ISO 527
 33.8 MPa
@Strain 12.0 %,
Temperature 60.0 °C		4900 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 527
 35.6 MPa
@Strain 20.0 %,
Temperature 90.0 °C		5160 psi
@Strain 20.0 %,
Temperature 194 °F		DAM; ISO 527
 36.2 MPa
@Strain 15.0 %,
Temperature 60.0 °C		5250 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 527
 36.2 MPa
@Strain 9.00 %,
Temperature 40.0 °C		5250 psi
@Strain 9.00 %,
Temperature 104 °F		50%RH; ISO 527
 36.9 MPa
@Strain 25.0 %,
Temperature 90.0 °C		5350 psi
@Strain 25.0 %,
Temperature 194 °F		DAM; ISO 527
 37.7 MPa
@Strain 30.0 %,
Temperature 90.0 °C		5470 psi
@Strain 30.0 %,
Temperature 194 °F		DAM; ISO 527
 37.7 MPa
@Strain 18.0 %,
Temperature 60.0 °C		5470 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 527
 38.2 MPa
@Strain 35.0 %,
Temperature 90.0 °C		5540 psi
@Strain 35.0 %,
Temperature 194 °F		DAM; ISO 527
 38.4 MPa
@Strain 6.00 %,
Temperature 60.0 °C		5570 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 527
 38.5 MPa
@Strain 40.0 %,
Temperature 90.0 °C		5580 psi
@Strain 40.0 %,
Temperature 194 °F		DAM; ISO 527
 38.6 MPa
@Strain 45.0 %,
Temperature 90.0 °C		5600 psi
@Strain 45.0 %,
Temperature 194 °F		DAM; ISO 527
 38.7 MPa
@Strain 50.0 %,
Temperature 90.0 °C		5610 psi
@Strain 50.0 %,
Temperature 194 °F		DAM; ISO 527
 38.7 MPa
@Strain 21.0 %,
Temperature 60.0 °C		5610 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 527
 39.4 MPa
@Strain 24.0 %,
Temperature 60.0 °C		5710 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 527
 39.5 MPa
@Strain 1.20 %,
Temperature 0.000 °C		5730 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 527
 39.8 MPa
@Strain 27.0 %,
Temperature 60.0 °C		5770 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 527
 40.0 MPa
@Strain 30.0 %,
Temperature 60.0 °C		5800 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 527
 40.1 MPa
@Strain 12.0 %,
Temperature 40.0 °C		5820 psi
@Strain 12.0 %,
Temperature 104 °F		50%RH; ISO 527
 41.3 MPa
@Strain 6.00 %,
Temperature 23.0 °C		5990 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 41.6 MPa
@Strain 1.60 %,
Temperature 40.0 °C		6030 psi
@Strain 1.60 %,
Temperature 104 °F		DAM; ISO 527
 42.6 MPa
@Strain 15.0 %,
Temperature 40.0 °C		6180 psi
@Strain 15.0 %,
Temperature 104 °F		50%RH; ISO 527
 43.7 MPa
@Strain 1.20 %,
Temperature -20.0 °C		6340 psi
@Strain 1.20 %,
Temperature -4.00 °F		DAM; ISO 527
 44.2 MPa
@Strain 9.00 %,
Temperature 60.0 °C		6410 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 527
 44.4 MPa
@Strain 18.0 %,
Temperature 40.0 °C		6440 psi
@Strain 18.0 %,
Temperature 104 °F		50%RH; ISO 527
 45.5 MPa
@Strain 21.0 %,
Temperature 40.0 °C		6600 psi
@Strain 21.0 %,
Temperature 104 °F		50%RH; ISO 527
 46.3 MPa
@Strain 24.0 %,
Temperature 40.0 °C		6720 psi
@Strain 24.0 %,
Temperature 104 °F		50%RH; ISO 527
 46.7 MPa
@Strain 27.0 %,
Temperature 40.0 °C		6770 psi
@Strain 27.0 %,
Temperature 104 °F		50%RH; ISO 527
 47.0 MPa
@Strain 30.0 %,
Temperature 40.0 °C		6820 psi
@Strain 30.0 %,
Temperature 104 °F		50%RH; ISO 527
 47.6 MPa
@Strain 12.0 %,
Temperature 60.0 °C		6900 psi
@Strain 12.0 %,
Temperature 140 °F		DAM; ISO 527
 48.2 MPa
@Strain 9.00 %,
Temperature 23.0 °C		6990 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 527
 48.5 MPa
@Strain 1.60 %,
Temperature 23.0 °C		7030 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 527
 49.7 MPa
@Strain 15.0 %,
Temperature 60.0 °C		7210 psi
@Strain 15.0 %,
Temperature 140 °F		DAM; ISO 527
 51.0 MPa
@Strain 18.0 %,
Temperature 60.0 °C		7400 psi
@Strain 18.0 %,
Temperature 140 °F		DAM; ISO 527
 51.8 MPa
@Strain 21.0 %,
Temperature 60.0 °C		7510 psi
@Strain 21.0 %,
Temperature 140 °F		DAM; ISO 527
 52.2 MPa
@Strain 24.0 %,
Temperature 60.0 °C		7570 psi
@Strain 24.0 %,
Temperature 140 °F		DAM; ISO 527
 52.2 MPa
@Strain 12.0 %,
Temperature 23.0 °C		7570 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 52.4 MPa
@Strain 30.0 %,
Temperature 60.0 °C		7600 psi
@Strain 30.0 %,
Temperature 140 °F		DAM; ISO 527
 52.4 MPa
@Strain 27.0 %,
Temperature 60.0 °C		7600 psi
@Strain 27.0 %,
Temperature 140 °F		DAM; ISO 527
 54.6 MPa
@Strain 15.0 %,
Temperature 23.0 °C		7920 psi
@Strain 15.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 54.9 MPa
@Strain 2.40 %,
Temperature 40.0 °C		7960 psi
@Strain 2.40 %,
Temperature 104 °F		DAM; ISO 527
 56.1 MPa
@Strain 18.0 %,
Temperature 23.0 °C		8140 psi
@Strain 18.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 57.0 MPa
@Strain 21.0 %,
Temperature 23.0 °C		8270 psi
@Strain 21.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 57.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		8270 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 527
 57.5 MPa
@Strain 24.0 %,
Temperature 23.0 °C		8340 psi
@Strain 24.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 57.7 MPa
@Strain 27.0 %,
Temperature 23.0 °C		8370 psi
@Strain 27.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 57.9 MPa
@Strain 30.0 %,
Temperature 23.0 °C		8400 psi
@Strain 30.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 58.9 MPa
@Strain 1.60 %,
Temperature -20.0 °C		8540 psi
@Strain 1.60 %,
Temperature -4.00 °F		50%RH; ISO 527
 63.0 MPa
@Strain 3.20 %,
Temperature 40.0 °C		9140 psi
@Strain 3.20 %,
Temperature 104 °F		DAM; ISO 527
 67.1 MPa
@Strain 4.00 %,
Temperature 40.0 °C		9730 psi
@Strain 4.00 %,
Temperature 104 °F		DAM; ISO 527
 67.5 MPa
@Strain 2.40 %,
Temperature 23.0 °C		9790 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 527
 71.9 MPa
@Strain 2.40 %,
Temperature 0.000 °C		10400 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 527
 72.0 MPa
@Strain 4.00 %,
Temperature 0.000 °C		10400 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 527
 75.8 MPa
@Strain 6.00 %,
Temperature 0.000 °C		11000 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 527
 75.8 MPa
@Strain 2.40 %,
Temperature -20.0 °C		11000 psi
@Strain 2.40 %,
Temperature -4.00 °F		DAM; ISO 527
 78.0 MPa
@Strain 8.00 %,
Temperature 0.000 °C		11300 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 527
 79.3 MPa
@Strain 10.0 %,
Temperature 0.000 °C		11500 psi
@Strain 10.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 80.0 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11600 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 527
 80.1 MPa
@Strain 12.0 %,
Temperature 0.000 °C		11600 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 80.6 MPa
@Strain 14.0 %,
Temperature 0.000 °C		11700 psi
@Strain 14.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 80.9 MPa
@Strain 16.0 %,
Temperature 0.000 °C		11700 psi
@Strain 16.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 81.1 MPa
@Strain 18.0 %,
Temperature 0.000 °C		11800 psi
@Strain 18.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 81.2 MPa
@Strain 20.0 %,
Temperature 0.000 °C		11800 psi
@Strain 20.0 %,
Temperature 32.0 °F		50%RH; ISO 527
 86.5 MPa
@Strain 4.00 %,
Temperature 23.0 °C		12500 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 527
 89.1 MPa
@Strain 3.20 %,
Temperature -20.0 °C		12900 psi
@Strain 3.20 %,
Temperature -4.00 °F		50%RH; ISO 527
 91.6 MPa
@Strain 3.60 %,
Temperature 0.000 °C		13300 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 527
 96.5 MPa
@Strain 3.60 %,
Temperature -20.0 °C		14000 psi
@Strain 3.60 %,
Temperature -4.00 °F		DAM; ISO 527
 98.1 MPa
@Strain 4.80 %,
Temperature -20.0 °C		14200 psi
@Strain 4.80 %,
Temperature -4.00 °F		50%RH; ISO 527
 100 MPa
@Strain 6.40 %,
Temperature -20.0 °C		14500 psi
@Strain 6.40 %,
Temperature -4.00 °F		50%RH; ISO 527
 100 MPa
@Strain 4.80 %,
Temperature 0.000 °C		14500 psi
@Strain 4.80 %,
Temperature 32.0 °F		DAM; ISO 527
 100 MPa
@Strain 6.00 %,
Temperature 0.000 °C		14500 psi
@Strain 6.00 %,
Temperature 32.0 °F		DAM; ISO 527
 101 MPa
@Strain 8.00 %,
Temperature -20.0 °C		14600 psi
@Strain 8.00 %,
Temperature -4.00 °F		50%RH; ISO 527
 108 MPa
@Strain 4.80 %,
Temperature -20.0 °C		15700 psi
@Strain 4.80 %,
Temperature -4.00 °F		DAM; ISO 527
 113 MPa
@Strain 6.00 %,
Temperature -20.0 °C		16400 psi
@Strain 6.00 %,
Temperature -4.00 °F		DAM; ISO 527
Tensile Strength, Yield  52.0 MPa
@Temperature 23.0 °C		7540 psi
@Temperature 73.4 °F		50%RH; ISO 527
 86.0 MPa
@Temperature 23.0 °C		12500 psi
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Break  >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
Elongation at Yield  5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		DAM; ISO 527
 27 %
@Temperature 23.0 °C		27 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  1.20 GPa
@Temperature 23.0 °C		174 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Shear Modulus  0.0400 GPa
@Temperature 250 °C		5.80 ksi
@Temperature 482 °F		DAM; ISO 6721
 0.0630 GPa
@Temperature 240 °C		9.14 ksi
@Temperature 464 °F		DAM; ISO 6721
 0.0830 GPa
@Temperature 230 °C		12.0 ksi
@Temperature 446 °F		DAM; ISO 6721
 0.0980 GPa
@Temperature 220 °C		14.2 ksi
@Temperature 428 °F		DAM; ISO 6721
 0.107 GPa
@Temperature 210 °C		15.5 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.114 GPa
@Temperature 200 °C		16.5 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.120 GPa
@Temperature 190 °C		17.4 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.125 GPa
@Temperature 180 °C		18.1 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.130 GPa
@Temperature 170 °C		18.9 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.135 GPa
@Temperature 160 °C		19.6 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.139 GPa
@Temperature 150 °C		20.2 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.144 GPa
@Temperature 140 °C		20.9 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.148 GPa
@Temperature 130 °C		21.5 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.153 GPa
@Temperature 120 °C		22.2 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.159 GPa
@Temperature 110 °C		23.1 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.171 GPa
@Temperature 100 °C		24.8 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.191 GPa
@Temperature 90.0 °C		27.7 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.233 GPa
@Temperature 80.0 °C		33.8 ksi
@Temperature 176 °F		DAM; ISO 6721
 0.322 GPa
@Temperature 70.0 °C		46.7 ksi
@Temperature 158 °F		DAM; ISO 6721
 0.431 GPa
@Temperature 60.0 °C		62.5 ksi
@Temperature 140 °F		DAM; ISO 6721
 0.667 GPa
@Temperature 50.0 °C		96.7 ksi
@Temperature 122 °F		DAM; ISO 6721
 0.776 GPa
@Temperature 40.0 °C		113 ksi
@Temperature 104 °F		DAM; ISO 6721
 0.834 GPa
@Temperature 30.0 °C		121 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 0.880 GPa
@Temperature 20.0 °C		128 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 0.915 GPa
@Temperature 10.0 °C		133 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 0.938 GPa
@Temperature 0.000 °C		136 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 0.951 GPa
@Temperature -10.0 °C		138 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 0.961 GPa
@Temperature -20.0 °C		139 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 0.975 GPa
@Temperature -30.0 °C		141 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 0.999 GPa
@Temperature -40.0 °C		145 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 1.04 GPa
@Temperature -50.0 °C		151 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 4.30 kJ/m²
@Temperature -30.0 °C		2.05 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.60 kJ/m²
@Temperature 23.0 °C		2.66 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 11.9 kJ/m²
@Temperature 23.0 °C		5.66 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.500 J/cm²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 2.00 J/cm²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+11 ohm-cm
@Temperature 23.0 °C		1.00e+11 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 4.3
@Frequency 100 Hz,
Temperature 23.0 °C		4.3
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 10.3
@Frequency 100 Hz,
Temperature 23.0 °C		10.3
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dielectric Strength 30.5 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		775 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.015
@Frequency 100 Hz,
Temperature 23.0 °C		0.015
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.024
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.024
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.075
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.075
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 100 µm/m-°C
@Temperature 23.0 - 55.0 °C		55.6 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 205 °C401 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C162 °FDAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.810 mm		HB
@Thickness 0.0319 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 263 °C505 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.050 %<= 0.050 %DAM
 
Descriptive Properties
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA66<ISO 11469; DAM
Processing MethodExtrusionDAM
 Injection MoldingDAM
Product CategoryExtrusion ResinsDAM
 Unreinforced ResinsDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45506.html

免责声明: 本文 DuPont Performance Polymers Zytel® E42A NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4