- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.7
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 82.7
- 弯曲模量 [MPa]: 3.79
- 热变形温度 [℃]: 254.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 5.4 % | 5.4 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 |
| Flexural Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C | 12.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D2133 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Long Term; ASTM UL746B |
| 241 °C | 465 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |