- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.814
- 弯曲模量 [MPa]: 4.1614
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec | 0.50 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 94.176 MPa | 13659 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Flexural Strength | 163.14 MPa | 23661 psi | ASTM D790 |
| Flexural Modulus | 4.1614 GPa | 603.56 ksi | ASTM D790 |
| Izod Impact, Notched | 0.814 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |
| Mold Temperature | 75.0 - 120 °C | 167 - 248 °F | |