- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.77
- 弯曲模量 [MPa]: 2.2563
- 热变形温度 [℃]: 185.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec | 0.40 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 58.86 MPa | 8537 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 95.16 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.2563 GPa | 327.25 ksi | ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm | 3.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |