- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 1.76
- 拉伸强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 11.298
- 硬度: 109.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 170.0 MPa | 24650 psi | ASTM D638 |
| Tensile Strength, Yield | 170.0 MPa | 24650 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 4.599 GPa | 667.1 ksi | ASTM D638 |
| Flexural Strength | 263.0 MPa | 38140 psi | ASTM D790 |
| Flexural Modulus | 11.298 GPa | 1638.7 ksi | ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |