- 密度 [g/cm3]: 1.49
- 断裂伸长率 [%]: 210
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 6.56
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 6.0 % | 6.0 % | Strain at break, ISO, 5 mm/min |
| Tensile Modulus | 7.49 GPa | 1090 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 210 MPa | 30500 psi | ASTM Data |
| Flexural Modulus | 6.56 GPa | 951 ksi | ASTM Data |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |