- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.5
- 断裂伸长率 [%]: 125
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 3.44
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO data |
| Water Absorption | 1.5 % | 1.5 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.9 % | 8.9 % | in water; 23°C; ISO data |
| Viscosity Measurement | 50 | 50 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 4.3 % | 4.3 % | Strain at break, ISO, 5 mm/min |
| 5.0 % | 5.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 125 MPa | 18100 psi | ASTM Data |
| Flexural Modulus | 3.44 GPa | 499 ksi | ISO Value |
| 3.86 GPa | 560 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO Data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 59.0 µm/m-°C @Temperature 20.0 °C | 32.8 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM Data |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |