- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 4.0
- 断裂伸长率 [%]: 215
- 弯曲强度 [MPa]: 157.0
- 弯曲模量 [MPa]: 8.965
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 4.0 % | 4.0 % | in water; 23°C; ISO data |
| Viscosity Measurement | 50 | 50 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 157 MPa | 22800 psi | ISO value at 5mm/min. |
| 160 MPa | 23200 psi | ASTM data at 5 mm/min. | |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 215 MPa | 31200 psi | ASTM Data |
| Flexural Modulus | 8.965 GPa | 1300 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM Data |
| Flammability, UL94 | V-0 @Thickness 0.840 mm | V-0 @Thickness 0.0331 in | |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
| 5VA @Thickness 2.50 mm | 5VA @Thickness 0.0984 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |
| 95.0 °C | 203 °F | See Materials Notes | |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |
| Injection Pressure | 3.45 - 10.3 MPa | 500 - 1500 psi | |