- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.58
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO data |
| Water Absorption | 1.6 % | 1.6 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 9.5 % | 9.5 % | in water; 23°C; ISO data |
| Viscosity Measurement | 64 | 64 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO, 50 mm/min |
| 55 % | 55 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Flexural Modulus | 2.58 GPa | 374 ksi | ISO data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO Data |
| 0.380 J/cm² @Temperature -30.0 °C | 1.81 ft-lb/in² @Temperature -22.0 °F | ISO data | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO Data |
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | |
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 °C | 500 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |