- 密度 [g/cm3]: 1.43
- 拉伸强度 [MPa]: 140.0
- 断裂伸长率 [%]: 195
- 弯曲强度 [MPa]: 138.0
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ISO value at 5mm/min. |
| 140 MPa | 20300 psi | ASTM data at 5 mm/min. | |
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 4.3 % | 4.3 % | Nominal strain at break, ISO, 50 mm/min and strain at break, ISO, 5 mm/min are both 4.3%. |
| 4.5 % | 4.5 % | Strain at break, ASTM, 5 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM Value at 50 mm/min. |
| 4.1 % | 4.1 % | ISO Value at 50 mm/min. | |
| Tensile Modulus | 8.97 GPa | 1300 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 195 MPa | 28300 psi | ASTM Data |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |