- 密度 [g/cm3]: 0.938
- 吸水率 [%]: 8.6
- 拉伸强度 [MPa]: 69.0
- 断裂伸长率 [%]: 95.0
- 弯曲模量 [MPa]: 2.39
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | Melt Density |
| 1.10 g/cc | 0.0397 lb/in³ | ISO data | |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.6 % | 8.6 % | in water; 23°C; ISO data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO value at 50 mm/min. |
| 70.0 MPa | 10200 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO, 50 mm/min |
| 70 % | 70 % | Nominal strain at break, ASTM, 50 mm/min | |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | ASTM Data |
| Flexural Modulus | 2.39 GPa | 347 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 3.89 J/g-°C | 0.930 BTU/lb-°F | Melt value |
| Thermal Conductivity | 0.168 W/m-K | 1.17 BTU-in/hr-ft²-°F | Melt |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM Data |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |