- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 5.8
- 拉伸强度 [MPa]: 75.0
- 断裂伸长率 [%]: 120
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.8 % | 5.8 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO data |
| 0.010 cm/cm | 0.010 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM value at 50 mm/min. |
| 76.0 MPa | 11000 psi | ISO value at 50 mm/min. | |
| Elongation at Break | 17 % | 17 % | Nominal strain at break, ISO, 50 mm/min |
| 20 % | 20 % | Nominal strain at break, ASTM, 50 mm/min | |
| Flexural Yield Strength | 120 MPa | 17400 psi | ASTM Data |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO Value |
| 4.30 GPa | 624 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO Data |
| 0.390 J/cm² @Temperature -30.0 °C | 1.86 ft-lb/in² @Temperature -22.0 °F | ISO data | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |