- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.9
- 断裂伸长率 [%]: 240
- 弯曲强度 [MPa]: 150.0
- 弯曲模量 [MPa]: 7.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO data |
| Water Absorption | 0.90 % | 0.90 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.5 % | 5.5 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
| 152 MPa | 22000 psi | ISO value at 5mm/min. | |
| Elongation at Break | 3.5 % | 3.5 % | Strain at break, ISO, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 240 MPa | 34800 psi | ASTM Data |
| Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO Data |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |