- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 1.2
- 断裂伸长率 [%]: 140
- 弯曲强度 [MPa]: 90.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO data |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.0 % | 7.0 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 5.0 % | 5.0 % | Strain at break, ISO, 5 mm/min |
| 5.0 % | 5.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 4.37 GPa | 634 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 140 MPa | 20300 psi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 1.60 GPa | 232 ksi | calculated |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO data |
| 210 °C | 410 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |