- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.1
- 拉伸强度 [MPa]: 50.0
- 断裂伸长率 [%]: 65.0
- 弯曲模量 [MPa]: 1.40
- 热变形温度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.7 % | 6.7 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ISO data |
| 0.014 cm/cm | 0.014 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 79 | 79 | ASTM Data |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM value at 50 mm/min. |
| 52.0 MPa | 7540 psi | ISO value at 50 mm/min. | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO data, 50 mm/min |
| >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 7.0 % | 7.0 % | ISO Value at 50 mm/min. |
| 7.0 % | 7.0 % | ASTM Value at 50 mm/min. | |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | ASTM Data |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO Value |
| 1.655 GPa | 240.0 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Charpy Impact, Notched | NB | NB | ISO Data |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ISO data |
| Comparative Tracking Index | 600 V | 600 V | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ISO data |
| 53.0 °C | 127 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 °C | 536 °F | See Materials Notes |
| Mold Temperature | 70.0 °C | 158 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |