- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 2.2
- 弯曲强度 [MPa]: 110.0
- 热变形温度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | |
| Water Absorption | 2.2 % | 2.2 % | |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | Humidity Absorption |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min |
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 5500 MPa | 798000 psi | |
| Tensile Creep Modulus, 1000 hours | 3890 MPa | 564000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz | 2.6 @Frequency 100 Hz | |
| 3.4 @Frequency 1e+6 Hz | 3.4 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.023 @Frequency 1e+6 Hz | 0.023 @Frequency 1e+6 Hz | |
| 0.064 @Frequency 100 Hz | 0.064 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Oxygen Index | 21 % | 21 % | |