- 熔体流动速率 [g/10min]: 12.0
- 吸水率 [%]: 3.1
- 热变形温度 [℃]: 166.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 3.1 % | 3.1 % | |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 235 °C | 12 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | |
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature 20.0 °C | 37.8 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature 20.0 °C | 42.2 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||