- 密度 [g/cm3]: 1.26
- 缺口冲击强度: 0.59
- 弯曲强度 [MPa]: 128.0
- 弯曲模量 [MPa]: 6.40
- 硬度: 118.0
- 热变形温度 [℃]: 214.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm | 9.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 271 °C | 500 - 520 °F | Approximate middle barrel temperature range |