- 密度 [g/cm3]: 0.932
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 0.740
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | Melt; ISO 1183 | ||
| 1.13 g/cc | 0.0408 lb/in³ | dry; ISO 1183 | |||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.5 % | 9.5 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM Test | ||
| 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ASTM Test | |||
| 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 2 in/min; ASTM Test | ||
| 36.0 MPa | 5220 psi | 50mm/min; ISO 527 | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ISO Data | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ISO Data | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ASTM Test | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| 2.5 % @Temperature -40.0 °C | 2.5 % @Temperature -40.0 °F | ASTM Test | |||
| 2.5 % @Temperature -40.0 °C | 2.5 % @Temperature -40.0 °F | ISO Data | |||
| Elongation at Yield | 16 % | 16 % | 50mm/min; ISO 527 | ||
| 16 % | 16 % | 2 in/min; ASTM Test | |||
| 35 % @Temperature 80.0 °C | 35 % @Temperature 176 °F | ASTM Test | |||
| 35 % @Temperature 80.0 °C | 35 % @Temperature 176 °F | ISO Data | |||
| 40 % @Temperature 120 °C | 40 % @Temperature 248 °F | ASTM Test | |||
| 40 % @Temperature 120 °C | 40 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 0.970 GPa | 141 ksi | 1mm/min; ISO 527 | ||
| 0.320 GPa @Temperature 120 °C | 46.4 ksi @Temperature 248 °F | ISO Data | |||
| 0.550 GPa @Temperature 80.0 °C | 79.8 ksi @Temperature 176 °F | ISO Data | |||
| 4.00 GPa @Temperature -40.0 °C | 580 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 25.0 MPa | 3630 psi | ISO Data | ||
| 35.0 MPa | 5080 psi | ASTM Test | |||
| 154 MPa @Temperature -40.0 °C | 22300 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.740 GPa | 107 ksi | ASTM Test | ||
| 0.770 GPa | 112 ksi | ISO Data | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature -40.0 °C | 0.806 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 3.728 J/g-°C | 0.8910 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.264 W/m-K | 1.83 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection molding | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||