- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.21
- 拉伸强度 [MPa]: 43.0
- 弯曲模量 [MPa]: 0.970
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.3 % | 9.3 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 0.2 in/min; ASTM Test | ||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ISO Data | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ISO Data | |||
| 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ASTM Test | |||
| 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50mm/min; ISO 527 | ||
| 48.0 MPa | 6960 psi | 2 in/min; ASTM Test | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ISO Data | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ASTM Test | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ISO Data | |||
| 142 MPa @Temperature -40.0 °C | 20600 psi @Temperature -40.0 °F | ASTM Test | |||
| 142 MPa @Temperature -40.0 °C | 20600 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| >= 100 % | >= 100 % | ||||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| >= 100 % @Temperature 120 °C | >= 100 % @Temperature 248 °F | ISO Data | |||
| >= 100 % @Temperature 80.0 °C | >= 100 % @Temperature 176 °F | ISO Data | |||
| >= 100 % @Temperature 120 °C | >= 100 % @Temperature 248 °F | ASTM Test | |||
| Elongation at Yield | 22 % | 22 % | 50mm/min; ISO 527 | ||
| 22 % | 22 % | 2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 25 % @Temperature 80.0 °C | 25 % @Temperature 176 °F | ISO Data | |||
| 25 % @Temperature 80.0 °C | 25 % @Temperature 176 °F | ASTM Test | |||
| 30 % @Temperature 120 °C | 30 % @Temperature 248 °F | ASTM Test | |||
| 30 % @Temperature 120 °C | 30 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 1.36 GPa | 197 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM Test | ||
| 168 MPa @Temperature -40.0 °C | 24400 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.970 GPa | 141 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.210 J/cm @Temperature -40.0 °C | 0.393 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.71 J/cm @Thickness 3.17 mm | 3.20 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection molding | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||