- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 1.4
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 65.0
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 1.97
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.3 % | 8.3 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM Test | ||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ISO Data | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ASTM Test | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ASTM Test | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ISO Data | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ASTM Test | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50mm/min; ISO 527 | ||
| 65.0 MPa | 9430 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | 20 % | 20 % | 50mm/min, Nominal strain; ISO 527 | ||
| 30 % | 30 % | 2 in/min; ASTM Test | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ASTM Test | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ISO Data | |||
| 20 % @Temperature 120 °C | 20 % @Temperature 248 °F | ISO Data | |||
| 20 % @Temperature 120 °C | 20 % @Temperature 248 °F | ASTM Test | |||
| 30 % @Temperature 80.0 °C | 30 % @Temperature 176 °F | ASTM Test | |||
| 30 % @Temperature 80.0 °C | 30 % @Temperature 176 °F | ISO Data | |||
| Elongation at Yield | 15 % | 15 % | 50mm/min; ISO 527 | ||
| 15 % | 15 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 3.10 GPa | 450 ksi | 1mm/min; ISO 527 | ||
| 1.50 GPa @Temperature 120 °C | 218 ksi @Temperature 248 °F | ISO Data | |||
| 1.90 GPa @Temperature 80.0 °C | 276 ksi @Temperature 176 °F | ISO Data | |||
| 6.40 GPa @Temperature -40.0 °C | 928 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM Test | ||
| 265 MPa @Temperature -40.0 °C | 38400 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 1.97 GPa | 286 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.55 J/cm @Thickness 3.17 mm | 2.90 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Blow Molding | ||||
| Processing | Blow molding | ||||
| Injection Molding | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||