- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.9
- 缺口冲击强度: 2.39
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 7.20
- 硬度: 121.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | Melt; ISO 1183 | ||
| 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.5 % | 5.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 152 MPa | 22000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 9.30 GPa | 1350 ksi | 1mm/min; ISO 527 | ||
| 2.66 GPa @Temperature 120 °C | 386 ksi @Temperature 248 °F | ISO Data | |||
| 9.20 GPa @Temperature -40.0 °C | 1330 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 215 MPa | 31200 psi | ISO Data | ||
| 241 MPa | 35000 psi | ASTM Test | |||
| 89.0 MPa @Temperature 120 °C | 12900 psi @Temperature 248 °F | ASTM Test | |||
| 105 MPa @Temperature 93.0 °C | 15200 psi @Temperature 199 °F | ASTM Test | |||
| 130 MPa @Temperature 65.0 °C | 18900 psi @Temperature 149 °F | ASTM Test | |||
| 310 MPa @Temperature -40.0 °C | 45000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO Data | ||
| 8.00 GPa | 1160 ksi | ASTM Test | |||
| 3.04 GPa @Temperature 120 °C | 441 ksi @Temperature 248 °F | ASTM Test | |||
| 3.28 GPa @Temperature 93.0 °C | 476 ksi @Temperature 199 °F | ASTM Test | |||
| 4.04 GPa @Temperature 65.0 °C | 586 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 2.39 J/cm @Thickness 3.17 mm | 4.48 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | ISO Test | ||
| 14.0 kJ/m² @Temperature -40.0 °C | 6.66 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 7.80 J/cm² | 37.1 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| 3.8 @Frequency 1e+9 Hz | 3.8 @Frequency 1e+9 Hz | ASTM Data | |||
| 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | ASTM Data | |||
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1e+9 Hz | 0.010 @Frequency 1e+9 Hz | ASTM Data | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C | 46.7 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 1.958 J/g-°C | 0.4680 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 210 °C | 410 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||