- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 1.4
- 缺口冲击强度: 0.4
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.30
- 硬度: 121.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.3 % | 8.3 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 0.2 in/min; ASTM Test | ||
| 45.0 MPa @Temperature 120 °C | 6530 psi @Temperature 248 °F | ISO Data | |||
| 45.0 MPa @Temperature 120 °C | 6530 psi @Temperature 248 °F | ASTM Test | |||
| 115 MPa @Temperature -40.0 °C | 16700 psi @Temperature -40.0 °F | ASTM Test | |||
| 115 MPa @Temperature -40.0 °C | 16700 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | ||
| 3.0 % | 3.0 % | 5mm/min; ISO 527 | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ISO Data | |||
| 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ASTM Test | |||
| 15 % @Temperature 120 °C | 15 % @Temperature 248 °F | ASTM Test | |||
| 15 % @Temperature 120 °C | 15 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 5.22 GPa | 757 ksi | 1mm/min; ISO 527 | ||
| 1.445 GPa @Temperature 120 °C | 209.6 ksi @Temperature 248 °F | ISO Data | |||
| 2.10 GPa @Temperature 80.0 °C | 305 ksi @Temperature 176 °F | ISO Data | |||
| 6.37 GPa @Temperature -40.0 °C | 924 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 165 MPa | 23900 psi | ASTM Test | ||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ASTM Test | |||
| 200 MPa @Temperature -40.0 °C | 29000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO Data | ||
| 4.65 GPa | 674 ksi | ASTM Test | |||
| 0.995 GPa @Temperature 120 °C | 144 ksi @Temperature 248 °F | ASTM Test | |||
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.450 J/cm @Thickness 3.17 mm | 0.843 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 5.90 kJ/m² | 2.81 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.710 J/cm² | 3.38 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 97.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 53.9 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C | 15.6 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 | ||
| 197 °C | 387 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Blow Molding | ||||
| Processing | Blow molding | ||||
| Injection Molding | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||