- 熔体流动速率 [g/10min]: 93.8
- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 6.3
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 5.00
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |||
| Melt Flow | 93.8 g/10 min @Load 5.00 kg, Temperature 275 °C | 93.8 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 110 MPa | 16000 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 6.00 GPa | 870 ksi | ISO 527 | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 | ||
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| 3.90 J/cm² @Temperature -30.0 °C | 18.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature -30.0 °C | 2.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 425 V | 425 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.350 - 0.400 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.194 - 0.222 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||